• Journal of Sensor Science and Technology
• /
• v.10 no.6
• /
• pp.328-337
• /
• 2001

The stochiometric mix of evaporating materials for the $CdGa_2Se_4$ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films, $CdGa_2Se_4$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were $630^{\circ}C$ and $420^{\circ}C$, respectively. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of $CdGa_2Se_4$ single crystal thin films measured from Hall effect by van der Pauw method are $8.27{\times}10^{17}cm^{-3}$, $345\;cm^2/V{\cdot}s$ at 293 K, respectively. From the photocurrent spectrum by illumination of perpendicular light on the c-axis of the $CuInSe_2$ single crystal thin film, we have found that the values of spin orbit splitting ${\Delta}So$ and the crystal field splitting ${\Delta}Cr$ were 106.5 meV and 418.9 meV at 10 K, respectively. From the photoluminescence measurement on $CdGa_2Se_4$ single crystal thin film, we observed free excition ($E_x$) existing only high quality crystal and neutral bound exiciton ($D^{\circ}$, X) having very strong peak intensity. Then, the full-width-at -half-maximum(FWHM) and binding energy of neutral donor bound excition were 8 meV and 13.7 meV, respectivity. By Haynes rule, an activation energy of impurity was 137 meV.

• Journal of Sensor Science and Technology
• /
• v.4 no.1
• /
• pp.51-63
• /
• 1995

Polycrystalline $CdS_{1-x}Se_{x}$ thin films were grown on ceramic substrate using a chemical bath deposition method. They were annealed at various temperature and X-ray diffraction patterns were measured by X-ray diffractometer in order to study $CdS_{1-x}Se_{x}$ polycrystal structure using extrapolation method of X-ray diffraction patterns for the CdS, CdSe samples annealed in $N_{2}$ gas at $550^{\circ}C$ it was found hexagonal structure which had the lattice constant $a_{0}=4.1364{\AA}$, $c_{0}=6.7129{\AA}$ in CdS and $a_{0}=4.3021{\AA}$, $c_{0}=7.0142{\AA}$ in CdSe, respectively. Hall effect on these samples was measured by Van der Pauw method and then studied on carrier density and mobility depending on temperature. We measured also spectral response, sensitivity(${\gamma}$), maximum allowable power dissipation and response time on these samples.

• Journal of Sensor Science and Technology
• /
• v.7 no.2
• /
• pp.131-139
• /
• 1998

$CdS_{0.67}Se_{0.33}$ single crystal was grown by vertical sublimation method of closed tube physical vapour deposition. The (0001) growth plane of oriented single crystals was confirmed from the back-ref1ection Laue patterns. From the Hall effects by van der Pauw method, the as-grown $CdS_{0.67}Se_{0.33}$ single crystals were found to be n-type semiconductors. The mobility appeared to be decreased by lattice scattering at temperature range from 150K to 293K and by impurity scattering at temperatures ranging from 30K to 150K In order to explore its applicability in photoconductive cells, we measured the ratio of photo-current to dark-current (pc/dc), maximum allowable power dissipation (MAPD), spectral response and response time respectively. The results indicated that for the samples annealed in Cu vapour the photoconductive characteristics are best. We obtained sensitivity of 0.99, the value of pc/de of $1.84{\times}10^{7}$, the MAPD of 323mW and the rise and decay time of 9.3 ms and 9.7 ms, respectively.

• Journal of Sensor Science and Technology
• /
• v.4 no.3
• /
• pp.60-70
• /
• 1995

Polycrystalline $Cd_{1-x}Zn_{x}S$ thin film were grown on slide glass(corning-2948) substrate using a chemical bath deposition (C.B.D) method. They were annealed at various temperature and X -ray diffraction patterns were measured by X-ray diffractometor in order to study $Cd_{1-x}Zn_{x}S$ polycrystal structure using extrapolation method of X-ray diffraction patterns for the CdS, ZnS sample annealed in $N_{2}$ gas at $550^{\circ}C$. It was found hexagonal structure which had the lattice constant $a_{0}\;=\;4.1364{\AA}$, $c_{0}\;=\;6.7129{\AA}$ in CdS and $a_{0}\;=\;3.8062{\AA}$, $c_{0}\;=\;6.2681{\AA}$ in ZnS, respectively. Hall effect on these sample was measured by Van der Pauw method and then studied on carrier density and mobility depending on temperature. We measured also spectral response, sensitivity maximum allowable power dissipation and response time on these sample.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.6 no.1
• /
• pp.32-43
• /
• 1996

