• Korean Journal of Materials Research
• /
• v.17 no.9
• /
• pp.484-488
• /
• 2007

Mo(Ti) alloy and pure Cu thin films were subsequently deposited on $SiO_2-coated$ Si wafers, resulting in $Cu/Mo(Ti)/SiO_2$ structures. The multi-structures have been annealed in vacuum at $100-600^{\circ}C$ for 30 min to investigate the outdiffusion of Ti to Cu surface. Annealing at high temperature allowed the outdiffusion of Ti from the Mo(Ti) alloy underlayer to the Cu surface and then forming $TiO_2$ on the surface, which protected the Cu surface against $SiH_4＋NH_3$ plasma during the deposition of $Si_3N_4$ on Cu. The formation of $TiO_2$ layer on the Cu surface was a strong function of annealing temperature and Ti concentration in Mo(Ti) underlayer. Significant outdiffusion of Ti started to occur at $400^{\circ}C$ when the Ti concentration in Mo(Ti) alloy was higher than 60 at.%. This resulted in the formation of $TiO_2/Cu/Mo(Ti)\;alloy/SiO_2$ structures. We have employed the as-deposited Cu/Mo(Ti) alloy and the $500^{\circ}C-annealed$ Cu/Mo(Ti) alloy as gate electrodes to fabricate TFT devices, and then measured the electrical characteristics. The $500^{\circ}C$ annealed Cu/Mo($Ti{\geq}60at.%$) gate electrode TFT showed the excellent electrical characteristics ($mobility\;=\;0.488\;-\;0.505\;cm^2/Vs$, on/off $ratio\;=\;2{\times}10^5-1.85{\times}10^6$, subthreshold = 0.733.1.13 V/decade), indicating that the use of Ti-rich($Ti{\geq}60at.%$) alloy underlayer effectively passivated the Cu surface as a result of the formation of $TiO_2$ on the Cu grain boundaries.

• Journal of Technologic Dentistry
• /
• v.27 no.1
• /
• pp.73-78
• /
• 2005

The surface-reacted layer of titanium castings greatly affects their mechanical properties. This study analyzed the interfacial zone of Ti-20%Zr-5%Cr alloy castings obtained from phosphate bonded investment and examined the relationship between the surface-reacted layer and hardness. The Vickers hardness of cast disks were tested at 20$\mu m$ intervals from the surface to 120$\mu m$ in depth. The cross-section was observed metallurgically, and line profile of the reacted layer was conducted under the EDX. The surface-reacted layer of Ti-20%Zr-5%Cr alloy is showed a similar tendency to Ti-6%Al-4%V alloy in thickness, and also Si diffusion in multiple reacted layer of Ti-20%Zr-5%Cr alloy is less than cp Ti and similar to Ti-6%Al-4%V alloy. The Vickers hardness in the surface layer was greater than in the inner part, and the Vickers hardness of Ti-20%Zr-5%Cr alloy ranged 650 to 390 and cp Ti ranged 810 to 160, Ti-6%Al-4%V alloy ranged 710 to 530 respectively.

• Korean Journal of Metals and Materials
• /
• v.47 no.12
• /
• pp.881-886
• /
• 2009

Research into the replacement of injured systems and tissue in the human body is advancing rapidly. Recently, Ti-Ni shape memory alloys have shown excellent biofunctionality related to their shape memory effect and superelasticity. In this study, the effect of an acid or an alkali treatment on the bioactivity in 49Ti-Ni and 51.5Ti-48.5Ni alloys is investigated in an effort to utilize Ti-Ni alloy as a biomaterial. In addition, the biocompatibility in a SBF solution is assessed through in vitro testing. A porous surface was formed on the surface of both alloys after a chemical treatment. According to the in vitro test, apatite formed on the surfaces of both alloys. The forming rate of apatite in the Ti-rich alloy was faster that in the Ni-rich alloy. The formation of apatite provided proof of the bioactivity of the Ti-Ni alloy. A small quantity of Ni was eluted at the initial stage, whereas Ni was not found for 12 days in the Ti-rich alloy and for 8 days in the Ni-rich alloy. In the case of the treated 51.5Ti-Ni alloy, the shape memory property was worsened but the biocompatibility was improved.

