• 한국세라믹학회지
• /
• 제26권3호
• /
• pp.395-401
• /
• 1989

The concentrations of Cu(II), Y(III) and Ba(II) ionic species in aqueous solution due to the formation of Cu2+-oxalate-complex have been theoretically calculated with respect to pH and their solubility diagrams could be obtained. It was verified from the calculation that the excess of Cu2+ and Ba2+ should be added in order to obtain oxalate coprecipitates with the molar ratio of Y : Ba : Cu=1 : 2 : 3. The exact amount of excess species has been calculated with respect to the initial concentrations of metal ions and pH.

• E2M - 전기 전자와 첨단 소재
• /
• 제5권3호
• /
• pp.278-283
• /
• 1992

123 초전도체에 마그네틱 모멘트가 큰 Ni불순물을 도핑하여 제작한 $Y_{1}$ Ba(C $u_{2.9}$ $N_{0.1}$) $O_{7-{\delta}}$ 초전도체의 X-ray diffraction pattern, susceptibility, 온도변화등에 따른 전류-전압관계, 임계온도 등에 대하여 연구하였다. 제작된 시료는 매우 뚜렷한 orthorhombic 피크를 가진 123상을 나타내고 있었다. N=0.1의 시료에서는 적은 양의 Ni 불순물과 단면적인 무정형상태의 잘 반응된 YBa(Cu, Ni)$_{3}$ $O_{7-{\delta}}$의 orthorhombic구조를 나타내고 있다. 전반적인 실험 결과로 부터 Ni는 Y-Ba-Cu-O 초전도 시스템에서 초전도에 중요한 역할을 담당하지 않는다는 결론을 얻었다.얻었다.다.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1996년도 재료학회 춘계학술발표회
• /
• pp.152-152
• /
• 1996

• E2M - 전기 전자와 첨단 소재
• /
• 제3권1호
• /
• pp.52-58
• /
• 1990

YBa$_{2}$ Cu$_{3}$O$_{7-{\delta}}$의 Ba대신 K를 일부 치환시킨 Y(Ba$_{1-x}$ , $K_{x}$ )$_{2}$Cu$_{3}$O$_{y}$ 에서 x의 값에 따른 초전도 특성의 변화를 연구하였다. XRD 무늬와 Infrared의 투과율로써 상의 변화를 관측하고 온도에 따른 전기저항의 변화를 측정함으로써 초전도성을 조사하였다. Ba 대신 K의 양이 증가할수록 Y(Ba$_{1-x}$ ,K$_{x}$)$_{2}$Cu$_{3}$O$_{y}$ 는 다중상이 되어 갔고 전기저항이 0이 되는 T$_{c}$는 점점 더 낮은 온도로 이동하다가 x.geq.0.6이 되면 초전도 특성을 잃었다.을 잃었다..

• 한국재료학회지
• /
• 제4권4호
• /
• pp.428-438
• /
• 1994

Y-Ba-Cu-O 계에서 123상의 성장에 미치는 Sn의 효과를 관찰하기 위하여 Sn이 첨가된 123+Sn성형체와 Sn이 첨가되지 않은 123성형체와의 couple시편을 만들었다. $1100^{\circ}C$에서 24시간 유지한 후 $970^{\circ}C$에서 1시간 유지한 시편에서 123상은 Sn이 첨가된 123+Sn 성형체의 표면에서부터 생성되어 Sn이 첨가되지 않은 123성형체 내부쪽으로 성장하였다. $1100^{\circ}C$에서 48시간 유지한 후 $970^{\circ}C$에서 1시간 유지한 시편에서는 123상이 관찰되지 않았으며 Y-Ba-Sn으로 구성된 결정립이 관찰되었다.

• 한국초전도ㆍ저온공학회논문지
• /
• 제14권4호
• /
• pp.28-31
• /
• 2012

We report the solid-liquid phase equilibria on the $GdBa_2Cu_3O_{7-{\delta}}$ (GdBCO) stability phase diagram in low oxygen pressures ($PO_2$) ranging from 1 to 100 mTorr. On the basis of the GdBCO stability phase diagram experimentally determined in low oxygen pressures, the isothermal sections of three different phase fields on log $PO_2$ vs. 1/T diagram were schematically constructed within the $Gd_2O_3-Ba_2CuO_y-Cu_2O$ ternary system, and the solid-liquid phase equilibria in each phase field were described. The invariant points on the phase boundaries include the following three reactions; a pseudobinary peritectic reaction of $GdBCO{\leftrightarrow}Gd_2O_3$ + liquid ($L_1$), a ternary peritectic reaction of $GdBCO{\leftrightarrow}Gd_2O_3+GdBa_6Cu_3O_y$ + liquid ($L_2$), and a monotectic reaction of $L_1{\leftrightarrow}GdBa_6Cu_3O_y+L_2$. A conspicuous feature of the solid-liquid phase equilibria in low $PO_2$ regime (1 - 100 mTorr) is that the GdBCO phase is decomposed into $Gd_2O_3+L_1$ or $Gd_2O_3+GdBa_6Cu_3O_y+L_2$ rather than $Gd_2BaCuO_5+L$ well-known in high $PO_2$ like air.

