• Membrane and Water Treatment
• /
• v.11 no.3
• /
• pp.223-229
• /
• 2020

Here magnetic iron oxide particles (MIOPs) were synthesized under atmospheric air and which size was controlled by regulating the flow rate of alkali addition and used for efficient removal of bovine serum albumin (BSA) from water. The MIOPs were characterized using field-emission scanning electron microscopy (FE-SEM), Fourier transformation-Infrared spectroscopy (FT-IR) and vibrating sample magnetometer (VSM). The results revealed a successful preparation of the MIOPs. The removal efficiency for BSA using MIOPs was found to be about 100% at lower concentrations (≥ 10 mg/L). The maximum adsorption of 64.7 mg/g for BSA was achieved as per the Langmuir adsorption model. In addition, microfiltration membrane for removal of BSA as model protein organic foulant is also studied. The effect of various MIOPs adsorbent sizes of 210, 680 and 1130 nm on the absorption capacity of BSA was investigated. Water permeability of the BSA integrated with the smallest size MIOPs membrane was increased by approximately 22% compared by the neat BSA membrane during dead-end filtration. Furthermore, the presence of small size MIOPs were also effective in increasing the permeate flux.

• Korean Journal of Materials Research
• /
• v.5 no.4
• /
• pp.433-444
• /
• 1995

BaCe$O_{3}$를 첨가하여 용융공정으로 제조한 단결정형 Y$Ba_{2}$$Cu_{3}$$O_{x}$(1-2-3) 초전도체의 온도에 대한 자화특성을 연구하였다. 고상반응법과 용융공정으로 0에서 30wt% BaCe$O_{3}$를 1-2-3 결정내에 미세 분산시켰다. 초전도체의 자화특성은 VSM(vibrating sample magnetometer)을 사용하여 77K, 60K, 40K와 20K, 2 Tesla 자장범위에서 측정하였다. BaCe$O_{3}$를 첨가하지 않은 겨우나 5wt% BaCe$O_{3}$를 첨가한 1-2-3 결정의 경우, 77K, 외부자장이 증가시 자화율 차이가 증가하는 비정상 자화특성이 관찰된다. 측정온도가 60K에서는 제2차 최대점이 나타나는 자장값이 고자장쪽으로 이동한다. 20K와 40K의 저온에서는 비정상자화특성이 2 T의 자장범위까지 관찰되지 않았다. 15wt%와 20wt% BaCe$O_{3}$첨가한 시편에서는 자장이 증가하면 자화율차이가 단순히 감소한다. Y-Ba-Cu-O의 flux pinning 기구를 BaCe$O_{3}$첨가에 의한 미세조직변화로 설명하였다.

• Journal of Powder Materials
• /
• v.26 no.6
• /
• pp.481-486
• /
• 2019

Iron oxides currently attract considerable attention due to their potential applications in the fields of lithiumion batteries, bio-medical sensors, and hyperthermia therapy materials. Magnetite (Fe₃O₄) is a particularly interesting research target due to its low cost, good biocompatibility, outstanding stability in physiological conditions. Hydrothermal synthesis is one of several liquid-phase synthesis methods with water or an aqueous solution under high pressure and high temperature. This paper reports the growth of magnetic Fe₃O₄ particles from iron powder (spherical, <10 ㎛) through an alkaline hydrothermal process under the following conditions: (1) Different KOH molar concentrations and (2) different synthesis time for each KOH molar concentrations. The optimal condition for the synthesis of Fe₃O₄ using Fe powders is hydrothermal oxidation with 6.25 M KOH for 48 h, resulting in 89.2 emu/g of saturation magnetization at room temperature. The structure and morphologies of the synthesized particles are characterized by X-ray diffraction (XRD, 2θ = 20°-80°) with Cu-kα radiation and field emission scanning electron microscopy (FE-SEM), respectively. The magnetic properties of magnetite samples are investigated using a vibrating sample magnetometer (VSM). The role of KOH in the formation of magnetite octahedron is observed.

