• 한국정밀공학회지
• /
• 제30권3호
• /
• pp.271-277
• /
• 2013

Inconel 718 super alloy was aging heat treated at the temperature range from $675^{\circ}C$ to $785^{\circ}C$ for 5~40 hours after solution annealing at $1025^{\circ}C$ for 1 hour. The aging treated specimens were investigated microstructure, mechanical properties and thermal expansion/contraction. Precipitates appeared for a long time aging treatment were niobium carbide and also ${\gamma}^{\prime}$ phase. For the aging treatment time of 10 hours, the changes in strength and hardness with increasing aging treatment temperature showed the maximum value at the temperature of $725^{\circ}C$. This maximum value is to be related with the precipitation of ${\gamma}^{\prime}$ and ${\gamma}^{{\prime}{\prime}}$ phases. The decrease in strength, elongation and hardness during long time aging at $725^{\circ}C$ were thought to be induced from the coarsening of the grain size and the transformation of ${\gamma}^{{\prime}{\prime}}$ phase to ${\gamma}^{\prime}$ phase. For the specimens treated for 10 hours, impact energy showed constant value of ~105 J with increasing the aging temperature, however this value continuously decreased with elapsing time at the aging temperature of $725^{\circ}C$. It was found that the decrease in impact value was induced from the coarsening of grain size and the carbide coarsening. The coefficient of thermal expansion of aging treated Inconel 718 alloy increased with raising test temperature, and the coefficient was appeared $11.57{\sim}12.09{\mu}m/m{\cdot}^{\circ}C$ and $14.28{\sim}14.39{\mu}m/m{\cdot}^{\circ}C$, respectively, after heating to $150^{\circ}C$ and $450^{\circ}C$.

• 한국포장학회지
• /
• 제21권1호
• /
• pp.27-34
• /
• 2015

전자레인지 가열용 제품에서 마이크로파에 의한 불균일한 가열이 일어남에 따라 포장재의 특정 부위에 열 변형이 발생하여 전자레인지 포장 소재에 따른 가열조리 패턴을 조사하였다. 전자레인지 가열용 포장재의 내면으로 이용되는 CPP의 grade에 따른 인장강도, 내열성 및 신장률을 비교하였다. High retortable CPP는 일반 CPP 재질과 비교하여 강한 열 접착강도 및 내열 저항성을 가지고 있었다. 국외 및 국내 CPP 제품의 인장강도 및 신장율은 차이가 있지만 대부분 $160^{\circ}C$ 정도 수준의 내열성을 가지고 있는 것으로 조사되었다. 하지만 소스의 높은 점도와 염분을 함유하는 hot spicy 제품에서는 전자파의 침투가 원활하지 못하여 전자레인지 조리 시 내용물의 균일한 가열이 어려워 국지적 또는 액위선 부위에 포장재의 열 변형이 관찰되었다. G-PET/PET/PET/CPP와 G-PET/PET/NY/CPP로 구성된 포장재를 레토르트 처리했을 때와 레토르트 후 전자레인지 가열 처리하였을 때 상태변화 및 합지강도에 대한 분석결과 합지강도의 차이는 없었으나 레토르트 처리 후 CPP 층의 변형이 관찰되었다. $TiO_2$가 포함된 유백 파우치와 투명 파우치의 열 변형 정도를 비교하였을 때는 $TiO_2$가 포함된 포장재의 열 변형이 더 심하였고, 알루미늄 호일을 부착한 후 전자레인지 가열하였을 때에는 액위선에서 열 변형이 발생되지 않았지만 바닥면에서 열 변형이 관찰되었다. 제품의 내면인 CPP 층의 개질/개선을 통한 내열안정성 확보 및 포장재의 전자파 투과-반사능을 조절하여 포장 내 전자파의 집중을 방지하는 등의 기술 도입 가능성의 검토가 필요할 것으로 판단된다.

