• Journal of the Semiconductor & Display Technology
• /
• v.18 no.1
• /
• pp.10-14
• /
• 2019

In this study, we synthesized two $Y_3Al_5O_{12}:Ce^{3+}$ phosphors ($7{\mu}m$-sized and $2{\mu}m$-sized YAG) with different sizes by controlling particles sizes of starting materials of the phosphors for white LED. In the smaller one ($2{\mu}m$-sized YAG), its photoluminescence intensity in the reflective mode was 63 % that of the bigger one ($7{\mu}m$-sized YAG); the quantum efficiencies were 93 % and 70 % for the smaller and the bigger ones. Two kinds of white LED packages with the same color coordinates were fabricated with a blue package (chip size $53{\times}30$) and two phosphors. The luminous flux of the white LED package with the smaller YAG phosphor was 92 % of that with the bigger one, indicating that the quantum efficiency of phosphor dispersed inside LED package was higher than that of the pure powder. It was consistently confirmed by the optical simulation (LightTools 6.3). It is notable according to the optical simulation that the white LED with the smaller phosphor showed 24 % higher luminous efficiency. If the smaller one had the same quantum efficiency as the bigger one (~93 %). Therefore, it can be suggested that the higher luminous efficiency of white LED can be possible by reducing the particle size of the phosphor along with maintaining its similar quantum efficiency.

• Journal of Sensor Science and Technology
• /
• v.31 no.6
• /
• pp.455-460
• /
• 2022

Brush-like ZnO hierarchical nanostructures decorated with MgxZn1-xO (x = 0.1, 0.2, 0.3, 0.4, and 0.5) were fabricated and examined for application to a gas sensor. They were synthesized using vapor phase growth (VPG) on indium tin oxide (ITO) substrates. To generate electronic accumulation at ZnO surface, MgZnO nanoparticles were prepared by sol-gel method, and the ratio of Mg and Zn was adjusted to optimize the device for NO₂ gas detection. As the electrons in the accumulation layer generated by the heterojunction reacted faster and more frequently with the gas, the sensitivity and speed improved. When tested as sensing materials for gas sensors at 100 ppm NO₂ at 300℃, these MgZnO decorated ZnO nanostructures exhibited an improvement from 165 to 514 times compared to pristine ZnO. The response and recovery time of the MgZnO decorated ZnO samples were shorter than those of the pristine ZnO. Various analyzing techniques, including field-emission scanning electron microscopy (FESEM), energy-dispersive X-ray spectroscopy (EDS), and X-ray powder diffraction (XRD) were employed to confirm the growth morphology, atomic composition, and crystalline information of the samples, respectively.

• The Journal of the Convergence on Culture Technology
• /
• v.9 no.3
• /
• pp.593-599
• /
• 2023

Nickel oxide (NiO) nanoparticles were successfully synthesized by a simple liquid phase process for producing ceramics powder using a precursor impregnated with a nickel(II) nitrate hexahydrate aqueous solution in an industrial pulp. The microfibrile structure of the precursor impregnated with nickel nitrate hexahydrate aqueous solution was confirmed by scanning electron microscope (SEM), and the crystal structure and particle size of nickel oxide (NiO) particles produced as the heat treatment temperature of the precursor were analyzed by X-ray diffraction (XRD) and SEM. As a result, it was confirmed through XRD and SEM analysis that the temperature at which the organic material of the precursor is completely thermally decomposed was 495-500℃, and the size and crystallinity of the nickel oxide particles produced increased as the heat treatment temperature increased. The size of the nickel oxide particles obtained by heat treatment at 500-800℃ for 1 hour was 50-200 nm. It was confirmed by XRD and SEM analysis that a NiO crystal phase was formed at a heat treatment temperature of 380℃, only a single NiO phase existed until 800℃.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.5
• /
• pp.200-207
• /
• 2020