• Journal of Korea Foundry Society
• /
• v.18 no.5
• /
• pp.488-493
• /
• 1998

Commercially pure titanium(cp-Ti) and Ti-15wt%Zr-4wt%Nb-4wt%Ta alloy were melted in vacuum induction furnace. According to the chemical analysis, the content of carbon was above ASTM standard in the cast ingots because of using graphite crucible. The TEM micostructures of cp-Ti and Ti alloy shows that chemically stable TiC precipitates distribute in ${\alpha}-Ti$ matrix. In order to examine the properties of cp-Ti and Ti-Zr-Nb-Ta alloy for dental applications, mechanical properties and corrosion resistance were investigated. The anodic polarization properties of Ti-Zr-Nb-Zr alloy were almost same as that of cp-Ti in 1% lactic acid. However, as the results of the anodic polarization test in 5% HCl, it was known that Ti-Zr-Nb-Zr alloy showed a rapid decrease in current density at higher potential in comparison with cp-Ti. The yield stress and tensile strengh in Ti-Zr-Nb-Ta were ${\sigma}_{0.2}=623\;MPa$, ${\sigma}_{T.S.}=708\;MPa$ and these results showed 30% increase in yield stress in comparison with cp-Ti.

• Journal of Technologic Dentistry
• /
• v.26 no.1
• /
• pp.97-104
• /
• 2004

A new Ti-10Ta-10Nb alloy has designed and examined some possibility of forming more passive oxide film by oxidation treatment which is closely related to corrosion resistance and biocompatibility. Ti-6Al-4V and Ti-10Ta-10Nb alloys were prepared by consumable vacuum arc melting and homogenized at 1050$^{\circ}C$ for 24hours. Alloy specimens were oxidized at the temperature range of 400 to 750$^{\circ}C$ for 30minutes, and the oxide films on Ti alloys were analysed by optical microscope, SEM, XPS and TGA. Cytotoxicity test was performed in MTT assay treated L929 fibroblast cell culture by indirect method. It is found out that the oxide film on Ti-10Ta-10Nb alloy is denser and thinner compared to Ti-6Al-4V alloy. The weight gain during the oxidation was increased rapidly at the temperature above 650$^{\circ}C$ for Ti-6Al-4V alloy and above 700$^{\circ}C$ for Ti-10Ta-10Nb alloy respectively. It was analysed that the passive film of the Ti alloys consisted of TiO2 through X-ray photoelectron spectroscopy (XPS) analysis. It is found out by cytotoxicity test that moderate oxidation treatment lowers cell toxicity, and Ti-10Ta-10Nb alloy showed better result compared to Ti-6Al-4V alloy.

• Journal of Technologic Dentistry
• /
• v.31 no.4
• /
• pp.31-36
• /
• 2009

This study evaluated the grindability of series of Ti-Cu alloys in order to develop a Ti alloy with better grindability than commercially pure titanium(CP Ti). Experimental Ti-Xwt%Cu alloys(X=2, 5, 10) were made in an argon-arc melting furnace. Slabs of experimental alloys were ground using a SiC abrasive wheel on an electric handpiece at circumferential speed(15000, 30000rpm) by applying a force(250, 300gr). Grindability was evaluated by measuring the amount of metal volume removed after grinding for 2 minutes. Data were compared to those for CP Ti and Ti-6wt%Al-4wt%V alloy. From results, It was observed that the grindability of Ti-Cu alloys increased with an increase in the Cu concentration compared to CP Ti, particularly the 10wt%Cu alloy exhibited the highest grindability at all speeds. By alloying with Cu, the Ti exhibited better grindability at high speed. The continuous precipitation of $Ti_2Cu$ among the ${\alpha}$-matrix grains made this material less ductile and facilitated more effective grinding because small segments more readily formed. The Ti-10wt%Cu alloy has a great potential for use as a dental machining alloy.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.4 no.1
• /
• pp.1-12
• /
• 2000

