• Progress in Superconductivity and Cryogenics
• /
• v.19 no.3
• /
• pp.13-17
• /
• 2017

We investigated the effect of self-assembled BSO nano-defects as pinning centers in BSO-added GdBCO films when the thicknesses of films were varied. 3.5 vol. % BSO-added GdBCO films with varying thicknesses from 200 nm to 1000 nm were deposited on $SrTiO_3$ (STO) substrate by using pulsed laser deposition (PLD) process. For the films with thicknesses of 400 nm and 600 nm, 'anomaly shoulders' in $J_c-H$ characteristic curves were observed near the matching field. The anomaly shoulders appeared in the field dependence of $J_c$ may be attributed to the existence of double pinning mechanisms in thin films. The fit to the pinning force density as a function of reduced field h ($H/H_{irr}$) using the Dew-Hughes' scaling law shows that both the 400 nm- and the 600 nm-thick films have double pinning mechanisms while the other films have a single pinning mechanism. These results indicate that the self-assembled property of BSO result in different role as pinning centers with different thickness.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.545-548
• /
• 2002

$(Ba_{0.6-x}Sr_{0.4}Ca_x)TiO_3$(BSCT) (x=0.10, 0.15, 0.20) powders were prepared by the sol-gel method and BSCT thick films were fabricated by the screen-printing method. The structural properties as a faction of the composition ratio were studied. As a result of the differential thermal analysis (DTA), exothermic perk was observed at around $860^{\circ}C$ dne to the formation of the polycrystalline perovskite phase. The BSCT thick films sintered at $1350^{\circ}C$ for 2h showed the average grain size of $2{\sim}7{\mu}m$. The average thickness of BSCT thick films, obtained by 3 times of screen-printing, was approximately $85{\mu}m$.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.11C no.2
• /
• pp.18-22
• /
• 2001

The thin films of high permitivity in ferroelectric materials using a capacitor are applied to DRAMs and FRAMs. (Ba, Sr)TiO$_3$ thin as ferroelectric materials were prepared by the sol-gel method and made by spin-coating on the Pt/Sio$_2$/Si substrate at 4,000 [rpm] for 10 seconds. The structural characteristics of the surface were analyzed by fractal dimension. The thickness of BST ceramics thin films was about 260∼280 [nm]. The property of the leakage current was stable with 10-9∼10-11[A] when the applied voltage was 0∼3[V]. BST thin films ha low leakage current properties when fractal dimension was low and a coating area was high.

• Progress in Superconductivity
• /
• v.7 no.2
• /
• pp.130-134
• /
• 2006

Buffer layers such as $CeO_2\;and\;Yb_2O_3$ films for YBCO coated conductors were deposited on (100) $SrTiO_3$ single crystals and (100) textured Ni substrates by a metal organic chemical vapor deposition (MOCVD) system of the hot-wall type. The substrates were moved with the velocity of 40 cm/hr. Source flow rate, $Ar/O_2$ flow rate and deposition temperature were main processing variables. The degree of film epitaxy and surface morphology were investigated using XRD and SEM, respectively. On a STO substrate, the $CeO_2$ film was well grown epitaxially above the deposition temperature of $450^{\circ}C$. However, on a Ni substrate, the XRD showed NiO (111) and (200) peaks due to Ni oxidation as well as (111) and (200) film growth. For the films deposited with $O_2$ gas as oxygen source, it was found that the NiO film was formed at the interface between the buffer layer and the Ni substrate. The NiO layer interrupts the epitaxial growth of the buffer layer. It seems that the epitaxial growth of the buffer layer on Ni metal substrates using $O_2$ gas is difficult. We are considering a new method avoiding Ni oxidation with $H_2O$ vapor instead of $O_2$ gas.

• Proceedings of the KIEE Conference
• /
• 1999.11d
• /
• pp.918-920
• /
• 1999

Recently, the ceramics of high permittivity are applied to DRAM and FRAM. In this study, (Ba, Sr)$TiO_3$ (BST) ceramics thin films were prepared by Sol-Gel method. BST solution was made and spin-coated on Pt/$SiO_2$/Si substrate at 4000[rpm] for 10 seconds. Coating process was repeated 3 times and then sintered at $750[^{\circ}C]$ for 30 minutes. Each specimen was analyzed structure and electrical characteristics. Thickness of BST ceramics thin films are about $2000[\AA]$. Dielectric constant and loss of thin films was little decreased at $1[kHz]{\sim}1[MHz]$. Dielectric constant and loss to frequency were 250 and 0.02 in BST3. In accordance with applied voltage, property of leakage current was stability when the was $0{\sim}3$[V]. According to voltage, leakage current was increased exponentially at $4{\sim}7$[V].

• Journal of Sensor Science and Technology
• /
• v.10 no.6
• /
• pp.295-303
• /
• 2001

White emission thin film electroluminecent device was fabricated with ZnS for phosphor layers and BST ferroelectric thin film for insulating layers. The ZnS:Mn and $ZnS:SmF_3$ layers were used for emission of red color. Also the $ZnS:TbF_3$ and $ZnS:AgF_3$ layers were used to emission of green and blue color, respectively. And the fabrication conditions of the BST insulating layers were followings, that is, the composition ratio of target, substrate temperature, working pressure and operating gas ratio were $Ba_{0.5}Sr_{0.5}Ti_{0.3}$, $400^{\circ}C$, 30 mTorr and 9:1, respectively. The thickness of phosphor were 150 nm for each layers and the insulating layers of upper and bottom were 400 nm and 200 nm, respectively. The luminesence threshold voltage was $75\;V_{rms}$ and the maximum brightness of the thin film electroluminecent device was $3200\;cd/m^2$ at $100\;V_{rms}$.

