• Korean Journal of Materials Research
• /
• v.16 no.2
• /
• pp.111-115
• /
• 2006

High-finned tubes have good thermal conductivity and have better cooling efficiency than plain tubes or low-fined tubes due to bigger air contact area. During high-fined tubes are manufactured by roll forming, the main technique is illustrated to optimizing primary material(copper pipe), optimized die matrix designing technique for roll forming, control manufacturing speed to develop productivity etc. In this study, a roll forming system was developed in oder to produce high-finned tube. Also a multi-step roll forming die was designed & built to produce high-finned tube that has over 10 mm fin height. And then, roll forming test using copper pipe was performed to produce high-finned tube. Roll forming process for producing highfinned tube was optimized by analyzing and adjusting misrostructure, hardness, and surface roughness of roll formed high-fined tube.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.08a
• /
• pp.242-251
• /
• 1999

The temperature distribution over the work roll length was estimated by solving a 2-dimensional heat transfer equation based on the rolling conditions and the thermal boundary conditions. In order to solve the governing equation, a finite volume method was employed. In the rolling conditions, the strip temperature, the contact time between roll and strip, the roll speed, the strip thickness, the rolling force and the rolling and idling time were used as input data. In order to verify the accuracy of temperature estimation, roll surface temperatures were measured in the roll shop. The measured temperatures showed a good correlation with the calculated ones.

• Tribology and Lubricants
• /
• v.33 no.6
• /
• pp.256-262
• /
• 2017

Molten zinc plating is a process in which zinc is thinly coated over a metallic or non-metallic surface. It is used in various industrial fields for corrosion resistance and decoration. During the process, a steel sheet is passed through a roll that rotates inside the molten zinc liquid in the temperature range of $460^{\circ}C$ to $680^{\circ}C$, and the plating liquid flows into the roll causing abrasion and erosion of the roll surface. This problem is known to accelerate the replacement cycle of the roll and cause considerable economic loss owing to production line stoppage. Here, we propose a mechanism that operates at high temperature and pressure with a labyrinth type seal design to resolve this problem. We theoretically investigate the flow of the plating solution inside the seal and compute the minimum rotation speed required to prevent the plating solution from entering the seal chamber. In addition, we calculate the thermal deformation of the seal during operation and display thermally deformed dimensions at high temperatures. To verify the theoretical results, we perform experiments using pilot test equipment working in the actual plating environment. The experimental results are in good agreement with theoretical results. We expect our results to contribute towards the extension of the roll's life span and thereby reduce the economic losses.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.18 no.3
• /
• pp.307-314
• /
• 2009

Large area micro pattern replication has promising application potential in many areas. Rolling imprint process has been demonstrated as one of the most competitive processes for such micro pattern replication, because it has advantages in low cost, high throughput and high efficiency. In this paper, we developed a prototype of roll-to-flat(R2F) thermal imprint system for large area micro pattern replication process, which is one of the key processes in the fabrication of flexible displays. Experimental tests were conducted to evaluate the feasibility of system and the parameters' effect on the process, such as flat mold temperature, loading pressure and rolling speed. 100mm $\times$ 100mm stainless steel flat mold and commercially available polycarbonate sheets were used for the tests. The experimental results showed that the developed R2F system is suitable for fabrication of various micro devices with micro pattern over large area.

• Journal of Surface Science and Engineering
• /
• v.55 no.3
• /
• pp.173-179
• /
• 2022

This study presents a roll-to-roll process which is capable of Ag nanowire (AgNW) transfer from polyethylene terephthalate (PET) film to polycarbonate (PC) film. We developed a roll-to-roll machine that consists of two film suppliers, a coater of photo-curable resin, a film laminator, an ultraviolet (UV) exposure unit, and a film winder to facilitate large-area electrode transfer between different flexible substates. Using the process, optimal fabrication condition was investigated by parametric experiments in terms of the UV exposure time, number of thermal cycling, and exposure time of high temperature and humidity. A fabricated AgNW on PC film showed sheet resistance of 52 Ω/sq and optical transmittance of approximately 80 % over a range of visible light.

