• 한국주조공학회지
• /
• 제31권1호
• /
• pp.18-25
• /
• 2011

Effect of Fe and Mn contents on the tensile properties has been studied in Al-9wt%Si-0.3wt%Mg alloy. As Fe content of Al-9wt%Si-0.3wt%Mg-0.5wt%Mn alloy increased from 0.15wt% to 0.45wt%, tensile strength of as-cast alloy decreased from 192 MPa to 174 MPa, and elongation of the alloy also decreased from 4.8% to 4.2%. Decrease of these properties can be explained as the formation of plate shape, ${\beta}-Al_5FeSi$ phase with high Fe/Mn ratio of the alloy. However when Mn content of Al-9wt%Si-0.3wt%Mg-0.45wt%Fe alloy increased from 0.3wt% to 0.5wt%, tensile strength of T6 aged alloy increased from 265 MPa to 275 MPa, and elongation of the alloy increased from 2.3% to 3.6%. These improvements attribute to chinese script, ${\alpha}-Al_{15}(Mn,Fe)_3Si_2$ phase shape-modified from ${\beta}-Al_5FeSi$ phase with low Fe/Mn ratio of the alloy.

• 대한금속재료학회지
• /
• 제50권10호
• /
• pp.769-774
• /
• 2012

Mg-x wt% $Fe_2O_3-y$ wt% Ni samples were prepared by reactive mechanical grinding in a planetary ball mill, and their hydrogen-storage properties were investigated and compared. Activations of $Mg-5Fe_2O_3-5Ni$ was completed after one hydriding (under 12 bar $H_2$) - dehydriding (in vacuum) cycle at 593 K. At n = 2, $Mg-5Fe_2O_3-5Ni$ absorbed 3.43 wt% H for 5 min, 3.57 wt% H for 10 min, 3.76 wt% H for 20 min, and 3.98 wt% H for 60 min. Activated $Mg-10Fe_2O_3$ had the highest hydriding rate, absorbing 2.99 wt% H for 2.5 min, 4.86 wt% H for 10 min, and 5.54 wt% H for 60 min at 593 K under 12 bar $H_2$. Activated $Mg-10Fe_2O_3-5Ni$ had the highest dehydriding rate, desorbing 1.31 wt% H for 10 min, 2.91 wt% H for 30 min, and 3.83 wt% H for 60 min at 593 K under 1.0 bar $H_2$.

• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 1995년도 춘계학술발표회논문집(2)
• /
• pp.745-752
• /
• 1995

고연소도 액체금속로용 금속연료를 개발하고자 U-l0wt%Zr 합금중 Zr 원소 대신에 X(:Si, Ta, Nb, W, Mo) 원소를 첨가한 U-7wt%Zr-3wt%X(:Si, Ta, Nb, W, Mo) 합금을 제조하여 미세조직에 미치는 합금원소 첨가의 영향을 조사하였다. 그 결과 U-7 wt%Zr-3wt%Si 합금을 제외한 모든 U-7wt%Zr-3wt%X(:Ta, Nb, W, Mo) 합금은 Matrix에 있어서 Laminar Structure를 그대로 유지하였다. U-7wt%Zr-3wt%Si 함금을 제외한 모든 U-7wt%Zr-3wt%X(:Ta, Nb, W, Mo) 합금의 주요한 상은 U-l0wt% Zr 합금과 마찬가지로 $\alpha$-U 및 $\delta$-UZr$_2$ 상이었다. U-7wt%Zr-3wt%X(:Ta, Nb, W, Mo) 합금은 U-l0wt%Zr 합금에 비해 Lamina Thickness가 크게 감소되었다. 특히 U-7wt%Zr-3wt%Mo 합금의 경우에 있어서는 U-l0wt%Zr 합금에 비해 1/3배 정도까지 Lamina Thickness가 크게 감소하였다. 이와 같은 합금원소 첨가에 의한 Laminar Structure의 미세화는 액체금속로강 금속연료내 Fission Gas의 Inter-connected Path가 보다 더 잘 형성됨으로 인해 Fission Gas Bubble에 대한 방출속도를 크게 증가시켜서 궁극적으로는 Fission Gas Bubble에 의한 Swelling을 저감시킬 것으로 기대된다.

