• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.39 no.9
• /
• pp.901-907
• /
• 2015

The Vickers hardness test is a common method used to characterize the hardness of ceramic materials. However, the hardness is not a deterministic value, but is a random variable. The objective of this paper is to investigate the statistical properties of the bending strength and a set of Vickers hardness values in single $ZrO_2$ and composite $ZrO_2/SiC$ with a SiC additive. In this work, we compare the characteristic value and variation with the results based on Weibull statistical analysis. The probability distributions of the bending strength and Vickers hardness agreed relatively well with the Weibull distribution. We evaluate the scale parameter and shape parameter in asreceived $ZrO_2$ and $ZrO_2/SiC$ composite ceramics, as well as in their heat treated ceramics.

• Journal of Conservation Science
• /
• v.25 no.4
• /
• pp.431-438
• /
• 2009

We have investigated the suitable measuring method and condition on the hardness testing for the earthenwares excavated from Poongnap mud castle in Hanseong Baekje period. The earthenwares which used on hardness testing have been classified according to Mohs hardness and external form and color. The Ultrasonic and Equotip testing method have used to the hardness testing on the surface of the earthenwares and the Rockwell and Micro-vickers testing methods have used to the hardness testing on the cross section of the earthenwares. As the results, the two methods applied to the surface of the earthenwares were very hard on the precise measurement and the measuring values were incompatible with the tendency classified according to Mohs hardness and external form and color. On the testing for the cross section of earthenware, the Rockwell-superficial hardness testing method was more suitable for the soft texture earthenware and highest reproducibility of the measuring value obtained at the test load and indentor are 15kgf and 1/16 “iron ball, respectively. The Micro-Vickers hardness testing method was suitable for the hard texture earthenware and highest reproducibility and accuracy of the measuring value obtained at the test load is 100gf. This results show strong possibility of progress on the classifying and comparing study for hardness of the earthenware and therefore active studies are expected on the field.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2007.06a
• /
• pp.639-640
• /
• 2007

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.28 no.3
• /
• pp.170-174
• /
• 2015

Composite ceramics of alumina-TZP(3Y) have good mechanical and electrical properties. So, They have been used as high strength refractory materials and thick film substrates, etc. In this study, Composite ceramics of alumina-TZP(3Y) were fabricated by uniaxial pressing and sintering at 1,400, 1,500, and $1,600^{\circ}C$, and their microstructures and mechanical properties were investigated. As the TZP(3Y) content in composite ceramics increases from 20 wt.% to 80 wt.%, the fracture toughness increases monotonically, which seems to be related to the higher relative density and/or toughening mechanism by means of stabilized tetragonal zirconia phase at room temperature. In contrast to the fracture toughness, Vickers hardness of the composite ceramics shows maximum value (1,938 Hv) at a 40 wt.% of TZP(3Y). The result of Vickers hardness is likely to be due to more dense sintered microstructure of composite ceramics than pure alumina and reinforcement of composite ceramics with TZP(3Y), considering that Vickers hardness of pure $Al_2O_3$ is greater than that of TZP(3Y). It is also shown that the $ZrO_2$ particles are $l^{\circ}Cated$ between $Al_2O_3$ grains and suppress grain growth each other.

• Applied Microscopy
• /
• v.46 no.1
• /
• pp.32-36
• /
• 2016

The Cu-based bulk glassy alloys in Cu-Zr-Ti-Ni systems were prepared by means of copper mold casting. The Cu-based bulk glassy alloys samples were tested by X-ray diffractomer (XRD), differential scanning calorimeter, scanning electron microscopy (SEM), Instron testing machine and Vickers hardness instruments. The result indicated that the prepared Cu-Zr-Ti-Ni alloys were bulk glassy alloys. The temperature interval of supercooled liquid region (${\Delta}T_x$) was about 45.48 to 70.98 K for the Cu-Zr-Ti-Ni alloy. The Vickers hardness was up to 565 HV for the $Cu_{50}Zr_{25}Ti_{15}Ni_{10}$ bulk glassy alloy. The $Cu_{50}Zr_{25}Ti_{15}Ni_{10}$ bulk glassy alloys were annealed in order to obtain nanocrystals. The results showed that the Vickers hardness was raise up to 630 HV from 565 HV. As shown in XRD results, the amorphous alloys changed to nanocrystals, which were $Cu_8Zr_3$, $Cu_3Ti_2$ and CuZr, improved the hardness. The SEM analysis showed that the compression fractured morphology of amorphous alloys was brittle fracture, and the fracture morphology after annealing was ductile fracture. This proved that annealing of amorphous to nanocrystals can improve the plasticity and toughness of amorphous alloys.

