• Journal of the Korean Vacuum Society
• /
• v.9 no.3
• /
• pp.267-272
• /
• 2000

Electroplating Cu was deposited on Si(100) wafer after seed Cu was deposited by sputtering first. TaN was deposited as a diffusion barrier before depositing the seed Cu. Electroplating Cu thin films show highly (111)-oriented microstructure for both before and after annealing at $450^{\circ}C$ for 30min and no copper silicide was detected in the same samples, which indicates that TaN barrier layer blocks well the Cu diffusion into silicon substrate. After annealing the electroplating Cu film up to $450^{\circ}C$, the Cu film became columnar from non-columnar, its grain size became larger about two times, and also defects density of stacking faults, twins and dislocations decreased greatly. Thus the heat treatment will improve significantly electromigration property caused by the grain boundary in the Cu thin films.

• Journal of Korean Medical Science
• /
• v.33 no.44
• /
• pp.279.1-279.16
• /
• 2018

Magnetic resonance-guided focused ultrasound (MRgFUS) is a new emerging neurosurgical procedure applied in a wide range of clinical fields. It can generate high-intensity energy at the focal zone in deep body areas without requiring incision of soft tissues. Although the effectiveness of the focused ultrasound technique had not been recognized because of the skull being a main barrier in the transmission of acoustic energy, the development of hemispheric distribution of ultrasound transducer phased arrays has solved this issue and enabled the performance of true transcranial procedures. Advanced imaging technologies such as magnetic resonance thermometry could enhance the safety of MRgFUS. The current clinical applications of MRgFUS in neurosurgery involve stereotactic ablative treatments for patients with essential tremor, Parkinson's disease, obsessive-compulsive disorder, major depressive disorder, or neuropathic pain. Other potential treatment candidates being examined in ongoing clinical trials include brain tumors, Alzheimer's disease, and epilepsy, based on MRgFUS abilities of thermal ablation and opening the blood-brain barrier. With the development of ultrasound technology to overcome the limitations, MRgFUS is gradually expanding the therapeutic field for intractable neurological disorders and serving as a trail for a promising future in noninvasive and safe neurosurgical care.

• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.55 no.6
• /
• pp.910-916
• /
• 2022

The purpose of this study is to evaluate the effect of underwater non-thermal dielectric barrier discharge plasma (DBD plasma) on the sterilization of three types of pathogenic bacteria that cause diseases in freshwater fish and the reduction of a tetracycline antibiotics. This experiment was conducted in the DBD plasma generator, and the voltages used to generate plasma were 11.6 kV and 23.1 kV. The measurement intervals were 0, 1, 5, 10 and 15 min. As a result of DBD plasma treatment, Aeromonas hydrophila, Edwardsiella tarda and Pseudomonas fluorescens were removed 93-99% after 5 min at 23.1 kV, and the tetracycline antibiotics were reduced 70-95% after 15 min at 23.1 kV. In this study, as a result of treating the effluent with DBD plasma at a fish farm where the medicinal bath was conducted with oxytetracycline-HCl (OTC-HCl) products, OTC-HCl decreased by 62% after 10 min at 23.1 kV.

• Restorative Dentistry and Endodontics
• /
• v.40 no.3
• /
• pp.179-187
• /
• 2015

Traditionally, apexification has been used to treat immature permanent teeth that have lost pulp vitality. This technique promotes the formation of an apical barrier to close the open apex so that the filling materials can be confined to the root canal. Because tissue regeneration cannot be achieved with apexification, a new technique called regenerative endodontic treatment was presented recently to treat immature permanent teeth. Regenerative endodontic treatment is a treatment procedure designed to replace damaged pulp tissue with viable tissue which restores the normal function of the pulp-dentin structure. After regenerative endodontic treatment, continued root development and hard tissue deposition on the dentinal wall can occur under ideal circumstances. However, it is difficult to predict the result of regenerative endodontic treatment. Therefore, the purpose of this study was to summarize multiple factors effects on the result of regenerative endodontic treatment in order to achieve more predictable results. In this study, we investigated the features of regenerative endodontic treatment in comparison with those of other pulp treatment procedures and analyzed the factors that have an effect on regenerative endodontic treatment.

