• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.05a
• /
• pp.182-183
• /
• 2009

플라즈마 원자층 증착법을 이용하여 Ru-TiN 빅막을 합성하였다. 박막 내 Ru의 함량은 Ru의 unit-cycle의 수에 따라 선형적으로 증가하였으며, Ru 함량이 증가함에 따라 박막의 비저항을 $3700{\mu}{\Omega}{\cdot}cm$에서 $190{\mu}{\Omega}{\cdot}cm$까지 자유롭게 조절할 수 있었다. Ru의 함량이 0.40 이상인 경우, Ru과 TiN 두물질이 교차 증착되어 서로의 결정 성장을 충분히 억제함으로서, 비정질구조를 가짐을 확인할 수 있었다. 또한, $O_2$ 분위기에서 열처리를 진행한 결과, Ru의 조성비가 0.40이상인 경우 $700^{\circ}C$까지 면저항의 변화가 거의 없음을 확인할 수 있었다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.1
• /
• pp.7-11
• /
• 2020

Carbon solubility on the paste deposition methods in the carbon-doped TiZrN coating was investigated in terms of lattice distortion and atomic concentration. After depositing the carbon paste by the dip coating, spin coating and screen printing, the laser was ablated to form the carbon gradient layer. Thickness and the concentration of doped carbon depended on the paste deposition method. Crystal structure analysis indicated that more lattice distortion occurred when coating layers were doped with spin coating and screen printing than when coating layers were doped with dip coating. The XPS depth profile showed that the thickness of carbon gradient layer by dip coating was about 30 nm, spin coating and screen printing are approximately 100 nm, formed more gradient layer. The hardness before laser carburization was about 30 GPa, and the hardness of 31 GPa with dip coating and 37 GPa with spin coating and screen printing. It was indicated that paste deposition methods for laser carburization contributed to lattice distortion and gradient layer.

• 한국신재생에너지학회:학술대회논문집
• /
• 2011.11a
• /
• pp.53.2-53.2
• /
• 2011

Dye-sensitized solar cells(DSSCs) have been recognized as an alternative to the conventional p-n junction solar cells because of their simple fabrication process, low production cost, and transparency. A typical DSSC consists of a transparent conductive oxide (TCO) electrode, a dye-sensitized oxide semiconductor nanoparticle layer, liquid redox electrolyte, and a Pt-counter electrode. In dye-sensitized solar cells, charge recombination processes at interfaces between coducting glass, $TiO_2$, dye, and electrolyte play an important role in limiting the photon-to-electron conversion efficiency. A layer of ZTO thin film less than ~200nm in thickness, as a blocking layer, was deposited by DC magnetron sputtering method directly onto the anode electrode to be isolated from the electrolyte in dye-sensitized solar cells(DSCs). This is to prevent the electrons from back-transferring from the electrode to the electrolyte ($I^-/I_3^-$). The presented DSCs were fabricated with working electrode of Ga-doped ZnO glass coated with blocking ZTO layer, dye-attached nanoporous $TiO_2$ layer, gel electrolyte and counter electrode of Pt-deposited GZO glass. The effects of blocking layer were studied with respect to impedance and conversion efficiency of the cells.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2006.10a
• /
• pp.67-68
• /
• 2006

• Journal of the Korean Ceramic Society
• /
• v.32 no.7
• /
• pp.761-768
• /
• 1995

Double layered BaTiO3 thin films with high dielectric constant as well as good insulating property were prepared for the application to low voltage driving thin film electroluminescent (TFEL) device. BaTiO3 thin films were formed by rf-magnetron sputtering technique. Amorphous and polycrystalline BaTiO3 thin films were deposited at the substrate temperatures of room temperature and 55$0^{\circ}C$, respectively. Two kinds of films prepared under these conditions showed high resistivity and high dielectric constant. The figure of merit (=$\varepsilon$r$\times$Eb.d) of polycrystalline BaTiO3 thin film was very high (8.43$\mu$C/$\textrm{cm}^2$). The polycrystalline BaTiO3 showed a substantial amount of leakage current (I), under the high electric field above 0.5 MV/cm. The double layered BaTiO3 thin film, i.e., amorphous BaTiO3 layer coated polycrystalline BaTiO3 thin film, was prepared by the new stacking method and showed very good dielectric and insulating properties. It showed a high dielectric constant fo 95 and leakage current density of 25 nA/$\textrm{cm}^2$ (0.3MV/cm) with the figure of merit of 20$\mu$C/$\textrm{cm}^2$. The leakage current density in the double layered BaTiO3 was much smaller than that in polycrystalline BaTiO3 under the high electric field. The saturated brightness of the devices using double layered BaTiO3 was about 220cd/$m^2$. Threshold voltage of TFEL devices fabricated on double layered BaTiO3 decreased by 50V compared to the EL devices fabricated on amorphous BaTiO3.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.31A no.5
• /
• pp.94-100
• /
• 1994

