• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.27 no.1
• /
• pp.45-53
• /
• 2014

In strength limit states design, it is assumed that after cracking, reinforcement carries all tension in the tension zone of reinforced concrete members. However, it can be seen the concrete between cracks will contribute to carrying a part of the tension stress in actual concrete members particularly at service load levels, this effect is referred as tension stiffening effect. In this study, tension stiffening models and high strength concrete beam flexural test results were verified through comparison. The relationship between moment-curvature and load-deflection was evaluated by result of tension stiffening model and test result values. The analysis results showed that ACI 318 and Owen & Damjanic generally shows good agreement.

• Journal of the Korea Concrete Institute
• /
• v.11 no.4
• /
• pp.83-93
• /
• 1999

This paper presents tension stiffening effect of Reinforced concrete members obtained from experimental results on direct tension and bending. From the direct tension test program, crack patterns were investigated with tension softening behaviors of concrete. Tension stiffening effects and losses of strain energy were, also, analyzed from the load-deflection curve with the main experimental variables such as concrete strength, yielding stress and reinforcement ratio of rebar. Tension stiffening effect of RC members increase linearly until the first crack initiate, decrease inversely with number of cracks, and then decrease rapidly when splitting cracks are happened. The tension stiffening effect is shown to be more important at the member of lower reinforcement than that of higher. Therefore, it necessitates to consider the tension stiffening effects at a nonlinear analysis. From the above analysis, a tension stiffening model of concrete is proposed and verified by applying it to bending members. From the numerical analysis by finite element approach, it is shown that the proposed model evaluates a little higher in analyzing at nonlinear region of high strength concrete, but, perform satisfactorily in general.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.1
• /
• pp.50-58
• /
• 2018

The verification of serviceability of concrete structures requires more informations on the composite behaviors between concrete and reinforcement. Among them, the investigation of crack widths and spacings is based on the tension stiffening effects. In this paper, the tension stiffening effects of high strength concrete members with compressive strength of 80 and 100MPa are investigated experimentally. It was found that the current design code which is based on the tests of normal strength concrete may not describe the tension stiffening effects in high strength concrete correctly. The coefficient that can appropriately reflect the tension stiffening effects in the high strength concrete was proposed. Also, the crack spacing was investigated through the cracking behaviors and the crack width according to the difference of the strains in steel and concrete was estimated. The results of this paper may be used to examine the tension stiffening effects of high strength concrete members.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.197-200
• /
• 2005

This paper presents an analytical model for evaluation of Tension Stiffening Effect by actual Bond-Slip relationships between the reinforcement and the surrounding concrete. The presence of longitudinal splitting cracks was found to significantly after the tension stiffening. The model is applied to the longitudinal splittings cracks and derived to Tension stiffening model. The predicted values are shown to be in good agreement with the experimentally measured data.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2010.05a
• /
• pp.71-72
• /
• 2010

In case of calculation of an immediate deflection according to EC2, a curvature and average curvature are calculated by reflecting tension stiffening effect. In this study, tension stiffening effects according to MC90 and EC2 were considered, and an immediate deflection was calculated. And also, it was compared to results in KCI provision and experimental data. In results, it has difference around 8~15% with respect to tension stiffening effect, but all of them predict well for the load-deflection behavior after yielding state.

• Journal of the Korea Concrete Institute
• /
• v.26 no.5
• /
• pp.581-589
• /
• 2014

This paper presents the tension stiffening behavior from experimental results of each 6 amorphous steel fibers and normal steel fibers reinforced direct tensile specimens with the main variables such as cover thickness to bar diameter ratio. A tension stiffening effect for steel fiber reinforced RC tension members improve on the increase in cover thickness, and also amorphous steel fiber is usually superior to normal steel fiber. The reinforcement of steel fibers controlled the splitting cracks and led to significant increase in the tension stiffening effect. In particular, if cover thickness is more than twice the bar diameter, the amorphous steel fiber reinforced specimen is controlled the splitting crack and increased the tension stiffening effect. And, the tension stiffening effect of amorphous steel fiber reinforced concrete tension members is different to current structural design code provision.

• Journal of the Korea Concrete Institute
• /
• v.23 no.6
• /
• pp.791-797
• /
• 2011

This paper presents the test results of 12 direct tensile specimens to investigate the effect of cover thickness on the tension stiffening behavior in axially loaded reinforced concrete tensile members. Six concrete cover thickness ratios are selected as a main experimental parameter. The results showed that, as cover thickness became thinner, more extensive split cracking along the reinforcement occurred and transverse crack spacing became smaller, making the effective tensile stiffness of thin specimens at the stabilized cracking stage to be much smaller than that of thick specimens. This observation is not implemented in the current design provisions, in which the significant reduction of tension stiffening effect can be achieved by applying thinner cover thickness. Based on the present results, a modified tension stiffening factor is proposed to account for the effect of the cover thickness.

• Proceedings of the Computational Structural Engineering Institute Conference
• /
• 1998.10a
• /
• pp.141-148
• /
• 1998

An analytical model which can simulate the post-cracking behavior of reinforced concrete structures subjected to in-plane shear and normal stresses is presented. Based on the force equilibriums, compatibility conditions, and bond stress-slip relationship between steel and concrete, a criterion to simulate consider the tension-stiffening effect is proposed. The material behavior of concrete is described by an orthotropic constitutive model, and focused on the tension-compression region with tension-stiffening and compression softening effects defining equivalent uniaxial relations in the axes of orthotropy. Correlation studies between analytical results and available experimental data are conducted with the objective to establish the validity of the proposed model.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.27 no.6
• /
• pp.47-54
• /
• 2023

In this study, the tensile behavior of concrete specimens reinforced with GFRP (Glass Fiber Reinforced Polymer), BFRP (Basalt Fiber Reinforced Polymer), and CFRP (Carbon Fiber Reinforced Polymer) bars was experimentally analyzed. The tensile strength of the FRP bars is appeared to be similar to the design strength, but the elastic modulus was somewhat lower. Additionally, the specimens for tension stiffening effect were manufacured using OPC (Ordinary Portland Cement) and SFRC (Steel Fiber Reinforced Concrete), with dimensions of 150(W)×150(B)×1000(H) mm. The crack spacing of specimens was most significant for GFRP reinforcement bars, which have a lower elastic modulus and a smoother surface, while BFRP and CFRP bars, with somewhat rougher surfaces and higher elastic moduli, showed similar crack spacings. In the load-strain relationship, GFRP bars exhibited a relatively abrupt behavior after cracking, whereas BFRP and CFRP bars showed a more stable behavior after the cracking phase, maintaining a certain level of tension stiffening effect. The tension stiffening index was somewhat smaller as the diameter increased, and GFRP, compared to BFRP, showed a higher tension stiffening index.

• Journal of the Korea Concrete Institute
• /
• v.22 no.6
• /
• pp.761-768
• /
• 2010

When cracks occur in reinforced concrete structures, a steel carries all tensile force at crack section, while the concrete between cracks carries a part of the tensile force due to bond, so that the steel is less elongated. This is called the tension-stiffening effect, that plays an important role in verification of a serviceability limit state. But it is a complicated work to use a complex strain distribution between cracks, therefore an average strain is used to calculate deflection and crack width. In Eurocode 2, tension-stiffening effect expressed in the first order form or the second order form is used in calculating an average curvature for deflection. In this study for a flexural member deflection and crack width are calculated using various models for the tension-stiffening effect and the results are compared with the values of Eurocode 2 and KCI provisions. As results, the predicted values using the second order form are appeared to be well agreed with the experimental values and it could secure more analytical consistency.