• Transactions on Electrical and Electronic Materials
• /
• v.14 no.3
• /
• pp.133-138
• /
• 2013

Acrylonitrile-butadiene-styrene (ABS) plastic is a polymer material extensively used in electrical and electronic applications. Nickel (Ni) thin film was deposited on ABS by electroless plating, after its surface was treated and modified with atmospheric plasma generated by means of dielectric barrier discharges (DBDs) in air. The method in this study was developed as a pre-treatment for electroless plating using DBDs, and is a dry process featuring fewer processing steps and more environmentally friendliness than the chemical method. After ABS surfaces were modified, surface morphologies were observed using a scanning electron microscope (SEM) to check for any physical changes of the surfaces. Cross-sectional SEM images were taken to observe the binding characteristics between metallic films and ABS after metal plating. According to the SEM images, the depths of ABS by plasma are shallow compared to those modified by chemically treatment. The static contact angles were measured with deionized (DI) water droplets on the modified surfaces in order to observe for any changes in chemical activities and wettability. The surfaces modified by plasma showed smaller contact angles, and their modified states lasted longer than those modified by chemical etching. Adhesion strengths were measured using 3M tape (3M 810D standard) and by 90° peel-off tests. The peel-off test revealed the stronger adhesion of the Ni films on the plasma-modified surfaces than on the chemically modified surfaces. Thermal shock test was performed by changing the temperature drastically to see if any detachment of Ni film from ABS would occur due to the differences in thermal expansion coefficients between them. Only for the plasma-treated samples showed no separation of the Ni films from the ABS surfaces in tests. The adhesion strengths of metallic films on the ABS processed by the method developed in this study are better than those of the chemically processed films.

• Journal of Microbiology and Biotechnology
• /
• v.16 no.7
• /
• pp.1053-1059
• /
• 2006

The effectiveness of a proteinaceous fibrous material formed during commercial fermentation of soy protein (PFSP) and cysteine addition were evaluated in order to improve on the properties of soy protein-based films. Nine types of films were prepared at pH 7, 9, and 11, with heat treatments at $70^{\circ}C\;and\;90^{\circ}C$ for 30 min, by casting 5% (w/w) PFSP aqueous solution, containing 2.25% (w/w) glycerol, on to polystyrene plates. The tensile strength (TS) of films ranged from 3.88 to 6.87 MPa. The highest puncture strength (PS) was observed with pH 7.0 films prepared from PFSP solution heated at $70^{\circ}C$ (P<0.05). Alkaline pH and temperature caused a decrease in both the TS and PS of the films. The thickness of films ranged from $58\;to\;74{\mu}m$. Water vapor permeabilities of the films decreased with increasing pH and temperature. To produce films from PFSP, pH value of 7.0 to 9.0 and heat treatment of $70^{\circ}C\;to\;90^{\circ}C$ were needed. A soluble nature of PFSP films in water might be useful for preparation of hot water-soluble pouches. Cysteine addition could be necessary to produce films with increased TS and enhanced barrier properties. The combination treatment that provided the best combination of barrier and mechanical properties was the PFSP film prepared at pH 7.0 with addition of 1% cysteine. The films were good oxygen barriers.

• Journal of Periodontal and Implant Science
• /
• v.26 no.1
• /
• pp.80-88
• /
• 1996

The aim of the present investigation was to see the effect of combined use of PDGF BB and IGF -1 on the guided tissue regeneration(GTR) using barrier membrane in the treatment of human furcation involvement. Twelve patients with initially diagnosed as having moderate to advanced adult periodontitis with mandibular class II buccal furcation defects have been wer selected. Initial scaling and root planing has been performed and baseline data consisting of probing depths and attachment levels have been recorded prior to surgical procedures. The GTR procedures using either barrier membrane(control : ePTFE) alone or together with the application of PDGF - BB and IGF -l(experimental : ePTFE+PDGF/IGF) have been done under the routine guidelines. During the surgery, the distance from CEJ either to the bottom of the bone defects(CEJ - BD) or to the bone crest(CEJ-BC) were measured. Horizontal distance to the deepest area in the furcal defects were measured from the reference line connection the most prominent bony walls of the two buccal roots. 6 months following the GTR therapy, all the measurements were made repeatedly. The probing attachment gain of the experimental and the control grous were 2.14mm and l.07mm, respectively with no statically significnant difference. Amont of vertical bone fill in the experimental and the control groups were 2.43mm and 2.29mm, rexpectively. Amonut of horizontal bone fill were 2.86mm in the experimental group and 2.17mm in the control group, respectively. However, there were no significant differences in the amount of bone fill(both vertical and horizontal)between the two groups.

