• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2009.11a
• /
• pp.43-46
• /
• 2009

The purpose of this study is to enhance durability of concrete structures that uses this surface protecting material by carrying out the performance test of the surface protecting material of concrete, and as s result, we reached out the conclusion as follow. 1. As a result of the test measuring the stability and adhesive power of conductive film against ultraviolet, freezing & thawing, and damage from seawater that deteriorate the surface protecting material, it was turned out to meet the performance criteria specifying in the KS standard enough to gain a good evaluation to use as a surface protecting material. 2. As a result of the test identifying the neutralization-furtherance, it was assessed to be capable of protecting effectively concrete structures from carbonic acid gas by a very low depth of 0.1mm of neutralization. 3. As a result of the test identifying Penetrated Resistance Properties of chloride ion, as it was turned out to have a very low value of 819 Coulombs, it was assessed that even in the environment where the corrosion by chloride such sea environment is very affective, the film can effectively protect the concrete structure. 4. As a result of the test identifying freezing & thawing, as there was no change in reduction of mass after 400 cycle, it was assessed that the film has a good resistance against freezing & thawing. According to the results of study above, it is expected that this technology can extend its durability of concrete structure and be widely used for concrete structure through means (methods) to prevent the neutralization and damage from seawater as original purposes of the surface protecting material.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.5
• /
• pp.1-8
• /
• 2014

Structures requiring chemical resistance are usually coated with surface protecting agents, but the cost for maintenance and re-construction is incurred due to the low durability. Therefore, in this study, sulfur was polymerized and the performance was examined so that it could be used as the concrete surface protecting agents for structures requiring chemical resistance. The evaluation results indicated that for the spray of the sulfur polymer surface coating agents, the application of the gravity type was appropriate; and for the number of coating times, about 3 cycle spray gave the best results. For the surface condition of the concrete to be coated with the surface protecting agents, outstanding quality was obtained above room temperature ($20{\sim}30^{\circ}C$), and the bond strength increased as the temperature increased. The evaluation results of the strength characteristics depending on the filler content of the surface protecting agents indicated that about 20~40% filler mixing contributed to the strength improvement as it reduced the shrinkage of the sulfur polymer. Also, the mixing of silica showed larger increase in the bond strength than the mixing of fly ash, and the most outstanding bond strength characteristics could be obtained by the mixing of both silica and fly ash. In the case of the chemical resistance, the strength reduction was minimized and outstanding chemical resistance was obtained when the fly ash and silica were substituted by 20%, respectively. The performance evaluation of the chloride ion penetration indicated that for the specimens coated with the sulfur polymer surface protecting agents, the chloride ion penetration resistance increased by 29~48% compared to the specimen without the coating of the surface protecting agent. The examination of the coating condition of the surface protecting agents, compressive strength, bond strength, chemical resistance, and salt damage resistance indicated that in the range of this study, the optimal level was when the silica and fly ash were substituted by 20%, respectively, as the filler for the sulfur polymer.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2009.11a
• /
• pp.117-120
• /
• 2009

It has been gradually increased with the use of resin based membrane forming agent for curing method, which plays a role in protecting moisture evaporation by forming resin membrane at the surface of concrete. In this paper, tests were carried out to examine moisture retention capability of cement mortar applying membrane forming agent. Dosages and types of the membrane forming agent were varied. It is found that sheet curing sealed with the surface of concrete closely has favorable moisture retention capability. However, the application of membrane forming curing method had superiority in moisture retention capability at early stage but at later age, its capability is deteriorated. Hence, further study regarding altering application method was necessary to secure enhanced moisture retention capability.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.176-179
• /
• 2004

The latest concrete structure has showed that the deterioration of durability has been increased by the damage from salt, carbonization, freezing & thawing and the others. Therefore, the measures for the concrete which has deteriorated durability have been taken. Among them, it has been often used that surface treatment which cuts off the deterioration factors of durability by protecting the surface of concrete. This study was evaluated the surface improving agent for permeability, watertightness, air-permeability, chemical resistance and elution resistance.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.6
• /
• pp.29-36
• /
• 2015

In this study, to examine the use of sulfur polymer as a coating agent for concrete, durability and hazard evaluations were performed. The result of the evaluation indicated that the chemical resistance of the coating agent for concrete was outstanding against acidic, base, and alkaline solutions. The evaluation of the bond strength after an accelerated weathering test depending on the mixing condition indicated that the most outstanding strength characteristic was obtained when silica powder and fly ash were mixed at the same time. The bond strength exceeded 1 MPa in every mixing condition even after the repeated hot and cold treatment of the coating agent specimen for concrete, and the SFS mix proportion showed the highest bond strength. The examination of the accelerated carbonation and chloride ion penetration resistance of the concrete coated with the coating agent indicated that the specimen coated with the coating agent using silica powder as a filler showed the most outstanding durability. When a fish toxicity test was performed to examine the hazard of the use of the functional polymer as a coating agent for concrete, the functional polymer was found to have no effect on the organisms. When the chemical resistance, freezing and thawing resistance, carbonation, and chloride ion penetration resistance of the coating agent were considered, substituting silica powder and fly ash as the fillers of the functional polymer by 20%, respectively, was the optimal level in the range of this study.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.563-566
• /
• 2005

