• 한국염색가공학회지
• /
• 제35권3호
• /
• pp.151-158
• /
• 2023

In this study, we investigated the durability properties of the recycled leather using shaving scrap with antioxidant. Recycled leather sheets were manufactured by mixing shaving scrap and NB latex as a binder. HALS(Hindered Amine Light Stabilizer) and UVA(UV absorbers) were used as antioxidant. Mechanical properties such as hardness, tensile strength, elongation, tear strength and abrasion resistance were measured. Light aging resistance was evaluated using UV lamp and the degree of discoloration of the recycled leather sheets using a gray scale. In addition, to evaluate heat aging and UV aging, the degree of discoloration of the recycled leather sheets over time was measured using colorimeter. Washing fastness was evaluated on the degree of dyeing of recycled leather sheets for six type of multi-fiber woven fabrics (Acetate, Cotton, Nylon-66, Polyester, Acryl, Wool). To determine whether hazardous substances were detected in recycled leather sheets, the contents of arylamine and Cr 6⁺ were evaluated. As a result, when used in combination with antioxidant, the heat aging and light aging of recycled leather were improved and hazardous substance were not detected.

• 한국응용과학기술학회지
• /
• 제26권4호
• /
• pp.467-472
• /
• 2009

Ultraviolet curable coating solution was prepared with poly(ethylene glycol) acrylate oligomer and various mono and multi-functional acrylate monomers. The optical properties of UV cured coating layer on PET film with acrylate coating solution containing metal oxides, such as fumed silica and alumina, were also investigated to reduce light reflection on films. Poly(ethylene glycol) diacrylate which has 575 of average molecular weight was used as oligomer acrylate, and pentaerythritol triacrylate and dipentaerythritolpenta-/hexa acrylate were used as multi-functional acrylate monomers. Also, butyl acrylate was used to improve the adhesion as well as to reduce glass transition temperature to give a better flexability. 1-hydroxy cyclohexyl phenyl ketone was used as photoinitiator. We found out the metal oxides in acrylate coating solution showed a homogeneous dispersion from energy dispersive spectroscopy data. Transmittance and light reflection of coated PET film was measured with UV/vis spectrometer and gloss meter, respectively. When 1.00 g of both metal oxides was added into coating solution, the transmittance and the glossiness were reduced from 90% to 30% and from 190 GU to 35 GU, respectively. However, adding up to 1.00 g of the metal oxide into coating solution did not affect on the hardness of coating layer and adhesion between coated layer and PET film. Conclusively, we can control transmittance and light reflection of coated film by adjusting the amounts of metal oxide in coating solution.

• 접착 및 계면
• /
• 제3권4호
• /
• pp.10-18
• /
• 2002

오늘날 플라스틱은 많은 분야에서 매우 중요한 역할을 하고 있으며, 플라스틱의 표면개질을 통해 경도, 마모, 내화학성과 같은 성질을 개선하여 성능을 향상시킬 수 있다. 본 연구의 목적은 polycarbonate, polymethylmethacrylate, acrylonitrilebutadienestyrene과 같은 플라스틱에 적용되는 기능성 하드코팅제를 개발하기 위한 것이다. 하드코팅제를 개발하기 위하여 먼저 실리콘아크릴레이트 올리고머(SAOE)를 합성하고, 이를 함유한 코팅필름을 PC 기재로 하였으며, 도막은 자외선경화에 의하였다. 실험의 결과에 의하면, SAOE를 함유하고 있는 도막의 물성이 SAOE를 함유하고 있지 않은 도막의 물성에 비해서 크게 향상되었다. 특히 코팅 조성물내에 1wt%의 SAOE가 함유되었을 때, 이로부터 얻어진 도막의 경도나 광택이 가장 우수함을 나타내었다.

