• International Journal of Oral Biology
• /
• v.46 no.4
• /
• pp.184-189
• /
• 2021

When luting indirect restorations with dual-cure resin cement (DCRC), excess cement can be easily removed by performing tack cure of DCRC for a few seconds. The purpose of this study was to evaluate whether different tack cure times affect polymerization shrinkage (PS) of the selected DCRC. One dual-cure resin cement (G-CEM LinkAce, GC) was used for measuring PS in light-cure (LC group), self-cure (SC group), and two tack-cure modes. In the first tack-cure subgroup, tack cure was performed for 1, 2, 3, and 5 seconds, followed by light cure after 2 minutes of remnant removal time in each case (TC-LC groups). In the other tack-cure subgroup, tack cure was performed for the same lengths of time, but followed by self-cure in each case (TC-SC groups). PS was measured by a modified bonded disc method for 1,800 seconds. One-way analysis of variance followed by Duncan's post hoc test was used to determine any statistically significant differences among the test groups (α = 0.05). When the DCRC was self-cured after tack cure, PS was significantly lower than when it was only self-cured (p < 0.05); however, tack cure time did not affect PS (p > 0.05). When the DCRC was light-cured, PS was not affected by tack cure or tack cure time (p > 0.05). Therefore, tack cure within 5 seconds did not negatively affect the final PS when the DCRC was light-cured after cement remnant removal.

• International Journal of Highway Engineering
• /
• v.16 no.6
• /
• pp.121-128
• /
• 2014

PURPOSES : The objective of this study is to evaluate the tack-coating material's properties using the bitumen bond strength(BBS) test and damping test as function of changed curing times. In this study, bonding strength tests were performed according to the curing time of tack coating materials. METHODS : In order to investigate bonding characteristic of tack coating materials, the Pneumatic Adhesion tensile Testing Instrument(PATTI) device is used to measure the bond strength between the tack coating materials and aggregate substrate based on the AASHTO TP-91. Also, damping test as in situ test was used to determine an appropriate traffic openting time for construction vehicle. Four different tack-coating materials were used in this study. The BBS tests were performed a one hour curing and testing temperatures of $5^{\circ}C$, $15^{\circ}C$, and $25^{\circ}C$. Damping test was conducted at 30min, 60min, 90min, and 120 min of curing times with temperatures of $20^{\circ}C$ and $30^{\circ}C$. RESULTS and CONCLUSIONS : The BBS test results show various bond strength as function of tack coat materials. At the same testing condition, A tack coat material shows almost two times higher than D tack coat materials although both materials are satisfied the criteria of material's physical properties. Also, Dampting test results shows similar trend with BBS test result. The damping test result was significantly changed as function of tack coat materials. Based on this study, the tack coating material's curing time is very important. Therefore, both curing time and the bond strength's characteristic has to be considered in standard specification.

• International Journal of Highway Engineering
• /
• v.18 no.5
• /
• pp.1-9
• /
• 2016

PURPOSES : This study focuses on the evaluation of interface performance with varying surface texture and tack coat application in an asphalt overlay. METHODS : The evaluation is carried out in two phases: tracking test and interface bond strength test. Using an image processing tool, tracking test is conducted to evaluate the susceptibility of the tack coat material to produce excessive tracking during application. Using the pull-off test method, the bond strength test is performed to determine the ability of the interface layer to resist failure. RESULTS : Results show that the underseal application yields less tracking compared to other applications. However, the bond strength is barely within the minimum acceptable value. On the other hand, RSC-4 produces higher bond strength for all surface types, but the drying time is long, which produces excessive tracking. CONCLUSIONS : While underseal application may be suitable for a trackless condition, the bond strength is less appealing compared to the rest of the tack applications available. RSC-4 demonstrated a high and consistent bond strength performance, but more time is required for drying to avoid excessive tracking. Tack coat application and surface type combination produce varying results. Therefore, these should be considered when selecting suitable future tack coat application options.

• Journal of Adhesion and Interface
• /
• v.4 no.4
• /
• pp.7-14
• /
• 2003

"Tack" is defined as "the property that enables an adhesive to form a bond with the surface of another material upon brief contact under light pressure". The tack depends on a number of experimental parameters. We can control various experimental factors (contact force, dwell time, pretest speed) using probe tack tester. We are here concerned with pretest speed of experimental factors using SIS-based hotmelt PSA and water-borne acrylic PSA.

