• Advances in concrete construction
• /
• 제12권6호
• /
• pp.479-490
• /
• 2021

Present research is mainly focused on, microstructural and durability analysis of Graphene Oxide (GO) in Wollastonite (WO) induced cement mortar with silica fume. The study was conducted by evaluating the mechanical properties (compressive and flexural strength), durability properties (water absorption, sorptivity and sulphate resistance) and microstructural analysis by SEM. Cement mortar mix prepared by replacing 10% ordinary portland cement with SF was considered as the control mix. Wollastonite replacement level varied from 0 to 20% by weight of cement. The optimum replacement of wollastonite was found to be 15% and this was followed by four sets of mortar specimens with varying substitution levels of cementitious material with GO at dosage rates of 0.1%, 0.2%, 0.3% and 0.4% by weight. The results indicated that the addition of up to 15%WO and 0.3% GO improves the hydration process and increase the compressive strength and flexural strength of the mortar due to the pore volume reduction, thereby strengthening the mortar mix. The resistance to water penetration and sulphate attack of mortar mixes were generally improved with the dosage of GO in presence of 15% Wollastonite and 10% silica fume content in the mortar mix. Furthermore, FE-SEM test results showed that the WO influences the lattice framework of the cement hydration products increasing the bonding between silica fume particles and cement. The optimum mix containing 0.3% GO with 15% WO replacement exhibited extensive C-S-H formation along with a uniform densified structure indicating that calcium meta-silicate has filled the pores.

• Advances in nano research
• /
• 제12권3호
• /
• pp.291-300
• /
• 2022

The behavior of hydrogen species on the surface of the catalyst during the Lewis acid transformation to form Brønsted acid sites over the spherical silica-supported WO_x catalyst was investigated. To understand the structure-activity relationship of Lewis acid transformation and hydrogen bonding interactions, we explore the potential of using the in situ diffuse reflection infrared Fourier transform spectroscopy (DRIFTS) with adsorbed ammonia and hydrogen exposure. From the results of in situ DRIFTS measurements, Lewis acid sites on surface catalysts were transformed into new Brønsted acid sites upon hydrogen exposure. The adsorbed NH₃ on Lewis acid sites migrated to Brønsted acid sites forming NH⁴⁺. The results show that the dissociated H atoms present on the catalyst surface formed new Si-OH hydroxyl species - the new Brønsted acid site. Besides, the isolated Si-O-W species is the key towards H-bond and Si-OH formation. Additionally, the H atoms adsorbed surrounding the Si-O-W species of mono-oxo O=WO₄ and di-oxo (O=)₂WO₂ species, where the Si-O-W species are the main species presented on the Inc-SSP catalysts than that of the IWI-SSP catalysts.

• 대한환경공학회지
• /
• 제27권8호
• /
• pp.859-869
• /
• 2005

소각장 off gas에 장기간 노출이 되어 활성이 저하된 상용 $V_2O_5-WO_3/TiO_2$ aged 촉매를 물리화학적 방법으로 재생 처리를 수행한 후, 재생 처리에 따른 촉매의 물성 변화를 확인하고 이에 따른 촉매 활성변화를 고찰하였다. 촉매의 특성분석은 XRD(x-ray diffractometer), BET, POROSIMETER, EDX(energy dispersive x-ray spectrometer), ICP(inductively coupled plasma), TGA(thermogravimetric Analyze,), SEM(scanning electron microscopy)등을 이용하여 수행하였고 NOx 전환반응실험은 소각장 off gas를 모사하여 $NH_3$에 의한 SCR 반응을 통해 수행하였다. 본 연구에서 수행된 재생처리 방법 중, 열처리 방법으로 재생처리를 수행 할 경우 fresh 촉매환성의 95% 이상을 회복하였으며, 화학적 재생 처리 방법으로는 산성용액의 경우는 pH가 5인 용액으로 재생 처리된 촉매가, 염기성 용액의 경우는 pH가 12인 용액으로 재생 처리된 촉매가 fresh 촉매활성의 90% 이상의 촉매 활성을 회복 하였다. 촉매 특성 분석 결과, 상기와 같은 방법으로 재생 처리된 촉매의 경우 비표면적은 fresh 촉매의 $85{\sim}95%$ 수준으로 회복 되었으며, aged 촉매 표면에 축적되어 있던 촉매 비활성 물질로 잘 알려진 황(S)이나 칼슘(Ca)등은 최대 99%이상 제거 되었다. Aged 촉매 표면상의 인(P), 크롬(Cr), 아연(Zn) 등과 같은 중금속의 경우는 최대 95% 이상 제거 되었으나 납(Pb)의 경우는 제거율이 $10{\sim}30%$ 수준으로 매우 미흡한 것으로 나타났다.