• Proceedings of the KIEE Conference
• /
• 1998.07d
• /
• pp.1279-1281
• /
• 1998

The Co-Cr thin films are one of the most suitable candidates for perpendicular magnetic recording media. The facing targets sputtering(FTS) method has a advantage of preparing films over a wide range of working gas pressure on plasma-free substrates. In this study, we investigated the possibility of employing FTS system for depositing Co-Cr films, Co-Cr thin films were deposited with continuously sputter gas pressure ($P_{Ar}$ = 0.1 mTorr) by FTS method at temperature of $40^{\circ}C$. We find that the change of thickness and deposition rate of sputtered Co-Cr thin films affect crystal orientation and magnetic properties. Crystallographic and magnetic properties were evaluated by x-ray diffractometry(XRD) and vibrating sample magnetometer(VSM) respectively. It has been confirmed that the FTS method is very useful for preparing Co-Cr thin film recording media.

• Journal of the Korean Ceramic Society
• /
• v.38 no.6
• /
• pp.551-557
• /
• 2001

La$_{0.7}$Ca$_{0.3}$MnO$_3$분말을 용액연소법으로 제조하였으며 분말 특성과 CMR에 응용하기 위해 박막의 전기적, 자기적 특성을 조사하였다. 조성과 구조 특성을 XRD와 SEM으로부터 조사하였으며 분말의 하소온도를 TG 분석으로부터 결정하였다. 또한 소결성은 dilatometer에 의해 조사되었으며 분말 특성은 BET에 의해 조사되었다. 소결성이 우수한 분말을 이용하여 스퍼터 타겟으로 제조하였으며 SiO$_2$/Si 기판 위에 스퍼터링한 후, 온도에 따른 four point probe 측정으로 막의 MR비를 측정하였다. VSM (Vibrating Sample Magnetometer)를 이용하여 증착된 막의 온도에 따른 자화율(Magnetization:M)을 측정하였다. 분말 특성으로는 평균입자 크기가 sub-micron 이하로 초미세하고 49.44$m^2$/g의 비표면적 값을 얻을 수 있었으며 고순도의 perovskite 구조를 갖는 La$_{0.7}$Ca$_{0.3}$MnO$_3$분말을 쉽게 얻을 수 있었다. 온도에 따른 저항값의 변화로부터 96K에서 최고의 MR값을 얻을 수 있었으며, 240K에서 강자성체로 전이되었다.로 전이되었다.

• Journal of Magnetics
• /
• v.14 no.4
• /
• pp.161-164
• /
• 2009

Iron-doped $Sn_{1-x}Fe_xO_2$ (x = 0.0, 0.05, 0.1, 0.2, 0.33) thin films on Si(100) substrates and powders were prepared by a chemical solution process. The x-ray diffraction (XRD) patterns of the $Sn_{1-x}Fe_xO_2$ thin films and powders showed a polycrystalline rutile tetragonal structure. Thermo gravimetric (TG) - differential thermal analysis (DTA) showed the final weight loss above $430{^{\circ}C}$ for all powder samples. According to XRD Rietveld refinement of the powders, the lattice parameters and unit cell volume decreased with increasing Fe content. The magnetic properties were characterized using a vibrating sample magnetometer (VSM) and M$\ddot{o}$ssbauer spectroscopy. The thin film samples with x = 0.1 and 0.2 showed paramagnetic properties but thin films with x = 0.33 exhibited ferromagnetic properties at room temperature. Mossbauer studies revealed the $Fe^{3+}$ valence state in the samples. The ferromagnetism in the samples can be interpreted in terms of the direct ferromagnetic coupling of ferric ions via an electron trapped in a bridging oxygen deficiency, which can be explained using the F-center exchange model.