MoSi₂, (Mo_1/2W_1/2)Si₂, and WSi₂ powders were synthesized by self-propagating high-temperature synthesis (SHS) method. The synthesized powders were heat-treated at 500, 1,000, 1,200, 1,300, 1,400, 1,500 and 1,600℃ in ambient atmosphere. Oxidation of Mo-W silicide powder was found at low temperature of 500℃. XRD structure analysis and DTA/TG data showed that MoO₃ was formed with 500℃ heat treatment for 1 hour, and that it was α-cristobalite phase that was formed with 1200℃ heat treatment, not α-quartz phase which is commonly found and stable at room temperature. Existence of W accelerated decomposition at both low and high temperature. Fully sintered MoSi₂ and (Mo_1/2W_1/2)Si₂ specimen did not show decomposition or weight loss by oxidation, with 1 hour heat treatment at either low or high temperature. Notably, it was difficult to sinter WSi₂ because of oxidation reaction at low temperature.

• Journal of Korean Society of Environmental Engineers
• /
• v.33 no.3
• /
• pp.162-166
• /
• 2011

Phosphorous contaminated in the effluent from sewage treatment plants can cause the eutrophication in surface water bodies. In this study, a powder of titanium oxysulfate-sulfuric acid made of ion-exchange materials was immobilized in an alginate gel and this material was examined to evaluate its phosphorous removal efficiency. Equilibrium and kinetic studies were carried out to quantify the adsorption capacity and time dependent removal rate of phosphorous. Adsorption isotherms and kinetic parameters were obtained for the entrapped titanium beads with three different methods. Equilibrium data were analyzed using Langmuir adsorption isotherm model and found to be well fitted to the model. The maximum adsorption capacity for phosphorous by the titanium bead synthesized with the solution method was 92.26 mg/g. Kinetic data followed a pseudo-second-order kinetic model. Due to the low production cost and high adsorption capacity, the titanium bead synthesized by the solution method has a potential to be utilized for the cost-effective removal of phosphorous from wastewater.

• Journal of the Korean Electrochemical Society
• /
• v.17 no.2
• /
• pp.111-118
• /
• 2014

The electrochemical properties using the cells assembled with the synthesized $LiCoO_2$(LCO) were evaluated in this study. The LCO was synthesized from high-purity cobalt sulfate($CoSO_4$) which is recovered from the cathode scrap in the wastes lithium ion secondary battery(LIB). The leaching process for dissolving the metallic elements from the LCO scrap was controlled by the quantities of the sulfuric acid and hydrogen peroxide. The metal precipitation to remove the impurities was controlled by the pH value using the caustic soda. And also, D2EHPA and $CYANEX^{(R)}272$ were used in the solvent extraction process in order to remove the impurities again. The high-purity $CoSO_4$ solution was recovered by the processes mentioned above. We made the 6 wt.% $CoSO_4$ solution mixed with distilled water. And the 6 wt.% $CoSO_4$ solution was mixed with oxalic acid by the stirring method and dried in oven. $LiCoO_2$ as a cathode material for LIB was formed by the calcination after the drying and synthesis with the $Li_2CO_3$ powder. We assembled the cells using the $LiCoO_2$ powders and evaluated the electrochemical properties. And then, we confirmed possibility of the recyclability about the cathode materials for LIBs.

• Korean Chemical Engineering Research
• /
• v.53 no.5
• /
• pp.603-608
• /
• 2015

Alumina powder have been expanded its application in industry and required to control its morphology such as powder size and aspect ratio of single particle. It can be synthesized by molten - salt method which is possible to obtain various shapes of ceramic particles by controlling the growth direction because each crystal face has different growth rate. In this study, various combinations of salts such as NaCl, $Na_2SO_4$, $Na_3PO_4$ and their mixture were used for control the growth of plate like alumina particle from the initial stage of synthesis because salt having different ionic strength can control the growth direction of ceramic particle under its melting condition around $800{\sim}900^{\circ}C$, and growth behavior of plate-like alumina particle with different reaction conditions such as temperature and concentration on the crystal size and shape was studied.

