• 한국세라믹학회지
• /
• 제42권4호
• /
• pp.276-281
• /
• 2005

산소분위기, $750^{\circ}C$서 36 h 동안 하소함으로써 연소법에 의해 $LiNi_{1-y}M_{y}O_{2}(M=Zn^{2+},\;Al^{3+},\;and\;Ti^{4+},\;0.000\{\le}y{\le}0.100)$를 합성하였다. 각 시료에 대해 XRD 분석, FE-SEM 관찰, 싸이클 수에 따른 방전 용량의 변화 조사가 행해졌다. $LiNi_{0.99}M_{0.01}O_{2}$ (M=Zn, Al, and Ti) 조성이 여러 조성 중에서 대체로 우수한 전기화학적 특성을 나타내었다. 결정성과 cation mixing의 평가에서 Zn을 치환한 경우 결정성이 나쁘게 나타났고 Ti를 치환한 경우 cation mixing이 크게 나타났으며, Al을 치환한 경우 결정성이 좋고 cation mixing이 적게 나타났다. Al을 치환한 경우 싸이클 특성이 개선되었다.

• 한국전기전자재료학회논문지
• /
• 제25권8호
• /
• pp.664-669
• /
• 2012

Nano-structured one-dimensional $Na_2Ti_6O_{13}$ particles were synthesized by a molten salt process. Effects of processing parameters on the microstructure and band gap energy of the $Na_2Ti_6O_{13}$ powder were studied in this paper. For the synthesis of the $Na_2Ti_6O_{13}$ particles, two different raw materials of tubular shaped Na-titanate (Na-TiNT) and spherical shaped $TiO_2$ were utilized. Synthesizing with the raw material of Na-TiNT, around 70nm thick 1D-$Na_2Ti_6O_{13}$ with the bandgap energy of 3.5 eV was obtained at $810^{\circ}C$. Below $810^{\circ}C$ or without the presence of NaCl, 1D-$Na_2Ti_6O_{13}$ was in a relatively short in length and agglomerated state. With the processing temperature increased, the thickness of the 1D-$Na_2Ti_6O_{13}$ was also observed to be increased. On the other hand, when $TiO_2$ was employed as a raw material, the mixed amount of $Na_2CO_3$ played an important role in transforming the morphology and phase of the raw material, affecting the bandgap energy of the synthesized product. Specific surface area of the synthesized 1D-$Na_2Ti_6O_{13}$ was significantly affected by the raw and mixed materials as well as processing temperature. When Na-TiNT was processed at $810^{\circ}C$ with NaCl, the specific surface area of the 1D-$Na_2Ti_6O_{13}$ showed the best value of 30.63 $m^2/g$.

• 한국전기전자재료학회논문지
• /
• 제17권10호
• /
• pp.1056-1060
• /
• 2004

In this study, 0.96B $i_{0.5}$($Na_{0.84}$ $K_{0.16}$)$_{0.5}$Ti $O_3$ + 0.04SrTi $O_3$ + 0.3 wt% N $b_2$ $O_{5}$+0.2 wt% L $a_2$ $O_3$ + xwt % Mn $O_2$ were investigated as a function of the amount of Mn $O_2$ addition in order to improve dielectric and piezoelectric properties of Lead-free piezoelectric ceramics. With increasing the amount of Mn $O_2$ addition, the density, electromechanical coupling factor( $k_{p}$), piezoelectric constant( $d_{33}$, $g_{33}$) and curie temperature (Tc) showed the maximum value of 5.7 g/㎤, 38 %, 219 pC/N, 26 mVㆍm/N and 32$0^{\circ}C$ at 0.1 wt% Mn $O_2$ addition, respectively, and mechanical quality factor( $Q_{m}$ ) showed the maximum value of 158 at 0.3 wt% Mn $O_2$ addition.ddition.ion.n.

• Korean Chemical Engineering Research
• /
• 제53권3호
• /
• pp.276-281
• /
• 2015

$TiO_2-SiO_2$ 나노복합소재는 자체가 화학적으로 안정할 뿐만 아니라 광학적, 열적 특성이 매우 우수하여 광화학센서, 촉매 등 다양한 분야에 적용되고 있다. 이러한 구조를 구현하는 방법으로 티타늄이 첨가된 폴리카보실란(PCS) 혼합용액을 전기방사한 후 이를 적절한 산화분위기에서 열처리하여 부직포상의 $TiO_2-SiO_2$ 나노복합섬유를 만들 수 있는데, 이는 기존의 졸겔공정에 의해 제조되는 섬유보다 더 쉽고 안정적인 방법이다. 공정 중 방사된 섬유를 산화분위기에서 $1200^{\circ}C$ 이상까지 열처리하게 되면 크리스토발라이트 기지조직 내에서 아나타제 나노결정상이 매우 균일하게 형성되었다. 또한, 열처리 후 섬유의 표면과 단면은 매우 치밀하고 매끈하였으며 10~20nm 크기의 아나타제 결정입자들이 내부에 균일하게 분포하였다.

• 한국전기전자재료학회논문지
• /
• 제16권12S호
• /
• pp.1195-1199
• /
• 2003

In this study, in order to develop the low temperature sintering ceramics for multilayer piezoelectric transformer, dielectric and piezoelectric properties of PSN-PZT[0.91Pb(Sb$\sub$1/2/Nb$\sub$1/2/)$\sub$0.03/(Zr$\sub$0.495/Ti$\sub$0.505/)$\sub$0.97/O$_3$-0.04Pb(Ni$\sub$1/2/W$\sub$1/2/)O$_3$+0.05BiFeO$_3$+0.3wt％MnO$_2$+0.6wt％CuO〕 ceramics were investigated according to Zr/Ti ratio. As Zr/Ti ratio is increased, electromechanical coupling factor(k$\sub$p/) and dielectric constant increased and then decreased after the ratio of Zr/Ti=50/50. Also, mechanical qualify factor(Q$\sub$m/) decreased and then increased after the ratio of Zr/Ti=50/50.

