• 한국재료학회지
• /
• 제27권9호
• /
• pp.507-511
• /
• 2017

An optimum route to fabricate oxide dispersion strengthened ferritic superalloy with desired microstructure was investigated. Two methods of high energy ball milling or polymeric additive solution route for developing a uniform dispersion of $Y_2O_3$ particles in Fe-Cr-Al-Ti alloy powders were compared on the basis of the resulting microstructures. Microstructural observation revealed that the crystalline size of Fe decreased with increases in milling time, to values of about 15-20 nm, and that an FeCr alloy phase was formed. SEM and TEM analyses of the alloy powders fabricated by solution route using yttrium nitrate and polyvinyl alcohol showed that the nano-sized Y-oxide particles were well distributed in the Fe based alloy powders. The prepared powders were sintered at 1000 and $1100^{\circ}C$ for 30 min in vacuum. The sintered specimen with heat treatment before spark plasma sintering at $1100^{\circ}C$ showed a more homogeneous microstructure. In the case of sintering at $1100^{\circ}C$, the alloys exhibited densified microstructure and the formation of large reaction phases due to oxidation of Al.

• Metals and materials international
• /
• 제24권6호
• /
• pp.1213-1220
• /
• 2018

The effects of Cr and Fe addition on the mechanical properties of Ti-6Al-4V alloys prepared by direct energy deposition were investigated. As the Cr and Fe concentrations were increased from 0 to 2 mass%, the tensile strength increased because of the fine-grained equiaxed prior ${\beta}$ phase and martensite. An excellent combination of strength and ductility was obtained in these alloys. When the Cr and Fe concentrations were increased to 4 mass%, extremely fine-grained martensitic structures with poor ductility were obtained. In addition, Fe-added Ti-6Al-4V resulted in a partially melted Ti-6Al-4V powder because of the large difference between the melting temperatures of the Fe eutectic phase (Ti-33Fe) and the Ti-6Al-4V powder, which induced the formation of a thick liquid layer surrounding Ti-6Al-4V. The ductility of Fe-added Ti-6Al-4V was thus poorer than that of Cr-added Ti-6Al-4V.

• 한국분말재료학회지
• /
• 제20권5호
• /
• pp.323-331
• /
• 2013

In this paper, two kinds of advanced powder processing techniques Metal Injection Molding (MIM) and Direct Laser Forming (DLF) are introduced to fabricate complex shaped Ti alloy parts which are widely used for medical and aerospace applications. The MIM process is used to strengthen Ti-6Al-4V alloy compacts by addition of fine Mo, Fe or Cr powders. Enhanced tensile strength of 1030 MPa with 15.1% elongation was obtained by an addition of 4 mass%Cr because of the microstructural modification and also the solution strengthening in beta phase. However, their fatigue strength was lower compared to wrought materials, but was improved by HIP. Subsequently, the effect of feeding layer height (FLH) on the characteristics of the DLF compacts was investigated. In the case of 100 ${\mu}m$ FLH, surface roughness was improved and nearly full density (99.8%) was obtained. Also, tensile strength of 1080 MPa was obtained, which is higher than the ASTM value.

• 소성∙가공
• /
• 제22권8호
• /
• pp.470-476
• /
• 2013

The aim of the current study was to predict shape recovery behavior of Ni-Ti shape memory alloy (SMA) wire after loading-unloading and after wire drawing. The superelasticity of SMA was analyzed by a hyper-elastic model for the Mullins effect using ABAQUS. Firstly, tensile tests and loading-unloading tests of the Ni-Ti SMA wire with a diameter 1.0 mm were performed using an MTS servo-hydraulic tester. The parameters for the Mullins effect were computed by ABAQUS based on curve-fitting of the loading-unloading test data. The proposed FE-model predicted the shape recovery of Ni-Ti SMA after wire drawing. Finally, the effectiveness of the model was verified by drawing experiments. The wire drawing experiments using the Ni-Ti SMA were conducted on a drawing machine(1ton, 50mm/s). In order to evaluate the shape recovery of Ni-Ti SMA, the drawn wires are annealed for 30min at $450^{\circ}C$.