• Journal of the Korean Chemical Society
• /
• v.39 no.8
• /
• pp.627-634
• /
• 1995

Layered double hydroxides ($Mg-Al-CO_3$ systems, LDH), which are hydrotalcite-like anionic clay minerals, having different $Mg^{2+}\;to\;Al^{3+}$ ratio were synthesized by coprecipitation method. The subsequent products were characterized by the following methods; elemental analysis, X-ray powder diffraction, thermal analysis (DSC and TGA), FT-IR and $^{27}$Al-MAS NMR. X-ray powder patterns showed that the products formed were layered structure materials. Two heat absorption peaks were observed around 20 ∼280$^{\circ}C$ (surface water and interlayer water) and 280∼500$^{\circ}C$ (water from lattice hydroxide and carbon dioxide from interlayer carbonate) in DSC diagrams, and they were quantitatively analyzed by TGA diagrams (in case LDH4 16.2% and 28.6% respectively). FT-IR spectra indicate that the interlayer carbonate ions occupied symmetrical sites between two adjacent layers in a parallel direction. $^{27}$Al-MAS NMR spectra show only single resonance (8.6 ppm) of the octahedrally coordinated aluminum similar magnesium. When LDH4 was calcined at 560$^{\circ}C$ for 3 hours in air, its layered structure was destroyed giving a mixed metal oxide. However it readily became rehydrated in aqueous chromate solution to its original structure.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.3
• /
• pp.122-129
• /
• 2017

For the production of a high-density ITO target, $In_2O_3$ powders with a small particle size and low agglomeration should be synthesized. The purpose of this study is to control the size and shape of the Indium hydroxide precursor which affects the properties of the $In_2O_3$ powder. As a starting raw material, Indium metal was dissolved in a Nitric acid ($HNO_3$) solution. The effect of concentration, pH, and temperature on the properties of Indium hydroxide was investigated using ammonium hydroxide as a precipitant. Crystallite size of each sample was analyzed by X-ray diffraction and the shape and the size of the powder was analyzed by transmission electron microscopy. As a result, the particle size of Indium hydroxide was increased with increase in the concentration of $In(NO_3)_3$ and the particle size and shape of the Indium hydroxide remained unchanged with increase in the pH of the solution. The particle size increased with increase in the precipitation temperature during precipitation.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.16 no.5
• /
• pp.216-221
• /
• 2006

An investigation of the influence of $WO_3$ and $V_2O_5$ catalysts on the microstructure, phase formation and selective catalytic reduction (SCR) efficiency of the synthesized SCR powders has been carried out. A commercial anatase-$TiO_2$ was used as the catalysts support. For $WO_3(10wt%)/TiO_2$, the W loading to the $TiO_2$ support led to the lower in anatase to rutile transition temperature from $1200^{\circ}C$ of $TiO_2$ support to ${\sim}900^{\circ}C$. The transition temperature was also lowered to below $650^{\circ}C$ in the $V_2O_5$(5 and 10 wt%) added composition. The $WO_3(10wt%)/TiO_2$ SCR powder obtained at $450^{\circ}C$ showed near 100% of $NO_x$ conversion efficiency at $350{\sim}400^{\circ}C$ and for the powder prepared at $650^{\circ}C$ the same efficiency was achieved in wider temperature range $300{\sim}400^{\circ}C$. The highest $NO_x$ conversion efficiency of 100% was obtained in the $V_2O_5(5wt%)/TiO_2$ SCR composition calcined at $650^{\circ}C$ in the relatively wider temperature range $250{\sim}350^{\circ}C$, while the catalytic efficiency considerably decreased for the $V_2O_5(10wt%)/TiO_2$. The lowered conversion efficiency of $NO_x$ observed in the $V_2O_5(10wt%)/TiO_2$ composition calcined at $650^{\circ}C$ was considered to be correlated with the lowered surface area resulting from the increased crystallite growth by highly reactive vanadium loading.