• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2001년도 춘계학술대회논문집A
• /
• pp.517-522
• /
• 2001

The purpose of this study is to investigate the thermal embrittlement and the mechanical properties of 2.25Cr-1Mo steel aged at high temperature and stress for 250 hours. Original, aged artificially material were tested to obtain the hardness and impact absorbed energy. Hardness and impact absorbed energy decreased with the increasing aging time. The carbide morphology with the thermal embrittlement was found to contribute to the mechanical property change by X-Ray diffraction method.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1997년도 하계학술대회 논문집 C
• /
• pp.1465-1468
• /
• 1997

In this study we investigated the aging characteristic such as leakage current, dielectric loss, contact angle, of EPDM for outdoor use by thermal treatment. And also observed the color change of surface, changing of chemical ingredient of the marterials by optical microscope. SEMI, FTIR and EDX at the section and surface. The test result show that leakage current is increased with thermal aging time. contact angle and dielectric loss is slightly decreased. Moreover, micro-void or crack in bulk is severely increased with aging time. However, the result affect to the tan $\delta$ at bulk of EPDM. It seems that carrier sources are removed by degassing with heat treatment.

• 한국분말재료학회지
• /
• 제2권3호
• /
• pp.208-215
• /
• 1995

The aging effects on the characteristics of the melt spun Cu based shape memory alloys have been investigated by the microhardness test, X-ray diffraction, differential scanning calorimetry, scanning electron microscopy and transmission electron microscopy. After aged for specific times, hardness of the ribbons began to increase and shape memory capacity diminished. At the initial stage of aging the austenitic transformation temperatures increased gradually, but at last became nearly constant: That is, the aging deteriorated the thermal stability. The increase in hardness was due to the formation of the $\gamma_2$ precipitates. The loss in the shape memory capacity was due to the decrement of solute atoms in the matrix by the formation of the $\gamma_2$ precipitates. In this study, it was confirmed that Mn is an effective element for Improving the thermal stability.

• 한국조명전기설비학회지:조명전기설비
• /
• 제11권1호
• /
• pp.99-105
• /
• 1997

본 논문에서는 주상변압기 절연유의 가속열화반응을 수행하였다. 유중가스를 air bubbling 법으로 추출하여 가스크로마토크라프로 성분을 분석하였으며 가스농도는 각 가스의 추출율을 감안하여 보정하였다. 절연재료의 열화는 열분해반응과산화반응에의하여 진행되었으며 두 종류의 반응은 모두 0차반응의 특성을 보였고 탄화수소류, CO+{{{{ { CO}_{2 } }}}} 및 수소가스의 생성속도식을 얻었다. 유중가스 분석과 UV-Visible 분광광도법에 의하여 변압기내의 철심과 동코일이 열화과정에서 촉매역활을 함을 확인하였다.

• 한국조명전기설비학회지:조명전기설비
• /
• 제11권1호
• /
• pp.24-33
• /
• 1997

본 논문에서는 주상변압기 절연유의 가속열화반응을 수행하였다. 유중가스를 air bubbling법으로 추출하여 가스크로마토그라프로 성분을 분석하였으며 가스농도는 각 가스의 추출율을 감안하여 보정하였다. 절연재료의 열화는 열분해반응과 산화반응에 의하여 진행되었으며 두종류의 반응은 모두 0차반응의 특성을 보였고 탄화수소류, $CO+CO_2$ 및 수소가스의 생성속도식을 얻었다. 유중가스 분석과 UV-Visible 분광광도법에 의하여 변압기내의 철심과 동코일이 열화과정에서 촉매역활을 함에 확인하였다.

• 한국추진공학회:학술대회논문집
• /
• 한국추진공학회 2017년도 제48회 춘계학술대회논문집
• /
• pp.172-178
• /
• 2017

열적 특성은 에너지 물질 분야에서 중요한 특성 중 하나로, 에너지 물질 분해 시 분해열을 방출하기 때문에 DSC(시차 주사 열량계, Differential Scanning Calorimetry)를 자주 사용하고 있다. 승온속도를 달리한 DSC 측정의 경우, 용융과 같은 열역학적 변화로 인해 물질의 열적 측정에 방해를 준다. 또한 kg 단위로 예측하기 때문에 mg 단위 때와는 다른 공간상의 열 변화의 변수가 생긴다. 이번 연구에서는 이 문제점을 해결하는 방안으로, 등온 조건으로 한 DSC(Differential Scanning Calorimetry) 기초 데이터로 ATKS thermokinetic 프로그램을 이용하여 열적 노화 특성을 예측한다. 그리고 g 단위로 측정하는 ARC(Accelerating Rate Calorimetry)의 데이터를 이용하여 열적 노화 특성을 예측하고 결과를 비교 할 것이다.

