• Corrosion Science and Technology
• /
• v.9 no.4
• /
• pp.171-174
• /
• 2010

MAO (micro-arc oxidation) is an eco-friendly convenient and effective technology to deposit high-quality oxide coatings on the surfaces of Ti, Al, Mg and their alloys. The roles of the electrolyte concentration and relative cathode electrode area sizes in the grown oxide film during titanium MAO were investigated. The higher the concentration of the electrolyte, the lower the $R_{total}A$ value. The oxide film produced by the lower concentration of the electrolyte is thinner and less uniform than the film by the higher concentration, which is thick and porous. The cathode area size must be bigger than the anode area size in order to minimize the voltage drop across the cathode. The ratio of the cathode area size to the anode area size must be bigger than 8. Otherwise, the cathode will be another source for voltage drop, which is detrimental to and slows down the oxide growth.

• Journal of the Korean Ceramic Society
• /
• v.47 no.6
• /
• pp.633-637
• /
• 2010

In this study, lithium manganese oxide spinel ($LiMn_{1.9}Fe_{0.1}Nb_{0.0005}O_4$) as a cathode material of lithium ion secondary batteries is synthesized with spray drying, and in order to increase its crystallinity and electrochemical properties, the granulated $LiMn_{1.9}Fe_{0.1}Nb_{0.0005}O_4$ particle surface is coated with lithium titanium oxide spinel ($Li_4Ti_5O_{12}$) through a sol-gel method. The granulated particles present a higher tap density and lower specific surface area. The crystallinity and discharge capacity of the $Li_4Ti_5O_{12}$ coated material is relatively higher than uncoated material. With the coating layer, the discharge capacity and cycling stability are increased and the capacity fading is suppressed successfully.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.306-306
• /
• 2007

The surface was transformed to porous titanium oxide by the anodization of pure titanium. Titanium was anodized in non-aqueous and aqueous electrolytes at different potentials between 5 V and 150 V. Various electrolytes were compose of ethylene glycerol, $H_2SO_4,\;NH_4F\;and\;H_2O$. We obtained titania nanotube arrays on the micro pore of titanium. Micro pores and nano tubes were obtained by anodization at high potentials and low potentials, respectively. Morphologies of nanotubes and micro pore were characterized by FE-SEM. The unique surface structure is very attractive to electrical and medical applications such as gas sensor, biosensor, dental implant and stent.

• Toxicological Research
• /
• v.25 no.4
• /
• pp.195-201
• /
• 2009

Recent publications showed that metal nanoparticles which are made from $TiO_2,\;CeO_2,\;Al_2O_3,\;CuCl_2,\;AgNO_3$ and $ZnO_2$ induced oxidative stress and pro-inflammatory effects in cultured cells and the responses seemed to be common toxic pathway of metal nanoparticles to the ultimate toxicity in animals as well as cellular level. In this study, we compared the gene expression induced by two different types of metal oxide nanoparticles, titanium dioxide nanoparticles (TNP) and cerium dioxide nanoparticles (CNP) using microarray analysis. About 50 genes including interleukin 6, interleukin 1, platelet-derived growth factor $\beta$, and leukemia inhibitory factor were induced in cultured BEAS2B cells treated with TNP 40 ppm. When we compared the induction levels of genes in TNP-treated cells to those in CNP-treated cells, the induction levels were very correlated in various gene categories (r=0.645). This may suggest a possible common toxic mechanism of metal oxide nanoparticles.

