• 치위생과학회지
• /
• 제9권2호
• /
• pp.153-160
• /
• 2009

본 연구는 금속-도재 수복물 제작에 사용되는 Ni-Cr alloy와 Co-Cr alloy, 그리고 티타늄에 gold bonding agent를 도포하여 Au coating 층을 형성하였다. 각 시편의 절단면을 전자현미경으로 Au coating 층과 porcelain bonder, 그리고 불투명 도재간의 결합을 관찰하였고, 각 계면의 상태를 SEM/EDS 방법으로 조사하였다. 실험에서 사용된 재료와 방법의 범위 내에서 다음과 같은 결론을 얻었다. 1. Gold bonding agent를 사용하여 형성한 Au coating 층은 미세다공성을 가진 구조로 판단되었다. 2. Au coating 층과 porcelain bonder 그리고 불투명 도재간의 결합은 잘 일어나 보였다. 3. Au coating 층은 도재 소성과정에서 발생하는 산화층의 확산을 제한하는 것으로 관찰되었다.

• 한국재료학회지
• /
• 제27권9호
• /
• pp.507-511
• /
• 2017

An optimum route to fabricate oxide dispersion strengthened ferritic superalloy with desired microstructure was investigated. Two methods of high energy ball milling or polymeric additive solution route for developing a uniform dispersion of $Y_2O_3$ particles in Fe-Cr-Al-Ti alloy powders were compared on the basis of the resulting microstructures. Microstructural observation revealed that the crystalline size of Fe decreased with increases in milling time, to values of about 15-20 nm, and that an FeCr alloy phase was formed. SEM and TEM analyses of the alloy powders fabricated by solution route using yttrium nitrate and polyvinyl alcohol showed that the nano-sized Y-oxide particles were well distributed in the Fe based alloy powders. The prepared powders were sintered at 1000 and $1100^{\circ}C$ for 30 min in vacuum. The sintered specimen with heat treatment before spark plasma sintering at $1100^{\circ}C$ showed a more homogeneous microstructure. In the case of sintering at $1100^{\circ}C$, the alloys exhibited densified microstructure and the formation of large reaction phases due to oxidation of Al.

• 한국수소및신에너지학회논문집
• /
• 제2권1호
• /
• pp.39-46
• /
• 1990

In order to improve the power of hydride heat pump, prototype heat pump was constructed using $Zr_{0.95}Ti_{0.05}Cr_{0.9}Fe_{1.1}$-$Zr_{0.9}Ti_{0.1}Cr_{0.6}Fe_{1.4}$ which had very good hydrogenation properties. The power changed with operating parameter such as cycle time, air flow rate, and temperature of hot air was investigated. The power shows maximum value with cycle time. The power increased with air flow rate and temperature of hot air. The power of the heat pump was $65-72 Kcal/Kg-alloy{\cdot}h$ under optimum operating condition, which was superior to that the system using $LaNi_{0.9}Al_{0.3}-MmNi_{4.15}Al_{0.66}Fe_{0.2}$ alloy pairs.

• 소성∙가공
• /
• 제8권3호
• /
• pp.265-265
• /
• 1999

The development of mechanical alloying (MA)-oxide dispersion strengthened (ODS) heat-resistant ferritic alloys of Fe-12%Cr with W, Ti and Y₂O₃additions were carried out. Fe-12%Cr alloys with 3%W, 0.4%Ti and 0.25% Y₂O₃additions showed a much finer and more uniform dispersion of oxide particles among the alloy system studied. Nano-sized oxides dispersed in the alloys suppress the grain growth during annealing at a high temperature and resulted in the remarkable improvement of creep strength. The oxide phase was identified as a complex oxide type of Y-Ti-O.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.708-709
• /
• 2006

New Al-based alloys with very high ultimate tensile strength were developed in high Al concentration range of 91-95 at.% for Al-Fe-Cr-Ti-M (M: Co and Mo) systems and Al-Fe-Cr-Mo-Ti-Co system by the dispersion of nanoscale quasicrystalline particles in Al phase. The effect of adding elements, M was discussed in the viewpoint of stability of super-cooled liquid state and formation ability of quasicrystalline phase. The P/M Al-Fe-Cr-Ti-M alloys with dispersed nanoscale quasicrystalline particles exhibited ultimate tensile strength of 350MPa at 573K and 200MPa at 673K.

• 한국표면공학회지
• /
• 제32권3호
• /
• pp.265-275
• /
• 1999

Titanium nitride and related overlayers produced by arc ion plating (AIP) are applied as commercial coatings in world-wide scale since the middle of 80s. Due to the achievements of low temperature deposition (LTD), they begin now to be used as wear and corrosion-resistant coatings for machine parts, besides applications on cemented carbide and high speed steel cutting tools. On the other side, TiN can be now applied successfully to brass, Al-alloy, ZnAl alloy articles as decorative coating through LTD. Various nitrides, carbonitrides, borides and other refractory compounds, such as (Ti, Al)N, TiCN, CrN, are used as the coatings for special heavy-duty working conditions instead of TiN since 90s. More and more multilayer coatings are applied now substituting single layer ones. Duplex processes are under development.