A $CdIn_{2}Te_{4}$ single crystal was grown by modified veritical bridgman method. The $CdIn_{2}Te_{4}$ single crystal was evaluated to be tetragonal by the powder method. The $CdIn_{2}Te_{4}$ single crystal was confirmed to be grown with its c axis along the lengthe of the boule by the Laue reflection method. Hall effect of $CdIn_{2}Te_{4}$ single crystal was estimated by van der pauw method from 293 K to 30 K. Hall data of the sample perpendicular to c axis was $n=8.75{\times}10^{23}electrons/m^{3},\;R_{H}=7.14{\times}10^{-5}m^{3}/C,\;{\sigma}=176.40{\omega}^{-1}m^{-1},\;{$\mu}=3.41{\times}10^{-2}m^{2}/V.s$ and the sample parallel to c axis was $n=8.61{\times}10^{23}electrons/m^{3},\;R_{H}=7.26{\times}10^{-5}m^{3}/C,\;{\sigma}=333.38{\omega}^{-1}m^{-1}\;and\;{$\mu}=2.42{\times}10^{-2}m^{2}/V.s$ for room temperature. The value of Hall coefficient on sample perpendicular or parallel to c axis were positive. There $CdIn_{2}Te_{4}$ single crystal was p-type semiconductor.

• Korean Journal of Crystallography
• /
• v.7 no.1
• /
• pp.44-56
• /
• 1996

CuInTe2 synthesised in a horizontal electric furnace was found to be polycrystalline. Single crystals of CuInTe2 were grown with the vertical Bridgman technique. The structure, Hall effect of the crystals were measured in the temperature range 30 to 293K. Both the polycrystals and single crystals of CuInTe2 were tetragonal in structure. The lattice constants of the polycrytals were measured as a=6.168Å and c=12.499Å, with c/a=2.026, these of the single crystals were measured as a=6.186Å and c=12.453Å, with c/a=2.013. The growth plane of the oriented single crystals was confirmed to be a (112) plane from the back-reflection Laue patterns. The Hall effect of the CuInTe2 single crystals was measured with the method of van der Pauw The Hall data of the samples measured at room temperature showed a carrier concentration of 2.14×1023holes/m3, a conductivity of 739.58Ω-1m-1, and a mobility of 2.16×10 -2m 2/V·s for the sample perpendicular to the c-axis. Values of 1.51×1023holes/m3, 717.55Ω-1m-1, and 2.97×10-2 m2/V·s were obtained for the sample parallel to the c-axis. The Hall coefficients for the samples both perpendicular and parallel to the c-axis in the temperature range 30K to 293K were always positive values. Thus the CuInTe2 single crystal was determined to be a p-type semiconductor.

• Journal of Sensor Science and Technology
• /
• v.2 no.1
• /
• pp.3-10
• /
• 1993

Polycrystalline CdS thin films were grown on ceramic substrate using a chemical bath deposition method. They were annealed at various temperature and X-ray diffraction patterns were measured by X-ray diffractometer in order to study CdS polycrystal structure. Using extrapolation method of X-ray diffraction patterns for the CdS samples annealed in $N_{2}$ gas at $550^{\circ}C$ it was found hexagonal structure whose lattice constants $a_{o}$ and $c_{o}$ were $4.1364{\AA}$ and $6.7129{\AA}$, respectively. Its grain size was about $0.35{\mu}m$. Hall effect on this sample was measured by Van der Pauw method and studied on carrier density and mobility defending on temperature. From Hall data, the mobility was likely to be decreased by piezo electric scattering at temperature range of 33K and 150k and by polar optical scattering at temperature range of 150K and 293K. We measured also spectral response, sensitivity (${\gamma}$), maximum allowable power dissipation and response time on these samples.