• Elastomers and Composites
• /
• 제48권3호
• /
• pp.225-231
• /
• 2013

본 연구에서는 carboxylated SBR latex와 zinc oxide가 SBS 복합재의 내마모성과 debris 특성 개선에 미치는 영향을 관찰하였다. 실리카를 첨가한 SBS 복합재는 실리카 입자간의 수소 결합에 의한 강한 filler-filler interaction으로 인한 낮은 분산성 때문에 기계적 강도, NBS 내마모성, debris 특성이 전체적으로 감소하는 것으로 나타났다. carboxylated SBR latex를 첨가한 SBS 복합재는 carboxyl group과 실리카의 silanol group간의 결합을 통하여 filler-filler interaction이 감소하고 실리카의 분산성이 증가하기 때문에 기계적 강도, NBS 내마모성, debris 특성이 향상되는 것을 확인 하였다. carboxylated SBR latex와 zinc oxide를 동시에 첨가한 경우, carboxyl group에 의한 실리카의 분산성 향상과 더불어 zinc ion과 carboxyl group간의 ion cluster 형성을 통하여 물성이 크게 증가하였다. Zinc ion과 carboxyl group간의 ion cluster 형성은 $1550{\sim}1650cm^{-1}$의 zinc carboxylate group stretch 피크의 FT-IR 분석 결과로 확인하였다. carboxylated SBR latex와 zinc oxide를 첨가한(SC-4) 복합재의 경우, 인장강도 $156kgf/cm^2$, 신장율 936%, 인열강도 59.4kgf/cm의 우수한 기계적 강도를 나타내었으며, NBS 내마모성은 338%로 가장 우수한 특성을 나타내었다. 또한, 표면 마찰 시에 debris 발생 역시 크게 감소하며, 표면 마찰 저항의 증가로 파도 형태의 마모 특성을 나타내었다.

• 한국산학기술학회논문지
• /
• 제17권1호
• /
• pp.175-180
• /
• 2016

폐 자동차에서 떼어낸 범퍼는 분쇄 및 도장 (paint)제거 공정을 거친 후 신재 (pristine materials)와 일정 비율 혼합하여 자동차 부품을 제조하는 공정에서 재활용된다. 본 연구에서는 신재와 도장이 제거된 범퍼 분쇄품을 일정 비율 혼합하여 혼합비에 따른 기계적인 물성 및 화학적인 성질을 연구하였다. 신재에 범퍼 분쇄 품을 혼합하였을 때 인장강도 및 굴곡탄성율과 같은 강성은 두 물질의 조성 평균으로 나타났지만, 충격강도와 파단 신율과 같은 인성 (toughness)은 조성 평균보다 낮은 negative deviation을 보였다. 이는 두 물질간의 혼화성이 부족하여 발생하는 결과라는 것을 FT-IR 분석을 통하여 알 수 있었다. 범퍼 분쇄품의 혼합 비율이 30% 이상에서 두 물성이 급격히 저하되었다. 이를 활용하면 최적의 배합 비율을 선정할 수 있을 것이다. 또한 이전 연구에서 밝힌 바와 같이 도장 제거율을 80 % 수준까지는 달성하기는 쉽지만 나머지 20%를 제거하기 위하여 많은 노력과 에너지가 소요되는 바, 도장이 제거되지 않은 분쇄품과 도장이 제거된 분쇄품의 혼합 비율에 따른 기계적인 물성에 대하여 실험하였다. 도장이 제거되지 않은 범퍼 분쇄품이 소량만 첨가되어도 기계적인 물성은 급격히 저하가 되어 폐 범퍼를 재활용하기 위해서는 도장 제거 공정이 매우 중요하다는 사실을 알 수 있었다.