• Journal of the Korean Society for Heat Treatment
• /
• v.33 no.3
• /
• pp.124-128
• /
• 2020

Recently, many studies on growth of single crystal diamond using MPECVD have been conducted. The heteroepitaxial method is one of the methods for growing diamonds on a large-area substrate, and research on synthesis of single crystal diamonds using SrTiO₃, MgO, and sapphire substrates has been attempted. In addition, research is being conducted to reduce the internal stress generated during diamond growth and to improve the crystallinity of the diamond. The compressive stress generated therein causes peeling and bowing from the substrate. This study aimed to synthesize heteroepitaxial single crystal diamonds with high crystallinity by surface modification. A diamond thin film was first grown on a sapphire/Ir substrate by MPECVD, and then etched with H₂ gas to modified the morphology and roughness of the surface. A secondary diamond layer was grown on the surface, and the internal stress, crystallinity of the diamond were investigated. As a result, the fabrication of single crystal diamonds with improved crystallinity was confirmed.

• Journal of information and communication convergence engineering
• /
• v.2 no.2
• /
• pp.93-96
• /
• 2004

The a-Si:H TFT using ferroelectric of $SrTiO_3$ as a gate insulator is fabricated on glass. Dielectric characteristics of ferroelectric are superior to $SiO_2$ and $Si_{3}N_{4}$. Ferroelectric increases on-current, decreases threshold voltage of TFT and also improves breakdown characteristics. The a-SiN:H has optical band gap of 2.61 eV, retractive index of 1.8∼2.0 and resistivity of $10^{13}$~$10^{15}$ $\Omega$cm, respectively. Insulating characteristics of ferroelectrics are excellent because dielectric constant of ferroelectric is about 60∼100 and breakdown strength is over 1MV/cm. TFT using ferroelectric has channel length of 8∼20 $\mu\textrm{m}$ and channel width of 80∼200 $\mu\textrm{m}$. And it shows that drain current is 3.4$\mu\textrm{A}$ at 20 gate voltage, $I_{on}$/$I_{off}$ is a ratio of $10^5$~$10^8$ and $V_{th}$ is 4∼5 volts, respectively. In the case of TFT without ferroelectric, it indicates that the drain current is 1.5 $\mu\textrm{A}$ at 20 gate voltage and $V_{th}$ is 5∼6 volts. With the improvement of the ferroelectric thin film properties, the performance of TFT using this ferroelectric has advanced as a gate insulator fabrication technology is realized.

• Progress in Superconductivity and Cryogenics
• /
• v.15 no.4
• /
• pp.15-20
• /
• 2013

We investigated the flux pinning properties of both 10 mol% Zr-and Sn-doped $YBa_2Cu_3O_{7-{\delta}}$ (YBCO) films with the same thickness of ~350 nm for a comparative purpose. The films were prepared on the $SrTiO_3$ (STO) single crystal substrate by the metal-organic deposition (MOD) process. Compared with Sn-doped YBCO film, Zr-doped one exhibited a significant enhancement in the critical current density ($J_c$) and pinning force density ($F_p$). The anisotropic $J_{c,min}/J_{c,max}$ ratio in the field-angle dependence of $J_c$ at 77 K for 1 T was also improved from 0.23 for Sn-doped YBCO to 0.39 for Zr-doped YBCO. Thus, the highest magnetic $J_c$ values of 9.0 and $2.9MA/cm^2$ with the maximum $F_p$ ($F_{p,max}$) values of 19 and $5GN/m^3$ at 65 and 77 K for H // c, respectively, could be achieved from Zr-doped YBCO film. The stronger pinning effect in Zr-doped YBCO film is attributable to smaller $BaZrO_3$ (BZO) nanoparticles (the average size ${\approx}28.4$ nm) than $YBa_2SnO_{5.5}$ (YBSO) nanoparticles (the average size ${\approx}45.0$ nm) incorporated in Sn-doped YBCO film since smaller nanoparticles can generate more defects acting as effective flux pinning sites due to larger incoherent interfacial area for the same doping concentration.

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2000.11a
• /
• pp.45-48
• /
• 2000

High dielectric (Ba,Sr)TiO$_3$thin films were etched in an inductively coupled plasma (ICP) as a function of C1$_2$/Ar gas mixing ratio. Under Cl$_2$(20)/Ar(80), the maximum etch rate of the BST films was 400$\AA$/min and selectivities of BST to Pt and PR were obtained 0.4 and 0.2, respectively. We investigated the etched surface of BST by x-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM) and x-ray diffraction (XRD). From the result of XPS analysis, we found that residues of Ba-Cl and Ti-Cl bonds remained on the surface of the etched BST for high boiling point. The surface roughness decreased as Cl$_2$increases in C1$_2$/Ar plasma because of non-volatile etching products. This changed the nature of the crystallinity of BST. From the result of XRD analysis, the crystallinity of etched BST film maintained as similar to as-deposited BST under Ar only and Cl$_2$(20)/Ar(80). However, (100) orientation intensity of etched BST film abruptly decreased at Cl$_2$only plasma. It was caused that Cl compounds were redeposited on the etched BST surface and damaged to crystallinity of BST film during the etch process.