• Journal of the Korean Wood Science and Technology
• /
• v.25 no.4
• /
• pp.29-38
• /
• 1997

The effect and control of wood property of reconstituted composite panels for improved board properties by wood-waste materials and development of combination method for heterogeneous materials have been of interest to the wood science researchers. The purpose of this study is to consider the properties in relation to hot pressing conditions and to develope the optimum hot pressing condition with waste wood and waste tire for the manufacturing of composite boards. The study of composite boards for recycling of wood and waste tire is nothing up to the present. Physical and mechanical properties such as specific gravity, moisture content, swelling coefficient, modulus of rupture and modulus of elasticity in bending test were studied. The condition of 3-stage press time for the lowest moisture content of composite board was $4{\rightarrow}3{\rightarrow}3$ minutes. Specific gravity of composite panels was affected mainly by the amount of rubber chip. Because of the low rigidity and high elasticity in rubber chip, it is considered the composite panel was adequate material in the place of compression load, but not bending load. Therefore, it was concluded that a use of rubber-based wood composite panel is proper to the interior materials such as floor a room than exterior materials. From the test results, the most optimum hot pressing conditions were $4{\rightarrow}3{\rightarrow}3$ minutes for 3-stage press time and $45{\rightarrow}20{\rightarrow}5kg/cm^2$ for 3-stage press pressure. The rubber-based wood composite panel was very excellent in elasticity by combination of rubber chip in comparison with existing other wood-based materials. Therefore, it was considered that rubber-based wood composites can be applicable to every interior materials such as floor a room and will be expected to effective reuse and recycle of waste tires and wood-waste materials, and will be contribute to protection of environment pollution in earth.

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.4
• /
• pp.505-514
• /
• 2016

To study mechanical properties of fiberglass reinforced wood-based composite (FRWC), fiberglass with a diameter of $20{\mu}m$ was selected to prepare test specimens. Mechanical properties of fiberglass reinforced wood-based composite were determined by three-point-bending test while its microstructure was characterizes by scanning electron microscopy (SEM). The results showed that mechanical properties of fiberglass reinforced wood-based composite were superior to that of the wood fiberboard based on the contrasting mechanical curves and the analysis of fracture mechanism. It is believed that the material design with this "sandwich" structure brings a unique buffering capacity of fiberglass into play in the composites. So the specimen did not produce a sudden fracture failure at high level of applied loads because it had a bearing ability. The SEM analysis showed that the working strength of PVAc adhesive was high; under a bearing force, it could properly transfer a load. In addition, glass fiber mesh and wood fiber board combined well.

• Journal of the Korean Wood Science and Technology
• /
• v.41 no.1
• /
• pp.58-63
• /
• 2013

This study is a basic research for practical applications of carbonized boards, which measured thermal conductivity and electrical properties of carbonized boards manufactured at different carbonization temperature ($400{\sim}1,100^{\circ}C$) using a medium density fiberboard, particleboard, plywood and wood (Fraxinus rhynchophylla). The highest value of thermal conductivity was 0.1326 m/k at carbonization temperature of $900^{\circ}C$ in the carbonized particleboard. Overall, the higher density of carbonized board, thermal conductivity was faster. As the electrical resistivity decreased with increased carbonization temperature, it was almost close to conductor after carbonization temperature of $1,000^{\circ}C$. When electricity has worked on the carbonized board by high voltage, the current and the electric power increased and surface temperature of carbonized board was high.

• Journal of the Korean Wood Science and Technology
• /
• v.42 no.2
• /
• pp.163-171
• /
• 2014

