• Journal of the Korean institute of surface engineering
• /
• v.52 no.2
• /
• pp.53-57
• /
• 2019

Stability and activity of boron doped diamond (BDD) electrode are key factors for water treatment. In this study, BDD electrodes were prepared on various substrates such as Nb, Si, Ti, and $TiN_x/Ti$ by hot filament chemical vapor deposition (HFCVD) method. BDD/Ti film showed the delamination between BDD and Ti substrate due to the formation of TiC layer caused by diffusion of carbon. On the other hand, $BDD/TiN_x/Ti$ showed remarkably improved stability, compared to BDD/Ti. It was confirmed that $TiN_x$ intermediate layer act as barrier layer for diffusion of carbon. High potential window of 2.8 eV was maintained on the $BDD/TiN_x/Ti$ electrode and, better wastewater treatment capability and longer electrode working life than BDD/Nb, BDD/Si and BDD/Ti were obtained.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.4 s.175
• /
• pp.900-906
• /
• 2000

Ceramic, PCD and CBN tools are available for the difficult-to-cut-materials such as hardened carbon tool steel, stainless steel, Inconel 718 and etc. Ceramic tools are likely to be chipped and abruptly broken before the appearance of normal wear in turning. Ceramic tools are suitable for continuous in turning, not for intermittent in milling. In this study, TiN/TiCN multi-layer coated ceramic tools were found to restrain the chipping, breaking and early fracture and to increase the critical cutting speed owing to TiN/TiCN multi-layer coating in Arc Ion Plating of PVD method.

• Journal of Advanced Marine Engineering and Technology
• /
• v.19 no.3
• /
• pp.62-69
• /
• 1995

In order to investigate the effect of TiN coating on corrosion fatigue behavior of metal, the rotary bending corrosion fatigue tests were carried out in 3% NaCl solution by using the round bar specimens of high-speed steel, SKH-9, coated with TiN by PVD method. From the experimental results, fatigue strength of TiN coating steel in air was obvious improvement as compared with that of the substrate because of the restriction of dislocation movement in near surface of the substrate by hard thin film. In 3% NaCl solution, corrosion fatigue life of TiN coating specimen in high stress level was improvement same as in air. But in low stress level, corrosion fatigue life of TiN coating one was equivalent to that without coating, due to much crack initiated from corrosion pits formed at the substrate by failure of coating layer.

• Proceedings of the IEEK Conference
• /
• 1998.10a
• /
• pp.581-584
• /
• 1998

TiN thin films were grown on (100) Si substrate by atomic layer epitaxy at 130 - $240^{\circ}C$ using TEMAT and NH3 as precursors. Reactants were injected into the reactor in sequence of TEMAT precursor vapor pulse, N2 purging gas pulse, NH3 gas pulse and N2 purging gas pulse so that gas-phase reactions could be removed. The films were characterized by means of x-ray diffraction(XRD), 4-point probe, atomic force microscopy(AFM) and auger electron spectroscopy(AES).

• Journal of the Korean Society for Heat Treatment
• /
• v.22 no.2
• /
• pp.88-94
• /
• 2009

The effect of high temperature gas nitrding (HTGN) on the surface microstructure in pure Ti was investigated. Two phases of TiN and $Ti_2N$ appeared at the outmost surface, and the wide ${\alpha}$-Ti layer was formed at the next layer. On the other hand, the interior region, where the nitrogen was not permeated, exhibited ${\alpha}$'phase. The outmost surface of TiN and $Ti_2N$ showed the maximum hardness of 1000Hv, while the interior ${\alpha}$'phase was ${\sim}350$ Hv. The permeation depth of nitrogen increased with increasing the gas nitriding temperature and time. The nitrogen concentration of the surface layer seems to be over 12.7% at $1100^{\circ}C$.

• Journal of the Korean institute of surface engineering
• /
• v.42 no.4
• /
• pp.161-168
• /
• 2009

Effects of TiN/Ti multilayer coating on the Ti-30Ta-xZr alloy surface were studied by using various experiments. The Ti-30Ta containing Zr (5, 10 and 15 wt%) were melted 10 times to improve chemical homogeneity by using a vacuum furnace. And then samples were homogenized for 24 hrs at $1000^{\circ}C$. The specimens were prepared for TiN/Ti coating by cutting and polishing. The prepared specimens were coated with TiN/Ti multilayers by using DC magnetron sputtering method. The analyses of coated surface and coated layer were carried out by field emission scanning electron microscope(FE-SEM), EDX, and X-ray diffractometer(XRD). From the microstructure and XRD analysis of Ti-30Ta-xZr alloys, The equiaxed structure was changed to needle-like structure with increasing Zr content. And $\alpha$-peak and elastic modulus increased as Zr content increased. The $\alpha$ and $\beta$ phase predominantly were found in the specimen containing high Zr content. According to the analysis of TiN/Ti coating layer, the surface defects and structures of Ti-30Ta-xZr were covered with TiN/Ti coating layer and surface roughness decreased.