• Journal of Magnetics
• /
• v.1 no.1
• /
• pp.19-23
• /
• 1996

In the present study, the $Sm_2Fe_{17}N_x$-type interstitial materials have been prepared by reaction between Nb-free or Nb-containing $Sm_2Fe_{17}$-type alloy and $N_2$ gas. Nitrogenation behaviour of the $Sm_2Fe_{17}N_x$-type material and disproportionation characteristics of the nitrogenated materials have been studied by means of differential thermal analysis (DTA) and thermopiezic analysis (TPA). Magnetic properties of the produced $Sm_2Fe_{17}N_x$-type interstitial materials were characterised in vibrating sample magnetometer (VSM) or thermomagnetic analyser (TMA). Epoxy-bonded or Zn-bonded $Sm_2Fe_{17}N_x$-type magnets were prepared, and their magnetic properties were investigated. It has been found that nitrogenation kinetics of the Sm2Fe17Nx-type alloy is improved significantly by the Nb-substitution for Fe in the alloy. The Nb-substitution is also found to enhance thermal stability of the $Sm_2Fe_{17}N_x$-type interstitial material. Hard magnetic properties of the interstitial materials produced from Nb-free orNb-containing alloy is high enough (intrinsic coercivity : over 7 kOe) for application as bonded permanent magnets. The good hard magnetic properties of the interstitial material are maintained in the epoxy-bonded magnet. Intrinsic coercivity of the Zn-bonded magnets is improved significantly as post-bonding annealing time increases.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.5
• /
• pp.418-422
• /
• 1998

The Co-Cr films are one of the most suitable candidates for perpendicular magnetic recording media. The facing targets sputtering(FTS) system has a advantage of preparing films over a wide range of working gas pressure on plasma-free substrate. In this study, we investigated the possibility of employing FTS system for depositing Co-Cr films. The Co-Cr thin films were deposited with various sputter gas pressure($P_Ar$, 0.1~10mTorr) by using FTS apparatus at temperature of $40^{\circ}C and 220^{\circ}C$, respectively. Crystallographic and magnetic characteristics were evaluated by x-ray diffractometry (XRD) and vibrating sample magnetometer(VSM), respectively. Under argon gas pressure at 0.1mTorr, films with morphologically dense microstructure, good c-axis orientation and higher coercivity were obtained. It has been confirmed that the FTS system is very useful for preparing Co-Cr thin film recording media.

• Journal of Radiation Industry
• /
• v.9 no.1
• /
• pp.15-20
• /
• 2015

Carbon fiber has received much attention owing to its properties, including a large surface-to-volume ratio, chemical and thermal stability, high thermal and electrical conductivity, and high mechanical strengths. In particular, magnetic nanopowder dispersed carbon fiber has been attractive in technological applications such as the electrochemical capacitor and electromagnetic wave shielding. In this study, the nickel-oxide-nanoparticle dispersed polyacrylonitrile (PAN) fibers were prepared through an electrospinning method. Electron beam irradiation was carried out with a 2.5 MeV beam energy to stabilize the materials. The samples were then heat-treated for stabilization and carbonization. The nanofiber surface was analyzed using a field emission scanning electron microscope (FE-SEM). The crystal structures of the carbon matrix and nickel nanopowders were analysed using X-ray diffraction (XRD). In addition, the magnetic and electrical properties were analyzed using a vibrating sample magnetometer (VSM) and 4 point probe. As the irradiation dose increases, the density of the carbon fiber was increased. In addition, the electrical properties of the carbon fiber improved through electron beam irradiation. This is because the amorphous region of the carbon fiber decreases. This electron beam effect of PAN fibers containing nickel nanoparticles confirmed their potential as a high performance carbon material for various applications.

• Journal of the Korean Magnetics Society
• /
• v.11 no.4
• /
• pp.168-172
• /
• 2001

Co-Zn ferrite thin films grown on thermally oxidized silicon wafers were fabricated by a sol-gel method. Magnetic and structural properties of Co-Zn thin films were investigated by using x-ray diffractometer (XRD), atomic force microscopy (AFM), auger electron spectroscopy (AES) and a vibrating sample magnetometer (VSM). Co-Zn ferrite thin films annealed at 400 $^{\circ}C$ presented have only a single phase spinel structure without any preferred crystallite orientation. Their surface roughness of Co-Zn ferrite thin films was shown as less than 3 nm and the grain size was about 40 nm for annealing temperatures over 600 $^{\circ}C$. A moderate saturation magnetization of Co-Zn ferrite thin films for recording media was obtained in this study and there is no significant difference of their magnetic property with those external fields of parallel and perpendicular to planes of the films. The maximum value of the coercivity was obtained as 1,900 Oe for Co-Zn ferrite thin film annealed at 600 $^{\circ}C$.