Environmental issues about indoor air quality have been increased and focused on volatile organic compounds (VOCs) caused cancer, asthma, and skin disease. Reducing VOCs has been attempted in many different methods such as using environmentally friendly materials and air cleaner or purifier. Charcoal is well known material for absorbing VOCs. Therefore, carbonized board from medium density fiberboard has been developed. We assumed that the source of carbonized boards can be any type of wood-based panels. In this study, carbonized boards were manufactured from oriented strand board (OSB) at 400, 600, 800, and $1000^{\circ}C$. Each carbonized OSB (c-OSB) was evaluated and determined physiomechanical characteristics such as exterior defects, dimensional shrinkage, modulus of elasticity, and bending strength. No external defects were observed on c-OSBs at all carbonizing conditions. As carbonizing temperature increased, less porosity between carbonized wood fibers was observed by SEM analysis. The higher rate of dimensional shrinkage was observed on c-OSB at $1000^{\circ}C$ (66%) than c-OSB at 400, 600, and $800^{\circ}C$ (47%, 58%, and 63%, respectively). The densities of c-OSBs were lower than original OSB, but there was no significant different among the c-OSBs. The bending strength of c-OSB increased 1.58 MPa (c-OSB at $400^{\circ}C$) to 8.03 MPa (c-OSB at $1000^{\circ}C$) as carbonization temperature increased. Carbonization temperature above $800^{\circ}C$ yielded higher bonding strength than that of gypsum board (4.6 MPa). In conclusion, c-OSB may be used in sealing and wall for decorating purpose without additional artwork compare to c-MDF which has smooth surface.

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.3
• /
• pp.424-429
• /
• 2016

In this study, the carbonized boards were manufactured from different types of wood-based panel and then their moisture absorption/desorption properties were investigated and compared. The carbonization temperature was maximum $600^{\circ}C$ with 2 h maintains. Test results showed higher absorption/desorption capacity on carbonized plywood than carbonized MDF, PB, and OSB, respectively. However, carbonized MDF, OSB, and plywood had similar absorption/desorption rate per hour. It means carbonized OSB and plywood can transfer moisture into deeper side and then possibly hold more amount of water. Based on SEM images, carbonized OSB and plywood showed more like wood structure, while carbonized MDF and PB had only wood fiber or/and chunk of wood fragments. Therefore, original wood structure may affect moisture absorption/desorption capacity. In order to manufacture high moisture absorbing/desorbing carbonized board, wood structure should be considered and then carbonized.

• Journal of the Korean Wood Science and Technology
• /
• v.28 no.3
• /
• pp.9-13
• /
• 2000

Wood demand is increasing more and more, but world has been confronted with decreasing forest resources. Korea has to depend upon foreign wood and wood-based products for more than 95 percent of total domestic demand per year. In order to heighten self-sufficiency for wood supply and demand, we have to develop wood substitutes. Rice hull is the cheapest agricultural by-product we can get in Korea, more over the production of rice hull amounts to 1 million tons per year. This study was carried out to utilize rice hull and to decide the optimum condition of rice hull pretreatment for manufacture of rice hull board. Steam explosion method gave the best result, and the next boiling treatment of 1 hour, the last 1 hour treatment with 1% NaOH solution. Optimum conditions of explosion method were 20kgf/$cm^2-1$ minute and 25kgf/$cm^2-1$ minute. Rice hull board made with exploded rice hull met the KS standard(KS F 3104, 1997) and showed the same strength as a control, PB. And also the 1 hour boiling treatment was more effective than the 1 hour treatment with 1% NaOH solution.

• Journal of the Korean Wood Science and Technology
• /
• v.41 no.1
• /
• pp.33-41
• /
• 2013

This study was performed to analyse cause of quality deterioration using byproduct of plywood and to determine physical and mechanical properties of particleboard used new bonding condition we found. The result of bending strength of Com-Ply board using EMDI is 57.7 $N/mm^2$ on linear direction and 25.1 $N/mm^2$ on vertical direction. EMDI has better water-resisting qualities than Urea formaldehyde adhesive according to result of thickness swelling and water absorption test. Pre-treatment soaked particle 72 hours in water caused increase of HCHO emission.

• Journal of the Korean Wood Science and Technology
• /
• v.15 no.2
• /
• pp.99-104
• /
• 1987

