• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.181.2-181.2
• /
• 2015

Sputtering is one of the most popular physical deposition methods due to their versatility and reproducibility. Synthesis of Cr thin films by DC magnetron sputtering using glancing angle deposition (GLAD) has been reported. Chromium thin films have been prepared at two different working pressure($2.0{\times}10-2$, 30, $3.3{\times}10-3torr$) on Si-wafer substrate using magnetron sputtering with glancing angle deposition (GLAD) technique. The thickness of Cr thin films on the substrate was adjusted about 1 mm. The electrical property was measured by four-point probe method. For the measurement of density in the films, an X-ray reflectivity (XRR) was carried out. The sheet resistance and column angle increased with the increase of glancing angle. However, nanohardness and density of Cr thin films decreased as the glancing angle increased. The measured density for the Cr thin films decreased from 6.1 to 3.8 g/cc as the glancing angle increased from $0^{\circ}$ to $90^{\circ}$ degree. The low density of Cr thin films is resulted from the isolated columnar structure of samples. The evolution of the isolated columnar structure was enhanced at the conditions of low sputter pressure and high glancing angle. This GLAD technique can be potentially applied to the synthesis of thin films requiring porous and uniform coating such as thin film catalysts or gas sensors.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.93-93
• /
• 2013

In recent years, multifunctional ternary nitride thin films have received extenstive attention due to its versatility in many applications. In particular, noble metal based ternary nitride thin films showed a promising properties in the application of Multifunctional heating resistor films because its good electrical properties and excellent resistance against oxidation and corrosion. In this study, we prepared multifunctional noble metal based ternary nitride thin films by atomic layer deposition (ALD) and plasma-enhanced ALD (PEALD) method. ALD and PEALD techniques were used due to their inherent merits such as a precise composition control and large area uniformity, which is very attractive for preparing multicomponent thin films on large area substrate. Here, we will demonstrate the design concept of multifunctional noble metal based ternary thin films. And, the relationship between microstructural evolution and electrical resistivity in noble metal based ternary thin films will be systemically presented. The useful properties of noble metal based ternary thin films including anti-corrosion and anti-oxidation will be discussed in terms of hybrid functionality.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.04b
• /
• pp.65-68
• /
• 2002

The effect of low-temperature ZnO buffer layer has been investigated for the optical properties of ZnO thin films. ZnO buffers and thin films have been deposited using the pulsed laser deposition technique. ZnO buffer layers were grown at $200^{\circ}C$ with various thickness of 0 to 60 nm, followed by raising the substrate temperature to $400^{\circ}C$ to grow $2{\mu}m$ ZnO thin films. The buffer layers could relax stresses induced by the lattice mismatch and different thermal expansion coefficients between ZnO thin films and sapphire substrate. In order to identify the optical properties of ZnO thin films, PL measurement was used. From the results of PL measurement, all the fabricated ZnO thin films with buffer layers have shown intensive UV emission with a narrow linewidth. ZnO thin films with buffer layer of 20 nm have shown the strongest UV emission. It was found that the use of ZnO buffer layer plays an important role to improve the intensive UV emission of the ZnO thin films.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.91-91
• /
• 2012

We aim in synthesizing various functional thin films thinner than ~ 10 nm for environmental applications and photovoltaic devices. Atomic layer deposition is used for synthesizing inorganic thin films with a precise control of the film thickness. Several examples about application of our thin films for removing volatile organic compounds (VOC) will be highlighted, which are summarized in the below. 1) $TiO_2$ thin films prepared by ALD at low temperature ($<100^{\circ}C$) show high adsorption capacity for toluene. In combination with nanostructured templates, $TiO_2$ thin films can be used as building-block of high-performing VOC filter. 2) $TiO_2$ thin films on carbon fibers and nanodiamonds annealed at high temperatures are active for photocatalytic oxidation of VOCs, i.e. photocatalytic filter can be created by atomic layer deposition. 3) NiO can catalyze oxidation of toluene to $CO_2$ and $H_2O$ at $<300^{\circ}C$. $TiO_2$ thin films on NiO can reduce poisoning of NiO surfaces by reaction intermediates below $200^{\circ}C$. We also fabricated inverted organic solar cell based on ZnO electron collecting layers on ITO. $TiO_2$ thin films with a mean diameter less than 3 nm on ZnO can enhance photovoltaic performance by reducing electron-hole recombination on ZnO surfaces.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.272.2-272.2
• /
• 2016

Copper-Tin (CuSn) thin films were synthsized by rf magnetron co-sputtering method with pure Cu and Sn metal targets with various rf powers and sputtering times. The obtained CuSn thin films were characterized by a surface profiler (alpha step), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), X-ray induced Auger electron spectroscopy (XAES), and contact angle measurement. The deposition rates were calculated by the thickness of CuSn thin films and sputtering times. We observed hexagonal Cu20Sn6 and cubic Cu39Sn11 phases from the films by XRD measurement. From the survey XPS spectra, the Cu and Sn main peaks were observed. Therefore, we could conclude CuSn thin films were successfully fabricated on the substrate in this study. The changes of oxidation states and chemical environment of the films were investigated with high resolution XPS spectra in the regions of Cu 2p, Cu LMM, and Sn 3d. Surface free energy (SFE) and wettability of the CuSn thin films were studied with distilled water (DW) and ethylene glycol (EG) using the contact angle measurement. The total SFE of CuSn thin films decreased as rf power on Cu target increased. The contribution to the total SFE of dispersive SFE was relatively superior to polar SFE.

