• Journal of the Korean Society for Precision Engineering
• /
• v.27 no.2
• /
• pp.40-49
• /
• 2010

The Purpose of this paper is to weld a rapid palatal expander using a continuous wave Nd:YAG laser. The rapid palatal expander has become a useful treatment method for severe maxillary transverse deficiencies and posterior crossbites. Rapid maxillary expansion is a well-established method to correct transverse maxillary deficiency and arch length discrepancy. The major process parameters studied in the present laser welding experiment were the positions of focus, laser power and travel speed of laser beam. We measured the fusion zone size and its shape using an optical microscope for the observation of cross-sectional area and tension stress of a rapid palatal expander welded. Through the experimental investigation, the optimum speeds and power of laser without deficiencies of weld cross-sectional area were obtained.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1998.04a
• /
• pp.292-299
• /
• 1998

Case hardening behavior of tool steel(SK5) was investigated after YAG laser irradiation. In the case of beam passes, martensite formed in the melt zone and in former pearlite regions of the austenization zone exhibited very high Vickers Hardness values. The molten depth and radius, micro structure, hardness were investigated as a function of defocusing distance, pulse width, and power density.

• Laser Solutions
• /
• v.8 no.1
• /
• pp.27-37
• /
• 2005

During laser spot welding of the braun tube electron gun, phenomena such as serious spattering and oxidative reaction, etc. were occurred. The spatter occurred from weld pool affects the braun tube, namely it blocks up a very small hole on the shadow mask and causes short circuit between two poles of the electron gun. We guessed that high power density and oxidative reaction are main sources of these problems. So, we studied to prevent and to reduce spatter occurring in spot welding of the braun tube electron gun using pulsed Nd:YAG laser. The characteristics of laser output power was estimated, and the loss of laser energy by optical parameter and spatter was measured by powermeter. The effects of welding parameters, laser defocused distance and incident angle, were investigated on the shape and penetration depth of the laser welded bead in flare and flange joints. From these results, the laser peak power was a major factor to control penetration depth and to occur spatter. It was found that the losses of laser energy by optic parameter and sticked spatter affect seriously laser weldability of thin sheets.

• Journal of Oral Medicine and Pain
• /
• v.24 no.4
• /
• pp.397-410
• /
• 1999

In order to obtain the basic data concerning the optimal parameters in using Nd:YAG laser as a therapeutic modality to dentinal hypersensitivity, the author prepared 3 sections of sound dentin and 10 sections of sclerotic dentin with thickness of $0.5mm{\pm}0.1mm$ from human extracted teeth of anteriors and premolars, and applied the laser energy from a fiberoptic delivered, free running, pulsed Nd:YAG laser (wavelength 1064nm, pulse duration $120{\mu}sec$, fiber diameter $320{\mu}m$) to surfaces of sound and sclerotic dentin sections for 1 second with contact/unidirectional moving mode of the fiber under speed of 3mm~4mm/sec and parameters of 0.5W/10Hz, 1.0W/10Hz, 1.5W/10Hz, 2.0W/10Hz: $62J/cm^2$, $124J/cm^2$, $187J/cm^2$, $249J/cm^2$. The author comparatively evaluated the characteristics of ultrastructural changes on surfaces of sound and sclerotic dentin sections irradiated by the pulsed Nd:YAG laser using the scanning electron microscopy. A fairly ill-defined bordered surface of partially closed and melted dentinal tubules can be seen on the scanning electron microscopic feature of the sound dentin surface irradiated by the pulsed Nd:YAG laser with energy density of $62J/cm^2$. The physical modification of sound dentin surface extensively occurred depended on the increase of energy density from $62J/cm^2$ to $124J/cm^2$, $187J/cm^2$, $249J/cm^2$. While, a fairly well-defined bordered surface of partially closed and melted dentinal tubules with thickened peritubular dentin can be seen on the scanning electron microscopic feature of the sclerotic dentin surface irradiated by the pulsed Nd:YAG laser with energy density of $62J/cm^2$. The physical modification of sclerotic dentin surface of a fairly rough, shallow depression with many cracks, thickened peritubular dentin and structureless dentinal tubules extensively occurred depended on the increase of energy density from $62J/cm^2$ to $124J/cm^2$, $187J/cm^2$, $249J/cm^2$ compared to those of sound dentin surface irradiated by the pulsed Nd:YAG laser under the same parameters. Therefore, it is recommended that the pulsed Nd:YAG laser as a therapeutic modality to dentinal hypersensitivity should be applied with the less energy density than $62J/cm^2$ on the sound dentin surface, and its energy density on the partially sclerotic dentin surface should be lower than that on the sound dentin surface to preserve tooth from unnecessary excessive structural destruction.