• 마이크로전자및패키징학회지
• /
• 제27권4호
• /
• pp.113-117
• /
• 2020

논문에서는 고분자 나노구조 필름의 기계적 물성을 향상하기 위하여 광열효과를 이용한 열처리 공정을 응용하여 나노임프린트로 제작된 고분자 나노구조 필름의 기계적 물성에 미치는 영향을 규명하였다. Hybrid resin과 UV 나노임프린트을 이용하여 저반사 나노구조를 성형하고 IPL (intense pulsed light)를 이용하여 열처리를 수행한 뒤, 제작된 나노구조 필름의 투과율과 내스크래치성을 평가하여 나노구조의 성형성과 기계적 물성의 변화를 관찰하였다. 나노패턴의 특성에 의해서 나노구조의 투과율은 550 nm 파장에서 97.6%로 고투과율의 기능을 확인하였으며, IPL을 이용한 열처리를 진행한 경우 Hotplate를 이용한 열처리보다 경도는 0.51 GPa로, 0.27 GPa로 열처리한 시편에 비해 1.8배 향상하였으며, 동일 실험 조건에서 탄성율은 Hotplate 이용 시 4 GPa에서 IPL 이용 시 5.9 GPa로 1.4배 증가하였다.

• 한국재료학회지
• /
• 제28권4호
• /
• pp.221-226
• /
• 2018

The property changes of 18, 14, and 8K green gold alloys for jewelry are observed by adding 0.0, 3.0, and 5.0 wt% of indium (In), respectively. To check the composition of the alloys, an energy dispersive spectroscopy (EDS) analysis is conducted. Color and microstructure analysis is executed through bare-eye, macro camera, UV-VIS-NIR-colormeter, and optical microscope. The melting point, wetting angle, and hardness are measured using TGA-DTA, a wetting angle tester, and a Vickers hardness tester. The EDS analysis result demonstrates that each of the green gold alloys was manufactured with purposed contents. The color analysis result shows that the color of the alloys is similar to the color of the conventional 4 wt%-Cd 18K green gold, and the green color improves as the In content increases. The micro structure analysis result demonstrates that grain refinement improves as the amount of In increases. Enhancements in the melting point, wettability, and Vickers hardness changes appear as the In content increases and Au content decreases. The hardness is up to 260, which implies good durability. Therefore, the results suggest that the proposed 18, 14, and 8K In-added green gold alloys enhance the properties of jewelry products with regard to the green color, castability, and durability.

• 박물관보존과학
• /
• 제21권
• /
• pp.1-16
• /
• 2019

본 논문은 유리제 문화재 복원에 안정한 물성을 지닌 복원재료를 선정하기 위한 연구이다. 아크릴계 광경화성수지(FLGPCL04 Clear^®)를 기준으로 우레탄계 광경화성수지(SECURE CP-7321^®)를 10%씩 가감한 혼합 시편 11종을 제작하고 6종의 물성실험을 실시하였다. 실험결과 굴절률, 비중, 접착력, 황변도의 측정값에 대해서는 11종 혼합재료 모두에 대하여 유사하였으나 표면경도 및 압축강도 측정값에서는 우레탄계 광경화성 수지의 혼합 비율이 10~20% 범위일 때 가장 적합하였다. 즉, 유리제 유물을 복원한 이후의 상태 유지에 가장 효과적이다. 이와 같은 연구결과를 바탕으로 아크릴계와 우레탄계 광경화성 수지를 9:1로 혼합한 재료(AU9010)를 경주 황남대총 북분에서 출토된 유리잔 (황북519)의 보존 처리에 적용하였다.

• 공업화학
• /
• 제24권5호
• /
• pp.499-506
• /
• 2013

전자 통신 산업의 발달로 터치 패널용 강화유리의 사용량이 급격히 증가함에 따라, 판유리 가공 공정 중 유리표면을 보호하기 위한 용도로 사용되는 UV경화형 코팅용액의 사용량이 함께 증가하고 있다. UV경화형 코팅은 열경화형에 비해 경화시간이 매우 짧고, 용제를 사용하지 않는 장점이 있다. 알칼리에 의한 박리 특성을 부여하기 위해 산성 고분자 styrene-acrylic acid copolymer를, 모노머로는 아크릴기가 각각 1개, 2개, 6개인 2-hydroxyl methylacrylate, 1,6-hexanediol diacrylate 그리고 dipentaerythritol hexaacrylate를 사용하였다. 광개시제로는 HP-8, TPO 및 DETX 3종을 조합하여 사용하였고 올리고머로는 bisphenol A epoxy diacrylate를 사용하였다. 본 연구에서는 산성 고분자와 아크릴계 모노머의 함량을 일정하게 유지하면서 광개시제, 올리고머, 그리고 첨가제인 talc의 함량을 변화시키며 실험을 수행하여 광개시제에 따른 제반 물성의 연계성을 고찰하였다. 시험결과 두 가지 이상의 광개시제를 사용해야 경도를 4H 이상 얻을 수 있었고 특히 TPO를 첨가하면 코팅막의 박리 형태를 시트형태로부터 조각형태로 조절하는 것이 가능하였다. 올리고머 함량이 증가하면 경도와 접착성이 증가하지만 박리시간 역시 증가하였고 talc 함량은 20 wt%에서 가장 우수한 결과를 나타내었다.