• 대한설비공학회:학술대회논문집
• /
• 대한설비공학회 2008년도 동계학술발표대회 논문집
• /
• pp.363-368
• /
• 2008

Nitrogen oxides (NO, $NO_2$ and $N_2O$) have been controlled effectively by the SCR catalysts coated on monolith or honeycomb in commercial sites with ammonia as reductant at high temperature range $300{\sim}400^{\circ}C$. However, the catalytic filter has much merit on the point of controlling the particles and nitrogen oxides simultaneously. It will be more advanced-system if the catalytic working temperature is reduced to the normal filtration temperature of under $200^{\circ}C$. This study has focus on the development of the catalytic filter working at the low temperature. So the additive effect of the components such as Pt and Mn (which are known the catalytic component of $V_2O_5/TiO_2$ was investigated. The $V_2O_5-WO_3$ catalytic filter exhibited high activity and selectivity at $250{\sim}320^{\circ}C$ showing more than 95% NO conversion for the treatment of 600 ppm NO at face velocity 2 cm/s. The Pt-$V_2O_5-WO_3$ catalytic filter shifted the optimum working temperature towards the lower temperature ($170{\sim}200^{\circ}C$). And NO conversion was 100% and higher than that of $V_2O_5-WO_3$ catalyst at $250{\sim}320^{\circ}C$. The $MnO_X-V_2O_5-WO_3$ catalytic filter showed the wide temperature range of $220{\sim}330^{\circ}C$ for more than 95% NO conversion. This is a remarkable advantage when considered the $MnO_X$ catalytic filter presents the maximum activity at $150{\sim}250^{\circ}C$ and $V_2O_5-WO_3$ catalytic filter shows the maximum activity at $250{\sim}320^{\circ}C$.

• 공업화학
• /
• 제34권4호
• /
• pp.357-364
• /
• 2023

선택적 촉매 환원(SCR)은 질소산화물 배출을 줄이는 가장 효과적인 방법이지만, V₂O₅-WO₃/TiO₂ 촉매가 좁은 작동온도 (300~400℃) 범위를 가지기 때문에, V₂O₅-WO₃/TiO₂ 촉매의 작동 온도범위가 200~450℃인 새로운 촉매를 개발하였다. SCR 과정에서 생성되는 촉매 독인 황산암모늄은 350℃ 이상으로 가열함으로써 제거할 수 있다. 촉매 활성 부위의 수를 증가시키고 활성 물질의 분산을 촉진하기 위해 TiO₂ 지지체에 티타늄 이소프로폭사이드(TTIP) 처리를 여러 TTIP/TiO₂ 질량비로 진행하였다. 그 중 5 wt% TTIP 부하에서 높은 W 분산성으로 인해 열 안정성이 증가하였고 V⁵⁺가 형성되어 최적의 성능을 보였다. 5 wt% TTIP 부하로 처리된 촉매를 One-step co-precipitation으로 제조하였을 때 기존의 방법보다 더 나은 V-OH와 W-OH 분산 및 상호작용 향상이 나타나 더 낮은 온도에서 높은 촉매 활성으로 인해 향상된 성능을 보였다. 이를 향후 TTIP를 이용하여 TiO₂촉매의 표면을 개선하려는 연구자에게 이해하기 쉽게 설명하고자 하였다.

• 한국재료학회지
• /
• 제11권11호
• /
• pp.953-959
• /
• 2001

Homogeneous spherical W-Co salt powders were made by spray drying of aqueous solution of ammonium $metatungstate(NH_4)_6(H_2W_{12}O_{40}){\cdot}4H_2O,\; AMT)$ and cobalt nitrate $hexahydrate(Co(NO_3)_2{\cdot}6H_2O)$. The thermal decomposition process of spray dried W-Co salt powders was studied by TG, XRD, SEM, TEM and FT-IR. Spray dried W-Co salt powders were calcined for 1 hour in the temperature from$ 350^{\circ}C$ to $800^{\circ}C$ in atmosphere of air. At the temperatures over $600^{\circ}C$, spherical $CoWO_4/WO_3$ composite oxide powders were obtained. The primary particle size of W/Co composite oxide powders increased with increasing thermal decomposition temperature due to the particle growth. The observed crystallite size by TEM was in the range of 60nm and that of $CoWO_4$ calculated by Scherrer's formula at $800^{\circ}C$ was smaller than 55nm. The crystallite site was identified by XRD and TEM.

