• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.718-721
• /
• 2004

The $(Sr_{0.9}Ca_{0.1})TiO_3$(SCT) thin films are deposited on Pt-coated electrode$(Pt/TiN/SiO_2/Si)$ using RF sputtering method at various substrate temperature. The optimum conditions of RF power and $Ar/O_2$ ratio were 140[W] and 80/20, respectively. Deposition rate of SCT thin films was about $18.75[{\AA}/min]$. The crystallinity of SCT thin films were increased with increase of substrate temperature in the temperature range of $100\sim500[^{\circ}C]$. The dielectric constant of SCT thin films were increased with the increase of substrate temperature, and changed almost linearly in temperature ranges of $-80\sim+190[^{\circ}C]$. The current-voltage characteristics of SCT thin films showed the increasing leakage current as the substrate temperature increases.

• Bulletin of the Korean Chemical Society
• /
• v.18 no.1
• /
• pp.56-61
• /
• 1997

Lead zirconate titanate (PZT) thin fills were deposited onto the Pt/Ti/SiO2/Si substrate by the pulsed laser deposition with the second harmonic wavelength (532 nm) of Nd:YAG laser. In order to determine the optimum conditions for the film deposition, the phase of the films were investigated as functions of ambient oxygen pressure, substrate temperature, and laser fluence. Also the chemical composition analysis was conducted for the PZT films deposited under various ambient oxygen pressure. When the distance between substrate and bulk PZT target is set to 20 mm, the optimum conditions have been determined to be 3 torr of oxygen pressure, 1.5 J/cm2 of laser fluence, and 823-848(±10) K range of substrate temperature. At these conditions, perovskite phase PZT films were obtained on platinized silicon. The chemical composition of the films is very similar to that of PZT bulk target. The physical structure of the deposited films analyzed by scanning electron microscopy shows a columnar morphology perpendicular to the substrate surface. Capacitance-Voltage hysteresis loop measurements show also a typical characteristics of ferroelectric thin film. The dielectric constant is found to be 528 for the 0.48 μm thickness of PZT thin film.

• Biomaterials and Biomechanics in Bioengineering
• /
• v.1 no.1
• /
• pp.1-12
• /
• 2014

Polymer multilayered hydrogels were prepared on a titanium alloy (Ti) substrate using a layer-by-layer (LBL) process to load a cell growth factor. Two water-soluble polymers were used to fabricate the multilayered hydrogels, a phospholipid polymer with both N, N-dimethylaminoethyl methacrylate (DMAEMA) units and 4-vinylphenylboronic acid (VPBA) units [poly(MPC-co-DMAEMA-co-VPBA) (PMDV)], and the polysaccharide alginate (ALG). PMDV interacted with ALG through a selective reaction between the VPBA units in PMDV and the hydroxyl groups in ALG and through electrostatic interactions between the DMAEMA units in PMDA and the anionic carboxyl groups in ALG. First, the Ti substrate was covered with photoreactive poly vinyl alcohol, and then the Ti alloy was alternately immersed in the respective polymer solutions to form the PMDV/ALG multilayered hydrogels. In this multilayered hydrogel, vascular endothelial growth factor (VEGF) was introduced in different layers during the LbL process under mild conditions. Release of VEGF from the multilayered hydrogels was dependent on the location; however, release continued for 2 weeks. Endothelial cells adhered to the hydrogel and proliferated, and these corresponded to the VEGF release profile from the hydrogel. We concluded that multilayered hydrogels composed of PMDV and ALG could be loaded with cell growth factors that have high activity and can control cell functions. Therefore, this system provides a cell function controllable substrate based on the controlled release of biologically active proteins.

