• Steel and Composite Structures
• /
• 제17권2호
• /
• pp.173-184
• /
• 2014

This study aimed to theoretical calculate the thermal residual stress in continuous SiC fiber reinforced titanium matrix composites. The analytical solution of residual stress field distribution was obtained by using coaxial cylinder model, and the numerical solution was obtained by using finite element model (FEM). Both of the above models were compared and the thermal residual stress was analyzed in the axial, hoop, radial direction. The results indicated that both the two models were feasible to theoretical calculate the thermal residual stress in continuous SiC fiber reinforced titanium matrix composites, because the deviations between the theoretical calculation results and the test results were less than 8%. In the titanium matrix composites, along with the increment of the SiC fiber volume fraction, the longitudinal property was improved, while the equivalent residual stress was not significantly changed, keeping the intensity around 600 MPa. There was a pronounced reduction of the radial residual stress in the titanium matrix composites when there was carbon coating on the surface of the SiC fiber, because carbon coating could effectively reduce the coefficient of thermal expansion mismatch between the fiber and the titanium matrix, meanwhile, the consumption of carbon coating could protect SiC fibers effectively, so as to ensure the high-performance of the composites. The support of design and optimization of composites was provided though theoretical calculation and analysis of residual stress.

• 한국안전학회지
• /
• 제27권6호
• /
• pp.99-108
• /
• 2012

Ultra High Performance Concrete(UHPC) has compressive strength higher than 180 MPa. The use of steel fibers in the dense UHPC matrix increases tensile strength, ductility and bond strength between UHPC and rebars. However, to apply the advance material behavior of UHPC to the design of a structure, we need design formulas. The crack formula is one of them. This paper investigated experimentally the bond behavior of a rebar and K-UHPC, the UHPC developed by Korea Institute of Construction Technology, and, modified CEB-FIP crack formula based on the test. In addition, this paper tested the crack behavior of K-UHPC reinforced with rebars to verify the modified crack formula. The result showed that the modified formula is reasonable to predict the width of cracks in the reinforced K-UHPC structures.

• Steel and Composite Structures
• /
• 제25권6호
• /
• pp.649-661
• /
• 2017

This paper is motivated by the lack of studies in the technical literature concerning to the influence of carbon nanotubes (CNTs) waviness and aspect ratio on the vibrational behavior of functionally graded nanocomposite annular sector plates resting on two-parameter elastic foundations. The carbon nanotube-reinforced (CNTR) plate has smooth variation of CNT fraction based on the power-law distribution in the thickness direction, and the material properties are also estimated by the extended rule of mixture. In this study, the classical theory concerning the mechanical efficiency of a matrix embedding finite length fibers has been modified by introducing the tube-to-tube random contact, which explicitly accounts for the progressive reduction of the tubes' effective aspect ratio as the filler content increases. Parametric studies are carried out to highlight the influence of CNTs volume fraction, waviness and aspect ratio, boundary conditions and elastic foundation on vibrational behavior of FG-CNT thick sectorial plates. The study is carried out based on three-dimensional theory of elasticity and in contrary to two-dimensional theories, such as classical, the first- and the higher-order shear deformation plate theories, this approach does not neglect transverse normal deformations. The annular sector plate is assumed to be simply supported in the radial edges while any arbitrary boundary conditions are applied to the other two circular edges including simply supported, clamped and free. For an overall comprehension on 3-D vibration of annular sector plates, some mode shape contour plots are reported in this research work.

• Structural Engineering and Mechanics
• /
• 제73권1호
• /
• pp.17-25
• /
• 2020

A finite element (FE) model for analyzing slender reinforced high-strength concrete (HSC) columns under biaxial eccentric loading is formulated in terms of the Euler-Bernoulli theory. The cross section of columns is divided into discrete concrete and reinforcing steel fibers so as to account for varied material properties over the section. The interaction between axial and bending fields is introduced in the FE formulation so as to take the large-displacement or P-delta effects into consideration. The proposed model aims to be simple, user-friendly, and capable of simulating the full-range inelastic behavior of reinforced HSC slender columns. The nonlinear model is calibrated against the experimental data for slender column specimens available in the technical literature. By using the proposed model, a numerical study is carried out on pin-ended slender HSC square columns under axial compression and biaxial bending, with investigation variables including the load eccentricity and eccentricity angle. The calibrated model is expected to provide a valuable tool for more efficiently designing HSC columns.

• Structural Engineering and Mechanics
• /
• 제74권3호
• /
• pp.435-443
• /
• 2020

The objective of this study was to determine the effective compressive strength of a column-slab connection with different compressive strengths between the column and slab concrete. A total of eight column specimens were fabricated, among which four specimens were restrained by slabs while the others did not have any slab, and the test results were compared with current design codes. According to ACI 318, the compressive strength of a column can be used as the effective compressive strength of the column-slab connection in design when the strength ratio of column concrete to slab concrete is less than 1.4. Even in this case, however, this study showed that the effective compressive strength decreased. The specimen with its slab-column connection zone reinforced by steel fibers showed an increased effective compressive strength compared to that of the specimen without the reinforcement, and the interior column specimens restrained with slabs reached the compressive strength of the column.