Fiber mats were made at various density levels, using fibers from papermill sludge, ricestraw and various mixtures of the two. The paper mill sludges were collected from Moorim Papermill Co, and Jeonjoo Papermill Co. They were soaked in the liquid sulfur compounds, sulfur-tall oil and sulfurpolyester compounds, and made into fiber-reinforced, sulfur-based composition board. Under optimum conditions of fiber mat preparation and saturation with molten sulfur and modified sulfur, the Young's moduls of the manufactured tiber-reinforced composition board are superior to those of conventional wood-based composition boards. For example, the moduli of elasticity of the composition board made from papermill sludge, with a density of 0.40gm/$cm^3$, were greater than 1,400,000psi as compared 800,000psi for high density hardboard(1.28gm/$cm^3$). The modulus of rupture of the best reinforced composition board manufactured was over 9000psi, comparable to 6000psi of high density hardboard. The proposed Bryant and Lee's theory, "Modified Rule of Mixtures" can be applicable to the nonoriented and short fibrous composition board, when it was modified from "Rule of Mixtures" established by Paul an Jones, and supplemented by Smith and Cox's theory, In the Bryant and Lee's theory of $E_c=\frac{1}{3}aE_fV_f+bE_mV_m$, the constants "a" and "b" for the composition boards made from papermill sludge and the mixtures of ricestraw and the sludge were identified to be in the ranges of 3.29~3.54 and -2.47~-2.80 respectively.

• Journal of the Korean Wood Science and Technology
• /
• v.13 no.3
• /
• pp.49-53
• /
• 1985

The effects of pre-treatments, the hot water extraction of wood meal and the addition of chemical ($CaCl_2$) to wood-cement water system on the properties of wood-cement composite such as modulus of rupture (MOR), modulus of elasticity (MOE), water sorption ratio and swelling ratio of resulting boards were studied in this experiment. The wood meals through 0.83mm(20 mesh) and retained on 0.42mm(35 mesh) screen were prepared from Pinus densiflora S. at Z. and Larix leptolepsis G. For hot water extraction, 500 grams of wood meal for each species were heated to boiling with 1,500ml of distilled water in 2-liter beaker for 6 hours. Every 2 hours, the wood meals were washed with boiling distil1ed water and reheated to boiling again. After 6 hours boiling, the boiled wood particles were collected by pouring this particles on 200 mesh screen. The collected particles then washed twice with hot distilled water and dried for 24 hours in an oven at $109{\pm}20^{\circ}C$. A mixture of 663.4 grams of cement with 331.7 grams of wood meal based on oven-dry weight were dry-mixed in a plastic vessel. The mixture was kneaded with 497.6ml of distilled water in the ratio of 1.5ml of water to a gram of wood meal. To add calcium chloride to the mixture as an accelerator, $CaCl_2$ 4% solution by weight per volume, was added to pine-or larch-cement board in the ratio of 3% to cement weight. To set wood-cement board, this mixture was clamped at 30cm ${\times}$ 30cm, in thickness of 1.5cm for 3 days at room temperature, declamped and then placed at open condition for 17 days. The target density was 1.0. The four specimens sized to 5cm in width and 28cm in length were used for MOR and MOE test for each treatment. After MOR test, the tested specimens were cut to the size of 5cm ${\times}$ 5cm for water sorption and swelling test. The twenty specimens used to measure the water sorption ratio (soaking 24 hours) and ten of these were used for swelling ratio measurement The results obtained were as follows: 1) Larch was not suitable for wood-cement boards because larch-cement board developed no strength, but pine showed 97.9kg/$cm^2$ by hot water extraction. 2) To increase MOR, hot water extraction was more effective than the addition of $CaCl_2$ in pine and larch because the $CaCl_2$ addition was seemed to speed up the ratio of cement hydration without reacting with the wood substances. 3) The water sorption ratio was lowered by the addition of $CaCl_2$ to wood-cement system because the chemical additive accelerated the rate of cement hydration. 4) In pine-cement board, the swelling ratio from 0.37 to 0.42 percent was observed in length and the swelling ratio from 0.88 to 2.0 percent in thickness. As a rule, the swelling ratio of wood-cement board was very low and the swelling ratio in thickness was higher than in length.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.47 no.1
• /
• pp.1-9
• /
• 2015

Wood fibers for medium density fiberboard (MDF) was used in the filler layer of the white duplex board for increasing thickness and bulk of the board. The MDF fibers were treated with ozone (3% based on dry weight of the fibers), and mixed together with OCC (old corrugated container) to form paper. Ozone-treated MDF fibers gave high bulk, high tensile strength, high internal bond and fast drainage to the furnish mixed with OCC. It was shown that there were possibilities to reduced basis weight of the filler layer without loss of thickness, stiffness, and tensile strength. Furthermore, it showed the possibility to develop a new kind of board product that has high stiffness as well as high strength properties with light basis weight by application of the ozone-treated MDF fibers.