The junction failure mechanism of W plugs has not been fully understood while the selective W deposition has been widely used for plugging interconnection lines. In this paper, the thermal stability and junction failure mechanism of sub-micron contacts using selective CVD-W plugs were intensively studied with the metal lines of AISiCu, Ti/AISiCu and TiN/AISiCu. The experimental results showed that the contact chain resistance and leakage current in the AISiCu and Ti/AISiCu metallizations were significantly degraded after annealing. From the SEM analysis, it was found that the junction spiking, due to the Al atoms diffusion along the porous interface between selective CVD-W and contactside wall, caused the junction failure. In constast, there was no degradation of the contact resistance and junction leakage current in TiN/AISiCu metal structu-re. It is believed that the TiN barrier layer could prevent AI(Ti) atoms Fromdiffusing. Therefore, TiN barrier between W plug and Al should be used to impro-ve the thermal stability of sub-micron contacts using the selective CVD-W plugs.

• Korean Journal of Materials Research
• /
• v.14 no.10
• /
• pp.688-695
• /
• 2004

The capacitor contact barrier(CCB) layers have been introduced in the FeRAM integration to prevent the Pt/Al reaction during the back-end processes. Therefore, the interdiffusion and intermetallic formation in $Pt(1500{\AA})/Al(3000{\AA})$ film stacks were investigated over the annealing temperature range of $100\sim500^{\circ}C$. The interdiffusion in Pt/Al interface started at $300^{\circ}C$ and the stack was completlely intermixed after annealing over $400^{\circ}C$ in nitrogen ambient for 1 hour. Both XRD and SBM analyses revealed that the Pt/Al interdiffusion formed a single phase of $RtAl_2$ intermetallic compound. On the other hand, in the presence of TiN($1000{\AA}$) barrier layer at the Pt/Al interface, the intermetallic formation was completely suppressed even after the annealing at $500^{\circ}C$. These were in good agreement with the predicted effect of the TiN diffusion barrier layer. But the conventional TiN CCB layer could not perfectly block the Pt/Al reaction during the back-end processes of the FeRAM integration with the maximum annealing temperature of $420^{\circ}C$. The difference in the TiN barrier properties could be explained by the voids generated on the Pt electrode surface during the integration. The voids were acted as the starting point of the Pt/Al reaction in real FeRAM structure.

• Journal of Powder Materials
• /
• v.31 no.3
• /
• pp.255-262
• /
• 2024

Nano-oxide dispersion-strengthened (ODS) superalloys have attracted attention because of their outstanding mechanical reinforcement mechanism. Dispersed oxides increase the material's strength by preventing grain growth and recrystallization, as well as increasing creep resistance. In this research, atomic layer deposition (ALD) was applied to synthesize an ODS alloy. It is useful to coat conformal thin films even on complex matrix shapes, such as nanorods or powders. We coated an Nb-Si-based superalloy with TiO₂ thin film by using rotary-reactor type thermal ALD. TiO₂ was grown by controlling the deposition recipe, reactor temperature, N₂ flow rate, and rotor speed. We could confirm the formation of uniform TiO₂ film on the surface of the superalloy. This process was successfully applied to the synthesis of an ODS alloy, which could be a new field of ALD applications.

• Applied Chemistry for Engineering
• /
• v.29 no.2
• /
• pp.196-200
• /
• 2018

In this study, the intermediate layer in Pd-based hydrogen separation membrane was synthesized to minimize the surface roughness and defects using powder-type and sol-type metal oxides. The surface properties and gas permeation characteristics were analysed by SEM and $N_2$ gas permeation test. The coating layer composed of sol type metal oxides has smooth surface, especially the layer coated by $TiO_2$ sol has little pin holes, cracks and defects. The binary layer composed of powder type and sol type metal oxides has similar flux characteristics to a single sol type layer. The Pd-based composite membrane improved by the binary intermediate layer exhibited $0.32mol/m^2s$ of the hydrogen permeation flux with a selectivity ($H_2/N_2$) of ~10,890 at 672 K and a pressure difference of 1 bar.

• Journal of Mechanical Science and Technology
• /
• v.17 no.12
• /
• pp.1904-1911
• /
• 2003

In order to determine the wear properties of AIP (Arc Ion Plating) deposition, wear process was evaluated by using a Falex test machine. Also, in order to determine the effects of coating material on the wear process, TiC, TiN, and TiCN coatings of thickness about 5 $\mu\textrm{m}$∼6 $\mu\textrm{m}$ coated by Arc ion plating deposition method were tested. The wear property was determined under a dry sliding condition as a function of the applied load, sliding distance, sliding velocity and temperature. The results show that when wear of the coating-layer occurred, specific wear amount increased with the wear rate. At initial state, the wear rate rapidly increased, but it gradually reduced as the velocity increased. Also, when raising the temperature, the wear rate increased in the order of TiCN, TiN and TiC due to the frictional heat.