• Membrane Journal
• /
• v.25 no.2
• /
• pp.107-114
• /
• 2015

PTMSP-NaA zeolite composite membranes were prepared by adding 0~50 wt% NaA zeolite to PTMSP. The membranes were characterized by FT-IR, $^1H$-NMR, GPC, DSC, TGA, SEM. The permeabilities of $H_2$ and $N_2$ gases through PTMSP-NaA zeolite composite membranes was studied as a function of NaA zeolite contents. According to TGA measurements, when zeolite was inserted into the polymer, weight loss temperature and weight loss wt% of PTMSP-NaA zeolite composite membranes were decreased. Based on SEM observation, NaA zeolite was dispersed in the PTMSP-NaA zeolite composite membrane with the size $2{\sim}5{\mu}m$. The permeability of PTMSP-NaA zeolite composite membranes increased added as NaA zeolite content increased. On the contrary, the selectivity ($H_2/N_2$) of the composite membranes decreased as NaA zeolite content increased. PTMSP-NaA zeolite composite membrane showed better permeability and selectivity ($H_2/N_2$) of $H_2$ and $N_2$ than PTMSP-NaY zeolite composite membrane.

• Membrane Journal
• /
• v.25 no.3
• /
• pp.295-300
• /
• 2015

PDMS-NaA zeolite membranes were prepared by adding 0~40 wt% NaA zeolite. Based on SEM observation, NaA zeolite was dispersed in the PDMS-NaA zeolite membranes with $2{\sim}5{\mu}m$. The permeabilities of $H_2$ and $N_2$ gases through PDMS-NaA zeolite membranes increased as NaA zeolite contents increased and $H_2$ gas had better permeabilities than $N_2$. The selectivity ($H_2/N_2$) of PDMS-NaA zeolite membranes increased as NaA zeolite contents increased.

• Membrane Journal
• /
• v.22 no.5
• /
• pp.342-351
• /
• 2012

In this study, PTMSP[poly(1-trimethylsilyl-1-propyne)]/PDMS[poly(dimethylsioxane)]-NaY zeolite and PTMSP/PDMS-NaA zeolite composite membranes were made to incorporate zeolite into PTMSP/PDMS graft copolymer in order to improve the selectivity and thermal stability, the drop of permeability by physical aging effect during long period of time for the PTMSP membrane. To investigate the physico-chemical characteristics of composite membranes, the analytical methods such as FT-IR, $^1H$-NMR, TGA, SEM, and GPC have been utilized. The gas permeability and selectivity properties of $H_2$ and $N_2$ were evaluated. The permeability of the PTMSP/PDMS-NaY zeolite and PTMSP/PDMS-NaA zeolite composite membranes than PTMSP/PDMS graft copolymer membrane increased, increased as zeolite content increased. On the contrary, the selectivity ($H_2/N_2$) of the composite membranes decreased as zeolite content increased. PTMSP/PDMS-NaA zeolite composite membrane showed better permeability and separation factor than PTMSP/PDMS-NaY zeolite composite membrane.

• Korean Journal of Soil Science and Fertilizer
• /
• v.36 no.6
• /
• pp.357-366
• /
• 2003

This study was conducted to develop n convenient and efficient granular type absorbent with high CEC from powdery zeolite, which is a waste produced while crushing the natural zeolite of Korea to get a particular particle size. The change of mineralogical characteristics during hydrothermal alternation of natural zeolite to Na-P zeolite in alkaline solution at various reaction times was determined by X-ray diffraction (XRD), scanning electron microscopy (SEM), and total elemental analysis. The columnar aggregate of Na-P Zeolite was produced by calcinating the natural zeolite-charcoal extrudates of about 3 mm diameter. In 24 hours reaction, clinoptillonite, mordenite and feldspar in natural zeolite were disappeared by 3 N NaOH treatment, while Na-P Zeolite with spherical granular structure was newly detected by XRD. As increasing reaction time, Si/Al ratio in remaining solution was deceased. The CEC of the synthesized material increased more than 2 times compared with that of natural zeolite, although the diameter of Na-P zeolite were rather increased.

• Bulletin of the Korean Chemical Society
• /
• v.20 no.5
• /
• pp.587-591
• /
• 1999

A molecular dynamics simulation study on the structure and dynamics of Na+ ions in non-rigid dehydrated Na12-A zeolite framework at 298.15 K was conducted using the same method reported in previous studies on rigid and non-rigid Na12-A zeolite frameworks. The agreement between the experimental and calculated results for the zeolite-A framework atoms of structural parameters for non-rigid dehydrated Na12-A zeolite is generally quite good, and for the adsorbed Na+ions the agreement is acceptable. The calculated bond lengths are generally in good agreement with the experimental results and other theoretical data. The calculated IR spectrum by Fourier transform of the total dipole moment autocorrelation function shows two major peaks around 2700 cm-1 and 7000 cm-1. The former appeared in the calculated IR spectra of non-rigid zeolite-A framework only system and the latter remains unexplained except, perhaps, indicating a new formation of a vibrational mode of the framework due to the adsorption of Na+ ions. The peaks above 6200-6800 cm-1 in non-rigid dehydrated Nal2-A zeolite are much larger than those in non-rigid dehydrated H12-A zeolite.

