• The Journal of Advanced Prosthodontics
• /
• 제13권6호
• /
• pp.385-395
• /
• 2021

PURPOSE. To characterize the microstructure of three yttria partially stabilized zirconia ceramics and to compare their hardness, indentation fracture resistance (IFR), biaxial flexural strength (BFS), and fatigue flexural strength. MATERIALS AND METHODS. Disc-shaped specimens were obtained from 3Y-TZP (Vita YZ HT), 4Y-PSZ (Vita YZ ST) and 5Y-PSZ (Vita YZ XT), following the ISO 6872/2015 guidelines for BFS testing (final dimensions of 12 mm in diameter, 0.7 and 1.2 ± 0.1 mm in thicknesses). Energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD) and scanning electron microscopy (SEM) analyses were performed, and mechanical properties were assessed by Vickers hardness, IFR, quasi-static BFS and fatigue tests. RESULTS. All ceramics showed similar chemical compositions, but mainly differed in the amount of yttria, which was higher as the amount of cubic phase in the diffractogram (5Y-PSZ > 4Y-PSZ > 3Y-TZP). The 4Y- and 5Y-PSZ specimens showed surface defects under SEM, while 3Y-TZP exhibited greater grain uniformity on the surface. 5Y-PSZ and 3Y-TZP presented the highest hardness values, while 3Y-TZP was higher than 4Y- and 5Y-PSZ with regard to the IFR. The 5Y-PSZ specimen (0.7 and 1.2 mm) showed the worst mechanical performance (fatigue BFS and cycles until failure), while 3Y-TZP and 4Y-PSZ presented statistically similar values, higher than 5Y-PSZ for both thicknesses (0.7 and 1.2 mm). Moreover, 3Y-TZP showed the highest (1.2 mm group) and the lowest (0.7 mm group) degradation percentage, and 5Y-PSZ had higher strength degradation than 4Y-PSZ group. CONCLUSION. Despite the microstructural differences, 4Y-PSZ and 3Y-TZP had similar fatigue behavior regardless of thickness. 5Y-PSZ had the lowest mechanical performance.

• 디지털산업정보학회논문지
• /
• 제12권3호
• /
• pp.25-31
• /
• 2016

Mechanical properties of Y2O3-containing tetragonal ZrO2 polycrystals(Y-TZP) were investigated. Several additives were used to modify the hardness and fracture toughness of Y-TZP. The effects of these individual additives were discussed and their interactions were also analysed. Each additive, such as CoO, Fe2O3, MnO2 was found to deteriorate the mechanical properties of Y-TZP when it was used singly. But the fracture toughness of Y-TZP was significantly improved when these additives and Al2O3 were added in combination at a certain ratio. The addition of CoO, Fe2O3 and MnO2 into Y-TZP resulted in the more complex behavior of fracture toughness and hardness. The specimen with 1.5 wt%-Fe2O3, 3.0 wt% -Al2O3 and 1.5 wt%-CoO showed the monoclinic to tetragonal phase ratio of 18% and the highest toughness of $10.8MPa{\cdot}m1/2$ with Vickers hardness of 1201 kgf/mm2. However, the toughness decreased as the ratio increased and macrocracks developed beyond the ratio of 25%. Sample No. 16 is improved high Physical and Mechanical Properties.

• 한국세라믹학회지
• /
• 제31권7호
• /
• pp.703-714
• /
• 1994

Sintering and microstructure of Ce-TZP/Al2O3 composite with $\alpha$-Al2O3 matrix containing dispersed 5~50 vol% ZrO2 were discussed. Sintered density was increased with elevating forming pressure in range of 6~300 MPa and about >99.2% of theoretical density was obtained at 1$600^{\circ}C$ for 2h in case of 300 MPa of 6~300 MPa uniaxially cold-pressed compacts containing 20 vol% ZrO2. All kinds of different batch composition exhibited nearly the same shrinkage behaviour with end-point shrinkage between 20 and 24%, and had the maximum shrinkage rate (0.41~0.54%/min) around 140$0^{\circ}C$. Grain growth was occurred faster in $\alpha$-Al2O3 than in {{{{ gamma }}-Al2O3 starting matrix during sintering at 1$600^{\circ}C$. Bimodal pore size distribution of interaglomerate pores with size of 0.03~0.2 ${\mu}{\textrm}{m}$ and of interaglomerate pores with size of around 60 ${\mu}{\textrm}{m}$ was obtained in Ce-TZP/$\alpha$-Al2O3 composite sintered at 130$0^{\circ}C$. But unimodal pore size distribution with around 0.1 ${\mu}{\textrm}{m}$ was observed in Ce-TZP/{{{{ gamma }}-Al2O3 composite sintered at the same temperature. Microcracks were occurred due to the tlongrightarrowm transformation of ZrO2 on cooling process.

• The Korean Journal of Ceramics
• /
• 제5권4호
• /
• pp.371-374
• /
• 1999

Y2O3 and Nb2O5 co-doped tetragonal zirconia polycrystals((Y, Nb)-TZP) containing 10 to 30 vol% $Al_2O_3$ were prepared and hydrothermal stability of the composites was evaluated after aging for 5 h at the temperature range of $150^{\circ}C$ $250^{\circ}C$ under 4 MPa $H_2O$ vapor pressure in an autoclave. The (Y, Nb)-TZP/Al2O3 composites showed excellent phase stability under the hydrothermal conditions, as compared with the 3Y-TZP/$Al_2O_3$ composites, due to the combined effects of the Y-Nb ordering in the $t-ZrO_2$ lattice, the reduction of oxygen vacancy concentration, and the $Al_2O_3$ addition. The strength and fracture toughness of the (Y, Nb)-TZP/$Al_2O_3$ composite, containing 20 vol% of 2.8 $Al_2O_3$ particles, were 700 MPa and 8.1 MP.$am^{1/2}$, respectively.