• 한국응용과학기술학회지
• /
• 제31권3호
• /
• pp.500-508
• /
• 2014

본 연구에서는 ethyl acrylate monomer(EAM)을 사용한 수용성 아크릴 수지를 합성한 후 monoammonium phophate를 수용액 상태로 녹인 뒤 이를 아크릴 수지에 함양을 달리한 시료를 준비하여 각각의 필름 상태 및 피혁 외부에 코팅하여 기계적 물성측정 및 열안정성 물성 측정 실시하여 각각의 시료를 비교 검토 하였다. DSC를 이용한 열안정성 측정 결과 monoammonium phosphate 함량이 높은 시료(WAC-APS3)의 Tm 값이 $410^{\circ}C$ 로 가장 높은 열안정성을 확인할 수 있었다. 내용제성 측정결과 아크릴 수지 및 브랜딩 된 수지 모두 높은 내용제성을 확인 할 수 있었다. 내마모성 측정결과는 monoammonium phosphate 함량이 높은 수지가 우수한 물성(68.729 mg.loss)을 보였으나, 인장 강도, 연신율 측정치에서는 monoammonium phosphate 함량이 높아질수록 물성이 저하되어 아크릴 수지의 인장력인 $1.505kgf/mm^2$ 보다 낮은 $1.275kgf/mm^2$ 이 측정되었으며, 연신율의 경우 수용성 아크릴 수지 단독 시료의 연신율인 425% 보다 낮은 384% 가 측정되었다.

• 대한금속재료학회지
• /
• 제56권11호
• /
• pp.787-795
• /
• 2018

The effects of tempering condition on the microstructure and mechanical properties of 30MnB5 hot stamping steel were investigated in this study. Before the tempering, hot-stamped 30MnB5 steel was composed of only ${\alpha}^{\prime}$-martensite microstructure without precipitates. After the tempering at $180^{\circ}C$ for 120 min, nano-sized ${\varepsilon}$-carbides were precipitated in the ${\alpha}^{\prime}$-martensite laths. After tempering at $250^{\circ}C$ for 60 min, cementite was precipitated along the ${\alpha}^{\prime}$-martensite lath boundaries. The cementite was also observed in the specimens tempered at $350^{\circ}C$ for 30 min and $450^{\circ}C$ for 6 min, respectively. The globular ${\alpha}$-ferrite appeared at $350^{\circ}C-30min$ tempering, and the volume fraction of ${\alpha}$-ferrite increased when the tempering temperature was increased. The yield strength increased after tempering, and it reached a peak with the tempering condition of $180^{\circ}C-120min$, due to the nano-sized precipitates in the ${\alpha}^{\prime}$-martensite lath. After the tempering, the steel's ultimate tensile strength (UTS) was decreased due to the reduction in dislocation density and C segregation to lath boundaries. The highest elongation was observed at the $180^{\circ}C-120min$ tempering condition, due to the reduction of residual stress, and the lack of precipitates along the lath boundaries. The $180^{\circ}C-120min$ tempering condition was considered to have outstanding crash performance, according to toughness and anti-intrusion calculation results. In drop tower crash tests, the 30MnB5 door impact beam tempered at $180^{\circ}C$ for 120 min showed better crash performance compared to a 22MnB5 door impact beam.

• 청정기술
• /
• 제25권1호
• /
• pp.7-13
• /
• 2019

일련의 dimethylformamide (DMF) 기반 폴리우레탄은 메틸렌 디 페닐 디 이소시아네이트(MDI) 1,4-부탄 디올 및 바이오 폴리올(1,3-프로판 디올: B-POL)에 기초한 폴리 트리 메틸렌 에테르 글리콜/폴리 에스터 폴리올(1,4-부탄디올: H-PET)으로 부터 합성하였다. 본 연구에서는 바이오 폴리올(B-POL)/폴리에스터 폴리올(H-PET)의 조성이 폴리우레탄의 물성에 미치는 영향을 조사하였다. B-POL/H-PET 혼합물의 B-POL 함량이 증가할수록 폴리우레탄의 소프트 세그먼트의 유리전이온도(Tgs)와 인장 강도는 감소하는 반면, 파괴 신도 및 인열 강도는 증가하였다. 한편 합성된 DMF 기반 폴리우레탄을 이용하여 습식공정으로 인조피혁을 제조하였다. 인조피혁에 형성된 다공성 셀의 평균 크기 및 밀도(단위부피당 셀의 수)에 미치는 B-POL/H-PET 조성의 영향의 차이는 거의 없는 것을 알 수 있었다. 이러한 결과들로부터 바이오 폴리올 기반 폴리우레탄을 습식공정으로 제조되는 인조피혁용으로 사용하는데 별 문제가 없음을 알 수 있었다.