• Tribology and Lubricants
• /
• v.18 no.2
• /
• pp.167-172
• /
• 2002

The wear behaviors of ultrahigh molecular weight polyethylene pins against titanium alloy and stainless steel disks moving in two different kinematic motion were investigated by conducting repeat pass rotational sliding and linear reciprocal sliding wear tests. Linear reciprocal motion wore more the polyethylene pin than did repeat pass rotational motion for both disk materials. It means that the repeated directional change of contact stresses generates more wear debris in polyethylene. For the linear reciprocal sliding tests, titanium alloy disks were damaged with some scratches after one million cycles but no surface damage was observed on the polyethylene pins. On the other hand, fur the repeat pass rotational sliding tests, all titanium alloy disks were severely abraded on the entire region of sliding track. This phenomenon can be interpreted by that stress fatigue under repeated sliding contact initiated titanium oxide layer wear particles from disk surface, and these hard particles were embedded into polyethylene pin and then they severely abraded the disk surface. From these results it can be concluded that the kinematic motion in pin-on-disk wear tests play a crucial role on the wear behaviors of UHMWPE pins against titanium alloy and stainless steef discs.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2000.11a
• /
• pp.67-71
• /
• 2000

The wear behaviors of ultrahigh molecular weight polyethylene pins against titanium alloy and stainless steel disks moving in two different kinematic motion were investigated by conducting repeat pass rotational sliding and linear reciprocal sliding wear tests. Linear reciprocal motion wore more the polyethylene pin than did repeat pass rotational motion for both disk materials. It means that the repeated directional change of contact stresses generates more wear debris in polyethylene. For the linear reciprocal sliding tests, titanium alloy disks were damaged with some scratches after one million cycles but no surface damage was observed on the polyethylene pins. On the other hand, for the repeat pass rotational sliding tests, all titanium alloy disks were severely abraded on the entire region of sliding track. This phenomenon can be interpreted by that stress fatigue under repeated sliding contact initiated titanium oxide layer wear particles from disk surface, and these hard particles were embedded into polyethylene pin and then they severely abraded the disk surface. From these results it can be concluded that the kinematic motion in pin-on-disk wear tests play a crucial role on the wear behaviors of UHMWPE pins against titanium alloy and stainless steel disks.

• Journal of the Korean institute of surface engineering
• /
• v.35 no.6
• /
• pp.383-390
• /
• 2002

To investigate behaviors of Ti and O elements and microstructures of anodic titanium oxide films, the films were prepared by anodizing pure titanium in $H_2$S $O_4$, $H_3$P $O_4$, and $H_2O$$_2$ mixed solution at 180V. The microstructures and chemical states of the elements were analyzed using SEM, X-ray mapping, AFM, XRD, XPS (depth profile). The films formed on a titanium substrate showed porous layers which were composed of pore and wall, And with increasing anodizing time a hexagonal shape of cell structures were dominant and solace roughness increased. From the XRD result the structure of the Ti $O_2$ layer was anatase type of crystal on the whole. In the XPS spectra it was found that Ti and O were chemically binded in forms of Ti $O_2$, TiOH, $Ti_2$ $O_3$ at Ti 2p, and Ti $O_2$, $Ti_2$ $O_3$, $P_2$ $O_{5}$, S $O_4^{2-}$ at O ls respectively. Concentration of Ti $O_2$ decreased as the depth increased from the surface of the oxide film towards the substrate, but to the contrary concentrations of TiOH and $Ti_2$ $O_3$ increased.d.

• Journal of Photoscience
• /
• v.2 no.1
• /
• pp.7-11
• /
• 1995

Powders of artificial crystallites of titanium(IV) oxide, TiO$_2$(B), were synthesized by the calcination of tetratitanic acid (hydrate, $H_2Ti_4O_9H_2O$; TTA). The relating titanates, potassium octatitanate ($K_2Ti_8O_{17}$) and octatitanic acid($H_2Ti_8O_{17}$), were also prepared. These powders, loaded with small amount of Pt, were suspended in an aqueous solution of 2-propanol and irradiated under argon atmosphere at 298 K + 0.5 deg. All the photocatalysts tested in this study produced almost equimolar amount of acetone and molecular hydrogen (H$_2$). Among them TiO$_2$(B) and TYA showed the higher photocatalytic activity but rather lower than commercial titanium(IV) oxide (TiO$_2$) powders. The photocatalytic activity of TiO$_2$(B) for 2-propanol dehydrogenation in deaerated aqueous suspension increased with the elevating calcination temperature. Comparison of rate of H$_2$ formation from methanol and 2-propanol solutions by the TiO$_2$(B) photocatalyst suggested a possibility of selection of substrate with its molecular size by TiO$_2$(B)