• 한국전기전자재료학회논문지
• /
• 제16권5호
• /
• pp.397-403
• /
• 2003

Microwave dielectric properties of (1-x)ZnW $O_4$-xTi $O_2$ ceramic systems were investigated with calcination temperatures and Ti $O_2$ contents. The ZnW $O_4$ ceramic could be suitably sintered at 1075$^{\circ}C$ and showed the dielectric constant of 13.6, quality factor(Q$\times$ $f_{O}$value) of 22,000 and temperature coefficient of resonant frequency($\tau$$_{f}$) of -65$\pm$2ppm/$^{\circ}C$. Increasing the amount of Ti $O_2$ in the range of 0.25 to 0.45 mol, the dielectric constant and $\tau$$_{f}$ increased due to the role of Ti $O_2$ but the quality factor decreased due to the increase of phase boundaries. The 0.7ZnW $O_4$-0.3Ti $O_2$ ceramic showed the dielectric constant of 19.8, qualify factor(Q$\times$ $f_{0}$) of 20,000 and $\tau$$_{f}$ of -3$\pm$1ppm/$^{\circ}C$.>.EX>.>.>.

• 자원리싸이클링
• /
• 제27권6호
• /
• pp.3-10
• /
• 2018

텅스텐은 고융점금속으로 주로 초경합금으로 사용되고 있다. 알칼리용액에서 텅스텐은 $WO{_4}^{2-}$로 존재하는데 용액의 pH가 감소함에 따라 중합반응이 일어나며 텅스텐산으로 침전된다. 따라서 원광석 및 2차 자원으로부터 텅스텐 회수를 위한 습식 제련 기술은 산침출과 알칼리침출로 대별된다. 2차 자원에 함유된 금속의 종류와 함유량 및 텅스텐의 소재화를 고려해서 2차 자원으로부터 텅스텐을 고순도로 회수하기 위한 공정을 선택해야 한다.

• Restorative Dentistry and Endodontics
• /
• 제41권3호
• /
• pp.176-181
• /
• 2016

Objectives: This study aimed to compare two nickel-titanium systems (rotary vs. reciprocating) for their acceptance by undergraduate students who experienced nickel-titanium (NiTi) instruments for the first time. Materials and Methods: Eighty-one sophomore dental students were first taught on manual root canal preparation with stainless-steel files. After that, they were instructed on the use of ProTaper Universal system (PTU, Dentsply Maillefer), then the WaveOne (WO, Dentsply Maillefer). They practiced with each system on 2 extracted molars, before using those files to shape the buccal or mesial canals of additional first molars. A questionnaire was completed after using each file system, seeking students' perception about 'Ease of use', 'Flexibility', 'Cutting-efficiency', 'Screwing-effect', 'Feeling-safety', and 'Instrumentation-time' of the NiTi files, relative to stainless-steel instrumentation, on a 5-point Likert-type scale. They were also requested to indicate their preference between the two systems. Data was compared between groups using t-test, and with Chi-square test for correlation of each perception value with the preferred choice (p = 0.05). Results: Among the 81 students, 55 indicated their preferred file system as WO and 22 as PTU. All scores were greater than 4 (better) for both systems, compared with stainless-steel files, except for 'Screwing-effect' for PTU. The scores for WO in the categories of 'Flexibility', 'Screwing-effect', and 'Feeling-safety' were significantly higher scores than those of PTU. A significant association between the 'Screwing-effect' and students' preference for WO was observed. Conclusions: Novice operators preferred nickel-titanium instruments to stainless-steel, and majority of them opted for reciprocating file instead of continuous rotating system.

• 한국전기전자재료학회논문지
• /
• 제19권9호
• /
• pp.855-861
• /
• 2006

Sinterability and microwave dielectric properties of $xZWO_{4}-(1-x)TiO_{2}$ ceramic systems with zinc-borosilicate glass and $TiO_{2}$ contents for LTCC(Low Temperature Co-fired Ceramics) were investigated. The addition of $3{\sim}10\;wt%$ ZBS glass ensured the sinterability below $900^{\circ}C$. In general, increasing ZBS glass content seemed to enhance the sinterability, but the quality factor($Qxf_{0}$) significantly decreased due to the formation of an excessive liquid and second phases. As for the addition of $TiO_{2}$, the dielectric constant(${\varepsilon}_{r}$) and temperature coefficient of resonant frequency(${\tau}_{f}$) showed to increase, while the quality factor($Qxf_{0}$) did not show an apparent change. The composition of $0.7xZnWO_{4}-0.3TiO_{2}$ ceramics sintered at $900^{\circ}C$ with 5 wt% ZBS glass demonstrated 21.6 in dielectric constant(${\varepsilon}_{r}$), 14,800 in quality factor($Qxf_{0}$), and $+5\;ppm/^{\circ}C$ in temperature coefficient of resonant frequency(${\tau}_{f}$).