• Journal of the Korean institute of surface engineering
• /
• v.24 no.1
• /
• pp.16-16
• /
• 1991

Generally brittle eta phase produced during TiC deposition has a effect on the TRS (transverse rupture strength ; thoughness). Therefore it is necessary to reduce eta(η), phase for the improvement of tool life. At this experiment some properties (TRS, bonding strength, tool life, eta phase)have been investigated by inserting TiN or TiCN underlayer between TiC layer and substrate. The results obtained were as follows; 1. by inserting underlayer eta phase were decreased and TRS was increased, but the bonding strength was decreased. 2. the diffusion of W, Co from the substrate was hindered by the underlayer. 3. TiC layer with TiCN underlayer had the finsest grain size. 4. by inserting underlayer (TiCN or TiN) the tool life was improved and especially notch and crater wear resistance was greatly improved.

• 연구논문집
• /
• s.28
• /
• pp.219-227
• /
• 1998

In order to investigate the interfacial structure between TiN and iron nitride, an AISI 4140 steel was nitrided to form a layer of thickness 15$\mum$ by DC ion nitriding, then the surface was bombarded with Ti ions and subsequently coated a TiN film of 5$\mum$ by arc ion plating method. The interfacial microstructure between TiN and iron nitride was characterized by optical microscope, SEM and XRD. So called black layer was observed in the duplex treatment. It was resulted from the decomposition of iron nitride during the bombardment. Its thickness was increased with increasing bombardment time at high bias voltage. But the thickness was greatly decreased when the iron nitride was bombarded with a nitrogen gas or at a reduced bias voltage. The adhesion strength of the top TiN coating was decreased with increasing thickness of the black layer. Furthermore, the reduced adhesion strength in this system was discussed in view of the interfacial structural relationship between TiN and iron nitride.

• Journal of Welding and Joining
• /
• v.13 no.3
• /
• pp.134-146
• /
• 1995

Aluminium nitride(AlN) is currently under investigation as potential candidate for replacing alumium oxide(Al$_{2}$ $O_{3}$) as a substrate material for for electronic circuit packaging. Brazing of aluminium nitride(AlN) to Cu with Ag base active alloy containing Ti has been investigated in vacuum. Binary Ag$_{98}$ $Ti_{2}$(AT) and ternary At-1wt.%Al(ATA), AT-1wt.%Ni(ATN), AT-1wt.% Mn(ATM) alloys showed good wettability to AlN and led to the development of strong bond between brate alloy and AlN ceramic. The reaction between AlN and the melted brazing alloys resulted in the formation of continuous TiN layers at the AlN side iterface. This reaction layer was found to increase by increase by increasing brazing time and temperature for all filler metals. The bond strength, measured by 4-point bend test, was increased with bonding temperature and showed maximum value and then decreased with temperature. It might be concluded that optimum thickness of the reaction layer was existed for maximum bond strength. The joint brazed at 900.deg.C for 1800sec using binary AT alloy fractured at the maximum load of 35kgf which is the highest value measured in this work. The failure of this joint was initiated at the interface between AlN and TiN layer and then proceeded alternately through the interior of the reaction layer and AlN ceramic itself.

• Journal of Powder Materials
• /
• v.27 no.5
• /
• pp.406-413
• /
• 2020

Ti_0.5Al_0.5N/CrN nano-multilayers, which are known to exhibit excellent wear resistances, were prepared using the unbalanced magnetron sputter for various periods of 2-7 nm. Ti_0.5Al_0.5N and CrN comprised a cubic structure in a single layer with different lattice parameters; however, Ti_0.5Al_0.5N/CrN exhibited a cubic structure with the same lattice parameters that formed the superlattice in the nano-multilayers. The Ti_0.5Al_0.5/CrN multilayer with a period of 5.0 nm exceeded the hardness of the Ti_0.5Al_0.5N/CrN single layer, attaining a value of 36 GPa. According to the low-angle X-ray diffraction, the Ti_0.5Al_0.5N/CrN multilayer maintained its as-coated structure up to 700℃ and exhibited a hardness of 32 GPa. The thickness of the oxidation layer of the Ti_0.5Al_0.5N/CrN multilayered coating was less than 25% of that of the single layers. Thus, the Ti_0.5Al_0.5N/CrN multilayered coating was superior in terms of hardness and oxidation resistance as compared to its constituent single layers.