• 한국분말재료학회지
• /
• 제10권5호
• /
• pp.325-332
• /
• 2003

The effect of extrusion temperature on the microstructure and mechanical properties was studied in gas atomized TEX>$Al_{81}Si_{19}$ alloy powders and their extruded bars using SEM, tensile testing and wear testing. The Si particle size of He-gas atomized powder was about 200-800 nm. Each microstructure of the extruded bars with extrusion temperature (400, 450 and 50$0^{\circ}C$) showed a homogeneous distribution of primary Si and eutectic Si particles embedded in the Al matrix and the particle size varied from 0.1 to 5.5 ${\mu}m$. With increasing extrusion temperature from 40$0^{\circ}C$ to 50$0^{\circ}C$, the ultimate tensile strength (UTS) decreased from 282 to 236 ㎫ at 300 K and the specific wear increased at all sliding speeds due to the coarse microstructure. The fracture behavior of failure in tension testing and wear testing was also studied. The UTS of extrudate at 40$0^{\circ}C$ higher than that of 50$0^{\circ}C$ because more fine Si particles in Al matrix of extrudate at 40$0^{\circ}C$ prevented crack to propagate.

• 한국자기학회지
• /
• 제24권2호
• /
• pp.51-55
• /
• 2014

$Fe_3O_4$ 나노입자는 hot-injection 제조법에 의해 제조되었으며 반응물질의 injection time에 변화를 주었다. 격자구조는 x-ray diffraction(XRD) 측정을 통해 Fd-3m 공간군을 갖는 cubic inverse spinel 구조로 분석되었으며, $Fe_3O_4$ 나노입자의 형상은 high-resolution transmission electron microscope(HR-TEM)으로 분석하였다. 반응물질을 각각 0.5분, 60분인 젝션시 각각 7.63 nm, 21.73 nm의 $Fe_3O_4$ 나노입자 사이즈를 얻을 수 있었다. $Fe_3O_4$ 나노입자의 자기적 특성은 다양한 온도에서 vibrating sample magnetometer(VSM)과 M$\ddot{o}$ssbauer spectroscopy로 측정하였으며, hyperthermia 측정을 통해 반응물질의 injection time이 60분일 때 50 kHz의 250 Oe에서 $Fe_3O_4$ 나노입자 파우더의 온도가 약 $120^{\circ}C$임을 관측할 수 있었다.

• 광물과 암석
• /
• 제36권3호
• /
• pp.213-220
• /
• 2023

본 연구에서는 고압 환경에서 합성된 결정 입자의 크기에 원시료(starting materials)의 상(phase)이 미치는 영향을 확인했다. 상이 다른 두 가지 원시료인 비정질 시료와 나노파우더 시료를 이용해 알루미늄이 부화된 고압의 환원환경에서 삼원계 시스템인 브리지마나이트-페리클레이스-칼슘 페라이트(calcium ferrite)상의 MgAl₂O₄을 합성했다. 시료는 40 GPa 2000 K의 압력온도 조건에서 20 시간 동안 가열하여 합성했다. 합성된 시료는 비정질 시료를 이용한 경우 입자 크기가 50-200 nm였으며, 나노파우더를 이용한 경우 ~500 nm로 나타났다. 이러한 차이는 1) 시료가 합성된 2000 K의 온도가 낮아 비정질 시료의 경우 결정 성장보다 결정핵 성장이 더 우세하게 나타났거나 2) 시료에 존재할 수 있는 산화 환원반응 상태의 차이로 생각된다. 추후 다원계 시스템에 대한 고압 실험을 수행할 때 비정질 시료보다 나노파우더를 원시료로 이용하는 것이 결정 성장에서 더 유리할 것으로 생각된다.

• 한국표면공학회지
• /
• 제48권2호
• /
• pp.50-55
• /
• 2015

$Al_2O_3$ thin films were deposited on the moth eye anti-reflective nanostructured polycarbonate films by atomic layer deposition (ALD) techniques. Without ALD-$Al_2O_3$ thin films, moth eye anti-reflective nanostructured films had a high optical transmittance of 95.47% at a wavelength of 550 nm and a very poor hardness of 0.1381 GPa. With increasing the thickness of $Al_2O_3$ thin films from 5 to 25 nm, the transmittance of moth eye anti-reflective nanostructured films was gradually decreased from 94.94 to 93.12%. On the other hand, the hardness of the films was greatly increased from 0.3498 to 0.7806 GPa with increasing the thickness of $Al_2O_3$ thin films. This result shows that ALD thin films can be applied to improve mechanical properties with an adequate optical transmittance of the conventional moth eye anti-reflection nanostructure films.

