• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2008년도 추계학술대회A
• /
• pp.1259-1264
• /
• 2008

This paper presents an accelerated life test for burn out of tungsten filament of automotive halogen lamp. There are many failure modes and failure factors that associated with tungsten filament. But in this explain the dominant failure mode of tungsten filament is the bumout of the filament failure. At first, over voltage, high temperature, inrush current and vibration are selected as stress factors by using of two stage Quality Function Deploymeng(QFD). And we planed accelerated life test that has one factor(voltage) and three levels. By experiment it has absorbed that over voltage has an effect on the life of halogen lamp. Using ALTA programs, we estimated the common shpae parament of Weibull distribution, life-stress relationship and $B_{100p}$ life.

• 한국방사선학회논문지
• /
• 제15권2호
• /
• pp.101-108
• /
• 2021

CT는 인체 내 장기의 해부학적 구조를 정확하게 나타낼 수 있으며, 영상의 분해능이 우수하다. Brain CT 검사 시 수정체의 방사선 감수성이 높아서 피폭의 영향을 많이 받는다. 본 연구는 수정체에 피폭선량을 감소하기 위해 비스무스와 텅스텐 필라멘트 차폐물질을 사용하여 Non-shield와 Shield에 대한 피폭선량의 변화와 차폐율을 비교 하고자 한다. 본 연구에서는 3D printing으로 제작한 비스무스, 텅스텐 필라멘트 차폐물질을 사용하여, 차폐물질 두께와 slice에 따라 피폭되는 선량을 측정하였다. 헤드팬텀을 고정시켜 안구에 Magicmax universal 선량계를 위치시켜 차폐 물질을 놓지 않았을 경우와 그 위에 차폐 물질을 놓았을 때 차폐율을 각각 비교하기 위해 두 물질을 1mm ~ 5mm 두께로 각각 측정하였다. 1 mm 두께의 필라멘트에서 비스무스 필라멘트는 26.8 %, 텅스텐 필라멘트는 43.1 % 차폐율이 나타났다. 따라서 비스무스 필라멘트보다 텅스텐 필라멘트에서 더 큰 차폐효과가 나타났다. 차폐체의 종류, 두께, 슬라이스 간격에 따라 선량을 측정한 결과, 비스무스 필라멘트 보다 텅스텐 필라멘트가 더 큰 차폐효과가 나타났다.

• Applied Science and Convergence Technology
• /
• 제24권5호
• /
• pp.142-150
• /
• 2015

A failure analysis of tungsten filaments used in quadrupole mass spectrometer for plasma process monitoring was carried by using SEM and EDS. Failed at high temperature, filaments showed two kinds of failure modes. The one is that diameter of filament became thinner gradually and finally snapped. The other is that filament abruptly snapped almost at a right angle. The EDS analysis showed Fe and C, including W and Fe, on the surface of failed filament. when failed filaments were treated with plasma in mixture of Ar and $CF_4$, the amount of Fe and C decreased. The failure analysis of filament showed that the cause of filament failure is thermal evaporation and grain growth of tungsten at high temperature.

• 한국신뢰성학회:학술대회논문집
• /
• 한국신뢰성학회 2004년도 정기학술대회
• /
• pp.129-137
• /
• 2004

This paper presents an accelerated life test for burnout of tungsten filament of incandescent lamp. From failure analyses of field samples, it is shown that their root causes are local heating or hot sports in the filament caused by tungsten evaporation and wire sag. Finite element analysis is performed to evaluate the effect of vibration and impact for burnout, but any points of stress concentration or structural weakness are not found in the sample. To estimate the burnout life of lamp, an accelerated life test is planned by using quality function deployment and fractional factorial design, where voltage, vibration, and temperature are selected as accelerating variables. We assumed that Weibull lifetime distribution and a generalized linear model of life-stress relationship hold through goodness of fit test and test for common shape parameter of the distribution. Using accelerated life testing software, we estimated the common shape parameter of Weibull distribution, life-stress relationship, and accelerating factor.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2003년도 추계학술대회 논문요약집
• /
• pp.206-206
• /
• 2003