• 한국초전도ㆍ저온공학회논문지
• /
• 제1권1호
• /
• pp.1-6
• /
• 1999

The microstructures of top seed mult processde $\textrm{YBa}_2\textrm{Cu}_3\textrm{O}_7$.$\delta$ single crystal were studied. Although shape of the seed was not faceted. the growth shape of Y123 single crystal was faceted. It was observed that Y211 phases were trapped in specific spaces of the faceted region. From the microstructural investigation. it was suggested that the segregation of Y211 is due to the difference of growth rates in crystal direction. When a single crystal was grown by the single seed with stepped multi surfaces. a microstrue was grown from multi-seed. The microstructure show the possibility of multi-seed growth. Corn kernel like structure without Y211 phase was observed and seemed to be formed by the diffusion reaction between Y211 phase in crystal and liquid wetted on the crystal. the diagonal line on Y123 crystal was observed that it was formed by the corn kernel like structure.

• Progress in Superconductivity
• /
• 제7권1호
• /
• pp.77-82
• /
• 2005

We report a successful fabrication of high-quality $SmBa_{2}Cu_{3}O_{7-{\delta}}$ (SmBCO) thin films on $LaAlO_3$(LAO)(100) single crystalline substrates by a modified TFA-MOD method. After the pyrolysis heat treatment of spin-coated films up to $400^{\circ}C$, SmBCO films were fired at various temperatures ranging from 810 to $850^{\circ}C$ in a reduced oxygen atmosphere (10 ppm $O_2$ in Ar). Optimally processed SmBCO films exhibited the zero-resistance temperature ($T_{c,zero}$) of 90.2 K and the critical current density ($J_c$) of $0.8\;MA/cm^2$ at 77K in self-field. Compared with the $J_c$ values (normally, > $2\;MA/cm^2$ at 77 K) of MOD-TFA processed YBCO films, rather depressed $J_c$ values in SmBCO films are most probably attributed to the existence of ${\alpha}$-axis oriented grains.

• 대한화학회지
• /
• 제36권1호
• /
• pp.16-23
• /
• 1992

고온초전도체 $YBa_2Cu_3O_{7-{\delta}}$에서 Y를 Eu로 치환시킨 $(Y_{1-x}Eu_x)Ba_2Cu_3O_{7-{\delta}}$ (x = 0.0, 0.2, 0.4, 0.6, 0.8, 1.0)를 제조한 후 물성변화를 관찰하였다. X-선 회절분석결과 모든 시료가 사방정계 구조를 갖고 있었으며 x값이 증가함에 따라 격자상수 a, b 및 c도 증가하였다. 전기저항과 자화율측정으로부터 순수한 90K 이상의 고온초전도상이 생성되었음을 알았으며, x값이 커짐에 따라 임계온도가 상승하였다. 주사전자현미경을 사용하여 구한 낟알크기와 자화측정결과로부터 각각의 시료들에 대한 부피 반자성자화율을 구하였으며, x값이 커질수록 이 값은 감소하였다. Eu의 농도가 증가함에 따라 결정격자내의 Ba의 양이 감소됨을 EPMA로 확인하였으며, 이것은 부피반자성 자화율의 감소에 직접적인 영향을 주는 것으로 판단된다.

• 한국전기전자재료학회논문지
• /
• 제11권9호
• /
• pp.752-757
• /
• 1998

Rotational Magnetization-vector measurements have been performed on a polycrystalline $Y_1Ba_2Cu_3O_{7-\delta}$ sample in field-cooled condition at 4.2 K. The experimental results show that vortex flux density(B) consists of 3 groups :(1) a weak pinning part ($B_w$) which stays at a fixed angle relative to the magnetic field f(H) ; (2) a strong pining part($B_s$) which rotates rigidly with the sample and has same magnitude with the sample rotation, and(3) and intermediated pining part ($B_i$) which rotates rigidly with the sample, but whose magnitude changes with the sample rotation Our results have been explained in terms of a distribution in the strength of the vortex pinning torque and a repulsive intervortex torque.