• 한국구조물진단유지관리공학회 논문집
• /
• 제7권1호
• /
• pp.139-145
• /
• 2003

Ternary blended concrete, which contains both fly ash and granulated blast furnace slag, has an initial cost effective and is environment friendly. Furthermore, it has a lot of technical advantages such as the improvement of long term compressive strength, high workability, and the reduction of hydration heat. However, as the use and study on the performance of ternary blended concrete is limited, it is worthwhile studying the actual performance of this technology. This study examined the durability performance of ternary blended concrete, compared to binary blended concrete and ordinary portland concrete. It led to the conclusion that ternary blended concrete is very suitable for submerged members under marine environment. However, it should be noticed that ternary blended concrete becomes weak on carbonation, when it is situated on combined deterioration environment of carbonation and chloride. Therefore, the curing duration of ternary blended concrete should be prolonged in order to enhance the resistance of carbonation.

• 한국도로학회논문집
• /
• 제15권5호
• /
• pp.101-110
• /
• 2013

PURPOSES : The purpose of this study is to evaluate the durability of ternary blended concrete mixtures adding ultra fine admixture. METHODS : From the literature review, crack was considered as the main distress failure criterion on concrete bridge deck pavement. To reduce the initial crack development due to drying shrinkage, CSA expansion agent and shrink reduction agent were used to ternary blended concrete mixtures as a admixture. Laboratory tests including chloride ion penetration test, surface scaling test, rapid freeze & thaw resistance test, non restrained drying shrinkage and restrained drying shrinkage test were conducted to verify the durability of ternary blended concrete mixtures. RESULTS : Based on the test results, proposed mixtures were verified as high qualified durable materials. Expecially initial drying shrinkage crack was not occurred in ternary blended concrete mixtures with CSA expansion agent. CONCLUSIONS : It is concluded that the durability of proposed ternary blend concrete mixture was acceptable to apply for the concrete bridge deck pavement.

• 한국도로학회논문집
• /
• 제15권5호
• /
• pp.81-89
• /
• 2013

PURPOSES : This study is to evaluate ASR(alkali silica reactivity) resistance of ternary blended binder adding ultra fine mineral admixture. METHODS : This study analyzes ASR expansion using ASTM C 1260 and 1567. RESULTS : This study showed that the fineness of mineral admixture had no effect on ASR expansion. The expansion of ternary blended binder(UFFA 20%+FGGBS 10%) were below 0.1%, and this binder met the ASR standard. Also when adding the CSA expansion agent, ASR expansion slightly decreased. The expansion of latex modified mixture increased by 80% comparing plain mixture. CONCLUSIONS : Ternary blended binder met the ASR standard, and this binder is available in concrete bridge deck overlay.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 봄학술 발표회 논문집(I)
• /
• pp.487-490
• /
• 2005

This study was performed to investigate the effect of ternary blended cement concrete mixed with slag cement and fly ash on the compressive strength, the resistance to chloride ion penetration and reduction of hydration heat. Each performance of ternary blended cement concrete compared with binary blended cement concrete and ordinary portland cement concrete. As a result, it was concluded that ternary blended cement concrete is suitable to mass concrete under marine environment.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2002년도 가을 학술발표회 논문집
• /
• pp.23-26
• /
• 2002

Ternary blended concrete containing both fly ash and granulated blast furnace slag is initial cost effective, and environment friendly. Furthermore, it has many technical advantages such as improvement of long term compressive strength, rheology property, reduction of hydration heat, etc. However, use and data on the performance of ternary blended concrete are limited, and it is necessary to study on the adoption of this technology. This study examined the durability performance of ternary blended concrete comparing with binary blended concrete and ordinary portland concrete. From the results of this study, it was concluded that ternary blended concrete is very suitable to submerged zone under maine environment.

• Advances in concrete construction
• /
• 제7권2호
• /
• pp.75-85
• /
• 2019

The present study is focused on the mechanical and durability properties of ternary blended cement concrete mix of different grades 30 MPa, 50 MPa and 70 MPa. Three mineral admixtures (fly ash, silica fume and lime sludge) were used as a partial replacement of cement in the preparation of blended concrete mix. The durability of ternary blended cement concrete mix was studied by exposing it to acids HCl and $H_2SO_4$ at 5% concentration. Acid mass loss factors (AMLF), acid strength loss factor (ASLF) and acid durability factor (ADF) were determined, and the results were compared with the control mix. Chloride ions penetration was investigated by conducting rapid chlorination penetration test and accelerated corrosion penetration test on control mix and ternary blended cement concrete. From the results, it was evident that the usage of these mineral admixtures is having a beneficiary role on the strength as well as durability properties. The results inferred that the utilization of these materials as a partial replacement of cement have significantly enhanced the compressive strength of blended concrete mix in 30 MPa, 50 MPa and 70 MPa by 42.95%, 32.48% and 22.79%. The blended concrete mix shown greater resistance to acid attack compared to control mix concrete. Chloride ion ingress of the blended cement concrete mix was low compared to control mix implying the beneficiary role of mineral admixtures.