• Journal of Sensor Science and Technology
• /
• v.2 no.1
• /
• pp.81-86
• /
• 1993

Polycrystalline CdSe thin films were grown on ceramic substrate using a chemical bath deposition (CBD) method. They were annealed at various temperature and X-ray diffraction patterns were measured by X-ray diffractometer in order to study CdSe polycrystal structure. Using extrapolation method of X-ray diffraction patterns for the CdSe samples annealed in $N_{2}$ gas at $450^{\circ}C$ it was found hexagonal structure whose lattice parameters $a_{o}$ and $c_{o}$ were $4.302{\AA}$ and $7.014{\AA}$, respectively. Its grain size was about $0.3{\mu}m$. Hall effect on this sample was measured by Van der Pauw method and studied on carrier density and mobility depending on temperature. From Hall data, the mobility was likely to be decreased by piezo electric scattering at temperature range of 33 K and 200 K, and by polar optical scattering at temperature range of 200 K and 293 K. We measured also spectral response, sensitivity (${\gamma}$), maximum allowable power dissipation and response time on these samples.

• Korean Journal of Materials Research
• /
• v.15 no.5
• /
• pp.293-300
• /
• 2005

ZnO:Li epilayers were synthesized on sapphire substrates by the pulesd laser deposition (PLD) after the surface of the ZnO:Li sintered pellet was irradiated by the ArF (193 nm) excimer laser. The growth temperature was fixed at $400^{\circ}C$. The crystalline structure of epilayers was investigated by the photoluminescence (PL) and double crystal X-ray diffraction (DCXD). The carrier density and mobility of epilayers measured by van der Pauw-Hall method are $2.69\times10cm^{-3}$ and $52.137cm^2/V{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of epilayers obtained from the absorption spectra is well described by the Varshni's relation, $E_g(T)=3.5128eV{\cdot}(9.51\times10^{-4}eV/K)T^2/(T+280K)$. After the as-grown ZnO:Li epilayer was annealed in Zn atmospheres, oxygen and vaccum the origin of point defects of ZnO:Li has been investigated by PL at 10 K. The Peaks of native defects of $V_{zn},\;V_o,\;Zn_{int},\;and\;O_{int}$ showned on PL spectrum are classified as a donors or accepters type. We confirm that $ZnO:Li/Al_2O_3$ in vacuum do not form the native defects because ZnO:Li epilayers in vacuum existe in the form of stable bonds.

• Journal of the Korean Vacuum Society
• /
• v.4 no.1
• /
• pp.85-90
• /
• 1995

본 연구에서는 투명 전극으로의 응용을 목적으로 PECVD법에 의해 증착된 B이 첨가된 ZnO 박막의 전기 및 광학적 특성을 살펴보았다. B을 첨가하지 않은 ZnO 박막은 비저항이 수 $\Omega$-cm 정도의 값을 가지고 있었으며 시간에 따른 비저항의 변화가 컸으나, 2% B2H6을 5-16sccm의 유량범위에서 첨가한 경우에는 5-9X10-2 $\Omega$-cm의 비저항을 가지고 시간 경과에 따른 비저항의 변화가 아주 작은 ZnO 박막을 얻을 수 있었다. Van der Pauw법에 의한 Hall 계수의 측정 결과에 의하면, B을 첨가하지 않은 ZnO 박막의 전자 농도는 1017/㎤정도였으나 B을 첨가함으로써 최고 1020/㎤까지 증가하였다. 그러나 B이 첨가되기 전에는 박막의 전하 나르게 이동도가 $4extrm{cm}^2$/V.sec 이었으나, B참가에 의해 $0.7\textrm{cm}^2$/V.sec 이하로 감소하였다. B을 첨가한 경우와 첨가하지 않은 경우의 ZnO 박막은 모두 가시광성영역에서 90%이상의 광투과율을 가지고 있었으며, B을 첨가한 경우는 전자농도가 증가함에 따라 광학적 밴드 갭이 3.3eV로부터 3.55eV로 증가하는 거동을 보였다.