• 대한화학회지
• /
• 제67권6호
• /
• pp.420-428
• /
• 2023

비닐화된 메조포러스 실리카와 재생 폴리에틸렌 사이에 가교결합을 도입하여 컴파운드를 제조하고 물성을 측정하였다. 메조포러스 실리카에 비닐기를 도입함으로써 비극성인 폴리에틸렌과의 가교결합을 유도할 수 있는 물질이 된다. 비닐화된 메조포러스 실리카를 합성하고 재생 폴리에틸렌과의 가교결합을 유도하여, 기존 재생 폴리에틸렌이 가지는 물성보다 더욱 향상된 재생 폴리에틸렌 복합체를 합성하였다. 또한 비닐화 된 메조포러스 실리카를 이용하였을 때, 재생 폴리에틸렌의 등급에 따라 소량 첨가하여도 가교반응이 진행되어 컴파운드의 모든 물리적 특성이 향상되었다. 비닐화된 메조포러스 실리카를 사용하여 4종의 컴파운드를 합성하였으며, 형태와 미세 구조 및 작용기는 TEM, FT-IR 및 XRD로 분석하였다. 비닐화된 메조포러스 실리카를 이용하여 재생 폴리에틸렌과 가교반응으로 3종류의 컴파운드를 배합하였다. 가교결합 유무를 확인하기 위해서 XPS, FT-IR 및 가교도 측정법으로 분석하였으며, Universal testing machine을 이용하여 인장강도, 신장율, 굴곡강도 및 굴곡 탄성율 같은 물리적 특성을 측정하였다. 그 결과, 비닐화된 메조포러스 실리카를 다양한 등급의 재생 폴리에틸렌에 적용함으로써, 기존의 재생 폴리에틸렌이 가지는 취약한 물성을 극복하였다. 비닐화된 메조포러스 실리카-재생폴리에틸렌 복합물질을 신재 폴리에틸렌에 적용한 결과, 복합 컴파운드는 상업적으로 사용할 수 있는 최선의 물성 지표를 나타내었다. 따라서 이 결과는 향후 재생 폴리에틸렌의 사용량을 증가시키고, 자원의 재순환화에 활용될 수 있을 것으로 기대된다.

• 한국응용과학기술학회지
• /
• 제35권1호
• /
• pp.173-185
• /
• 2018

화학 관능기가 다른 지방산 에스터계, 지방산 금속염 및 아마이드계 분산 및 흐름개선 첨가제가 EPDM과 카본블랙을 충전제로 사용한 고무 배합물의 가류 특성과 가류된 고무 배합물의 기계적 물성 및 노화특성에 미치는 영향을 무니점도계, 레오미터, 경도계, 만능재료시험기 등을 이용하여 측정하였다. $125^{\circ}C$에서 측정된 무니점도는 아마이드계 > 금속염계 > 에스터계 첨가제의 순으로 감소하는 경향을 보였으며, 스코치시간은 에스터계와 금속염계 첨가제는 첨가 유무에 따라 거의 차이가 없거나 조금 늦어지며, 아마이드계 첨가제는 1분 이상 빨라졌다. $160^{\circ}C$에서의 레오미터 측정 결과 가류시간은 금속염계와 아마이드계 첨가제의 경우는 가류반응이 빨리 진행되었다. 델타토크 값은 금속염계와 아마이드계 첨가제가 있는 경우 전반적으로 증가하였으나, 에스터계 첨가제가 있는 경우는 약간 감소하였다. EPDM 배합물의 인장강도는 에스터계 첨가제가 첨가된 경우 크게 향상되었으며, 아마이드계와 금속염계 첨가제의 경우는 큰 영향이 없었다. 신율의 경우는 금속염계 첨가제의 경우 크게 향상되었으며, 나머지의 경우는 큰 영향이 없었다. 인열강도는 첨가제의 첨가에 따라 전반적으로 상승하였으며 금속염계 첨가제의 경우에서 확연히 상승하였으며 경도는 첨가제의 종류와 상관없이 유사한 값을 나타내었다. $100^{\circ}C$에서 24시간 열노화시킨 EPDM 배합물은 금속염계와 아마이드계 첨가제의 경우는 거의 변화가 없었으며 신율의 변화는 첨가제를 함유한 모든 EPDM 배합물이 10-20% 정도 감소하는 경향을 보였다.