• 한국입자에어로졸학회지
• /
• 제7권3호
• /
• pp.79-85
• /
• 2011

Porous $TiO_2-SiO_2$ particles were synthesized by co-assembly of nanoparticles of $TiO_2$ and $SiO_2$ in evaporating aerosol droplets. Poly styrene latex (PSL) particles were employed as a template of porous particles. Flowrate of dispersion gas, weight ratio of $TiO_2/SiO_2$ and $SiO_2$ concentration in the precursor, and PSL size were chosen as process variables. The morphology, crystal structure, chemical bonding, and pore size distribution were analyzed by FE-SEM, XRD, FT-IR, BET. The morphology of porous $TiO_2-SiO_2$ particles was spherical and the average particle size range were from 1 to $10{\mu}m$. The particles were composed of meso and macro pores. The average particle diameter and pore volume of the as prepared particles were dependant on process variables. It was found that UV-Vis absorption of the porous particles was comparable with pure $TiO_2$ nanoparticles even though $TiO_2/SiO_2$ ratio is low in the porous particles.

• 한국입자에어로졸학회지
• /
• 제4권1호
• /
• pp.21-25
• /
• 2008

$Pb(Zr_{0.53}Ti_{0.47})O_3$ (PZT) was synthesized by a multiple wet dry process. Precipitates prepared from reaction between $ZrOCl_2{\cdot}8H_2O$ and $TiOCl_2$ and $NH_4OH$ in an aqueous solution was dried at $100^{\circ}C$, and calcined at $500^{\circ}C$ and $700^{\circ}C$. The mixture mixed with PbO and as-dried or calcined $Zr_{0.53}Ti_{0.47}O_4$ (ZT) powders was calcined again at 700 and $800^{\circ}C$. Well crystallized ZT and PZT were formed at even $700^{\circ}C$. PZT piezoelectric ceramics of more than 98.5% in a relative density was obtained by sintering at as low as $900^{\circ}C$.

• 한국진공학회지
• /
• 제17권5호
• /
• pp.442-447
• /
• 2008

강유전체 0.65Pb$(Mg_{1/3}Ta_{2/3})O_3-0.35PbTiO_3$ 고용체에 $Ag_2O$를 첨가하여 $1200^{\circ}C$에서 소결하여 시료를 제작하였다. 완성된 시료의 미세구조는 주사 전자현미경(SEM)을 이용하여 관찰하였고, 전기적 특성의 관찰을 위하여 유전상수와 유전손실, 초전계수를 측정하였다. 제작된 시료 중에서 0.2 mol%의 $Ag_2O$를 과잉 첨가한 시료에서 유전상수와 초전계수가 가장 크게 나타났다. 각 시료에서 유전상수와 초전계수의 최대값의 온도는 $Ag_2O$ 첨가량이 증가할수록 저온으로 이동하였다.

• 청정기술
• /
• 제21권4호
• /
• pp.271-277
• /
• 2015

본 연구에서는 효율적인 광 전기화학적 수소제조를 위하여 광촉매로써 상용화 촉매인 P25-티타니아와 합성한 Ag_xO를 적정 질량비로 혼합한 촉매를 사용하였다. Ag_xO는 일반적인 솔-젤법으로 합성하였으며, 은 용액의 안정화를 위해 합성과정 중에 수산화테트라메틸암모늄을 첨가하고 열처리 온도를 -5, 25, 50 ℃로 다양화시켜 세 가지 형태의 산화은을 얻었다. 합성한 Ag_xO의 물리화학적 특성은 X-선 회절분석법(XRD), 주사전자현미경(SEM), 자외선-가시선 분광광도계(UV-Visible spectroscopy), X-선 광전자 분광법(XPS)을 이용하여 확인하였다. 물/메탄올(무게 비 1:1) 혼합용액을 광분해 한 결과, 순수 P25-티타니아보다 Ag_xO가 첨가된 혼합촉매에서 현저히 높은 양의 수소가 발생하였다. 보조 산화제로써 H₂O₂를 첨가한 경우 그리고 Ag_xO의 합성온도가 50 ℃일 때 가장 높은 수소 제조효율을 나타내었다. 특히, 0.9 g의 P25-티타니아와 0.1 g의 Ag_xO (50 ℃)를 혼합한 촉매를 사용하였을 때 8시간 반응하는 동안에 13,000 μmol의 수소가 발생하였다.

• 한국분말재료학회지
• /
• 제28권5호
• /
• pp.423-428
• /
• 2021

Here, we report the development of a new and low-cost core-shell structure for lithium-ion battery anodes using silicon waste sludge and the Ti-ion complex. X-ray diffraction (XRD) confirmed the raw waste silicon sludge powder to be pure silicon without other metal impurities and the particle size distribution is measured to be from 200 nm to 3 ㎛ by dynamic light scattering (DLS). As a result of pulverization by a planetary mill, the size of the single crystal according to the Scherrer formula is calculated to be 12.1 nm, but the average particle size of the agglomerate is measured to be 123.6 nm. A Si/TiO₂ core-shell structure is formed using simple Ti complex ions, and the ratio of TiO₂ peaks increased with an increase in the amount of Ti ions. Transmission electron microscopy (TEM) observations revealed that TiO₂ coating on Si nanoparticles results in a Si-TiO₂ core-shell structure. This result is expected to improve the stability and cycle of lithium-ion batteries as anodes.