• Journal of the Korean Ceramic Society
• /
• v.40 no.1
• /
• pp.52-61
• /
• 2003

$SrBi_2Ta_2O_9(SBT)$and$ZrO_2$thin films for MFIS structure(Metal-Ferroelectric-Insulator-Semiconductor) were deposited by RF magnetron sputtering method. In order to investigate the effect of heat treatment of insulator layers and MFIS structure, the insulator layers were heat treated from $550^{circ}C;to; 850^{\circ}C$in conventional furnace or RTA furnace under$O_2$and Ar ambient, respectively. After then, C-V characteristics and leakage current were measured. The capacitor with 20 nm thick $ZrO_2$layer treated at RTA$750^{circ}C;in;O_2$ atmosphere had the largest memory window. The C-V and leakage current characteristics of the$Pt/SBT(260nm)/ZrO_2(20nm)/Si$structure were better than those of$Pt/SBT(260nm)/Si$ structure. These results showed that$ZrO_2$films took a role of buffer layer effectively.

• Journal of the Korean Magnetics Society
• /
• v.6 no.5
• /
• pp.323-328
• /
• 1996

NiFe($60\;{\AA}$)/Cu($60\;{\AA}$)/Co($30\;{\AA}$) trilayers were formed on the $4^{\circ}$ tilt-cut Si(111) substrate by rf magnetron sputtering method. With a Cu($50\;{\AA}$) underlayer, NiFe($60\;{\AA}$)/Cu($60\;{\AA}$)/Co($30\;{\AA}$) trilayers developed in-plane magnebc anisotropy and in-plane perpendicular alignment of easy axes in two magnetic components of NiFe($60\;{\AA}$)/Cu($60\;{\AA}$)/Co($30\;{\AA}$) trilayers has been found. The easy axis of Co layer consisbng of NiFe($60\;{\AA}$)/Cu($60\;{\AA}$)/Co($30\;{\AA}$) trilayers turned out to be along $4^{\circ}$ tilt Si <112> direcbon and that of NiFe layer along Si <110> direction. [NiFe($60\;{\AA}$)/Cu($60\;{\AA}$)/Co($30\;{\AA}$)]/Cu($50\;{\AA}$)/Si(111, $4^{\circ}$ tiIt-cut) trilayers showed about 2.2 % MR ratio at room temperature and large plateau in MR curves, which are more improved MR characteristics than those in [NiFe($60\;{\AA}$)/Cu($60\;{\AA}$)/Co($30\;{\AA}$)]/Cu($50\;{\AA}$)/glass trilayers with no appreciable magnetic anisotropy.

• Journal of the Korean Magnetics Society
• /
• v.24 no.4
• /
• pp.101-106
• /
• 2014

The glass/Ta(5.8 nm)/NiFe(5 nm)/Cu(2.3 nm)/NiFe(3 nm)/IrMn(12 nm)/Ta(5.8 nm) GMR-SV (giantmagneto-resistance-spin valve) multilayer structure films with a magnetoresistance ratio (MR) of 5.0 % and a magnetic sensitivity (MS) of 1.5%/Oe was deposited by dc magnetron sputtering method. Also, GMR-SV device having a width of $7{\mu}m{\sim}8{\mu}m$ similar to the diameter of RBC (red blood cell) was fabricated by the light lithography process. When RBCs coupled with several magnetic beads with a diameter of $1{\mu}m$ dropped upon the GMR-SV device having MR = 1.06% and MS = 0.3 %/Oe, there is observed the variation of about included of a resistance value of ${\Delta}R=0.4{\Omega}$ and ${\Delta}MR=0.15%$ around a external magnetic field of -0.6 Oe. From these results, the GMR-SV device having the width magnitude of a few micron size can be applied as the biosensor for the analysis of a new magnetic property of hemoglobin inside of RBC combined to magnetic beads.