• 한국압력기기공학회 논문집
• /
• 제7권2호
• /
• pp.26-33
• /
• 2011

To evaluate steam oxidation behaviours of Alloy 617 and Haynes 230, oxidation test were performed at $900^{\circ}C$ in steam and $steam+20\;vol.-%\;H_2$ environments. Oxidation rate in steam condition was similar to that in air for Alloy 617, while it was slightly lower for Haynes 230. When hydrogen was added to steam, oxidation rate was enhanced. Isolated $MnTiO_3$ particle were formed on $Cr_2O_3$ oxide layer and sub layer $Cr_2O_3$ were formed in steam and $steam+20\;vol.-%\;H_2$ for Alloy 617. On the other hands, $MnCr_2O_3$ layer were formed on top of $Cr_2O_3$ oxide layer for Haynes 230. The extensive sub layer $Cr_2O_3$ formation was resulted from the oxygen inward diffusion in such environments. When hydrogen was added, the oxide morphology was changed from polygonal to platelet because of the accelerated diffusion of cations under the oxide layer. In addition, decarburized zone was extended as hydrogen participated into the reactions causing carbide dissolution.

• 한국재료학회지
• /
• 제13권10호
• /
• pp.640-644
• /
• 2003

NiCr thin films were fabricated by rf magnetron sputtering for applying to both the top electrode and absorption layer on Pb(Zr, Ti)O$_3$(PZT) thin films for infrared sensors. The rms roughness and resistivity of NiCr films prepared with Ni power of 80 W and Cr power of 50 W showed the most stable oxidation resistance after annealing at $600^{\circ}C$ for 5 min in oxygen ambient. The rms roughness and resistivity of NiCr films annealed at $V^{\circ}C$ in oxygen ambient were about 2$0\AA$ and $70 \mu$Ω-cm, respectively. As-deposited Ni/PZT/Pt and NiCr (Ni 80 W, Cr 50 W)/PZT/Pt structures showed well saturated hysteresis loops. However, in case of the samples annealed at $500^{\circ}C$ in oxygen ambient, only NiCr/PZT/Pt showed saturated loops having a remanent polarization of 20$\mu$C/$\textrm{cm}^2$. Ultra-thin NiCr films showed a possibility as a top electrode for infrared sensors.

• 한국주조공학회지
• /
• 제21권1호
• /
• pp.24-32
• /
• 2001

Recently, iron aluminides based on Fe3Al and FeAl are ordered intermetallic alloys that offer good oxidation resistance, excellent sulfidation resistance, and potentially lower cost than many high-temperature structural materials. They have better strength, elasticity to weight ratio and high temperature strength, therefore, they can be cosidered as candidate heat resistance structural materials for automobiles, ships, airplanes and spaceships applications. The changes in the mechanical properties and fracture behavior were investigated for Fe-30at.%Al-5at.%Cr alloys when Ti, Hf and Zr were added respectively. For mechanical properties such as Rockwell hardness and yield strength at room temperature, those were decreased in the case of Fe-30at.%Al-5at.%Cr alloy then increased in the case of 5at.% and 10at.% addition of Ti alone. However, Rockwell hardness and yield strength decreased again at 15%Ti then increased dramatically due to the precipitation hardening of the second phase on the specimen at 20%Ti. For fracture modes, cleavage fracture showed in the case of Fe-30at.%Al and Fe-30at.%Al-5at.%Cr alloys. As the amount of Ti addition changed cleavage to transgranular fracture and to quasi-cleavage fracture at 20%Ti. When Hf, Zr and Hf+Zr were added respectively, transgranular, cleavage and quasi-cleavage fracture were coexisted.

• 한국재료학회지
• /
• 제19권11호
• /
• pp.619-624
• /
• 2009

Titanium alloys have been attractive due to a high ratio of strength to weight as well as good corrosion resistance. However, strengthening causes a decrease in ductility in Ti alloys, as is usual in other alloys. For enhanced strength without ductility reduction, grain refinement and tensile properties were investigated as functions of thickness reduction of cold rolling and annealing condition in Ti-15V-3Cr-3Sn-3Al alloy with a ${\beta}$ single phase. The average grain size of the specimen, which was cold-rolled by 90% and annealed at 700$^{\circ}C$ for 5 min, was decreased to approximately 19 ${\mu}m$. The grain refinement of 63 μm to 19 ${\mu}m$ increased yield stress by 90 MPa without a significant decrease in total elongation. The Ti-15-3 alloy exhibited very low work hardening during tensile test at a crosshead speed of 2 mm/min. This result was discussed based on dynamic recovery associated with dislocation annihilation in grain boundaries.