• Journal of Welding and Joining
• /
• v.33 no.6
• /
• pp.49-54
• /
• 2015

Welding process is of importance to assemble products or structures, but also the process is structural weakness due to stress concentration in welding joint. The fatigue design of welded joint requires time & labor consuming fatigue test because the fatigue life is various according to the depth of joint, joint type and load type etc. In fatigue design codes, they guide to classify welding joints with their shape( BS7608, IIW Documents) and provide fatigue assessment information. In terms of numerical method for fatigue analysis, it is also difficult to decide the stress peak in joint because of mesh sensitivity which means that stress value is varies with element type or size on stress concentration zone. Hot-spot method is used generally, but Battelle of United States proposed Master S-N Curve based on structural stresses converted by mechanical equilibrium theory. In this research, we extracted master S-N curve from Battelle's fatigue test DB including test data of various welding joints to apply on Non-Load-Carrying cruciform Joint. Comparing fatigue results between the case of using normal stress and case of structural stress cor the cruciform Joint, The suggested Battelle method showed successive results.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2006.05a
• /
• pp.127-131
• /
• 2006

There are being a lot of studies for achievement of high speed Dehydration, high-strength and Lightweight of washing machine in the latest washing machine business. It is essential that Press-joining Strength of Spin Drum Seaming division is improved .to attain that target. Generally, we are using Mechanical press-joining by Seaming and T.I.G (Tungsten Inert Gas) welding among part joint method. Mechanical press-joining method that is mainly using for Stainless Steel (STS430) Drum have lots of merit that consumption of energy is low more than welding and production costs cut down and generation of the corrosion is solved by removing weld zone defect and materials having different properties are enable to join without special equipment. But, it is difficult to realize joint strength required at high speed operation because joint strength of mechanical press-joining method is low remarkably in comparison with welding. Also, there are a lot of analysis difficulties and very limited research is under way due to the dynamic factor such as multistage plastic working, elastic recovery, residual stress etc. The results of this study show optimal joining condition for mechanical press-joining by performing lots of tensile joining strength test with various specimen under multi-change of important design factor such as seaming width, bead area and bead depth etc.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.17 no.11
• /
• pp.2486-2491
• /
• 2013

There are invisible defects by naked eyes in ceramic material images such as internal stomata, cracks and foreign substances. In this paper we propose a method to detect and extract such defects from ceramic pipe weld zone by applying ART2 learning. In pre-processing, we apply Ends-in Search Stretching to enhance the intensity and then perform fuzzy binarization with triangle type membership function followed by enhanced ART2 that interacts with random input patterns to extract such invisible defects. The experiment verifies that this proposed method is sufficiently effective.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.10
• /
• pp.1626-1635
• /
• 1997

It is important to ensure the reliability of the first localized reactor vessel steel. To satisfy with this purpose, a study on the impact/hardness, low cycle fatigue(LCF), crack growth rate(da/dN) and fracture toughness( ) of base material(BM) and weld metal(WM) were performed under room temperature air and corrosion conditions. A summary of the results is as folows : (1) Charpy impact absorbed energy of BM was the highest value, heat affected zoon(HAZ) and the lowest, WM. The hardness of BM was similar to HAZ. (2) Coefficients of Manson equation using the monotonic tensile test data were obtained for the present material. (3) The effects of stress ratio and ambient (120.deg. C and NaCl) condition on da/dN were investigated, da/dN with NaCl condition expressed the highest value. (4) The results of Charpy V-notch impact test had good correlation with $K_{IC}$ characteristics and the lowest curve of $K_{IC}$ for BM was derived, more researches about WM and HAZ are required hereafter.

• Steel and Composite Structures
• /
• v.28 no.6
• /
• pp.759-766
• /
• 2018

Friction Stir Welding (FSW) is a solid-state process, where the objects are joined together without reaching their melting point. It has been shown that this method is a suitable way to join dissimilar aluminium alloys. The current article employed hole drilling technique to measure the residual stress distribution experimentally in different zones of dissimilar aluminium alloys AA6061-T6 and AA7075-T6 Butt welded using FSW. Results are compared with those of similar AA6061-T6 plates joined using a conventional fusion welding method called tungsten inert gas (TIG). Also, the evolution of the residual stresses in the thickness direction was investigated, and it was found that the maximum residual stresses are below the yield strength of the material in the shoulder region. It was also revealed that the longitudinal residual stresses in the joint were much larger than the transverse residual stresses. Meanwhile, Vickers micro hardness measurements were performed in the cross-section of the samples. The largest hardness values were observed in the stir zone (SZ) adjacent to the advancing side whereas low hardness values were measured at the HAZ of both alloys and the SZ adjacent to the retreating side.