• Corrosion Science and Technology
• /
• 제18권3호
• /
• pp.92-101
• /
• 2019

This study investigates how rivet head height affects the corrosion performance of carbon fiber reinforced plastic (CFRP) to aluminum alloy self-piercing riveted joints. Specimens with two different head heights were prepared. A rivet head protruding out of the top CFRP laminate forms the proud head height while a rivet head penetrating into the top CFRP generates the flush head height. The salt spray test evaluated corrosion performance. The flush head joints suffered from severe corrosion on the rivet head. Thus, the tensile shear load of flush head joints was substantially reduced. Electrochemical corrosion tests investigated the corrosion mechanisms. The deeper indentation of the flush head height damaged the CFRP around the rivet head. The exposure of damaged fibers from the matrix increased the cathodic potential of local CFRP. The increased potential of damaged CFRP accelerated the galvanic corrosion of the rivet head. After the rivet head coating material corroded, a strong galvanic couple was formed between the rivet head base metal (boron steel) and the damaged CFRP, further accelerating the flush rivet head corrosion. The results of this study suggest that rivet head flushness should be avoided to enhance the corrosion performance of CFRP to aluminum alloy self-piercing riveted joints.

• Steel and Composite Structures
• /
• 제32권5호
• /
• pp.633-642
• /
• 2019

In this work, lightweight sandwich plates consisting of a functionally graded porous (FGP) core and two laminated composite face sheets resting on elastic foundation have been proposed. Three different profiles are considered for the distributions of porosities along core thickness. The main aim of this paper is the investigation of the buckling behavior of the proposed porous sandwich plates (PSPs) by reporting their critical mechanical loads and their corresponding mode shapes. A finite element method (FEM) based on first order shear deformation theories (FSDT) is developed to discretize governing equations for the buckling behavior of the proposed sandwich plates. The effects of porosity dispersion and volume, the numbers and angles of laminated layers, sandwich plate geometrical dimensions, elastic foundation coefficients, loading and boundary conditions are studied. The results show that the use of FGP core can offer a PSP with half weight core and only 5% reduction in critical buckling loads. Moreover, stacking sequences with only ${\pm}45$ orientation fibers offer the highest values of buckling loads.

• Advances in concrete construction
• /
• 제7권4호
• /
• pp.219-229
• /
• 2019

This paper presents an experimental study on the structural performance of an innovative ultra-high performance fiber reinforced concrete (UHPFRC) deck with coarse aggregate of composite bridge under shear force. Test parameters included curing method and shear span-to-height ratio. Test results indicated that more short fine cracks developed beside the existing cracks due to the randomly dispersed fibers, resulting in re-distributing and homogenizing of the concrete stress beside cracks and allowing for the occurrence of more cracks with small spacing compared to normal strength concrete beams. Curing methods, incorporating steam curing and natural curing, did not have obvious effect on the nominal bending cracking strength and the ultimate strength of the test specimens. Shear reinforcement need not be provided for UHPFRC decks with a fiber volume fraction of 2%. UHPFRC decks showed superior load resistance ability after the appearance of cracks and excellent post-cracking deformability. Lastly, the current shear provisions were evaluated by the test results.

• 대한건축학회논문집:구조계
• /
• 제35권5호
• /
• pp.125-132
• /
• 2019

Ultra-high performance concrete (UHPC) has high compressive and tensile strengths due to the particle packing, and its ductile behavior can be ensured by utilizing steel fibers. However, since the UHPC members exhibit different characteristics of crack behavior and tensile behavior from normal concrete, the tension stiffening and cracking characteristics of the UHPC should be accurately modeled for the design and analysis of the UHPC members. In this study, uniaxial tension tests was conducted on the UHPC members with strands, where the test variables were diameter and reinforcing ratio of strands. Detailed analyses were also conducted to identify the tensile characteristics and crack behavior of the UHPC members. By comparing the test results with current code provisions and other models proposed by existing researchers, their applicability for estimation of crack behavior of the UHPC members was examined.

• Advances in concrete construction
• /
• 제11권1호
• /
• pp.19-32
• /
• 2021

In the present experimental study, the high performance hybrid fiber reinforced concrete (HPHFRC) is prepared using the Modified Andreasen and Andersen (A&A) particle packing model. Total of 16 trial mixes of HPHFRC with Indian standard sand (SS) and natural river sand (NS) are prepared to achieve the selection criteria (flow percent>150 and compressive strength>80 MPa). Based on the flow percent and compressive strength criteria, the selected mixes evaluated to study the effect of usage of natural river sand (NS) and the expensive Indian standard sand (SS) on the mechanical, durability, and microstructure property of designed HPHFRC. It has been found that the Modified A&A model is reliable to design the mix for HPHFRC with excellent mechanical, durability, and microstructure properties. In addition to that, a moderate difference in the mechanical and durability properties of NS contained HPHFRC and SS contained HPHFRC is found. Based on the obtained results of NS contained HPHFRC, it can be concluded that the use of natural river sand (NS) can be successfully adopted for the production of HPHFRC, resulted in a reduction of the production cost without compromising the excellent performance of HPHFRC.