• 대한화장품학회지
• /
• 제30권4호
• /
• pp.515-524
• /
• 2004

쌀눈에서 추출한 inositol과 phytic acid를 화장품에 적용하기 위해 피부에 미치는 영향에 대해 연구하였다 $20{\~}40$대의 아시안 여성 45명을 대상으로 7주간 inositol $0{\~}3.0\;wt\%$와 phytic acid $0{\~}1.50\;wt%$가 함유된 스킨로션을 제조, 사용 후 피부의 수분, 유분, 탄력, 주름에 미치는 영향에 대해서 알아보았다 Inositol $1.0\;wt\%가$ 함유된 스킨로션을 사용한 경우 피부의 수분 함유량은 $19\%$ 증가하였으며, 주름은 $12.4\%$ 개선되었고, 피부탄력은 $12.4\%$ 증가되었다. 또한 phytic acid $0.50\;wt\%$를 함유한 스킨 로션을 사용한 경우 피부의 수분은 $71.6\%$ 증가하였으며, 주름은 $16.9\%$ 감소하였고, 탄력은 $21.9\%$가 증가하였다. Inositol과 phytic acid를 지성과 건성피부에 적용한 결과 $2{\~}4$주 후면 정상피부의 유분량으로 조절됨을 알 수 있었다 Inositol과 phytic acid는 모두 피부개선에 효과적이나, phytic acid는 민감한 피부에는 적용하기 어려운 점이 있다. 따라서 $1.0\;wt\%의$ inositol에 $0{\~}0.5\;wt\%$의 phytic acid를 첨가한 스킨로션을 제조하여 그 효과에 대해서 알아보았다. 이 경우 $1.0\;wt\%$의 phytic acid에 $1.0\;wt\%$의 inositol을 사용한 경우 수분은 $63.8\%$, 탄력은$17.2\%$ 증가하였으며, 주름은 $17.4\%$ 개선되었고, 피부 유분량은 약 2주 후에 정상적인 상태로 개선됨을 알 수 있었다. 따라서 inositol $1.0\;wt\%$에 $0.10\;wt\%$의 phytic acid를 첨가하여도 피부 개선효과가 나타남을 알 수 있다. 본 연구의 결과 내에서 $1.0\;wt\%$의 phytic acid와 $1.0\;wt\%$의 inositol을 사용한 경우 적은 양으로도 피부 개선 효과가 우수한 상승효과가 나타남을 알 수 있었다.

• 한국수소및신에너지학회논문집
• /
• 제23권2호
• /
• pp.111-116
• /
• 2012

Na promoted Pt/$CeO_2$ catalysts with various Na amounts (1, 2, and 3wt%) have been applied to water gas shift reaction (WGS) at a gas hourly space velocity (GHSV) of 45515 $h^{-1}$. 1wt%Pt-2wt%Na/$CeO_2$ catalyst exhibited the highest WGS activity at $240^{\circ}C$ among the catalysts prepared in this study. In addition, 1wt%Pt-2wt%Na/$CeO_2$ catalyst showed relatively stable activity with time on stream. The high activity/stability of 1wt%Pt-2wt%Na/$CeO_2$ catalyst was correlated to its easier reducibility and higher oxygen storage capacity (OSC). As a result, 2wt% Na promoted Pt/$CeO_2$ can be a promising candidate catalyst for the single stage WGS, which requires high intrinsic activity at very high GHSV.

• 대한환경공학회지
• /
• 제36권3호
• /
• pp.185-191
• /
• 2014

본 논문에서는 저농도 $CO_2$ 조건에서 알카놀아민 흡수제 별 $CO_2$ 흡수 특성을 도출하였다. 단일흡수제의 경우 MEA 농도가 1 wt%, 2 wt%, 3 wt% 증가 시 $CO_2$ 흡수량은 0.34 mol-$CO_2/mol$-absorbent, 0.32 mol-$CO_2/mol$-absorbent, 0.30 mol-$CO_2/mol$-absorbent로 감소하였고, AMP 농도가 1 wt%, 2 wt%, 3 wt% 증가 시 $CO_2$ 흡수량은 0.32 mol-$CO_2/mol$-absorbent, 0.30 mol-$CO_2/mol$-absorbent, 0.28 mol-$CO_2/mol$-absorbent로 감소하였다. 혼합흡수제의 경우 MEA 0.5 wt%와 AMP 0.5 wt%을 혼합했을 때 0.52 mol-$CO_2/mol$-absorbent로 최대치를 나타냈다.

