Abstract
The stochiometric mix of evaporating materials for the $CdGa_2Se_4$ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films, $CdGa_2Se_4$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were $630^{\circ}C$ and $420^{\circ}C$, respectively. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of $CdGa_2Se_4$ single crystal thin films measured from Hall effect by van der Pauw method are $8.27{\times}10^{17}cm^{-3}$, $345\;cm^2/V{\cdot}s$ at 293 K, respectively. From the photocurrent spectrum by illumination of perpendicular light on the c-axis of the $CuInSe_2$ single crystal thin film, we have found that the values of spin orbit splitting ${\Delta}So$ and the crystal field splitting ${\Delta}Cr$ were 106.5 meV and 418.9 meV at 10 K, respectively. From the photoluminescence measurement on $CdGa_2Se_4$ single crystal thin film, we observed free excition ($E_x$) existing only high quality crystal and neutral bound exiciton ($D^{\circ}$, X) having very strong peak intensity. Then, the full-width-at -half-maximum(FWHM) and binding energy of neutral donor bound excition were 8 meV and 13.7 meV, respectivity. By Haynes rule, an activation energy of impurity was 137 meV.
수평 전기로에서 $CdGa_2Se_4$ 다결정을 합성하여 HWE 방법으로 $CdGa_2Se_4$ 단결정 박막을 반절연성 GaAs(100) 위에 성장하였다. $CdGa_2Se_4$ 단결정 박막은 증발원과 기판의 온도를 각각 $630^{\circ}C$, $420^{\circ}C$로 성장하였다. 10K에서 측정한 광발광 exciton 스펙트럼과 이중결정 X-선 요동곡선(DCRC)의 반치폭(FWHM)을 분석하여 단결정 박막의 최적 성장 조건을 얻었다. Hall 효과는 van der Pauw 방법에 의해 측정되었으며, 온도에 의존하는 운반자 농도와 이동도는 293K에서 각각 $8.27{\times}10^{17}/cm^3$, $345\;cm^2/V{\cdot}s$였다. 광전류 봉우리의 10K에서 단파장대의 가전자대 갈라짐(splitting)에 의해서 측정된 ${\Delta}Cr$ (crystal field splitting)은 106.5 meV, ${\Delta}So$ (spin orbit splitting)는 418.9 meV였다. 10K의 광발광 측정으로부터 고품질의 결정에서 볼 수 있는 free exciton 과 매우 강한 세기의 중성 주개 bound exciton등의 피크가 관찰되었다. 이때 중성 주개 bound exciton의 반치폭과 결합 에너지는 각각 8 meV와 13.7 meV였다. 또한 Haynes rule에 의해 구한 불순물의 활성화 에너지는 137 meV 였다.