• Elastomers and Composites
• /
• v.50 no.1
• /
• pp.18-23
• /
• 2015

Vinyl acetate (VA) contents of poly(ethylene-co-vinyl acetate) (EVA) analyzed by infrared spectroscopy (IR), nuclear magnetic spectroscopy (NMR), and thermogravimetric analysis (TGA) were compared. Four grade EVAs supplied by Aldrich Co. and four grade EVAs manufactured by DuPont Co. were used. For IR analysis, VA contents were determined using calibration curve (absorbance ratio of $1739cm^{-1}/2922cm^{-1}$ or $609cm^{-1}/1464cm^{-1}$) of reference EVAs. Correlation coefficients of the calibration curves were not sufficiently high ($r^2{\leq}0.96$). For NMR analysis, VA contents were determined using peaks of $CH_3$, $CH_2$, and CH. VA contents determined by NMR analysis were less than those marked by suppliers more than 10%. For TGA, VA contents were determined using weight loss through deacetylation. VA contents determined by TGA were slightly different with those marked by suppliers. Difference in the VA contents determined by different analytical methods was discussed, and difference in the analytical results according to the EVA suppliers was also examined.

• Elastomers and Composites
• /
• v.48 no.2
• /
• pp.161-166
• /
• 2013

Thermal degradation behavior of chlorine cure-site ACM and carboxylic cure-site ACM rubbers was studied by non-isothermal TGA thermal analysis. Carboxylic cure-site ACM rubber exhibited comparatively more thermally stable than chlorine cure-site ACM, showing higher peak temperature, at which maximum reaction rate occurred. Activation energies from Kissinger method were calculated as 118.6 kJ/mol for the chlorine cure-site ACM and 105.5 kJ/mol for the carboxylic cure-site ACM, showing similar values from Flynn-Wall-Ozawa analysis over the conversion range of 0.1~0.2. From the analysis of the reaction order change, both samples seemed thermally decomposed through the multiple reaction mechanism as is the common rubber materials.

• Fire Science and Engineering
• /
• v.33 no.1
• /
• pp.1-6
• /
• 2019

The activation energy of CPVC (Chlorinated Poly Vinyl Chloride) used for non-metallic synthetic resin piping in fire-fighting was measured by thermogravimetric analysis (TGA). The activation energy was determined using by TGA kinetic methods, such as Kissinger and Flynn-Wall-Ozawa method. The calculated activation energy was 128.07 kJ/mol (Kissinger method) and 145.60 kJ/mol (Flynn-Wall-Ozawa method). The difference in activation energies calculated by the Kissinger method and Flynn-Wall-Ozawa method was not considered to be significant considering that the different analysis methods. The combustion characteristics will be tested in a future study through an evaluation of thermal deterioration using an accelerated deterioration and air oven aging test and the lifetime of CPVC will be predicted.

• Journal of the Korean Magnetic Resonance Society
• /
• v.6 no.1
• /
• pp.45-53
• /
• 2002

Objectives: This study investigated alterations in regional cerebral blood flow (rCBF) in patients with transient global amnesia (TGA) using statistical parametric mapping 99 (SPM99). Methods: Noninvasive rCBF measurements using 99mTc-ethyl cysteinate dimer (ECD) SPECT were performed on 8 patients with TGA who have ongoing symptoms and 17 age matched controls. The relative rCBF maps in patients with TGA and controls were compared. Results: In patients with TGA, significant decreased rCBF was found along the L superior temporal extending to L parietal region of the brain and L thalamus. There were areas of increased rCBF in the R temporal, R frontal region and R thalamus. Conclusion: We could demonstrate decreased perfusion in left cerebral hemisphere and increased perfusion in right cerebral hemisphere in patients with TGA using SPM99. The imbalanced change of rCBF between bilateral cerebral hemisphere in patients with TGA might suggest that imbalanced neuronal activity between the bilateral hemispheres may have strong relationship to the pathogenesis of the TGA. For quantitative SPECT analysis in TGA patients, we recommend SPM99 rather than the ROI method because of its definitive advantages.

• Elastomers and Composites
• /
• v.44 no.3
• /
• pp.269-273
• /
• 2009

A study on the life-time expectation of a CR-modified NR rubber composite through the change of thermal degradation characteristics was performed using both isothermal thermogravimetric analysis (TGA) and thermomechanical analysis (TMA). Master curves at reference temperature of $90^{\circ}C$ could be obtained with shift factor $a_T$, which was determined empirically using Time-Temperature Superposition Principle (TTSP). Activation energies could be calculated from the slope of Arrhenius plot of shift factor and showed similar values of $E_{a,TGA}$= 41.2 and $E_{a,TMA}$= 54.5 kJ/mol, respectively. It was considered from the results that chemical degradation resulting weight loss of the sample might be closely related to a physical degradation such as the dimensional change of the sample.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2018.11a
• /
• pp.169-170
• /
• 2018

In this study, TGA analysis of hardened cement paste with fire damage was performed. The mass reduction rate of 600 ℃ specimens was about 22 ~ 25%, and the sample of 800 ℃ showed the mass loss rate of 9 ~ 13%. As the target temperature and hold time increased, the mass reduction rate decreased. As the depth increased, the mass reduction rate decreased.

• Polymer Science and Technology
• /
• v.4 no.5
• /
• pp.387-397
• /
• 1993

• Elastomers and Composites
• /
• v.56 no.1
• /
• pp.1-5
• /
• 2021

Tire and road wear particles (TRWPs) were collected from road dust and thermogravimetric analysis (TGA) was performed to measure the content of tire wear particles (TWPs) in the TRWPs. The TGA thermograms of TRWPs showed two weight loss steps associated with polymer decomposition including weight loss after 480℃ which may be due to road wear particles. Different samples gave different TGA thermograms because the types and contents of the road wear particles attached to the TWPs should be different from each other, and each TWP might have different composition. The TGA results of the model asphalt pavement wear particles, with (volatile organics + polymers + carbon black) : ash = 33.5 : 66.5, was applied to the TRWP results, and the TWP contents of TRWPs were found to be 50-65%. The zinc oxide content in the rubber compound was negligible.

• Journal of the Korean Chemical Society
• /
• v.40 no.6
• /
• pp.385-393
• /
• 1996

The interaction between poly(HEMA) which is material of contact lens containing about 45% water and amino acids (alanine, arginine, methionine, proline, glycine, serine, lysine) have been studied by using the thermal analysis methods through DSC and TGA. The experimental results of DSC and TGA were shown that lysine, arginine and alanine have the most stable interaction between poly(HEMA) and amino acids.

• Elastomers and Composites
• /
• v.48 no.4
• /
• pp.276-281
• /
• 2013

Polyester type polyurethane foam modified with acrylic polyol was prepared by quasi prepolymer method. Thermal and dynamic mechanical properties of polyurethane foam were analysed by thermal gravimetric analysis(TGA) and dynamic mechanical analysis(DMA). Also, glass transition temperature was measured by differential scanning calorimeter(DSC). As acrylic polyol contents were increased, thermal stability measured by TGA was slightly decreased. Storage modulus was increased and tan delta was decreased with increasing of acrylic polyol contents.