• Journal of Welding and Joining
• /
• v.7 no.4
• /
• pp.46-55
• /
• 1989

Zirconia coatings are performed by the plasma spraying on the substrate of Al-Si alloy. In case of plasma sprayed ceramic coatings, it is important to control properly residual stress occurred during cooling process. Residual stress in coating layer varies with sprayed conditions and is influenced greatly by the coating layer thickness. Surface residual stress due to coating layer thickness is measured by X-ray diffraction method and the residual stress in coating layer is estimated by the deflection of coating layer when the restraint force in substrate was removed. When zirconia was coated on the substrate, tensile residual stress remains on zirconia coated surface layer. The tensile stress is increased to 0.35mm thickness and after 0.45mm thickness it is decreased abrouptly. A thick bond and composite coating reduce the zirconia surface stress and composite coating controls effectively the thick zirconia surface stress.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.1
• /
• pp.25-31
• /
• 2011

In the tensile test necking occurs at the maximum load point and non-uniform stress state is generated in this section. The equivalent stress becomes quite different from the axial stress as necking proceeds. Methods for obtaining the true stress-true strain curves, by overcoming difficulties due to the necking phenomena, have been developed by many authors. One of the methods based on the finite element analysis simulation is a very promising method. In this paper, general-purpose finite element program is used to simulate the tensile test. A round specimen and a flat specimen prepared from the same steel block are tested and simulated. The true stress-true strain curves are determined without assuming that the material follows Hollomon's law.

• Journal of the Korean Magnetics Society
• /
• v.13 no.2
• /
• pp.76-81
• /
• 2003

Non-linear anisotropic materials were used to simulate the effects of tensile stress in 3D finite element analysis (FEA). FEA was used to calculate the effects of far and near-side pit depth and tensile stress on magnetic flux leakage (MFL) signals. The axial and radial MFL signals were depended on far and near-side double circular pit depth and on the stress, but the circumferential MFL signal was not depended on them. The axial and radial MFL signals increased with greater pit depth and applied stress, but the circumferential MFL signal was scarcely changed.

• Structural Engineering and Mechanics
• /
• v.19 no.2
• /
• pp.173-184
• /
• 2005

For reducing construction cost, two-plate-girder bridges are getting popular in Japan. This type of bridge employs a PC slab, which is often cast-in-place. In such a case, concrete is not usually cast over the whole slab at one time: some portions are constructed earlier than the rest. Therefore, a construction joint is inevitably created. Due to the drying shrinkage of concrete, tension stress may occur in concrete slab. High tensile stress can be expected near the construction joint where concretes with different ages meet. Moreover, prestressing is not applied over the whole length of slab at one time. This may also serve as a source of tensile stress in the slab. Thus there is a chance that cast-in-place PC slab, especially near the construction joint, may be subjected to tensile cracking. In the present study, stress states near the construction joint in the cast-in-place PC slab of a two-plate-girder bridge are investigated numerically. The finite element method is employed and the three-dimensional analysis is conducted to see the influence of dry shrinkage and prestressing. The stress states in the PC slab thus obtained are discussed. The simplified model of a plate girder for this class of analysis is also proposed.

• Korean Journal of Materials Research
• /
• v.31 no.3
• /
• pp.172-180
• /
• 2021

In this study, using the plasma spray method, tensile and compression fatigue tests are performed in saline solution to examine the effect of Ti undercoat on corrosion fatigue behavior of alumina-coated specimens. The alumina-coated material using Ti in the undercoat shows better corrosion fatigue strength than the base material in the entire stress amplitude range. Fatigue cracking of UT specimens occurs in the recess formed by grit-blasting treatment and progresses toward the base metal. Subsequently, the undercoat is destroyed at a stage where the deformation of the undercoat cannot follow the crack opening displacement. The residual stress of the UT specimen has a tensile residual stress up to about 100 ㎛ below the surface of the base material; however, when the depth exceeds 100 ㎛, the residual stress becomes a compressive residual stress. In addition, the inside of the spray coating film is compressive residual stress, which contributes to improving the fatigue strength characteristics. A hardened layer due to grit-blasting treatment is formed near the surface of the UT specimen, contributing to the improvement of the fatigue strength characteristics. Since the natural potential of Ti spray coating film is slightly higher than that of the base material, it exhibits excellent corrosion resistance; however, when physiological saline intrudes, a galvanic battery is formed and the base material corrodes preferentially.