• Korean Journal of Materials Research
• /
• v.27 no.7
• /
• pp.386-391
• /
• 2017

Using a customized diffusion bonder, we executed diffusion bonding for ring shaped white gold and red gold samples (inner, outer diameter, and thickness were 15.7, 18.7, and 3.0 mm, respectively) at a temperature of $780^{\circ}C$ and applied pressure of 2300 N in a vacuum of $5{\times}10^{-2}$ torr for 180 seconds. Optical microscopy, field emission scanning electron microscopy (FE-SEM), and energy-dispersive X-ray spectroscopy (EDS) were used to investigate the microstructure and compositional changes. The mechanical properties were confirmed by Vickers hardness and shear strength tests. Optical microscopy and FE-SEM confirmed the uniform bonding interface, which was without defects such as micro pores. EDS mapping analysis confirmed that each gold alloy was 14K with the intended composition; Ni and Cu was included as coloring metals in the white and red gold alloys, respectively. The effective diffusion coefficient was estimated based on EDS line scanning. Individual values of Ni and Cu were $5.0{\times}10^{-8}cm^2/s$ and $8.9{\times}10^{-8}cm^2/s$, respectively. These values were as large as those of the melting points due to the accelerated diffusion in this customized diffusion bonder. Vickers hardness results showed that the hardness values of white gold and red gold were 127.83 and 103.04, respectively, due to solid solution strengthening. In addition, the value at the interface indicated no formation of intermetallic compound around the bonding interface. From the shear strength test, the sample was found not to be destroyed at up to 100,000 gf due to the high bonding strength. Therefore, these results confirm the successful diffusion bonding of 14K white-red golds with a diffusion bonder at a low temperature of $780^{\circ}C$ and a short processing time of 180 seconds.

• Journal of Technologic Dentistry
• /
• v.21 no.1
• /
• pp.5-14
• /
• 1999

Glass ceramics for dental crown prosthesis were prepared by crystallization of CaO-MgO-SiO2-$P_2O_5-TiO_2$ glasses. Their crystallization behaviors have been investigated as a function of heattreatment temperature, holding time and chemical composition in relation to mechinical properties. Crystallization peak temperatures were determined by differential thermal analysis(DTA). Crystalline phases and mircostructures of heat-treated sample were determined by the means of powder X-ray diffraction(XRD) and scanning electron microscopy(SEM). The final crystalline phase assemblages and the microstructures of the samples were found to be dependent on glass compositions, heattreatment temperature, and holding time. 1st crystallization peak temperature(TP), affected strongly by apatite, was found to be increased or decreased. From the experiment, the following results were obtained : 1. The crystallization peak temperature($T_P$) formed by apatite increased until adding up to 9wt% $TiO_2$ to base glass composition, then decreased above that. 2. Apatite($Ca_{10}P_6O_{25}$), whitlockite(${\beta}-3CaO-P_2O_5$), $\beta$-wollastonite($CaSiO_3$), magnesium tianate($MaTiO_3$) and diopside(CaO-MgO-$2SiO_2$) crystal phase were precipitated in MgO-CaO-$SiO_2-TiO_2-P_2O_5$ glass system containing 9wt% and 11wt% of $TiO_2$ 3. Vickers hardness of samples increased with increasing heat-treatment temperature and Vickers hardness of S415T9 samples heat-treated at 1075 was approxi-mately 813Kg $mm^{-2}$ as maximum value. 4. Vickers hardness of samples increased due to precipitation of apatite, whitlockite, $\beta$-wollastonite, magnesium titanate, and diopside crystal phases within glass matrix.