• 대한치과교정학회지
• /
• 제31권1호
• /
• pp.149-157
• /
• 2001

본 연구의 목적은 새로이 생산된 국산 스테인레스 스틸호선의 특성을 평가하기 위하여, 현재까지 사용하고 있는 다른 스테인레스 스틸호선과 비교하여, 국산 스테인레스 스틸호선의 특성과 장단점을 분석하고 평가하여 임상적 사용시에 도움을 주고자 하는 것이다. 이를 위해 Unitek의 Standard, Resilient, Hi-T 3종류의 스테인레스 스틸호선과 Ormco 의 Stainless Steel, 진성기업의 Stainless Steel등 5종(0.016x0.022과 0.019x0.025)을 가지고 성분, 치수비교, 인장물성, 만곡피로도물성, 비틀림물성, 경도 및 표면등을 관찰하여 비교하여 다음과 같은 결론을 얻었다. 1. 인장물성을 보면, 최대강도는 0.016x0.025의 경우 Unitek Hi-T, Unitek Resilient, Jinsung Stainless Steel, Ormco Stainless Steel, Unitek Standard 순이고, 0.019x0.025의 경우 Unitek Hi-T, Jinsung, Ormco, Unitek Resilient, Unitek Standard 의 순이었다. 2. 연신율은 0.016x0.022의 경우는 Unitek Standard, Ormco Stainless Steel, Unitek Hi-T, Unitek Resilient, Jinsung Stainless Steel의 순이었고, 0.019x0.025의 경우는 Unitek Hi-T, Unitek Standard, Ormco Stainless Steel, Jinsung Stainless Steel, Unitek Resilient의 순이었다. 3. 탄성계수는 0.016x0.022의 경우 Jinsung Stainless Steel, Unitek Hi-T, Unitek Resilient, Ormco Stainless Steel, Unitek Standard의 순이었고, 0.019x0.025의 경우 Unitek Resilient, Jinsung Stainless Steel, Ormco Stainless Steel, Unitek Hi-T, Unitek Standard의 순이었다. 4. 만곡피로도실험은 0.016x0.022의 경우 Jinsung Stainless Steel이 8.4회로 구부림에 대한 가장 파절저항도가 컸으며, Unitek Hi-T, Unitek Standard, Unitek Resilient, Ormco Stainless Steel의 순이고 0.019x0.025의 경우는 Unitek Hi-T가 10.4회 견디고, Jinsung Stainless Steel, Unitek Resilient, Unitek Standard, Ormco Stainless Steel의 순이었다. 5. 비틀림실험은 0.016x0.022의 경우 Unitek Resilient가 가장 비틀림에 대한 저항이 큰데, 64.8회의 회전후 파절한다. 그 다음으로 Jinsung Stainless Steel, Unitek Hi-T, Ormco Stainless Steel, Unitek Standard(50.6회) 순이었다. 0.019x0.025의 경우 Jinsung Stainless Steel이 가장 커서 83.2회의 회전에 저항하고, Unitek Resilient, Unitek Standard의 순이고 Ormco와 Unitek Hi-T가 가장 저항력이 작았다. 6. 주사전자현미경으로 본 표면은 모든 제품에서 생산과정 중에 보이는 압흔과 pitting이 관찰되는데, 진성기업의 Stainless Steel은 가늘고 긴 압흔이 있으며 비교적 매끄러운 표면을 보이고, Unitek사의 경우 압흔과 함께 pitting 이 관찰되며, Ormco Stainless Steel의 경우 불규칙한 pitting이 다수 존재했다.