• 한국광물학회지
• /
• 제19권1호통권47호
• /
• pp.1-5
• /
• 2006

본 연구에서는 $0.1{\sim}0.3mm$ 입도의 규석을 대상으로 물리적 선별공정을 적용하였을 때의 정제효과를 조사하였다. $SiO_2$ 품위가 99.41 wt.%, 99.54 wt.%이고 불순물 함량이 각각 5,864 mg/kg과 4,568 mg/kg인 시료에 대하여 자력선별, 비중선별 및 scrubbing 공정을 단계별로 적용시킨 결과, 주요 불순물인 철 성분은 자력선별에 의하여, 알루미늄 성분은 비중선별에 의해 효과적으로 제거되었다. 최종 정제산물의 $SiO_2$ 품위는 99.98 wt.%였으며, 산출율은 각각 79.05 wt.%와 75.43 wt.%였다. 이때 불순물의 함유량은 각각 126 mg/kg, 174 mg/kg을 나타내어, 불순물의 제거율은 97.85wt.%, 96.19 wt.%였다. 따라서 물리적 분리 선별에 의하여 저급 품위(Low grade)의 규석을 불순물 함유량이 200 mg/kg 이하인 중 고급 품위(Medium-high grade) 이상으로의 품위 향상이 가능하였다.

• 한국산학기술학회논문지
• /
• 제11권5호
• /
• pp.1547-1551
• /
• 2010

통상의 은합금 장신구 재료로 쓰이는 925 은합금 (Ag-7.5wt%Cu)의 가공 중 고온산화에 의한 변색 또는 착용 중 산화에 의한 색변화를 방지하기 위해서 Ag-5wt%Ge-2.5wt%Cu, 5wt%In-2.5wt%Cu의 새로운 조성을 제안하였다. 전체는 기존 925 은합금의 조성을 유지하여 기존 7.5wt%Cu합금원소를 Ge, In으로 대치하여 기존 925 은합금과 비교하여 주조공정 시의 형상변화와 주조능, 가공경화에 의한 물성과 내식성 변화를 확인하였다. 새로이 제안된 Ge, In 은합금은 기존 925은합금과 동일하거나 우수한 주조특성을 보였고, 특히 가공 중에 생기는 가공경화능력이 우수하여 내구성이 증가하였고 고온 내식성과 신체 착용 시의 내부식성이 향상됨을 확인하였다.

• 한국주조공학회지
• /
• 제21권4호
• /
• pp.239-245
• /
• 2001

Microstructure and mechanical properties of Sn-3.1 wt.%Ag-6.9 wt.%Bi system solders on Cu-substrate were studied. The Sn3.1 wt.%Ag-6.9 wt.%Bi alloy was designed by phase diagram and chemical properties and was prepared by melting in argon atmosphere. The mechanical properties of solder/Cu joints were examined by shear strength test, and also creep test. The microstructure of Sn-3.1 wt.%Ag-6.9 wt.%Bi alloy consists of Bi-rich phase and $Ag_3Sn$ precipitate in {\beta}-Sn$ matrix phase. The shear strength of the joint was decreased with aging treatment. Crack path under shear test was through the solder. Similar crack path change mode was observed at the creep test of solder/Cu joint. The creep behavior of Sn-3.1 wt.%Ag-6.9 wt.%Bi alloy represented the inverse primary creep behavior at all test condition. It is suggested that the inverse primary creep behavior is induced from Bi solute atoms in Sn-matrix. The creep resistance of Sn-3.1Ag-6.9Bi alloy is better than that of Sn-3.5 wt.%Ag alloy at all test conditions.

• 한국응용과학기술학회지
• /
• 제20권1호
• /
• pp.44-50
• /
• 2003

We studied on the preparation and evaluation of O/W type microemulsion containing "wax, liquid paraffine and quaternary ammonium salt". And also it was obtained to stability of microemulsions by mono ethylene glycol(MEG) addition. The microemulsions were generally prepared at 96${\sim}$97$^{\circ}C$ by the phase inversion method. We used polyoxyethylene(20) sorbitan monooleate(POE(20)SMO) and distearyl dimethyl ammonium chloride(D.D.A.C.) as the emulsifiers at microemulsion preparation. From the results, we could get best condition for microemulsion preparation, in case of oil phase, montanic ester wax ; 1.1wt%, paraffine wax ; 1.1wt%, liquid paraffine ; 3.1wt%, propylene glycol ; 0.6wt% and ethylene glycol monobutyl ether ; 0.6wt%, when the ratio(wt%) of D.D.A.C. and POE(20)SMO were 2 : 3. And also we could obtained that the distributed particle size of the final microemulsions were about 8${\pm}$1.5nm and the mean particle size was 7${\pm}$0.5nm. We got following results from final microemulsions that the percent of transmittance; 96${\sim}$98% at 700nm. And the microemulsion blended with MEG of 5${\sim}$15wt% showed smaller particle size and more stable distribution than non-containing MEG.