• Journal of Industrial Technology
• /
• v.21 no.A
• /
• pp.329-336
• /
• 2001

In this study, a series of fatigue tests are carried out in order to estimate quantitatively the characteristics of fatigue crack growth rate for high strength steels of SM570, POSTEN60, and POSTEN80 steel, that is, the influence on fatigue crack growth rate according to the welding line, the characteristics of fatigue crack growth according to the welding method and the kinds of steel, and the characteristics of fatigue crack growth for base metal, heat affected zone and weld metal. From the test results, in case that the notch if parallel to welding line, it knows that the retardations of fatigue crack growth rate in crack tip at early stage increase remarkably than in case that the notch is perpendicular to welding line due to compressive residual stress. And the characteristics of fatigue crack growth rate according to welding method are that the dispersion of fatigue crack growth rate in case of FCAW method is smaller than that of SAW method. Also, it knows that the fatigue crack growth rate converges in high stress intensity factor range.

• Corrosion Science and Technology
• /
• v.2 no.1
• /
• pp.36-40
• /
• 2003

An attractive combination of corrosion resistance and mechanical properties in the temperature range -50 to $250^{\circ}C$ is offered by duplex stainless steel. However, undesirable secondary precipitation phase such as $\sigma$, $\gamma_2$ and $Cr_2N$ may taken place at the cooling stage from the welding processes. Therefore, this paper describes the influence of different welding procedures such as manual metal arc welding (MMA), tungsten inert gas welding (TIG) and vacuum brazing on corrosion resistance of the welded joint for UNS S31803 duplex stainless steel. Microstructure and chemical compositions of the welded joint were examined. The weight loss of specimens immersed in 6% $FeCl_3$ solution at $47.5^{\circ}C$ for 24-hours was determined and used to evaluate the pitting resistance of duplex stainless steel and their welds. The region of heat-affected zone of specimen obtained by the MMA is much wider than that resulted from TIG, therefore, the weight loss of welds by MMA was larger than that of weld by TIG. The weight loss of brazed specimens cooled from slow cooling rate was larger than those of specimens cooled from high cooling rate, because the precipitation of $\sigma$ phase. Beside that, the weight loss of brazed specimen is greater than those of the welded specimens. The galvanic corrosion was observed in brazed duplex stainless steel joints in the chloride solution.

• Laser Solutions
• /
• v.2 no.3
• /
• pp.42-51
• /
• 1999

This research was conducted as a fundamental study to apply tailored blank welding technique into automotive production process. The materials used in this study were 2.0mm thickness low carbon steel sheets and 1.2mm Zn-coated low carbon steel sheets. To ensure the reproducibility and to consider various factors, experiments were. conducted by applying Taguchi experimental method with 6 factors. Every welding process was repeated 3 times to offset the effect of uncontrolled factors. Elongation and LDH(Limited Dome Height)were measured to evaluate formability of specimens and Optical microscopy, XRD, SEM, and EDS analysis were performed to observe the microstructures and to determine the solidification mode in the weld. The elongation of specimen welded with optimum condition was 83% of base metal, and LDH was 84% of base metal. In case of laser treated specimen where Zn coating was removed, elongation was 85% of base metal, and LDH was 85% of base metal. In fusion zone, phases were consisted of quasi-polygonal ferrite, banitic ferrite, and martensite.

• Journal of Welding and Joining
• /
• v.32 no.5
• /
• pp.50-57
• /
• 2014

Friction Stir Welding (FSW) is a complex process with several mutually interdependent parameters. A slight difference from known settings may lead to imperfections in the stirred zone. These inhomogeneities affect on the mechanical properties of the FSWed joints. In order to prevent the failure of the welded joint it is necessary to detect the most critical defects non-destructive. Especially critical defects are wormhole and lack of penetration (LOP), because of the difficulty of detection. Online thermography is used process-accompanying for defect detecting. A thermographic camera with a fixed position relating to the welding tool measures the heating-up and the cool down of the welding process. Lap joints with sound weld seam surfaces are manufactured and monitored. Different methods of evaluation of heat distribution and intensity profiles are introduced. It can be demonstrated, that it is possible to detect wormhole and lack of penetration as well as surface defects by analyzing the welding and the cooling process of friction stir welding by passive online thermography measurement. Effects of these defects on mechanical properties are shown by tensile testing.

• Steel and Composite Structures
• /
• v.25 no.5
• /
• pp.535-544
• /
• 2017

Box sections are symmetrical sections and they have high moment of inertia in both directions, therefore they are good members in tall building structures. For the rigid connection in structures with box column continuity plates are used on level of beam flanges in column. Assembly of the continuity plates is a difficult and unreliable work due to lack of weld or high welding and cutting in the fourth side of column in panel zone, so the use of experimental stiffeners have been considered by researchers. This paper presented an experimental investigation on connection in box columns. The proposed connection has been investigated in four cases which contain connection without internal and external stiffeners(C-0-00), connection with continuity plates(C-I-CP), connection with external vase shape stiffener (C-E-VP) and connection with surrounding plates(C-E-SP). The results show that the connections with vase plates and surrounding plates can respectively increase the ultimate strength of the connection up to 366% and 518% than the connection without stiffeners, in case connection with the continuity plates this parameter increases about 39%. In addition, the proposed C-E-VP and C-E-SP connection provide a rigid and safe connection to acquire rigidity of 95% and 98% respectively. But C-I-CP connection is classified as semi-rigid connections.