• 전기학회논문지
• /
• 제58권7호
• /
• pp.1375-1379
• /
• 2009

Insulation tests have been performed on two generator stator bars under accelerated aging under a laboratory environment. Electrical stress was applied to stator bar No.1, and electrical and thermal stresses were applied to stator bar No.2. Nondestructive stator insulation tests including the ac current, dissipation factor($tan{\delta}$), and partial discharge tests have been performed on both bars as the bars were aged for 11460 hours. Experimental test results show that ${\Delta}I$, ${\Delta}tan{\delta}$, and partial discharge of No. 1 and No.2 stator bars increased with increased in aging time. It has been concluded from the test that the stator insulation of the two generators are in good condition.

• 한국자동차공학회논문집
• /
• 제10권2호
• /
• pp.110-116
• /
• 2002

At elevated temperature, very complex precipitations occur in STS316. To investigate the effect of the precipitation on mechanical properties in SIS316, tensile tests and fatigue crack growth tests were carried out at $650^{\circ}C$ using artificially degraded materials. The material degradation was simulated by aging for up to 20000 hrs. at $750^{\circ}C$, which is equal to 179000hrs (about 20yrs) of service life at $650^{\circ}C$, after conducting solution treatment for 20 min. at $11300^{\circ}C$. The result of the hardness test and the tensile test showed that both properties are closely related to the mean free distance of carbides. Also, from the results of fracture tests at $650^{\circ}C$, ${\triangle}K_{th}$, after values were found to decrease as aging time and microstructure, as the volume fraction of $\sigma$ phase increased.

• 대한기계학회논문집 C: 기술과 교육
• /
• 제4권2호
• /
• pp.101-109
• /
• 2016

발전소 내열강의 물성치는 고온 가동시간이 누적됨에 따라 열시효의 영향을 받는다. 본 연구에서는 제 4 세대 원자력시스템의 재료로 널리 채택되고 있는 Mod.9Cr-1Mo (ASME Grade 91)강을 대상으로 항복강도, 인장강도 및 파괴거동에 열시효가 미치는 영향에 대해 조사 및 분석하였다. 국내에서 가동 중인 초초임계(USC) 화력발전소의 배관계통에서 채취한, 73,716 시간의 가동 이력을 겪은 Gr.91 강 재료가 재료 실험을 위해 사용되었고, 동 시험결과와 가동 이력을 겪지 않은 신재의 시험결과를 비교 분석하였다. 또한 ASME 코드의 물성치와 RCC-MRx 의 물성치와 비교 분석하였고, 이들 설계기술기준 물성치의 보수성은 신재 및 가동 이력을 겪은 재료의 시험결과와 비교 분석을 통해 정량화하였다.

• Elastomers and Composites
• /
• 제59권2호
• /
• pp.73-81
• /
• 2024

In the field of electronic components, the potting material, which is a part of the electronic circuit package, plays a significant role in protecting circuits from the external environment and reducing signal interference among electronic devices during operation. This significantly affects the reliability of the components. Therefore, the accurate prediction and assessment of the lifespan of a material are of paramount importance in the electronics industry. We conducted an accelerated thermal aging evaluation using the Arrhenius technique on elastic potting material developed in-house, focusing on its insulation, waterproofing, and contraction properties. Through a comprehensive analysis of these properties and their interrelations, we confirmed the primary factors influencing molding material failure, as increased hardness is related to aggregation, adhesion, and post-hardening or thermal-aging-induced contraction. Furthermore, when plotting failure times against temperature, we observed that the hardness, adhesive strength, and water absorption rate were the predominant factors up to 120 ℃. Beyond this temperature, the tensile properties were the primary contributing factors. In contrast, the dielectric constant and loss tangent, which are vital for reducing signal interference in electric devices, exhibited positive changes(decreases) with aging and could be excluded as failure factors. Our findings establish valuable correlations between physical properties and techniques for the accurate prediction of failure time, with broad implications for future product lifespans. This study is particularly advantageous for advancing elastic potting materials to satisfy the stringent requirements of reliable environments.