• Proceedings of the KIEE Conference
• /
• 1998.07d
• /
• pp.1349-1351
• /
• 1998

Platinum-Cobalt alloy thin films were deposited on $Al_2O_3$ substrates by r.f. cosputtering for RTD temperature sensors. We made Pt-Co alloy resistance patterns on the $Al_2O_3$ substrates by lift-off method and investigated the physical and electrical characteristics of these films under various conditions (the input power, working vacuum, annealing temperature, thickness of thin films) and also after annealing these films. At input power of Pt : $4.4 W/cm^2$. Co:6.91W/$cm^2$. working vacuum of 10 mTorr and annealing conditions of $1000^{\circ}C$ and 60 min, the resistivity and sheet resistivity of Pt-Co thin films was $15{\mu}{\Omega}{\cdot}cm$ and $0.5{\Omega}/{\square}$, respectively. The TCR value of Pt-Co alloy thin films was measured with various thickness of thin films and annealing conditions. The optimum TCR value is gained under conditions $3000{\AA}$ of thin films thickness and $1000^{\circ}C$ of annealing temperature. These results indicate that Pt-Co alloy thin films have potentiality for the high resolution RTD temperature sensors.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.10a
• /
• pp.22.1-22.1
• /
• 2011

In this study, off-axis RF magnetron sputtering was used for the crystallized ITO thin films at a low temperature of about $120^{\circ}C$ instead of the conventional RF sputtering because the off-axis sputtering can avoid the damage for the plasma as well as fabrication of thin films with a high quality. The structural, optical and electrical properties of the obtained films depending on deposition parameters, such as sputtering power, gas flow and working pressure, have been investigated. The ITO thin films grown on PET substrate at $120^{\circ}C$ were crystallized with a (222) preferred orientation. 100-nm thick ITO films showed a resistivity of about $4.2{\times}10^{-4}{\Omega}-cm$ and a transmittance of about 81% at a wavelength of 550nm. The transmittance of the ITO thin films by an insertion of $SiO_2$ thin films on ITO films was improved.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.10 no.4
• /
• pp.96-101
• /
• 2011

The thin films of TiN have been used extensively as wear-resistant materials, for instance, such as tools of high-speed cutting, metal mold forming etc. In these days, because the thin films capable of being used more severe conditions are needed, the technologies of arc ion plating are tried to improve its characteristics. The purpose of this study is to investigate the characteristics of thin films of (Ti,Cr)N compared with those of TiN. The method of arc ion plating, which is known as showing good tight-adherence and productivity, was used. After manufacturing thin films of ($Ti_{1-x}Cr_{x}$)N (x=0~1) with change of Cr in (Ti,Cr) target, atomic concentration, structure, size of crystallite, residual stress and surface roughness of thin films on substrate were investigated. As the results, it was confirmed that Cr atomic concentrations of thin films were proportionally changed with Cr atomic concentrations of target, and thin films of ($Ti_{1-x}Cr_{x}$)N (x=0~1) showed NaCl type and CrN existed as solid solution to TiN.

• Electrical & Electronic Materials
• /
• v.9 no.7
• /
• pp.690-695
• /
• 1996

We have systematically investigated the characterization of V$_{2}$O$_{5}$ thin films as a counter electrode for lithium based complementary electrochromic devices. The V$_{2}$O$_{5}$ thin films were prepared by thermal vacuum evaporation with varing the substrate temperature and film thickness. In electrochromic devices for smart windows, the WO$_{3}$ thin films with 400-800 nm thickness require to be capable of reversibly injection 10-15 mC/cm$^{2}$ of lithium, which is readily accomplished charge-balanced switching in a V$_{2}$O$_{5}$ thin films with 100-150nm thick. The V$_{2}$O$_{5}$ thin films produces considerably small changes in optical modulation properties in the visible and near infrared region(500-1100 nm) compared to the amorphous WO$_{3}$ thin films on 10-15 mC/cm$^{2}$ of lithium injection and the V$_{2}$O$_{5}$ thin films can therefore act as a counter electrode to WO$_{3}$ in a lithium based complementary clectrochromic devices. After 10$^{5}$ coloration/bleaching switching time, the degradation does not occurs and the devices exhibit a stable optical modulation in V$_{2}$O$_{5}$ thin films. It has shown that the injected lithium ion amounts in crystalline V$_{2}$O$_{5}$ thin films with the same thickness is large by 3-5 mC/cm$^{2}$ of lithium compared to the amorphous thin films in the same driving conditions. Therefore, to optimize the device performance, it is necessary to choose an appropriate film thickness and crystallinity of V$_{2}$O$_{5}$ for amorphous WO$_{3}$ film thickness as a working electrode.

• Proceedings of the KIEE Conference
• /
• 2004.07c
• /
• pp.1618-1620
• /
• 2004

The $Pb(Zr_{0.4}Ti_{0.6})O_3/Pb(Zr_{0.6}Ti_{0.4})O_3$ [PZT(4060)/(6040)] multilayered thin films were deposited by RF Sputtering method on the Pt/Ti/$SiO_2$/Si substrate. This procedure was repeated several times to form PZT(4060)/(6040) heterolayerd thin films. The effects on the structural and dielectric properties of PZT multilayered thin films were investigated. The MFM(Metal Ferroelectric Metal) type capacitors were made using the PZT(4060)/(6040) multilayered thin films deposited with optimum deposition condition. An enhanced dielectric property was observed in the PZT(4060)/(6040) multilayered thin films. The relative dielectric constant and dielectric loss at 100Hz of the PZT(4060)/(6040)-5 multilayered thin films were about 1106 and 0.016, respectively.