Concrete structures have been damaged by salt, carbonization, freezing and thawing and the others. Therefore, it is needed to protect durability and performance according to the appropriate materials and methods in the concrete structures. In general, several types of polymer and silicate are used as protecting deterioration agents of concrete structures, but these agents have many problems because of low durability and properties. In this study, It developed the deterioration restraining agent using polycondensed silicate and monomer that can block a deterioration cause such as $CO_2$ gas, salt and water from the outside and enhance waterproofing ability by reinforcing the concrete surface when applying it to concrete structures. Also, it developed the systems for improving concrete performance using a deterioration restraining agent.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.321-324
• /
• 2006

The latest concrete has showed that the deterioration of durability has been increased by the damage from salt, carbonation, freezing & thawing and the others. Therefore, it is needed to protect durability and performance according to the appropriate materials and methods in the concrete structures. In general, several types of polymer and silicate are used as protecting deterioration agents of concrete structures, but these agents have many problems because of low durability and properties. In this study, It developed the deterioration restraining agent using polycondensed silicate and monomer that can block a deterioration cause such as CO2 gas, salt and water from the outside and enhance waterproofing ability by reinforcing the concrete surface when applying it to concrete structures. Also, it evaluated improving concrete performance using a deterioration restraining agent.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.9 no.4
• /
• pp.177-186
• /
• 2005

The latest concrete structure has showed that the deterioration of durability has been increased by the damage from salt, carbonization, freezing & thawing and the others. Therefore, the measures for the concrete which has deteriorated durability have been taken. Among them, it has been often used that surface treatment which cuts off the deterioration factors of durability by protecting the surface of concrete. However, troubles such as fracture and rupture in the repair layer have been reported as time goes by due to the difference between the organic repair material like epoxy and concrete properties. Researchers have been developing the repair material which can cut off the deterioration factors of durability such as $CO_2$ gas, chloride ion and water by making the formation of concrete elaborate through the reaction with calcium ion when the surface improving agent is coated on the concrete. The main ingredient of that is inorganic substance which is the same as the concrete property. This study was evaluated the surface improving agent for permeability, watertightness, air-permeability, chemical resistance and elution resistance. As a result, it has been reported that the surface improving agent improves watertightness and air-permeability by penetration more than 10mm within concrete. Therefore, it is concluded that the surface improving agent developed in this research prevents deterioration of concrete durability when it is coated on the concrete structure.

• Journal of the Korean Graphic Arts Communication Society
• /
• v.25 no.1
• /
• pp.43-52
• /
• 2007

Offset printing is one of the well known printing technique of lithographic process and consists of image area and 'non-image area on a flat image carrier. The surface tension of dampening water can be controlled by adding IPA after mixing of raw water and etching solution. The etching solution contains a surfactant for reducing surface energy, a clean agent for non-imaging area, wetting agent for protecting non-imaging area from oil components like ink and also an emulsifying agent for controlling emulsification. In this study, the present situation of dampening water maintenance has examined by collecting dampening water using at domestic companies. The pH related to dampening water, conductivity, contact angle, emulsification curve are measured to define the current situation of dampening water control of each companies and to analyze the relationship among measured properties. In the study most of companies among 16 printing companies tested controlling dampening water through pH value. However, the quality of printing has varied depending upon conductivity, contact angle, IPA content, and emulsification value. The control of dampening water should be carry at the state of the standard when adding proper ratio of etching solution. It would be more effective when pH or conductivity control carries out in parallel with controlling dampening water. Therefore the concept that pH5.5 is correct is based concept. Based on these initial tests it is defined that the standardization of dampening water control is required.

• Applied Chemistry for Engineering
• /
• v.23 no.3
• /
• pp.271-278
• /
• 2012

In this work, we have prepared the nanocomposite by the reaction of mica and zinc oxide, and investigated the application of nanocomposite to UV protecting creams. Mica treated with 3-aminopropyltrimethoxysilane (APTMS) reacted with 1,4-phenylenediisothiocyanate (PDC) to give -N=C=S functionalized surface, which was further reacted with zinc oxides coated with APTMS to give mica-zinc oxide nanocomposites. The composites were characterized by EA, EDS, TGA, SEM, zeta potential measurement, powder XRD, and DRS UV/Vis analyses. Finally, we measured transmittances of ultraviolet protection creams manufactured by using mica composite covered with zinc oxides in the range of 280~400 nm. The nanocomposites developed in this work might be applicable as inorganic hybrid materials for UV protecting creams.