• 한국결정성장학회지
• /
• 제6권2호
• /
• pp.254-262
• /
• 1996

수열합성법을 이용하여 $1~3\;\mu\textrm{m}$의 입자 크기를 갖는 균일한 $Pb(Zr_{0.52}Ti_{0.48})O_{3}$ (PZT)분말을 제조하였다. 출발물질의 종류에 따라 반응조건이 다소 차이를 보였지만, 일반적으로 10 M의 KOH를 광화제로 사용하여, $180^{\circ}C$ 이상에서 2시간 동안 반응시켜 PZT 분말을 합성 할 수 있었다. 또한, 광화제의 농도, 수열반응 온도, 그리고 반응시간이 증가할수록 균일상의 분말이 형성됨을 보였다.

• The Korean Journal of Ceramics
• /
• 제4권1호
• /
• pp.33-36
• /
• 1998

Epitaxially grown $Bi_4Ti_3O_{12}$ thin films on the MgO(100) substrates was prepared by dipping-pyrolysis process using metal naphthenates as starting materials. The films annealed at various temperatures were charactrized by X-ray diffraction $\theta$-2$\theta$ scans and pole-figure analysis ($\beta$ scanning). Highly c-axia oriented Bi4Ti3O12 films were crystallized by heat-treatment at 700$^{\circ}$ and 75$0^{\circ}C$ from precursor films pyrolyzed at 50$0^{\circ}C$. The X-ray pole-figure analysis indicated that the $Bi_4Ti_3O_{12}$ thin films have an epitaxial relationship with the MgO(100) substrates.

• 한국세라믹학회지
• /
• 제30권1호
• /
• pp.25-33
• /
• 1993

Formation reaction of Mn-Zn ferrite depending on various synthetic conditions of wet process was investigated using FeCl2.nH2O(n≒4), MnCl2.4H2O, ZnCl2 as starting materials. A stable intermediate precipitate was formed by the addition of H2O2. And the precipitate was hard to transform to spinel phase of Mn-Zn Fe2O4. Single phase of Mn-Zn Fe2O4 spinel was obtained above 8$0^{\circ}C$ reaction temperature. The powder had spherical particle shape and 0.02~0.05${\mu}{\textrm}{m}$ particle size. Fe(OH)2 solid solution, -FeO(OH) solid solution, -FeOOH, Mn-Zn Fe2O4 spinel were formed with air flow rate 180$\ell$/hr. However, single phase of Mn-Zn Fe2O4 spinel with cubic particle shape and 0.1~0.2${\mu}{\textrm}{m}$ particle size was formed with synthetic conditions of 8$0^{\circ}C$ and 90 munutes. The particle shape of the -FeOOH was needle-like.

• The Korean Journal of Ceramics
• /
• 제4권3호
• /
• pp.231-234
• /
• 1998

LaNiO3 thin films were fabricated on various substrates by spin-coating technique using metal naphthenates as starting materials. Highly-oriented LaNiO3 films with smooth and crack-free surfaces were grown on SrTiO3 (100) and LaAlO3(100) substrates, while films on MgO(100) and Si(100) substrates showed random orientation. In this study, we concluded that lattice-mismatches between LaNiO3 films and substrates used affect film's properties.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 제2회 학술대회 논문집 일렉트렛트 및 응용기술전문연구회
• /
• pp.73-76
• /
• 2000

Traction motors that is one of the rotating machines for urban transit EMU have been subjected to increased demand for higher operating temperature, more demanding duty cycles, higher starting current, frequent voltage transients and severe environmental exposure. With the advent of PWM drives using power IGBTs in addition to the thermal considerations, it is important to take into account the impact of the dielectric stress upon the winding insulation system life. In analyzing the life of the stator winding, which is the heart of the motor, the majority of all winding failures are usually caused by a combination of various stresses acting on the insulation materials and system. In this paper, to evaluate the expected life of traction motor for urban transit E.M.U. it is proposed a new test method of complex accelerating degradation.