• Laser Solutions
• /
• v.11 no.2
• /
• pp.15-19
• /
• 2008

Electron beam (EB) weldability of pure grade Nb sheet was studied. One of Nb sheets was as-annealed and the other was cold rolled. Microstructures, Vickers hardness, and transverse weld tensile test were carried out for the base metal, the heat affected zone (HAZ) and weld metal. In the case of the EB welds made using the annealed Nb sheeet, fine equiaxed grains and coarse grains were dominant at the base metal and the HAZ, respectively, and columnar grains were observed at the weld metal. For the EB welds made using the cold rolled Nb sheet, elongated grains in the rolling direction at the base metal, and the microstructures of the weld metal and the HAZ are similar to those of the EB welds made using the annealed Nb sheet, respectively. For both annealed and cold rolled Nb sheet, the width of the HAZs are unusually wide in spite of using high density heat source, i.e. electron beam, and the grain sizes of both HAZs are similar. When tensile test was carried out using the transverse weld specimens, the failure occurred at the HAZ for both EB welds made using Nb sheets annealed and cold rolled, respectively and the tensile strengths of both specimens were 161MPa. Vickers hardness of EB welds made using annealed Nb was 56-57 Hv at both base metal and weld metal, 52-53 Hv at the HAZ. On the other hand, Vickers hardness of EB welds made using cold rolled Nb was 97-99 Hv at the base metal, but the hardness values of weld metal were similar to those obtained at the weld metal of annealed Nb.

• Korean Journal of Materials Research
• /
• v.28 no.4
• /
• pp.221-226
• /
• 2018

The property changes of 18, 14, and 8K green gold alloys for jewelry are observed by adding 0.0, 3.0, and 5.0 wt% of indium (In), respectively. To check the composition of the alloys, an energy dispersive spectroscopy (EDS) analysis is conducted. Color and microstructure analysis is executed through bare-eye, macro camera, UV-VIS-NIR-colormeter, and optical microscope. The melting point, wetting angle, and hardness are measured using TGA-DTA, a wetting angle tester, and a Vickers hardness tester. The EDS analysis result demonstrates that each of the green gold alloys was manufactured with purposed contents. The color analysis result shows that the color of the alloys is similar to the color of the conventional 4 wt%-Cd 18K green gold, and the green color improves as the In content increases. The micro structure analysis result demonstrates that grain refinement improves as the amount of In increases. Enhancements in the melting point, wettability, and Vickers hardness changes appear as the In content increases and Au content decreases. The hardness is up to 260, which implies good durability. Therefore, the results suggest that the proposed 18, 14, and 8K In-added green gold alloys enhance the properties of jewelry products with regard to the green color, castability, and durability.

• Journal of Technologic Dentistry
• /
• v.31 no.3
• /
• pp.9-14
• /
• 2009

This study evaluated the mechanical properties of Ti-Cu alloys with the hope of developing an alloy for dental casting with better mechanical properties than unalloyed titanium. Ti-Cu alloys with four concentrations of Cu(2,5,10wt%) were made in an argon-arc melting furnace. The microstructure and micro-Vickers hardness were determined. X-ray diffraction pattern test was performed on the polished specimens. The microstructure of 2%Cu and 5%Cu alloys are shown acicular ${\alpha}Ti$ phase formed on the surfaces of previously formed $\beta$grains. The 10%Cu alloys has essentially a eutectoid structure; this structure includes lamella of ${\alpha}Ti$ and $Ti_2Cu$ phase that transformed from ${\alpha}Ti$ at the eutectoid temperature. The micro-Vickers hardness of CP Ti specimens was significantly(p<0.05) lower than that of any of the other alloys. Among the Ti-Cu alloys, the 10%Cu alloys exhibited a significantly(p<0.05) higher hardness value. but lower than that of Ti-6%Al-4%V alloy. From these results, it was concluded that new alloys for dental castings should be designed as Ti-Cu based alloys if other properties necessary for dental castings were obtained.