• 한국세라믹학회지
• /
• 제47권5호
• /
• pp.439-444
• /
• 2010

The usual ceramic process of mixing and milling in state of oxide of $ZrO_2$ and $CeO_2$ was adopted in wet process to manufacture Ce-TZP in this study. The maximum dispersion point of every slurry manufactured with mixture of $ZrO_2$ and $CeO_2$ was neat at pH10. The stable slurry in average particle size of 90 nm can be manufactured when it is dispersed with use of ammonia water and polycarboxylic acid ammonium. The sintered Ce-TZP ceramics manufactured with addition of $CeO_2$ less than 10 mol% was progressed to the fracture of specimen due to the monoclinic phase existence more than 30% at the room temperature. More than 99% of tetragonal phase was created for the sintered body with addition of $CeO_2$ beyond 18 mol%, but the mechanical property degrade on the entire specimen was brought due to the $CeO_2$ existing above 3%. Consequently, the optimal Ce-TZP combined in oxide state was identified in 16 mol% of $CeO_2$ contents.

• 한국세라믹학회지
• /
• 제29권4호
• /
• pp.265-272
• /
• 1992

Role of CaO in the sintering of 12Ce-TZP ceramics was studied. The addition of small amounts of CaO increase the densification rate of 12Ce-TZP by altering lattice defect structure and the diffusion coefficient of the rate controlling species, namely cerium and zirconium cations. CaO also inhibits grain growth during sintering and allows the sintering process to proceed to theoretical density by maintaining a high diffusion flux of vacancies from the pores to the grain boundaries. The inhibition of grain growth is accomplished by the segregation of solute at the grain boundaries, causing a decrease in the grain boundary mobility. The segregation of calcium was revealed by AES study.

• 대한치과의사협회지
• /
• 제49권5호
• /
• pp.260-264
• /
• 2011

Zirconia ($ZrO_2$) is a crystalline dioxide of zirconium. Dental zirconia blocks for CAD/CAM are usually fabricated with powders of tetragonal zirconia polycrystals (TZP) stabilized with 3mol% yttria. Because of its mechanical properties similar to those of metals and color similar to tooth, it is evaluated to attain the two purposes at a time, strength and aesthetic in prosthetic dentistry. The ability of transformation of Y-TZP from tetragonal to monoclinic helps to prevent crack propagation and contributes the increase of strength and fracture toughness. Two different types of blocks, soft and hard, are used to prepare the zirconia frameworks. The fuzzy-sintered block is difficult in machining, so pre-sintered soft 3Y-TZP block is usually used to mill by computer aided machining.

• 한국세라믹학회지
• /
• 제29권5호
• /
• pp.341-346
• /
• 1992

The effects of CaO addition on the low temperature degradation behavior of 2.5Y-TZP ceramics were investigated. Y2O3-CaO-ZrO2 ceramics were prepared from the commercial Y-TZP powder added within 1 mol% of CaO. Fully tetragonal phase could be obtained at each composition under sintering condition of 1500$^{\circ}C$ for 1 hour. As the amount of CaO increased, grain size was decreased. From the result of heat treatment at 200$^{\circ}C$, volume fraction of monoclinic phase formed on the surface of each specimen was decreased with higher CaO amount. Stability of tetragonal ZrO2 phase for low temperature heat treatment was increased by CaO addition without the degradation of mechanical properties.

• 소성∙가공
• /
• 제16권5호통권95호
• /
• pp.348-353
• /
• 2007

The propagation of a macro-scale crack and the accompanying transformation zone around it was visualized in an Y-TZP ceramic using a mechano-luminescence (ML) technique. The technique allows realistic fractures that take place catastrophically in actual applications to be realistically stimulated. Unlike conventional quasi-static R-curves, the ML technique on a relatively fast time frame permitted a so-called quasi-dynamic R-curve in the crack speed range from 50 to 140 m/sec. to be measured. Effective toughening then commenced and the applied stress intensity factor increased to 27 $MPa{\sqrt{m}}$. The transformation zone height obtained from the ML observations was in good agreement with that predicted by the Marshall model, and coincided with previously observed results for quasi-static conditions by Raman spectorscopy and x-ray analysis.

• 한국세라믹학회지
• /
• 제52권1호
• /
• pp.56-60
• /
• 2015

Discontinuous, polycrystalline $Al_2O_3$-dispersed TZP fibers were prepared by the centrifugal spinning of a colloidal $ZrO_2$ sol containing Y and Al nitrates and poly(vinyl alcohol). Factors affecting the rheological properties of the sols, such as sol concentrations, aging, and the amounts and types of additives, were investigated by measuring the shear viscosities. The flow characteristics of the sols were studied in relation to the spinnability by measuring the viscosity with respect to the shear rate. The spinnability was obtained through the addition of a polymer which increases the viscosity to a range of optimum viscosity values for spinning. Aging the sols containing the additives did not noticeably change the sol viscosities at room temperature up to 30 days. The flow behavior of the spinnable sols progressively changed from nearly Newtonian to pseudoplastic with an increase in the sol concentration.