• Journal of Adhesion and Interface
• /
• v.5 no.2
• /
• pp.22-36
• /
• 2004

Several in-situ testing methods of adhesively bonded joints under static short-time tensile loading are critically analyzed in terms of experimental procedure and data evaluation. Due to its rather homogeneous stress state across the glue line, the tensile-shear test with thick single-lap specimens, according to ISO 11003-2, has become the most important test process for the determination of realistic materials parameters. This basic method, which was improved in both, the experimental part by stepped adherends and easily attachable extensometers and the evaluation procedure by numeric substrate deformation correction and test simulation based on the finite element method (FEM), is therefore demonstrated by application to several kinds of adhesives and metallic adherends. Multi-axial load decreases the strength of a joint. This effect, which is illustrated by an experimental comparison, impedes the derivation of realistic mechanical characteristics from measured force-displacement curves. It is shown by numeric modeling that tensile-shear tests with thin plate substrates according to ISO 4587, which are widely used for quick industrial quality assurance, reveal an inhomogeneous stress state, especially because of relatively large adherend deformation. Complete experimental determination of the elastic properties of bonded joints requires independent measurement of at least two characteristics. As the thick-adherend tensile-shear test directly yields the shear modulus, the tensile butt-joint test according to ISO 6922 represents the most obvious complement of the test programme. Thus, validity of analytical correction formulae proposed in literature for the derivation of realistic materials characteristics is verified by numeric simulation. Moreover, the influence of the substrate deformation is examined and a FEM correction method introduced.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2010.05a
• /
• pp.193-194
• /
• 2010

• Korean Journal of Materials Research
• /
• v.26 no.7
• /
• pp.370-375
• /
• 2016

Tensile tests and creep tests were carried out at high temperatures on an Al-$Al_4C_3$ alloy prepared by mechanical alloying technique. The material contains about 2.0% carbon and 0.9% oxygen in mass percent, and the volume fractions of $Al_4C_3$ and $Al_2O_3$ particles are estimated at 7.4 and 1.4%, respectively, from the chemical composition. Minimum creep rate decreased steeply near two critical stresses, ${\sigma}_{cl}$ (the lower critical stress) and ${\sigma}_{cu}$ (the upper critical stress), with decreasing applied stress at temperatures below 723 K. Instantaneous plastic strain was observed in creep tests above a critical stress, ${\sigma}_{ci}$, at each test temperature. ${\sigma}_{cu}$ and ${\sigma}_{ci}$ were fairly close to the 0.2% proof stress obtained by tensile tests at each test temperature. It is thought that ${\sigma}_{cl}$ and ${\sigma}_{cu}$ correspond to the microscopic yield stress and the macroscopic yield stress, respectively. The lower critical stress corresponds to the local yield stress needed for dislocations to move in the soft region within subgrains. The creep strain in the low stress range below 723 K arises mainly from the local deformation of the soft region. The upper critical stress is equivalent to the macroscopic yield stress necessary for dislocations within subgrains or in subboundaries; this stress can extensively move beyond subboundaries under a stress above the critical point to yield a macroscopic deformation. At higher temperatures above 773 K, the influence of the diffusional creep increases and the stress exponent of the creep rate decreases.

• Bulletin of the Society of Naval Architects of Korea
• /
• v.20 no.4
• /
• pp.17-24
• /
• 1983

In this study, it was investigated the distribution of residual stress in the direction of loading between the root and toe the load fillet welds for thick steel plate. Residual stress distributions are measured by sectioning method which is one of stress-relaxation technique in welded joint, and analyzed by two dimensional finite element method on thermo-elasto-plastic theory under plane stress condition. These are compared the results of F.E.M analysis with the experimental result by stress-relaxation techniques. As a results, the following conclusion were obtained. (1) In the no penetration fillet welded joint specimen using mild steel plate with 25mm in thickness, the residual stress of loading direction near the root was about $10kg/mm^2$ tensile. (2) The tensile residual stress has been observed in fillet region of the fillet joint by F.E.M. analysis method. (3) The range of compressive residual stress distribution from the root was largest in the case of 5mm root penetration.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2001.05a
• /
• pp.13-15
• /
• 2001

Compression test has been used to measure material flow stress due to limited capability of tensile test at the fast strain rate. Since the frictional stress unavoidable during compression test should be properly eliminated from the measured stress, calibration of the measured stress by using friction factor has been made for the flow stress measurement. Also, calibrated stresses by interrupted and continuous compression tests have been compared with the true stress measured by tensile test at $0.2\%$ carbon steel.