This study summarizes the numerical analyses of a Ti alloy deformation under a back extrusion process. Amongst metallic parts in a small propulsion motor case, a Ti-6Al-4V alloy is used extensively. However, the Ti alloy shows a great deal of shear band formation which often leads to a fracture due to a narrow working temperature window. Moreover, the shear band tends to develop over an area where a contact occurs between the hot work piece and the die wall, due to localized cooling. Thus, heating the dies is often required to overcome the deformation localization. Therefore, it becomes necessary to investigate the internal temperature and strain rate distribution during forging process of a Ti alloy. Furthermore, a shear band analysis is peformed using a finite difference scheme and a comparison is made between steel and Ti alloy.

• Journal of Powder Materials
• /
• v.8 no.1
• /
• pp.42-49
• /
• 2001

Ti-50Ni(at%) and Ti-40Ni-10Cu(at%) alloy powders have been fabricated by ball milling method, and their microstructure and phase transformation behavior were investigated by means of scanning electron microscopy/energy dispersive spectrometry, differential scanning calorimetry (DSC), X-ray diffractions and transmission electron microscopy. In order to investigate the effect of ball milling conditions on transformation behavior, ball milling speed and time were varied. Ti-50Ni alloy powders fabricated with the milling speed more than 250 rpm were amorphous, while those done with the milling speed of 100rpm were crystalline. In contrast to Ti-50Ni alloy powders, Ti-40Ni-10Cu alloy powders were crystalline, irrespective of ball milling conditions. DSC peaks corresponding to martensitic transformation were almost discernable in alloy powders fabricated with the milling speed more than 250 rpm, while those were seen clearly in alloy powders fabricated with the milling speed of 100 rpm. This was attributed to the fact that a strain energy introduced during ball milling suppressed martensitic transformation.

• Journal of Technologic Dentistry
• /
• v.23 no.2
• /
• pp.223-230
• /
• 2002

Pure titanium and Ti6Al4V alloy have been mainly used as implant materials but the cytotoxicity of V, neurotoxicity of Al resulting in Alzheimer disease had been reported. This paper was described the influence of composition of Ti-Nb alloys with 3 wt%Nb, 20 wt%Nb on the microstructure and corrosion resistance. Specimens of Ti alloys were melted in vacuum arc furnace and homogenized at $1000^{\circ}C$ for 24hr. The alloys were rolled in $\beta$ and ${\alpha}+{\beta}$ regions. The corrosion resistance of Ti alloys were evaluated by potentiodymic polarization test in 0.9% NaCl and 5% HCl solutions. The results can be summarized as follows: 1. The microstructure was transformed from $\alpha$ phase to ${\alpha}+{\beta}$ phase by adding Nb 2. The hardness of Ti-20Nb alloy was greater than Cp- Ti, Ti-3Nb alloy. 3. The corrosion resistance of Ti-20Nb alloy was better than that of Cp-Ti, Ti-3Nb alloy in 0.9%NaCl and 5%HCl solutions.

• Journal of Korea Foundry Society
• /
• v.29 no.2
• /
• pp.59-63
• /
• 2009

Effects of Ti on damping capacity and mechanical properties are investigated in hot rolled Fe-17%Mn alloy. The existing damping alloy with Fe-Mn binary system was limited the use by high production cost, however in case of using scrap iron instead of pure iron although the content of carbon is higher it is possible to be applied wider field especially construction items because the production cost is lower. However, the excellent specific damping capacity is dropped due to the high content of carbon, we developed advanced type of damping alloy included Ti. TiC is formed with added Ti and it holds the specific damping capacity similar to existing damping alloy. The effect of Ti on damping capacity is found to be beneficial in carbon-containing alloy, which is attributed to the depletion of carbon solute due to the formation of TiC.