• Membrane Journal
• /
• v.24 no.4
• /
• pp.285-291
• /
• 2014

The PTMSP[Poly(1-trimethylsilyl-1-propyne)]-NaY zeolite composite membranes were prepared by adding 0~50 wt% NaY zeolite to PTMSP. In order to investigate the characteristics of these membranes, we used the analytical methods such as FT-IR, $^1H$-NMR, GPC, DSC, TGA, and SEM. Gas permeation experiments were carried out at $23{\sim}26^{\circ}C$, $2kgf/cm^2$, and the permselectivity of $H_2$ and $N_2$ gases through the composite membranes was studied as a function of the NaY zeolite contents. According to TGA measurements, when NaY zeolite was inserted within the PTMSP, thermal stability of PTMSP was enhanced. Based on SEM observation, NaY zeolite was dispersed in the PTMSP-NaY zeolite composite membrane with a size of $1.5{\mu}m$. The permeability of $H_2$ and $N_2$ through the PTMSP-NaY zeolite composite membranes increased as NaY zeolite content increased. On the contrary, the selectivity($H_2/N_2$) of the PTMSP-NaY zeolite composite membranes decreased as zeolite content increased.

• Applied Chemistry for Engineering
• /
• v.16 no.1
• /
• pp.61-67
• /
• 2005

Zeolite membranes show better thermal, mechanical, chemical stabilities than polymer membranes. Water was separated from water/ethanol mixtures by pervaporation using the NaA and the NaY zeolite membranes synthesized in our laboratory. The effects of concentration of ethanol at the feed side and temperature were studied on the permeation flux and separation factor of water. The separation factors obtained with the NaA zeolite membrane was found to be 1000 times higher than those obtained with the NaY. However, the water flux through the NaA zeolite membrane was observed to be lower than 1/2 of that through the NaY zeolite membrane.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.1 no.2
• /
• pp.33-40
• /
• 2000

The present invention relates to a absorption rotor for removed VOC(volatile organic compound) and humidity in semiconductor clean room system. A absorption rotor medium is made by NaX zeolite and TS-1 zeolite formed on a honeycomb matrix of ceramic papers. The crystallization of NaX zeolite was hydrothermal reaction, and NaX zeolite crystals of a uniform particle size of 5$\mu$m were synthesized that NaX zeolite seed crystals (2~3$\mu$m) added in a batch composition at levels of 3~15 wt$\%$. The seeding resulted in an increase in the fraction of large crystals compared with unseeded batches and successfully led to a uniform NaX zeolite crystal. The microporous zeolite-type titanosilicate(TS-1) was synthesized by different of the reactant solution pH. The pH range of reactant solution has been changed from 10.0 to 11.5 TS-1 zeolite (ETS-10), having a large pore(8~10 $\AA$), was synthesized at 10.4 of pH, since TS-1 zeolite (ETS-4), having a small pore(3~5$\AA$), was synthesized at 11.5 of pH.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.1
• /
• pp.6-13
• /
• 1999

NaX zeolite crystal were grown from seed elements of synthetic NaX(2~3$\mu\textrm{m}$) Powder in a mother liquor having an approximate reactant composition ${4.12{Na}_{2}O{\cdot}{Al}_{2}{O}_{3}{\cdot}3.5{SiO}_{2}{\cdot}593{H}_{2}O$.The result was that crystallization time of NaX zeolite was reduced with adding seed materials to the initial mixture and crystal size was reduced . but with increasing crystallization time, NaX zeolite. In this study, We investigated detailed factors which NaX crystal has been determined by a combination of SEM, XRD, FT-IR, and BET.

• Applied Biological Chemistry
• /
• v.25 no.2
• /
• pp.99-104
• /
• 1982

Natural zeolite rock was pulverized and dispersed in water. Clay fraction was collected by sedimentation method. The dominant clay mineral was Clinoptiolite with some Mordenite and Smectite. $P^{32}$ adsorption on Na-zeolite was determined in different ionic strengths using $P^{32}$ isotope by sludge method. The lower the pH of suspension, the longer the contact time, and the more the amount of zeolite, the more inorganic P was adsorbed by Na-zeolite, whereas the more P adsorption per unit gram of zeolite was observed at a 100mg addition than a 200mg in same volume of P-NaCl solution (20ml), indicating that the whole positively charged surface of Na-zeolite was not occupied by inorganic P. Furthermore, the more P adsorption on Na-zeolite was observed in higher ionic strength than in the lower. The maximum P adsorption on Na-zeolite was about 1me/g, and the zero point charge (ZPC) is assumed to be below pH 3.7.