• 콘크리트학회논문집
• /
• 제20권4호
• /
• pp.439-449
• /
• 2008

혼화재를 사용한 혼합콘크리트는 콘크리트의 품질을 개선시키며 지속가능한 콘크리트구조물의 건설에도 기여하고 있다. 실리카퓸 (SF), 고로슬래그미분말 (GGBS), 플라이애쉬 (PFA) 등의 시멘트계 결합재는 고성능콘크리트의 혼화재로서 인식이 증가되고 있으나, 삼성분계 혼합콘크리트에 대한 연구는 매우 제한적이며, 특히 염해에 의한 부식저항성 측면에서의 연구는 상당히 취약한 실정이다. 본 연구에서는 보통포틀랜드시멘트의 경우를 50%의 치환율로 고정한 후 고로슬래그미분말의 경우는 $20{\sim}40%$, 실리카퓸의 경우에는 $5{\sim}15%$, 플라이애쉬의 경우는 $10{\sim}45%$로 치환한 경우의 각종 배합에 의한 염해부식저항성에 관한 실험연구를 수행하였다. 삼성분계 혼합콘크리트의 염해부식저항성을 평가한 본 연구에서는, 수행 실험으로서 부식 저항성 실험, 염소이온 고정화 능력 실험, 급속 염화물 촉진 실험, 산중성화 저항 능력 실험 등을 수행하였다. 연구 결과로서, 삼성분계 콘크리트는 미세구조를 치밀화 하여 염소이온의 이동을 지연시키고 있음을 확인하였다. 또한, 염분을 함유한 삼성분계 혼합콘크리트 내의 염소이온 고정화 능력 및 산중성화 저항 능력이 크게 개선되고 있음을 확인하여 염해에 대한 부식 저항성이 향상됨을 알 수 있었다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제24권2호
• /
• pp.41-49
• /
• 2020

상온에서 발생하는 1, 2성분계 무시멘트 콘크리트의 강도저하 문제를 개선하기 위해 시멘트를 실리카 흄, 플라이애시, 고로슬래그 미분말로 치환한 3성분계 무시멘트 콘크리트의 슬럼프와 압축강도 특성을 통해 비교분석을 실시하여 다음과 같은 결론을 얻었다. 3성분계 무시멘트 콘크리트는 2성분계에 비해 높은 압축강도를 나타냈으며 실리카 흄을 10% 혼입한 경우 슬럼프 감소가 적은 것으로 나타났다. 또한, 삼각조성도를 통해 슬럼프 및 압축강도 수준별 각 무기결합재의 적정 구성비율 범위를 제시하였다.

• 한국건설순환자원학회논문집
• /
• 제10권2호
• /
• pp.159-167
• /
• 2022

본 연구에서는 보통 포틀랜드시멘트를 사용한 콘크리트와 광물질 혼화재료 및 알칼리활성화제를 첨가한 4종류의 배합으로 시편을 제작한 후 X선 회절분석, 미세구조분석, 압축강도, 동결융해저항성 및 SEM Image 분석을 실시하여 각 배합별 강도발현, 상대동탄성계수, 중량변화 등을 측정하여 기초물성 평가를 진행하였다. 페로니켈슬래그 혼입 삼성분계 시멘트는 보통포틀랜드 시멘트 배합(OPC)과 비슷한 수화물을 생성하는 경향을 보였으며, MgO 성분으로 인한 팽창성 수화물은 확인되지 않았다. 페로니켈슬래그를 혼입 시 3성분계 시멘트(30SP20FN)의 경우 OPC와 비교 시 공극률이 커지는 경향을 보였지만, 알칼리활성화제를 첨가할 경우 공극 분포가 변화하는 경향을 보였다. 또한, 알칼리활성화제의 첨가는 30SP20FN의 장기강도발현을 앞당기는 효과를 보였으며, 18~26 % 가량 강도가 증가함을 확인하였다. 30SP20FN의 경우 dilution effect로 인한 낮은 수화도의 영향으로 동결융해저항성이 떨어졌지만, 알칼리활성화제를 첨가할 경우 높은 상대동탄성계수를 유지하였으며, 동결융해 저항성이 우수한 것을 알 수 있었는데, 이는 변화된 공극 분포 때문인 것으로 사료된다. 본 연구에서 실시한 상대동탄성계수 측정 실험에 사용된 콘크리트 시편 모두 300 사이클에서 상대동탄성계수가 60 % 이상으로 우수한 동결융해 저항성을 나타내었다. 동결융해 작용을 받은 콘크리트의 미세구조를 분석한 결과, OPC 및 30SP20FN 콘크리트의 경우 비정질의 수화물이 서로 결합되어 있지 않고, 미세 균열이 발생함을 확인한 반면, 알칼리 활성화제를 혼입한 배합의 경우 균질한 내부 구조를 유지하였다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2011년도 추계 학술논문 발표대회
• /
• pp.55-56
• /
• 2011

This study is to investigate the engineering properties of low heat concrete incorporating improved ternary blended cement by combining OPC(original portland cement), blast furnace slag and fly ash. The results were summarized as following ; For ITB(Improved Ternary Blend)mixture was that setting time proved to be accelerated, and adiabatic temperature rises were low. The use of ITB resulted in an increase of initial compressive strength.