Dielectric and Pyroelectric Properties for 0.65PbMg1/3Ta2/3)O3-0.35PbTiO3 Solid Solution Modified with Ag2O

Ferroelectric samples of the 0.65Pb$(Mg_{1/3}Ta_{2/3})O_3-0.35PbTiO_3$ modified with $Ag_2O$ were prepared by sintering at $1200^{\circ}C$ for 4 h. The fractured surface of sintered pellets were examined by scanning electron microscopy(SEM). The dielectric constant, loss, and pyroelectric coefficient of the ceramics samples were determined. The dielectric and pyroelectric properties could be improved with the addition of small amount of $Ag_2O$ up to 0.2 mol%. The dielectric and pyroelectirc peak temperatures are continuously shifted to lower temperature with addition of small amounts of $Ag_2O$.

Ag2O가 첨가된 0.65PbMg1/3Ta2/3)O3-0.35PbTiO3 고용체의 유전, 초전 특성

강유전체 0.65Pb$(Mg_{1/3}Ta_{2/3})O_3-0.35PbTiO_3$ 고용체에 $Ag_2O$를 첨가하여 $1200^{\circ}C$에서 소결하여 시료를 제작하였다. 완성된 시료의 미세구조는 주사 전자현미경(SEM)을 이용하여 관찰하였고, 전기적 특성의 관찰을 위하여 유전상수와 유전손실, 초전계수를 측정하였다. 제작된 시료 중에서 0.2 mol%의 $Ag_2O$를 과잉 첨가한 시료에서 유전상수와 초전계수가 가장 크게 나타났다. 각 시료에서 유전상수와 초전계수의 최대값의 온도는 $Ag_2O$ 첨가량이 증가할수록 저온으로 이동하였다.