• Applied Chemistry for Engineering
• /
• v.27 no.6
• /
• pp.627-632
• /
• 2016

Ethyl methacrylate (EMA) monomer coupling onto the polyvinylidene fluoride (PVDF) film surface was attempted to enhance the interfacial adhesive force between PVDF-polyvinyl chloride (PVC) bilayer films via dielectric barrier corona discharge. The interfacial forces were quite enhanced when PVDF films were treated by corona discharge in an EMA 1% atmosphere. The contact angle of PVDF films decreased due to corona treatment. X-ray photoelectron spectroscopy (XPS) analysis showed that the carbon and oxygen content of the PVDF film surface increased with corona discharge while the fluoride content decreased. The curve fitting of XPS $C_{1s}$ peaks revealed that the non-polar C-C bonded carbon and oxygen-bonded carbon increased gradually with corona treatment, while the fluorine-bonded carbon decreased.

• Journal of Periodontal and Implant Science
• /
• v.27 no.1
• /
• pp.19-43
• /
• 1997

The barrier membranes for GTR procedure could be affected bY bacterial contamination after exposure to oral environment. This study was done to evaluate whether the tetracycline impregnated barrier membranes could inhibit bacterial attachment and penetration into membranes. The resorbable membrane(polylactic and polyglycolide copolymer, $Resolute^{(R)}$, W.L Gore and Associates, Inc..USA) and the non-resorbable membrane(e-PTFE; Gore-TexTM, W.L. Gore & Associates, Inc.,USA) were cut into 4mm discs and trated with 5% tridodecylmethylammonium chloride solution in ethanol and dried in air. The membranes were immersed in tetracycline(TC) solution (100mg/ml, pH 8.0) and dried. To the maxillary canine-premolar region in six periodontally healthy volunteers, removable acrylic devices were inserted, on which 8 cylindrical chambers were glued with TC impregnated and non-impregnated discs, the membrane discs were examined for bacterial attachment and penetration, and structural changes under SEM and LM. From the 1st day to the 7th day, membranes showed bacterial plaque formation composed of cocci and rods. Thereafter, filamentous bacteria appeared and the plaque thickness increased. The TC impregnated e-PTFE membranes showed less bacterial attachment and delayed in bacterial plaque maturation than non-treated membranes. As for bacterial penetration, the TC impregnated e-PTFE membranes showed superficial invasion and infrequent presence of bacteria in unexposed inner surface at the 4th week. while the non-treated e-PTFE membranes showed deep bacterial invasion at the 2nd week and frequent presence of internal bacteria at the 4th week. The resorbable membranes started to be resorbed at the 2nd week and were perforated at the 4th week, regardless of TC treatment. In conclusion, bacterial plaque formation and penetration was efficiently delayed in TC impregnated e-PTFE membranes, whereas resorbable membranes were similar in bacterial invasion due to membrane degradation and perforation, regardless of TC treatment.

• Journal of Animal Reproduction and Biotechnology
• /
• v.39 no.2
• /
• pp.105-113
• /
• 2024

Background: Aflatoxin B1 (AFB1) is a toxic metabolite generated by Aspergillus species and is commonly detected during the processing and storage of food; it is considered a group I carcinogen. The hepatotoxic effects, diseases, and mechanisms induced by AFB1 owing to chronic or acute exposure are well documented; however, there is a lack of research on its effects on the intestine, which is a crucial organ in the digestive process. Dogs are often susceptible to chronic AFB1 exposure owing to lack of variation in their diet, unlike humans, thereby rendering them prone to its effects. Therefore, we investigated the effects of AFB1 on canine small intestinal epithelial primary cells (CSIc). Methods: We treated CSIc with various concentrations of AFB1 (0, 1.25, 2.5, 5, 10, 20, 40, and 80 μM) for 24 h and analyzed cell viability and transepithelial-transendothelial electrical resistance (TEER) value. Additionally, we analyzed the mRNA expression of tight junction-related genes (OCLN, CLDN3, TJP1, and MUC2), antioxidant-related genes (CAT and GPX1), and apoptosis-related genes (BCL2, Bax, and TP53). Results: We found a significant decrease in CSIc viability and TEER values after treatment with AFB1 at concentrations of 20 μM or higher. Quantitative polymerase chain reaction analysis indicated a downregulation of OCLN, CLDN3, and TJP1 in CSIc treated with 20 μM or higher concentrations of AFB1. Additionally, AFB1 treatment downregulated CAT, GPX1, and BCL2. Conclusions: Acute exposure of CSIc to AFB1 induces toxicity, and exposure to AFB1 above a certain threshold compromises the barrier integrity of CSIc.