• 한국주조공학회지
• /
• 제21권1호
• /
• pp.24-32
• /
• 2001

Recently, iron aluminides based on Fe3Al and FeAl are ordered intermetallic alloys that offer good oxidation resistance, excellent sulfidation resistance, and potentially lower cost than many high-temperature structural materials. They have better strength, elasticity to weight ratio and high temperature strength, therefore, they can be cosidered as candidate heat resistance structural materials for automobiles, ships, airplanes and spaceships applications. The changes in the mechanical properties and fracture behavior were investigated for Fe-30at.%Al-5at.%Cr alloys when Ti, Hf and Zr were added respectively. For mechanical properties such as Rockwell hardness and yield strength at room temperature, those were decreased in the case of Fe-30at.%Al-5at.%Cr alloy then increased in the case of 5at.% and 10at.% addition of Ti alone. However, Rockwell hardness and yield strength decreased again at 15%Ti then increased dramatically due to the precipitation hardening of the second phase on the specimen at 20%Ti. For fracture modes, cleavage fracture showed in the case of Fe-30at.%Al and Fe-30at.%Al-5at.%Cr alloys. As the amount of Ti addition changed cleavage to transgranular fracture and to quasi-cleavage fracture at 20%Ti. When Hf, Zr and Hf+Zr were added respectively, transgranular, cleavage and quasi-cleavage fracture were coexisted.

• Journal of Magnetics
• /
• 제21권1호
• /
• pp.35-39
• /
• 2016

$Cr_{100-x}Ti_x$ amorphous texture-inducing layers (TIL) were investigated to realize highly (002) oriented $L1_0$ FePt-C granular films through hetero-epitaxial growth on the (002) textured bcc-$Cr_{80}Mn_{20}$ seed layer (bcc-SL). As-deposited TILs showed the amorphous phase in Ti content of $30{\leq}x(at%){\leq}75$. Particularly, films with $40{\leq}x{\leq}60$ kept the amorphous phase against the heat treatment over $600^{\circ}C$. It was found that preference of the crystallographic texture for bcc-SLs is directly affected by the structural phase of TILs. (002) crystallographic texture was realized in bcc-SLs deposited on the amorphous TILs ($40{\leq}x{\leq}70$), whereas (110) texture was formed in bcc-SLs overlying on crystalline TILs (x < 30 and x > 70). Correlation between the angular distribution of (002) crystal orientation of bcc-SL evaluated by full width at half maximum of (002) diffraction (FWHM) and a grain diameter of bcc-SL indicated that while the development of the lateral growth for bcc-SL grain reduces FWHM, crystallization of amorphous TILs hinders FWHM. $L1_0$ FePt-C granular films were fabricated under the substrate heating process over $600^{\circ}C$ with having different FWHM of bcc-SL. Hysteresis loops showed that squareness ($M_r/M_s$) of the films increased from 0.87 to 0.95 when FWHM of bcc-SL decreased from $13.7^{\circ}$ to $3.8^{\circ}$. It is suggested that the reduction of (002) FWHM affects to the overlying MgO film as well as FePt-C granular film by means of the hetero-epitaxial growth.

• 한국진공학회지
• /
• 제6권S1호
• /
• pp.127-132
• /
• 1997

Microstructure of the Fe-Ti system by ion beam mixing of multilayers at 300 K and 77 K has been studied in a wide composition range. The ion bombardment was carried out using $Ar^+$ ions at 80 keV. Using grazing angle x-ray diffraction we find that the lattice parameters of these bcc solid solutions are very close to that of $\alpha$-Fe. Extended x-ray absorption fine-structure spectroscopy have been performed to investgate the short-range order in the ion-beam-mixed state. The structure parameters, such as the interatomic distance and the coordination number are estmated from the Fe K-edge Fourier filtered EXAFS spectra. The interatomic distance is independent of the alloy concentration and it is almost constant. The study of x-ray absorption near-edge structure gives information on the individual $\rho$components of the partial densityof states of the conduction band of the Fe and Ti We also find that a charge transfer from Ti to Fe atoms takes place.

