• 수산해양기술연구
• /
• 제36권2호
• /
• pp.132-138
• /
• 2000

The effect of fluid flow on corrosion and erosion-corrosion of metal is a well-recognized phenomenon in pipelines and machinery equipment, and so on. Not only are fluid hydrodynamics important, but also the corrosiveness of the process or production stream affects the corrosion system. Recent research demonstrates that it is possible to erosion-corrosion(E/C) phenomena in terms of hydrodynamics, electrochemical corrosion kinetics and film growth/removal phenomena. Stress corrosion cracking behavior under cavitation erosion-corrosion of mild steel(SS41) was investigated of base metal and weldment under loaded stress. Main result obtained are as follows : 1) The cavitation erosion sensitivity of base metal affected weight loss is more susceptive than heat affected zone, 2) The corrosion sensitivity affected weight loss of welding heat cycle is less susceptive on stress corrosion under cavitation erosion-corrosion than stress corrosion.

• 한국철도학회논문집
• /
• 제15권6호
• /
• pp.597-603
• /
• 2012

본 연구에서는 바이어스 궤도계전기의 접점재료를 선정하는데 있어 Ag 접점과 AgC 접점의 문제점을 분석하고, 안전성을 평가하는데 목적이 있다. 접점의 용착실험과 반복개폐 실험을 실시하여 접점의 특성을 알아보았다. 실험 결과, Ag 접점은 비교적 낮은 전류에서 용착이 발생하였고, AgC 접점은 온도특성이 우수하여 대전류에서도 용착이 발생하지 않았다. 반복개폐 실험에서는 AgC 접점의 개폐횟수가 증가할수록 저항이 불안정하고 접점에 전이현상이 발생하여 접점소모가 큰 것으로 나타났다. 연구 결과, AgC 접점은 용착특성에서는 우수하나 반복개폐 실험에서 저항변화가 많아 사용상 주의가 요구되며, Ag 접점은 반복개폐 특성은 우수하나 용착특성에서 취약한 것으로 나타났다.

• Journal of Welding and Joining
• /
• 제33권2호
• /
• pp.14-17
• /
• 2015

Cleaning effect is well known mechanism of oxide layer removal in DCEP polarity. It is also known that DCEN has higher heat input efficiency than DCEP in GTAW process. Based on these two renowned arc theories, conventional variable polarity arc for aluminum welding was set up to have minimum DCEP and maximum DCEN duty ratio to achieve the highest heat input efficiency and weldability increase. However, recent several variable polarity GTA research papers reported unexpected result of proportional relationship between DCEP duty ratio and heat input. The authors also observed the same result then suggested combination of tunneling effect and random walk of cathode spot to fill up the gap between experiment and conventional arc theory. In this research, suggested combinational work of tunneling effect and rapid cathode spot changing is applied to another unexpected phenomena of variable polarity aluminum arc welding. From previous research, it is reported that wider oxide removal range, narrower bead width and shallower penetration depth are observed in thin oxide layered aluminum compared to the case of thick oxide. This result was reported for the first time and it was hard to explain the reason at that time therefore the inference by the authors was hardly acceptable. However, the suggested combinational theory successfully explains the result of the previous report in logical way.

• 한국분말재료학회지
• /
• 제22권3호
• /
• pp.181-186
• /
• 2015

In this study, the effect of the friction stir welding (FSW) was compared with that of the gas tungsten arc welding (GTAW) on the microstructure and microhardness of Cu-Ni alloy weldment. The weldment of 10 mm thickness was fabricated by FSW and GTAW, respectively. Both weldments were compared with each other by optical microstructure, microhardness test and grain size measurement. Results of this study suggest that the microhardness decreased from the base metal (BM) to the heat affected zone (HAZ) and increased at fusion zone (FZ) of GTAW and stir zone (SZ) of FSW. the minimum Hv value of both weldment was obtained at HAZ, respectively, which represents the softening zone, whereas Hv value of FSW weldment was little higher than that of GTAW weldment. These phenomena can be explained by the grain size difference between HAZs of each weldment. Grain size was increased at the HAZ during FSW and GTAW. Because FSW is a solid-state joining process obtaining the lower heat-input generated by rotating shoulder than heat generated in the arc of GTAW.

• Journal of Welding and Joining
• /
• 제20권2호
• /
• pp.82-89
• /
• 2002

In order to clarify hot cracking phenomena occurred in Inconel 690 welds and it's prevention, in this study, the cracking behavior and the influence of welding variables on cracking in Inconel 690 overlay welds on Mn-Ni-Cr-Mo steel(SA 508 cl.3) for pressure vessel were investigated by using mock-up test. The main results are as follows: The cracks in Inconel 690 overlay welds were mainly generated near the start and the end part of welding beads adjacent to STS 309L welded outside of Inconel 690 welds. Most of the cracks showed typical solidification crack, and also it was assumed that there was possibility of liquation cracking in HAZ. The existence of Nb constituents or concentration of Nb was recognized on the fracture facets of the solidification cracks in the welds by SMAW. Therefore Nb was considered to be the main factor of the solidification cracking. As the weld heat input was more increased and the weld bead length was longer, the extent of cracking was more increased. Moreover the extent of cracking was considerably decreased by changing of welding sequence to the start and the end part of welds. Hot cracking in welds by GTAW was considerably decreased as compared with that of SMAW. And cracks were well generated in the Inconel 690 overlay welds adjacent to 575 309L welds. This means that the hot cracking susceptibility of Inconel 690 welds was largely varied by chemical components and/or compositions of filter metals, base metals and neighboring welds.