• 한국산학기술학회논문지
• /
• 제10권9호
• /
• pp.2396-2401
• /
• 2009

본 연구는 건축자재로 널리 사용되는 PVC 바닥상재의 표면을 스크래치로부터 보호하기 위하여 기존에 사용하는 광경화형 우레탄-아크릴 수지에 내마모성을 향상시킨 광경화형 하드 코팅액 개발에 관한 것이다. PVC 바닥상재용으로 사용되는 내마모성이 없는 우레탄-아크릴 수지에 $Al_2O_3$(Al-160SG-3), $Al(OH)_3$(SH-8W) 및 $SiO_2$(KS-5000) 등 서로 다른 내마모성을 지닌 물질을 분말 형태로 수지의 양 대비 함량(wt%)을 $10{\sim}30%$로 변화하여 첨가한 후 링밀(Ring Mill)을 사용, 배합하여 수지의 내마모성을 향상시킨 하드 코팅액을 제조하였다. 제조한 하드 코팅액은 코팅층의 두께조절이 가능한 코팅(Bar-coating)을 사용하여 PVC 바닥상재에 코팅 한 후 내마모성, 연필경도, 부착력, 코팅두께 등의 코팅층 표면물성을 평가하였다. 연구결과, 수지에 $Al_2O_3$ 분말 30%를 혼합하여 제조한 하드 코팅액이 내마모성 1등급, 연필경도 H, 부착력 100%로 가장 좋은 물성을 보였으며, 전반적으로 입자크기가 작고, 분말 함량이 많을수록 또한 코팅두께가 두꺼워 질수록 경도 및 내마모성이 우수한 것으로 나타났다.

• 한국진공학회지
• /
• 제21권6호
• /
• pp.328-332
• /
• 2012

Ag (silver)의 일함수는 T-OLED (Top Emission Organic Light Emitting Diode)의 전극소자로 사용하기에는 다소 낮다는 단점이 있다(~4.3 eV). 이러한 단점을 해결하기 위한 대안으로 Ag 박막의 표면을 플라즈마, UV, 열처리를 통하여 일함수를 높이는 연구가 진행되어 왔다(~5.0 eV). 하지만 현재의 대부분 연구는 후 처리된 박막의 일함수에 초점을 맞춰 연구가 진행되어, 박막의 mechanical property에 대한 연구는 매우 부족하며 이는 T-OLED의 효율과 수명 등의 연구에 매우 중요하다. 본 논문에서는 Ag와 $AgO_x$ 박막의 mechanical property에 초점을 맞춰 분석을 실시하였다. Ag는 유리기판 위에 rf-magnetron sputter를 이용하여 100 W의 power에서 150 nm 두께로 증착되었다. 증착된 박막은 UV 램프를 이용하여 다양한 시간동안 UV 처리되었다(0~9분). 본 논문에서는 처리된 박막의 면저항을 측정하고 nano indenter, Scanning Probe Microscopy의 Atomic Force Microscopy mode를 이용하여 mechanical property를 분석하였다. 실험 결과 UV 처리 시간이 3분을 넘어가는 시편과 3분 이내의 시편은 면저항값 및 경도 값에 큰 차이가 있었다. 이러한 결과는 Ag 박막의 후처리에 따른 Ag 물질의 산화 및 결합상태에 따라 박막 내에 존재하는 stress의 영향으로 예상되어진다.

• 한국인쇄학회지
• /
• 제28권1호
• /
• pp.65-75
• /
• 2010

Environmentally friendly, stencil and screen printing for cost-effective for maskless. In this study, UV -LED light source for the dispersion characteristics and high competence photoresist coating was prepared. Wavelength of 365nm UV-LED exposure device using the maskless lithography, 1.7kgf/$cm^2$ $2600mmH_2O$ the injection pressure and the suction pressure by using a dry photoconductor symptoms were dry emulsion on the market as a result, curing properties and adhesion, hardness, solvent resistance and excellent reproduction of fine patterns and ecological stencil technology was available and could be confirmed as a possibility.