• 전자공학회논문지D
• /
• 제36D권5호
• /
• pp.29-35
• /
• 1999

Pt박막의 ICP 식각을 위한 Cl\sub 2 \/Ar 가스 플라즈마에 O\sub 2\ 가스를 첨가하여 Pt 식각 메카니즘을 XPS와 QMS로 조사하였다. 또한 single Langmuir probe를 사용하여 이온전류밀도를 Ar/Cl\sub 2 \/O\sub 2\ 가스 플라즈마에서 측정하였다. O\sub 2\가스 첨가비가 증가할수록 Cl과 Ar species가 급격하게 감소하고 이온전류밀도 역시 감소함을 QMS와 single Langmuir probe로 확인하였다. Pt 식각율의 감소는 O\sub 2\가스 첨가비가 증가할수록 반응성 species와 이온전류밀도의 감소에 기인함을 의미한다. 150 nm/min의 치대 식각율과 2.5의 산화막식각 선택비가 50 sccm의 Ar/Cl\sub 2 \/O\sub 2\ 가수 유량, 600 W의 RF 전력, 125 V의 dc 바이어스 전압 및 10mTorr의 반응로 압력에서 얻었다.

• 전기전자학회논문지
• /
• 제22권4호
• /
• pp.1230-1233
• /
• 2018

에어로졸 데포지션 (aerosol deposition)공정을 통해 $Al_2O_3$막을 4H-SiC 상에 50 nm 두께로 제조하였고, 후열처리 공정에 따른 전기적 특성을 분석하였다. 그 결과 $N_2$분위기 열처리 시 $Al_2O_3$와 SiC 계면의 고정전하량이 감소하였으나 산소공공 생성에 의한 누설전류의 증가를 확인하였다. 본 결과로부터 계면특성 향상과 누설전류의 감소를 위해서는 적절한 $N_2$와 $O_2$가스의 혼합이 중요함을 확인하였다.

• Journal of Magnetics
• /
• 제10권1호
• /
• pp.14-22
• /
• 2005

Precisely refined Mossbauer study and nano structure observation revealed that intergranular phase formed between a-Fe and Nd₂Fe₁₄B phase in NdFeNbB alloys plays a significant role on the magnetic properties. The intergranular interaction was characterized in term of Henkel Plot (δM plot), and hyperfine field, quardrupole splitting and isomer shift were refined to predict the presence and role of the intergranular phase. By the addition of Nb into Nd₈Fe₈₆B₆ composition, coercivity was found to increase by 25% due to the refinement of average grain size of both the soft and hard magnetic phases which was decreased from 50 nm of virgin Nd/sub 8/Fe/sub 86/B/sub 6/ to 25 nm in Nd₈Fe ₈₅Nb₁B₆ alloys. The role of Nb addition was confirmed to stabilize the Nd₂Fe₁₄B lattice preventing from thermal vibration of the corresponding sites substituted Fe by Nb atoms in all sites in the Nd₂Fe₁₄B lattice. The enhanced coercivity was originated from the exchange hardening of soft and amorphous phases surrounding the hard magnetic Nd₂Fe₁₄B crystal.

• 한국세라믹학회지
• /
• 제43권9호
• /
• pp.569-574
• /
• 2006

Transparent glass-ceramics containing fresnoite crystals have been prepared by controlled heat treatment in $K_2O-BaO-TiO_2-SiO_2$ and their nonlinear optical and luminescent properties were investigated using Maker fringe method and Spectrofluorometer. The second harmonic generation was observed in all samples and the values decreased with increasing $K_2O$ content. The luminescence of blue light at ${\sim}482nm$ could be observed and it was shown that the luminescent property was controlled by the $K_2O$ content.

• 한국전기전자재료학회논문지
• /
• 제32권4호
• /
• pp.341-348
• /
• 2019

This paper reports the microstructure and electrochemical properties of Si-Al-Fe ternary amorphous alloys prepared by rapid solidification as an anode for lithium secondary batteries. The microstructure was analyzed using XRD and HR-TEM with EDS mapping. In accordance with DSC analysis, annealing was performed to crystallize the active nano-Si in the amorphous alloy. Thus, nano-Si forms (~80 nm) embedded in the matrix alloy, such as $Fe_2Al_3Si_3$, $FeSi_2$, and $Fe_{0.42}Si_{2.67}$, were successfully synthesized. The electrode based on the Si-Al-Fe ternary alloy delivered an initial discharge capacity of approximately $700mAh^{g-1}$, and exhibited a high Coulombic efficiency of 99.0~99.6% from the $2^{nd}$ to $70^{th}$ cycles.

• Bulletin of the Korean Chemical Society
• /
• 제35권10호
• /
• pp.2935-2940
• /
• 2014

Monodispersed $Bi_2O_2CO_3$ nanoplates with an average width of 320 nm and thicknesses of 50-90 nm were successfully synthesized by a simple solvothermal method in a mixture solution of polyethylene glycol and $H_2O$. The obtained nanoplates were characterized by means of XRD, FT-IR, SEM and TEM. The effect of surfactant sodium dodecyl benzene sulfonate on the morphology of $Bi_2O_2CO_3$ product was investigated. Under simulated solar light irradiation, $Bi_2O_2CO_3$ nanoplates exhibited superior photocatalytic activities towards the degradation of RhB as well as high chemical stability upon cycling photocatalytic test. The nanoplates also showed promising photodegradation ability for eliminating refractory pollutant of phenol. The excellent photocatalytic performance of $Bi_2O_2CO_3$ nanoplates as compared with P25-$TiO_2$ endows them as promising high efficiency photocatalysts.