• Journal of Periodontal and Implant Science
• /
• v.27 no.4
• /
• pp.819-828
• /
• 1997

The purpose of this study was to evaluate the abrasion-resistance of root surface after NaF iontophoresis, Nd:YAG laser irradiation and combined treatment 50 anterior teeth with flat interproximal root surface that had been extracted due to periodontal destruction were selected. All teeth were treated by the same procedure as conventional periodontal root treatment, such as scaling and root planing, root conditioning with tetracycline HCI(lOOmg/ml, 5min). The pre-treatment weight of each tooth was measured by a dial scale(SHIMADEU Co, LIBROR EB-220HU, capacity 220.000 g, Japan). All teeth were divided into 5 groups as follows: Nd:YAG laser irradiation(group 1, 1 W, 100 mJ, 10Hz, fiberoptic-root surface distance=5mm, $10\;sec.{\times}6times$, EL.EN.EN060, Italy): NaF iontophoresis(group 2, $150{\mu}A$, 4 min}: Nd:YAG laser irradiation following NaF iontophoresis(group 3): NaF iontophoresis following Nd:YAG laser irradiation(group 4): No treatment(control group). Electric toothbrushing (Oral-B, Brown Co, Germany) was conducted during 1 hour($lO\;min.{\times}6\;times$). Subsequently post-treatment weight was remeasured by the same method as pre-treatment weight measurement. The difference of abrasion rate among all groups was statistically analyzed by ANOVA(SAS program). Following results were obtained: 1. The abrasion rate was significantly lower in Nd:YAG laser irradiation group than NaF iontophoresis group(p < 0.001). 2. The abrasion rate was significantly lower in combined groups of Nd:YAG laser irradiation and NaF iontophoresis than either Nd:YAG laser irradiation group or NaF iontophoresis group(p < 0.001). 3. There was no significant difference in abrasion rate according to application order in the combined groups(p > 0.05). 4. The abrasion rate was significantly lower in all experimental groups than control group(p < 0.001). The results suggest that combined treatment of Nd:YAG laser irradiation and NaF iontophoresis on exposed root surface after periodontal therapy can enhance the abrasion-resistance of root surface and may inhibit the root caries development.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.4C no.3
• /
• pp.96-100
• /
• 2004

The Nd： YAG laser is commonly used throughout many fields such as accurate material processing, IC marking, semiconductor annealing, medical operation devices, etc., due to the fact that it has good thermal and mechanical properties and is easy to maintain. In materials processing, it is essential to vary the laser power density for specific materials. The laser power density can be mainly controlled by the current pulse width and pulse repetition rate. It is important to control the laser energy in those fields using a pulsed laser. In this paper we propose the constant-frequency current resonant half-bridge converter and monitoring of capacitor charging voltage. This laser power supply is designed and fabricated to have less switching loss, compact size, isolation with primary and secondary transformers, and detection of capacitor charging voltage. Also, the output stabilization characteristics of this Nd： YAG laser system are investigated. The test results are described as a function of laser output energy and flashlamp arc discharging constant. At the energy storage capacitor charges constant voltage, the laser output power is 2.3％ error range in 600[V].

• Laser Solutions
• /
• v.10 no.4
• /
• pp.1-6
• /
• 2007

This study includes the effects of shielding gas types and flow rate on Nd:YAG Laser weldability of sintered material. The types of shielding gas were evaluated for He, Ar and N2. Bending strength, porosity rate, hardness and aspect ratio testing of laser weld are carried out to evaluated the weldability. As a results, Ar gas was showed the best welding strength even it has the most porosity content on weld metal, and depend on increases the gas flow rate, it was not only got deeper penetration depth but also showed higher bending strength. Therefore we could know that bending strength is not only affect the porosity content but also melting area.

• Proceedings of the KWS Conference
• /
• 2006.05a
• /
• pp.248-250
• /
• 2006

The study on a surface transformation hardening of a rod-shaped SM45C carbon steel is carried out by using CW Nd:YAG laser. Conventionally, $CO_2$ laser has been usually used as a laser source for a transformation hardening. however, it is needed to an additional absorbent coating like a colloidal graphite owing to a lower absorbtion rate. On the other hand, no cost and post-removal process of coating is required to Nd:YAG laser, due to a higher absorbtion rate relatively. Moreover, there is a merit which is capable of building up the more flexible processing system resulted from a beam delivery through a optical fiber. In this study, we were going to recognize characteristics of a transformation hardening using a optic head with a gaussian beam distribution.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.28 no.4
• /
• pp.481-488
• /
• 2004

Laser chemical vapor deposition can be used as a new approach for a rapid prototyping technique. The purpose of the study is to fabricate several 3-dimensional objects that are relatively simple as well as to find the characteristics of SiC rod growth that is the first step in developing a new rapid prototyping technique with laser chemical vapor deposition. In the study, SiC rods were generated with varying precursor pressure for 5 minutes. Deposition rates with varying precursor pressure, shapes of rods, surface roughness and component organization were investigated, in particular. Finally, several simple objects like a branch or a propeller were successfully fabricated using laser chemical vapor deposition.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2002.10a
• /
• pp.85-89
• /
• 2002

This paper used the Laser Speckle Interferometry to present the strain analysis of Nd:YAG Laser welding zone. Previous TIG welding to sheet plate, which welds only high-skilled engineer, produces residual stress nearby welding zone due to thermal effect. However, Laser welding makes sheet pate welding easy and thermal effect minimum. Thermal effect zone is measured by strain analysis of the laser-welding zone by ESPI under tensile testing of sheet plate welded by Nd:YAG laser. The ESPI results, which compared with strain gage method, are agreed within error 3 %.