• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.12 no.1
• /
• pp.7-10
• /
• 2002

$TiO_2$ thin films were prepared by coating and subsequent pyrolysis processes using Titanium-naphthenate as a raw material. $TiO_2$ thin films were made by spin-coating technique on the glass substrates, and heat treated at 45$0^{\circ}C$, The transmittance, refractive index, crystallinity and surface morphology of the $TiO_2$ thin films were measured by UV/Vis spec trophotometer, x-ray diffractometer and scanning electron microscope. $TiO_2$thin films on the slide glass showed the trans mittance of 70-90% and refractive index of 2.6 at 420 nm. The results of XRD and SEM showed that the $TiO_2$ thin films exhibited the anatase phase and the thread-like surface morphology.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.6
• /
• pp.378-380
• /
• 2000

The epitaxial $BaTiO_{3}$ thin film was prepared on the MgO substrate by the coating-pyrolysis process using a mixed solution of Ba-naphthenate and Ti-naphthenate. The crystal structure of the epitaxial $BaTiO_{3}$ thin film was characterized by XRD ${\theta}/2{\theta}$ scan and asymmetric {303} rocking curve scan. The epitaxial $BaTiO_{3}$ thin film had the cubic phase with the lattice parameter of a = c = 0.4018 nm.

• Journal of Korean Ophthalmic Optics Society
• /
• v.10 no.3
• /
• pp.185-191
• /
• 2005

Photo-reactive $TiO_2$ thin films on soda-lime-silica slide glass were prepared by spin coating technique with a Ti-naphthenate precursor. Optical, structural and photo-catalytic properties of the films after annealing at $500^{\circ}C{\sim}600^{\circ}C$ were evaluated. As increase with annealing temperature, absorption bands and total transmittance of the films showing an average transmittance (about 80%) at visible spectra range were shifted to UV spectra range and slightly decreased. Refractive index and thickness of the films were increased from 2.16 to 2.63 and decreased from 484 nm to 439 nm, respectively, with increase of annealing temperature. Anatase phase was visible at all annealing temperature. More rougher surface structure was obtained at $600^{\circ}C$ than those of films annealed at $500^{\circ}C$ and $550^{\circ}C$. The hydrophilic conversion was found within 45 min by UV stimulation and optical activation was UVC>UVA>UVB at the case of $500^{\circ}C{\sim}550^{\circ}C$ and UVA>UVC>UVB at the annealing temperature of $600^{\circ}C$. The lowest initial contact angle was obtained at $600^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.39 no.12
• /
• pp.1153-1157
• /
• 2002

The fabrication of a three-layered asymmetric ceramic membrane was performed by slip casting of the porous alumina support and dip coating of the alumina intermediate layer using high purity ${\alpha}-Al_2O_3$ powders that have different particle size, followed by screen printing-pyrolysis of the $Tio_2$ layer as an ultrafilteration membrane using Ti-naphthenate solution. The bending strength, porosity and mean pore size of the alumina support were 231 kg/$cm^2$s, 30.26% and 0.19 ${mu}m$, respectively. The thickness of the intermediate layer was 30 ${mu}m$ and the mean pore size of that was 0.063 ${mu}m$. Also, the top layer was 0.5 ${mu}m$ thick and micropores with about 20 nm size were formed uniformly.

• Journal of Korean Ophthalmic Optics Society
• /
• v.12 no.1
• /
• pp.17-22
• /
• 2007

Metal-doped $TiO_2$ thin films were prepared on soda-lime-silica glass substrates by using a spin coating-pyrolysis process. As-deposited films were prefired at $500^{\circ}C$ or 10 min in air. Five-coated films were finally annealed at $600^{\circ}C$ for 30 min in air. High resolution X-ray diffraction, field emission scanning electron microscope and UV spectrophotometer were used to analyze film's property. The largest red shift in optical energy gap is obtained in the Fe-doped $TiO_2$ film.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.12 no.5
• /
• pp.240-246
• /
• 2002

$TiO_2$ films on soda-lime-silica glasses were prepared by spin coating-pyrolysis process using titanium naphthenate as a starting material. As-deposited films were pyrolyzed at $500^{\circ}C$ for 10 min in air and annealed at 500, 550 and $600^{\circ}C$ for 30 min in air. Crystallinity of the film was investigated by X-ray diffraction analysis. A field emission-scanning electron microscope and an atomic force microscope were used for characterizing the surface morphology and the surface roughness of the film. After annealing at 550 and $600^{\circ}C$, the X-ray diffraction patterns consist of only anatase peak. Films annealed at 500 and $550^{\circ}C$ exhibited flat surfaces. While with the increase in annealing temperature to $600^{\circ}C$, the $TiO_2$ film showed abnormal growth of three-dimensional needle-shaped grains. For all samples, high transmittance, above 90 % at 500 nm, was obtained at visible range. To investigate photocatalytic properties, IR absorbance associated with the C-H stretching vibrations of a thin solution-cast film of stearic acid under 365 nm (2.4 mW/$\textrm{cm}^2$) UV irradiation was estimated.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.2
• /
• pp.56-62
• /
• 2003

Epitaxial $Bi_4Ti_3O_{12}$ films on $SrTiO_3$(100), L$aA1O_3$(100) and MgO(100) were prepared by sol-gel process using metal naphthenate as a starting material. As-deposited films were pyrolyzed at $500^{\circ}C$ for 10 min In air and annealed at $750^{\circ}C$ for 30 min in air. Crystallinity and in-plane alignment of the film were investigated by X-ray diffraction $\theta$-2$\theta$ scan and P scanning. A field emission-scanning electron microscope and an atomic force microscope were used for characterizing the surface morphology and the surface roughness of the film. The film prepared on MgO(100) showed the most poor crystallinity and in-plane alignment, compared to those on the other substrates. While the films on $LaA1O_3$(100) and $SrTiO_3$(100) having high crystallinity and in-plane alignment showed the form of columnar grain growth, the film on MgO(100) which had poor crystallinity showed the form of acicula grain growth.