• 대한방사선기술학회지:방사선기술과학
• /
• 제44권6호
• /
• pp.615-621
• /
• 2021

In the medical field, radiation provides information for the diagnosis and treatment of diseases. As the use of radiation increases and the risk of exposure increases, interest in radiation protection is also rapidly increasing. Lead shielding material is mainly used, which has a risk of lead poisoning and absorption into the body. Tungsten mixed filament shielding sheets were fabricated with a size of 70 × 70 mm and a thickness of 1, 2, and 4 mm by using a 3D printer. In the general shooting experiment, the thickness of the shielding sheet is 1 ~ 5mm, the tube voltage is 60, 80, 100, 120 kVp and the tube current is 20, 40 mAs. In general photography, Tungsten showed better shielding rate compared to Brass, Copper, and Lead protective tools under all irradiation conditions, and in particular, Tungsten 5 mm showed 100% shielding rate. The 3D-printed tungsten mixed filament shielding is expected to be used as a new shield that can replace the existing lead protection tools as it shows a better shielding rate than the existing lead protection tools in Radiography.

• 대한기계학회논문집A
• /
• 제29권7호
• /
• pp.921-929
• /
• 2005

This paper presents an accelerated life test for burnout of tungsten filament of incandescent lamp. From failure analyses of field samples, it is shown that their root causes are local heating or hot spots in the filament caused by tungsten evaporation and wire sag. Finite element analysis is performed to evaluate the effect of vibration and impact for burnout, but any points of stress concentration or structural weakness are not found in the sample. To estimate the burnout life of lamp, an accelerated life test is planned by using quality function deployment and fractional factorial design, where voltage, vibration, and temperature are selected as accelerating variables. We assumed that Weibull lifetime distribution and a generalized linear model of life-stress relationship hold through goodness of fit test and test for common shape parameter of the distribution. Using accelerated life testing software, we estimated the common shape parameter of Weibull distribution, life-stress relationship, and accelerating factor.

• 한국공작기계학회:학술대회논문집
• /
• 한국공작기계학회 2004년도 춘계학술대회 논문집
• /
• pp.160-165
• /
• 2004

At this research, we examined probability of light bulb's life span value and prediction on purpose to inquire out the span of repeat velocity as fracture probability by executing the fatigue test, which is considered property of Tungsten filament's thermal fatigue used as an automobile bulb. As a result we can confirm what the most suitable solution is weibull distribution and log normal distribution. Tungsten filament's span gets longer as the fatigue repeat velocity gets shorter And, repeat span is about 15%~40% shorter than sequence life span.

• 환경위생공학
• /
• 제14권2호
• /
• pp.1-7
• /
• 1999

In the tungsten industry as light source material, tungsten filament which used as light source material ould form after molybdenum wire which used as the center supporter for coil shape tungsten wire was removed. The purpose of this study is to develop new process named "hydrogen peroxide dissolution method". This process uses hydrogen peroxide, which is harmless to human body and oxidize molybdenum wire selectively. The results were as follows:1. The dissolution of molybdenum wire was proportion to a solution and contact surface of molybdenum wire. 2. The optimum $H_2O_2/H_2O$ were 1:0.5 ~ 1:1.75. 3. The time of dissolution was 65~70 minutes, and the PCS of sample were 20,800 PCS(1,820g). 4. Total cost($H_2O_2$, catalyst) was ￦19,088.

• Applied Science and Convergence Technology
• /
• 제25권6호
• /
• pp.116-119
• /
• 2016

In this study, we fabricated the $K^+$ ion source for the various purposes and investigated the emission characteristics. The fabricated $K^+$ ion source was painted in the tungsten filament to make filament type ion source. The RGA spectra show that the filament type $K^+$ ion source has a good out gassing character, so it can be used in the ultra-high vacuum system. The maximum $K^+$ ion current was 20 mA when filament temperature was 1410 K and filament potential was 50 V. When the filament temperature was 1070 K, the initial beam current was 50 mA and decreased only by 2% during 4 hours. The emitting energy was measured to be 2.04 eV. This low value means that the fabricated specimen is a good $K^+$ ion source. We conclude that this filament type ion source can be used in various fields, including the LEIS research.