• Progress in Superconductivity and Cryogenics
• /
• v.6 no.3
• /
• pp.6-11
• /
• 2004

YBa$_2$Cu$_3$$O_{7-x}$ (YBCO) films were deposited on MgO(100) and SrTiO$_3$(100) single crystal substrates by cold-wall type MOCVD method using continuous source supplying system. Under the deposition temperature of 740∼76$0^{\circ}C$, c-axis oriented YBCO films were obtained. In case of the YBCO films deposited on MgO (100) single crystal substrate, the critical temperature (T$_{c}$) was under 81 K regardless of the deposition conditions, whereas T$_{c}$ of the YBCO films deposited on SrTiO$_3$(100) single crystal substrate was 83∼84 K. The critical current (I$_{c}$) of the YBCO film deposited on SrTiO$_3$(100) single crystal substrate for 30 min was 49 A/cm-width and the critical current density (J$_{c}$) was 0.82 MA/$\textrm{cm}^2$ to film thickness of 0.6 ${\mu}{\textrm}{m}$. I$_{c}$ increased to 84.4 A/cm-width as the deposition time increased to 50 min, but J$_{c}$ decreased to 0.53 MA/$\textrm{cm}^2$ to film thickness of 1.8 ${\mu}{\textrm}{m}$.rm}{m}$.

• Journal of Sensor Science and Technology
• /
• v.18 no.5
• /
• pp.343-348
• /
• 2009

$NiO{\cdot}(Co_{0.25}Mn_{0.75})_2O_3$(Mn-Ni-Co) and $Ba_{0.5}Sr_{0.5}TiO_3$(BST) thick films were screen printed on Pt patterned alumina substrate to investigate the effects of sintering temperature on humidity and temperature sensing properties of ceramic sensors. A raise in sintering temperature increased resistance and B constant of the Mn-Ni-Co temperature sensor. This may have derived from the synergic effects of the reduction in charge carriers caused by the substitution of Co for Mn as well as the formation of microcracks from the difference in thermal expansion coefficients. Dependence of resistance on humidity of the Mn-Ni-Co temperature sensor, however, was not found. BST films sintered at temperatures in the range of $1100^{\circ}C$ to $1150^{\circ}C$ showed excellent humidity sensing properties. The BST humidity sensor was faster in its response than the Mn-Ni-Co temperature sensor. The humidity sensor, however, proved to be unstable under various temperatures, suggesting a need for a temperature stabilizing device. In contrast, the Mn-Ni-Co temperature sensor was stable under humid conditions.

• Corrosion Science and Technology
• /
• v.21 no.5
• /
• pp.340-347
• /
• 2022

In this research, mixed metal oxide (TiO₂, RuO₂) coating was applied to grade 1 titanium as a bipolar plate for polymer electrolyte membrane fuel cell (PEMFC). Electrochemical experiments were carried out in an aqueous solution of pH 3 (H₂SO₄ + 0.1 ppm HF, 80 ℃) determined by DoE. The air was bubbled to simulate a cathode environment. Potentiodynamic polarization test revealed that corrosion current densities of the titanium substrate and MMO-coated specimen were 0.180 µA/cm² and 4.381 µA/cm², respectively. There was no active peak. After potentiostatic experiment, current densities of the titanium substrate and the MMO-coated specimen were 0.19 µA/cm² and 1.05 µA/cm², respectively. As a result of observing the surface before and after the potentiostatic experiment, cracked dried clay structures were observed without corrosion damage. Both the titanium substrate and the MMO-coated specimen could not satisfy the interfacial contact resistance suggested by the DoE. Thus, further research is needed before they could be applied as bipolar plates.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2010.05a
• /
• pp.3.1-3.1
• /
• 2010