• International Journal of Highway Engineering
• /
• v.19 no.2
• /
• pp.25-34
• /
• 2017

PURPOSES: The purpose of this paper is to evaluate interface performance while using various tack coat materials for asphalt overlay. METHODS : The evaluation was conducted with tracking test, permeability, and interface bond strength. Tracking test was conducted using an image processing technique, to investigate the susceptibility of the tack coat materials. BBS and pull-off test were conducted to evaluate bond strength. The permeability test was conducted to evaluate the effect of tack coat materials. RESULTS : Results reveal that the trackless tack coat material demonstrates less tracking compared to other materials. Moreover, both BBS and pull-off tests can effectively evaluate the bond strength at the interface. RSC-4 was measured less bond strength. Moreover, tack coat prevents water penetration through the surface and aids the extension of the surface life of asphalt pavement. CONCLUSIONS : Trackless tack coat demonstrated a high and consistent bond strength performance. The tack coat types demonstrate marginally different performance as function of curing times. Field applicability was tested based on visual observation. Therefore, these should be considered when trackless tack coat is slightly enhanced the pavement performance based on limited this study results. Finally, it is necessary to allow reasonable time for the tack coat to completely cure.

• Resources Recycling
• /
• v.10 no.1
• /
• pp.32-41
• /
• 2001

Bond shear strengths of recycled asphalt concrete were evaluated under different tack coat applications. Regardless of the new and old mixtures, the bond shear strengths at $30^{\circ}C$ were increased by 10-20% than those at 1$0^{\circ}C$. The bond shear strengths of recycled asphalt concrete without tack coat showed very low ones. These are the main reasons for the frequent longitudinal interface crack in the field. The effect of tack coat curing time on bond shear strengths was inferior to the tack coat construction temperature.

• Journal of Adhesion and Interface
• /
• v.14 no.3
• /
• pp.117-120
• /
• 2013

The prepreg material is a sheet of the reinforcement pre-impregnated with a resin. In this study, two types of prepreg were prepared with a general phenolic resin and the polyvinyl butyral (PVB) modified phenolic resin, respectively, with resin content of 40 wt%. After resin impregnation, the prepregs were heat treated in an oven to make them the B-stage. Surface morphology of the prepreg was observed by using a scanning electron microscope (SEM). Tack property of the prepreg is one of the major properties that govern the ability of prepreg to be laid up. In this study, the tack of prepreg was measured under various test parameters by a probe tact test. Test parameters were contact time, contact force and debonding rate. Most of the tack properties of the prepreg increased with the test parameters. Then tack properties exhibited a linear behavior with test parameters before a saturation point. Also, the tack of prepreg was investigated in relation with the fibrillation phenomena involved in the prepreg surface with the debonding rate.

• Journal of Adhesion and Interface
• /
• v.14 no.4
• /
• pp.167-174
• /
• 2013

In this study, Ultraviolet (UV) curable urethane acrylates for ink binder was prepared by reaction of IPDI, polyether polyol and HEA. The UV curing behavior of compositions with HEA/PETA ratio on UV irradiation time was investigated by FT-IR spectrophotometer, probe tack tester and Photo-DSC. Conversion % and gel content were increased with increasing UV irradiation time, but probe tack was decreased. Storage modulus, tensile strength and decomposition temperature were increased as PETA content increased. In case of HEA/PETA ratio was 30/70, adhesion property of UV-cured composition on PMMA sheet was excellent.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.41 no.6
• /
• pp.737-744
• /
• 2021

Spray paving minimizes material lost during the construction or repair of a road surface, and it can be done in conjunction with tack coating. This approach involves applying the asphalt mixture at the same time as spraying the tack coat by attaching a spraying device to the asphalt paver. When applying an asphalt overlay to an aged concrete surface, it is important to ensure the adhesion performance between different material properties. Accordingly, there is a need for a tack coat that can be applied by spray paving and that exhibits good adhesive performance on different materials. In this study, bonding strength tests under various conditions were performed to evaluate the basic performance of a tack coat developed for use with a spray paver. The bonding performance of the tack coat was observed to be affected by curing conditions and material lost during construction. The test results also showed that the tensile and shear bonding strengths of the developed tack coat were 1.21 and 1.99 times higher than those of a conventional one, respectively. As a result, the developed tack coat is considered suitable for application to spray paving.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.10
• /
• pp.1521-1527
• /
• 2010

Since inkjet printing is being employed in production lines of electronics and display industries, the tack time for inspection of jetting failure has become very important because the throughput of the inkjet printing system can be extended to the maximum limit by adopting a shorter jetting inspection time. The most popular method for inspecting jetting failure involves the use of a linear stage, a high magnification lens, and a charge coupled devicecamera. However, this conventional approach requires approximately 60 s to complete the jetting inspection and might not be suitable for a high-speed reciprocating jetting inspection in endurance tests due to the unwanted mechanical vibration. In this study, a novel concept of an inkjet monitoring module is introduced, which has an overall inspection time of 18 s. For the shorter tack time of jetting inspection, the parameters affecting the tack time are discussed in this paper.