• 한국안전학회지
• /
• 제13권1호
• /
• pp.85-91
• /
• 1998

Sol-gel derived silica films were prepared by dip-coating onto polymethylmethacylate with Tetraethoxysilane(TEOS) as starting materials. Film properties such as viscosity and thickness were investigated as a function of dip speed, waterprecursor ratio, sol aging time. IR spectra of the gel films prepared from TEOS at various R are given. At small values of R the absorption peaks assignable to C-H vibration in $-OC_2H_5$ groups are observed around 3000 and 1500-1300 $cm^{-1}$. These bands indicate that the -$-OC_2H_5$ groups are retained in the gel at small values of R because of incomplete hydrolysis of TEOS. Film behaviour was interpreted in terms of the dependence of hydrolysis and condensation rates on the interplay between sol pH and waterprecursor ratio. Film thickness was found to increase by approximately a factor of two as waterprecursor ratio increased from two to six. Film thickness also increased with sol prepolymerization time. Surface quality was correlated with processing conditions.

• 자원리싸이클링
• /
• 제13권1호
• /
• pp.54-58
• /
• 2004

Wollastonite-type glass ceramics were prepared by milling and firing at various temperatures using an automobile waste glass and waste shell as starting materials. Powder mixture ground by disk-type ball mill for 3 hours was pressed into a disk. The pressed specimen was fired at $850^{\circ}C$,$950^{\circ}C$ and $1050^{\circ}C$ for 1 hour in air. From FE-SEM observation, with an increase of the firing temperature from $850^{\circ}C$ to $1050^{\circ}C$, whisker-type phase was grown to about 10 $\mu\textrm{m}$ in length. Specimen fired at $1050^{\circ}C$ showed the formation of well-crystallized whisker-type wollastonite grains and the highest compressive strength.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2010년도 제39회 하계학술대회 초록집
• /
• pp.292-292
• /
• 2010

Among the semiconducting materials, ZnO has considerably attracted attention over the past few years due to the high activities in removing organic contaminants created from industry. In this work, ZnO nanoparticles were synthesized by spray pyrolysis method using the zinc acetate dihydrate as starting material at various synthesis temperatures. The structures of the synthesized ZnO were characterized by X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Brunauer, Emmett & Teller (BET), Fourier Transformation Infrared (FT-IR), and UV-vis spectroscopy. The Miller indices of XRD patterns indicate that the synthesized ZnO nanoparticles showed a hexagonal wurtzite structure. With increasing synthesis temperature, the mean diameter of ZnO nanoparticles increased, and their crystallinity was improved. Also, the photocatalytic activity of ZnO was studied by the photocatalytic degradation of methyleneblue (MB) under UV irradiation (365 nm) at room temperature. The results show that the photocatalytic efficiency of ZnO nanoparticles was enhanced by increasing synthesis temperature.

• 한국세라믹학회지
• /
• 제26권4호
• /
• pp.493-498
• /
• 1989

High purity, submicron BaTiO3 powder was prepared by a hydrothermal technique using Ba(OH)2.8H2O, TiCl4 and NH4OH as starting raw materials. The submicron BaTiO3 powder was synthesized at 130~23$0^{\circ}C$ for 2.5h to yield highly crystalline particles with a narrow particle distribution. The mole ratio of Ba(OH)2.8H2O/TiO(OH)2 was 1.5. It is possible to obtain BaTiO3 with Ba : Ti=1.00$\pm$0/01. The samples densified well at 13$25^{\circ}C$, showing a uniform and fine grain structure. The grain size ranged between 0.3 and 0.5${\mu}{\textrm}{m}$. The products obtained by hydrothermal treatment at various temperatures from 130 to 23$0^{\circ}C$ were characterized by XRD, DTA, BET and SEM etc.

• 대한화장품학회지
• /
• 제22권2호
• /
• pp.89-98
• /
• 1996

A novel polymeric sunscreen agent was developed. It was prepared by the coupling reaction of 2-ethylhexyl 4-hydroxycinnamate with poly vinylbenzyl chloride(PVBC, average MW 6,500). In this reaction the reactivity was mostly affected by catalyst. In the absence of catalyst the yield was approximately 55% and in the presence of tetrabutylammonium bromide the yield was about 65%, but in the presence of tetrabutylammonium iodide the yield was 100% to give a average molecular weight 20,000 polymeric sunscreen agent. There were no side reactions, and its structure and purity were confirmed by various analytical methods, such as NMR, IR, and so on. UV radiation absorption efficiency is more than 70% compared with that of octyl methoxycinnamate. The solubility in polar oil, for example C12-15 alkylbenzoate and caprylic/capric triglyceride, is more than 50%. It showed high stability in the time course of test including acceleration test. This polymer is safe to skin because of poor permeability to skin, no side products in the process of preparing, and easy elimination of excess starting materials.