• Journal of Periodontal and Implant Science
• /
• v.32 no.3
• /
• pp.615-630
• /
• 2002

Various long-term studies have shown that titanium implants as abutments for different types of prostheses have become a predictable adjunct in the treatment of partially or fully edentulous patients. The continuous exposure of dental implants to the oral cavity with all its possible contaminants creates a problem. A lack of attachment, together with or caused by bacterial insult, may lead to peri-implantitis and eventual implant failure. Removal of plaque and calculus deposits from dental titanium implants with procedures and instruments originally made for cleaning natural teeth or roots may cause major alterations of the delicate titanium oxide layer. Therefore, the ultimate goal of a cleaning procedure should be to remove the contaminants and restore the elemental composition of the surface oxide without changing the surface topography and harming the surrounding tissues. Among many chemical and mechanical procedure, air-powder abrasive have been known to be most effective for cleaning and detoxification of implant surface. Most of published studies show that the dental laser may be useful in the treatment of pen-implantitis. $CO_2$ laser and Soft Diode laser were reported to kill bacteria of implant surface. The purpose of this study was to obtain clinical guide by application these laser to implant surface by means of Non-contact Surface profilometer and X-ray photoelectron spectroscopy(XPS) with respect to surface roughness and atomic composition. Experimental rough pure titanium cylinder models were fabricated. All of them was air-powder abraded for 1 minute and they were named control group. And then, the $CO_2$ laser treatment under dry, hydrogen peroxide and wet condition or the Soft Diode laser treatment under Toluidine blue O solution condition was performed on the each of the control models. The results were as follows: 1. Mean Surface roughness(Ra) of all experimental group was decreased than that of control group. But it wasn't statistically significant. 2. XPS analysis showed that in the all experimental group, titanium level were decreased, when compared with control group. 3. XPS analysis showed that the level of oxygen in the experimental group 1, 3($CO_2$ laser treatment under dry and wet condition) and 4(Soft Diode laser was used under toluidine blue O solution) were decreased, when compared with control group. 4. XPS analysis showed that the atomic composition of experimental group 2($CO_2$ laser treatment under hydrogen peroxide) was to be closest to that of control group than the other experimental group. From the result of this study, this may be concluded. Following air-powder abrasive treatment, the $CO_2$ laser in safe d-pulse mode and the Soft Diode laser used with photosensitizer would not change rough titanium surface roughness. Especially, $CO_2$ laser treatment under hydrogen peroxide gave the best results from elemental points of view, and can be used safely to treat peri-implantitis.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.39 no.5
• /
• pp.1-7
• /
• 2002

Deep sub-micron bulk CMOS circuits require gate electrode materials such as metal silicide and titanium silicide for gate oxides. Many authors have conducted research to improve the quality of the sub-micron gate oxide. However, few have reported on the electrical quality and reliability of an ultra-thin gate. In this paper, we will recommend a novel shallow trench isolation structure and a two-step TiS $i_2$ formation process to improve the corner metal oxide semiconductor field-effect transistor (MOSFET) for sub-0.1${\mu}{\textrm}{m}$ VLSI devices. Differently from using normal LOCOS technology, deep sub-micron CMOS devices using the novel shallow trench isolation (STI) technology have unique "inverse narrow-channel effects" when the channel width of the device is scaled down. The titanium silicide process has problems because fluorine contamination caused by the gate sidewall etching inhibits the silicide reaction and accelerates agglomeration. To resolve these Problems, we developed a novel two-step deposited silicide process. The key point of this process is the deposition and subsequent removal of titanium before the titanium silicide process. It was found by using focused ion beam transmission electron microscopy that the STI structure improved the narrow channel effect and reduced the junction leakage current and threshold voltage at the edge of the channel. In terms of transistor characteristics, we also obtained a low gate voltage variation and a low trap density, saturation current, some more to be large transconductance at the channel for sub-0.1${\mu}{\textrm}{m}$ VLSI devices.