• 대한조선학회지
• /
• 제14권4호
• /
• pp.15-22
• /
• 1977

In this paper, two dimensional theoretical solutions of temperature distribution and thermal stress due to tandem cooling in an infinite plate were studied. Temperature distribution and thermal stress were calculated by numerical integration. Calculated temperature distributions were in good agreement with the result of the experiments by Park, and calculated thermal stresses were in good agreement with physical phenomena. This solutions could be applied to the practical tandem cooling operations.

• 전력전자학회:학술대회논문집
• /
• 전력전자학회 1998년도 전력전자학술대회 논문집
• /
• pp.143-148
• /
• 1998

A dynamic electrical parameter monitoring device was designed to simultaneously record the instantaneous value of voltage, current, power, and resistance during spot welding. The data obtained using this technique have been analyzed in term of the relationships of these parameters to the phenomena occuring during the formation(surface break-down, nugget formation and mechanical collapse) of spot weld. Finally, a database implementation is undertaken to develop techniques for improving weld quality of the resistance spot welder.

• International Journal of Korean Welding Society
• /
• 제4권1호
• /
• pp.53-60
• /
• 2004

Adhesive-bonded joints are widely used in the industry. Recently, applications of adhesive bonding joints have been increased extensively in automobile and aircraft industry. The strength of adhesive joints is influenced by the surface roughness, adhesive shape, stress distribution, and etc. However, the magnitude of the influence has not yet been clarified because of the complexity of the phenomena. In this study, as the fundamental research of adhesive bonding joints, the effects of adhesive shape and loading speed on bonding strength properties and durability of aluminum to polycarbonate single-lap joints were studied. To evaluate the effect of adhesive shape, several modified shapes were used, and loading speeds were varied from 0.05 to 5mm/min. As a result, the load distribution showed a brittle fracture tendency. The trigonal edged single lap and bevelled lap joints showed the higher strength than the plain single lap, trigonal single lap, joggle lap and double lap joints in same adhesive area. The fractures of trigonal single lap and trigonal edged single lap joints that had the higher strength level were shown as the mixture type of the cohesive and interfacial-failure, mostly joggle lap joints that had the lower strength level were shown as the adhesive-failure.

• 제어로봇시스템학회논문지
• /
• 제13권11호
• /
• pp.1060-1066
• /
• 2007

When a high-energy ultrasound propagates through a solid body that contains a crack or a delamination, the two faces of the defect do not ordinarily vibrate in unison, and dissipative phenomena such as friction, rubbing and clapping between the faces will convert some of the vibrational energy to heat. By combining this heating effect with infrared imaging, one can detect a subsurface defect in material efficiently. In this paper a detection of the welding defect of thin SUS 304 plates using the UIR (ultrasonic infrared imaging) technology is described. A low frequency (20kHz) ultrasonic transducer was used to infuse the welded thin SUS 304 plates with a short pulse of sound for 280ms. The ultrasonic source has a maximum power of 2kW. The surface temperature of the area under inspection is imaged by a thermal infrared camera that is coupled to a fast frame grabber in a computer. The hot spots, which are a small area around the defect tip and heated up highly, are observed. From the sequence of the thermosonic images, the location of defective or inhomogeneous regions in the welded thin SUS 304 plates can be detected easily.

• Journal of Welding and Joining
• /
• 제21권2호
• /
• pp.82-88
• /
• 2003

The bonding phenomenon and mechanism in the transient liquid phase bonding(TLP Bonding) of directionally solidified Ni base superalloy, GTD-111 was investigated. At the bonding temperature of 1403K, liquid insert metal was eliminated by isothermal solidification which was controlled by the diffusion of B and Si into the base metal and solids in the bonded interlayer grew epitaxially from mating base metal inward the insert metal. The number of grain boundaries formed at the bonded interlayer was corresponded with those of base metal. The liquation of grain boundary and dendrite boundary occurred at 1433K. At the bonding temperature of 1453K which is higher than liquation temperature of grain boundary, liquids of the Insert metal were connected with liquated grain boundaries and compositions in each region mixed mutually. In Joints held for various time at 1453t phases formed at liquated grain boundary far from the interface were similar to those of bonded interlayer. With prolonged holding time, liquid phases decreased gradually and liquids of continuous band shape divided many island shape. But liquid phases did not disappeared after holding for 7.2ks at 1453k. Isothermal solidification process at the bonding temperature which is higher than the liquation temperature of the grain boundary was controlled by diffusion of Ti to be result in liquation than B or Si. in insert metal. (Received January 15, 2003)