• 한국세라믹학회지
• /
• 제36권8호
• /
• pp.835-842
• /
• 1999

본 연구에서는 Ag-Cu-Ti 와 Ag-Cu-In-Ti 를 사용하여 브레이징법으로 질화규소 간 접합체를 제작하고 $400^{\circ}C$와 $650^{\circ}C$에서 장시간(2000 h) 열처리 후 파괴 강도의 변화를 살펴보았다. 접합후 강도는 Ag-Cu-Ti 가 높게 나왔지만, 열처리 시간이 증가할수록 Ag-Cu-In-Ti 의 경우가 강도의 감소 정도가 작은 것으로 나타났다. 또한 고온 응용을 위해 개발된 새로운 접학 합금인 Au-Ni-Cr-Mo-Fe 계를 이용하여 질화 규소 간의 접합체를 제작하여 $650^{\circ}C$에서 100시간까지 장시간 열처리 하였다 접합 당시의 강도는 상용 접합 합금보다는 낮은 값을 보였지만, 열처리를 함에 따라 강도의 증가를 보였다 SUS316과의 접합시에는 중간재로 몰리브데늄 또는 구리를 사용하였으며 $400^{\circ}C$에서 1000시간 동안 열처리하였다. 강도는 몰리브데늄을 사용한 경우가 높게 나왔지만, 접합체의 형성이 어렵다는 단점이 있었다. 산화 실험에서는 Ti가 첨가된 접합 합금인 Ag-Cu-Ti 의 경우가 첨가되지 않은 Ag-Cu의 경우보다 산화가 잘 일어나며, 인듐을 첨가한 Ag-Cu-In-Ti 의 경우는 산화 억제의 효과가 나타났다. 전반적으로 In을 포함한 접합 합금이 고온 신뢰도 면에서 우수한 것으로 나타났다.

• 한국재료학회지
• /
• 제25권11호
• /
• pp.642-646
• /
• 2015

Super alloys, which can be divided into three categories, i.e. Ni-base, Co-base, and Fe-base alloys, are widely used for high temperature applications. Since superalloys contain many alloying elements and precipitates, their chemistry and processing parameters need to be carefully designed. In this study, we designed a new Ni alloy to prevent corrosion due to water vapor and gases at high temperatures. The new alloy was designed using the theoretical value of the resulting energy electronic state calculation($DV-X{\alpha}$ method). The components that were finally used were Cr, Mo, and Ti, with Ni as a base. For these alloys, elements were selected in order to compare their values with that of the average theoretical basis for an Inconel 625 alloy. Finally, two kinds of Ni alloy were designed: Ni-28Cr-4Mo-2Ti and Ni-20Cr-10Mo-1Ti.

• 한국주조공학회지
• /
• 제21권1호
• /
• pp.15-23
• /
• 2001

The changes in the microstructures and $D0_3{\leftrightarrow}B2$ transition temperature were investigated for Fe-30at.%AI-5at.%Cr alloy with the ordered $D0_3$, structure when Ti, Hf and Zr were added respectively. The addition of Cr has no effect on the microstructure. However, as the amount of Ti addition increased, the grain size became smaller. Addition of Ti+Hf, Ti+Zr and Ti+Hf+Zr also showed the similar effect. When 20at.% of Ti was added, the second phase precipitates on the substrate. The addition of Cr, Hf and Zr alone has no effect on $D0_3{\leftrightarrow}B2$ transition temperature. However, as the amount of Ti addition increased by 5, 10, 15 and 20at.%, the transition temperatures showed 929, 930, 960 and $930^{\circ}C$ respectively.