Water splitting reaction using photocatalysts is of great interest in the utilization of solar energy [1]. In the present work, visible light-responsive $TiO_2$ thin films (Vis-$TiO_2$) were prepared by a radio frequency magnetron sputtering (RF-MS) deposition method and applied for the separate evolution of $H_2$ and $O_2$ from water as well as the photofuel cell. Special attentions will be focused on the effect of HF treatment of Vis-$TiO_2$ thin films on their photocatalytic activities. Vis-$TiO_2$ thin films were prepared by an RF-MS method using a calcined $TiO_2$ plate and Ar as the sputtering gas. The Vis-$TiO_2$ thin films were then deposited on the Ti foil substrate with the substrate temperature at 873 K (Vis-$TiO_2$/Ti). Vis-$TiO_2$/Ti thin films were immersed in a 0.045 vol% HF solution at room temperature. The effect of HF treatments on the activity of Vis-$TiO_2$/Ti thin films for the photocatalytic water splitting reaction have been investigated. Vis-$TiO_2$/Ti thin films treated with HF solution (HF-Vis-$TiO_2$/Ti) exhibited remarkable enhancement in the photocatalytic activity for $H_2$ evolution from a methanol aqueous solution as well as in the photoelectrochemical performance under visible light irradiation as compared with the untreated Vis-$TiO_2$/Ti thin films. Moreover, Pt-loaded HF-Vis-$TiO_2$/Ti thin films act as efficient and stable photocatalysts for the separate evolution of $H_2$ and $O_2$ from water under visible light irradiation in the presence of chemical bias. Thus, HF treatment was found to be an effective way to improve the photocatalytic activity of Vis-$TiO_2$/Ti thin films. Furthermore, unique separate type photofuel cell was fabricated using a Vis-$TiO_2$ thin film as an electrode, which can generate electrical power under solar light irradiation by using various kinds of biomass derivatives as fuel. It was found that the introduction of an iodine ($I^-/{I_3}^-$) redox solution at the cathode side enables the development of a highly efficient photofuel cell which can utilize a cost-efficient carbon electrode as an alternative to the Pt cathode.

• Journal of the Korean institute of surface engineering
• /
• v.35 no.4
• /
• pp.211-217
• /
• 2002

Ti-Si-N films were deposited onto WC-Co substrate by a RF-PECVD technique. The deposition behaviors of Ti-Si-N films were investigated by varying the deposition temperature, RF power, and reaction gas ratio (Mx). Ti-Si-N films deposited at 500, 180W, and Mx 60% had a maximum hardness value of 38GPa. The microstructure of films with a maximum hardness was revealed to be a nanocomposite of TiN crystallites penetrated by amorphous silicon nitride phase by HRTEM analyses. The microstructure of maximum hardness with Si content (10 at.%) was revealed to be a nanocomposite of TiN crystallites penetrated by amorphous silicon nitride phase, but to have partly aligned structure of TiN and some inhomogeniety in distribution. and At above 10 at.% Si content, TiN crystallite became finer and more isotropic also thickness of amorphous silicon nitride phase increased at microstructure.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.11a
• /
• pp.75-78
• /
• 1996

The deposition condition Gf TiN films as electrode was studied by sheet resistance, TiN depositon Thickness X-ray diffraction. TiN was made by reactively DC magnetron sputtering with varying $N_2$/Ar mixture gas and substrate temperature. After finding The deposition condition of TiN films, The samples with the structure of Cu/Ta$_2$O$_{5}$, TiN/Ta$_2$O$_{5}$Si, Cu/TiN/Ta$_2$O$_{5}$ Si were prepared and were measured I-V, C-V. As a results, it was found that when TiN was deposited in an $N_2$a results, it was found that when TiN was deposited in an $N_2$atmosphere its Sheet resistance is lower n than n V$_2$Ar mixtureixture

• Journal of the Korean Electrochemical Society
• /
• v.11 no.2
• /
• pp.95-99
• /
• 2008

This study has made the electrode that is coated zirconium oxide on the titanium by ESD(Electrostatic spray deposition) coating methode. It has investigated the effects of the etching method of a Ti substrate as the preparation, making of zirconium oxide film and electrochemical characteristics of the electrode that is etched on the titanium. The HCl etching develops a fine and homogeneous roughness on the Ti substrate. Fabrication and material properties of the metal oxide electrode, which is known to be so effective to generate ozone and hypochlorous acid (HOCl) as power oxidant, were studied. A proper metal oxide material is focus zirconium oxide through reference. A coating method to enhance the fabrication reproducibility of the zirconium oxide electrode was used ESD coating method by zirconium oxychloride. Zirconium oxide films on the Ti substrate were tested using SEM, XRD, Cyclic voltammetry.