• Journal of Korea Foundry Society
• /
• v.16 no.2
• /
• pp.124-131
• /
• 1996

High temperature properties such as hot hardness and thermal fatigue resistance of high speed steel roll of hot finishing mill have been investigated. Two kinds of roll having compositions, Fe-1.75%C-5.9%Cr-1.74%Mo-4.94%V-2.03%W(A specimen) and Fe-2.27%C-8.86%Cr-2.91%Mo-3.92%V-1.86%W(B specimen)were prepared for investigating the microstructure and crack propagation mode. A specimen has greater amounts of $M_7C_3$ type carbides and less amounts of MC type carbides in comparison with B specimen. Hot hardness showed sudden decrease over $400^{\circ}C$, resulting in the hardness decrease of 50% at the temperature of $600^{\circ}C$, and showed little variation with time at $500^{\circ}C$ and $800^{\circ}C$. Thermal crack was developed at $550^{\circ}C$ in A specimen and $600^{\circ}C$ in B specimen.

• Current Optics and Photonics
• /
• v.3 no.5
• /
• pp.445-450
• /
• 2019

The influence of high-power laser diode (HPLD) emitter width on the device performance is investigated for 975-nm (In,Ga)(As,P)/(Al,Ga)As broad-area HPLDs, using self-consistent electro-thermal-optical simulation. To guarantee the simulation's accuracy, simulated results are matched with the measured results for a sample HPLD with fitting parameters. The influences of HPLD emitter width on temperature distribution, output power, and the beam product parameter (BPP) are analyzed for three different emitter widths of 50, 70, and $90{\mu}m$. It is found that a device with smaller emitter width exhibits both thermal rollover and thermal blooming at lower output power, but smaller BPP.

• Journal of Institute of Convergence Technology
• /
• v.2 no.1
• /
• pp.1-6
• /
• 2012

The cold chain system in South-East Asia is requiring to maintain freshness of refrigerated or frozen food. In this study, Thermal storage system using Phase change material (PCM) was developed and evaluated its performance about temperature and cold keeping time. For various application of cold chain system, we developed portable cold box, cold roll container and freezing station. Keeping time on laboratory tests of portable cold box in case of refrigeration and freezing were 6 hours and 4 hours, respectively. Cold container was developed to 2.5 ton scale. Evaluation in Indonesia, it was showed to keep the setting temperature of $-10^{\circ}C$ over 40 hours at $30^{\circ}C$ of ambient air. Freezing station using PCM was kept over 24 hours under $-20^{\circ}C$.

• Journal of Surface Science and Engineering
• /
• v.50 no.3
• /
• pp.198-205
• /
• 2017

Thermal dissipation was investigated for poly methyl methacrylate (PMMA) composite films containing graphite and multi wall carbon nanotube(CNT) powders as filler materials. After mixing PMMA with fillers, solvent, and dispersant, the pastes were prepared by passing through a three roll mill for three times. The prepared pastes were coated $15{\sim}40{\mu}m$ thick on a side of 0.4 mm thick aluminium alloy plate and dried for 30 min at $150^{\circ}C$ in an oven. The content of fillers in dried films was varied as 1, 2, and 5 weight % maintaining the ratio of graphite and CNT as 1:1. Raman spectra from three different samples exhibited D, G and 2D peaks, as commonly observed in graphite and multi wall CNT. Among those peaks, D peak was prominent, which manifested the presence of defects in carbon materials. Thermal emissivity values of three samples were measured as 0.916, 0.934, and 0.930 with increasing filler content, which were the highest ever reported for the similar composite films. The thermal conductivities of three films were measured as 0.461, 0.523, and $0.852W/m{\cdot}K$, respectively. After placing bare Al plate and film coated samples over an opening of a polystyrene box maintained for 1 h at $92^{\circ}C$, the temperatures inside and outside of the box were measured. Outside temperatures were lower by $5.4^{\circ}C$ in the case of film coated plates than the bare one, and inside temperatures of the former were lower by $3.6^{\circ}C$ than the latter. It can be interpreted that the PMMA composite film coated Al plates dissipate heat quicker than the bare Al plate.

• Journal of the Optical Society of Korea
• /
• v.13 no.4
• /
• pp.416-422
• /
• 2009

We have demonstrated a highly efficient cladding-pumped ytterbium-doped fiber laser, generating $>$2.1 kW of continuous-wave output power at 1.1 μm with 74% slope efficiency with respect to launched pump power. The beam quality factor ($M^2$) was better than 1.2. The maximum output power was only limited by available pump power, showing no evidence of roll-over even at the highest output power. We present data on how the beam quality depends on the fiber parameter, based on our current and past fiber laser developments. We also discuss the ultimate power-capability of our fiber in terms of thermal management, Raman nonlinear scattering, and material damage, and estimate it to 10 kW.