• Corrosion Science and Technology
• /
• v.8 no.4
• /
• pp.162-169
• /
• 2009

Pure titanium and its alloys are drastically used in implant materials due to their excellent mechanical properties, high corrosion resistance and good biocompatibility. However, the widely used Ti-6Al-4V is found to release toxic ions (Al and V) into the body, leading to undesirable long-term effects. Ti-6Al-4V has much higher elastic modulus than cortical bone. Therefore, titanium alloys with low elastic modulus have been developed as biomaterials to minimize stress shielding. For this reason, Ti-30Ta-xZr alloy systems have been studied in this study. The Ti-30Ta containing Zr(5, 10 and 15 wt%) were 10 times melted to improve chemical homogeneity by using a vacuum furnace and then homogenized for 24 hrs at $1000^{\circ}C$. The specimens were cut and polished for corrosion test and Ti coating and then coated with TiN, respectively, by using DC magnetron sputtering method. The analyses of coated surface were carried out by field emission scanning electron microscope(FE-SEM). The electrochemical characteristics were examined using potentiodynamic (- 1500 mV~+ 2000 mV) and AC impedance spectroscopy(100 kHz~10 mHz) in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. The equiaxed structure was changed to needle-like structure with increasing Zr content. The surface defects and structures were covered with TiN/Ti coated layer. From the polarization behavior in 0.9% NaCl solution, The corrosion current density of Ti-30Ta-xZr alloys decreased as Zr content increased, whereas, the corrosion potential of Ti-30Ta-xZr alloys increased as Zr content increased. The corrosion resistance of TiN/Ti-coated Ti-30Ta-xZr alloys were higher than that of the TiN-coated Ti-30Ta-xZr alloys. From the AC impedance in 0.9% NaCl solution, polarization resistance($R_p$) value of TiN/Ti coated Ti-30Ta-xZr alloys showed higher than that of TiN-coated Ti-30Ta-xZr alloys.

• Journal of the Korean Magnetics Society
• /
• v.11 no.5
• /
• pp.189-195
• /
• 2001

We prepared TMR junctions of NiFe(170 )/CoFe(48 )/Al(13 )-O/CoFe(500 )/Ta(50 ) structure on 2.5$\times$2.5 $\textrm{cm}^2$ area Si/SiO$_2$ substrates in order to investigate the uniformity of magnetoresistance(MR) value using a ICP magnetron sputter. Each layer was deposited by the ICP magnetron sputter and tunnel barrier was formed by the plasma oxidation method. We measured MR ratio and resistance of TMR devices with four-terminal probe system by applying external magnetic field. Although we used ICP sputter which is known as superior to make uniform films, the standard variation of MR ratio was 2.72. The variation was not dependent on the TMR devices location of a substrate. We found that MR ratio and spin-flip field (H's) increased as the resistance increased, which may be caused by local interface irregularity of the insulating layer. The variation of resistance value was 64.19 and MR ratio was 2.72, respectively. Our results imply that to improve the insulating layer fabrication process including annealing process to lessen interface modulation in order to mass produce the TMR devices.

• Journal of the Korean Magnetics Society
• /
• v.10 no.5
• /
• pp.196-202
• /
• 2000

Top synthetic spin valves with structure Ta/NiFe/CoFe/Cu/CoFe(P1)/Ru/CoFe(P2)/FeMn/Ta on Si(100) substrate with natural oxide were prepared by dc magnetron sputtering system, and investigated on the magnetoresistance properties and effective exchange bias field. As the thickness of FeMn increased above 150 $\AA$, MR ratio was decreased due to the current shunting effect. As the thickness of free layer decreased below 40$\AA$, MR ratio was reduced rapidly. In case of 40 $\AA$ thick of free layer, spin valve film with a structure Si(100)/Ta(50 $\AA$)/NiFe(27 $\AA$)/CoFe(13 $\AA$)/Cu(26 $\AA$)/CoFe(30 $\AA$)/Ru(7 $\AA$)/CoFe(15 $\AA$)/FeMn(100 $\AA$)/Ta(50 $\AA$) exhibited maximum MR ratio of 7.5 % and an effective exchange bias field of 600 Oe, respectively. Thickness difference dependence in this synthetic spin valve structure on effective exchange field was investigated and interpreted by the analytical method. It should be noted that thickness increase of CoFe(P 1) and decrease of CoFe(P2) in synthetic antiferromagnet leaded to the decrease in effective exchange bias field by experimentally and analytically.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.330-332
• /
• 2013

소 분위기에서 플라즈마 표면 처리의 경우 기판 표면에 존재하는 수소와 탄소 유기물들이 산소와 반응하여 $H_2O$와 $CO_2$ 등으로 제거되며 표면에 오존 결합을 유도하여 표면 에너지를 증가시키는 것으로 알려져 있다. ZnO 나노구조물을 성장시키는 방법으로는 MOCVD (Metal-Organic Chemical Vapor Deposited), PLD (Pulsed Laser Deposition), VLS (Vapor-Liquid-Solid), Sputtering, 습식화학합성법(Wet Chemical Method) 방법 등이 있다. 그중에서도 습식화학합성법은 쉽게 구성요소를 제어할 수 있고, 저비용 공정과 낮은 온도에서 성장 가능하며 플렉서블 소자에도 적용이 가능하다. 그러므로 본 연구에서는 플라즈마 표면처리에 따라 표면에너지를 변화하여 습식화학합성법으로 성장시킨 ZnO nanorods의 밀도를 제어하고 photolithography 공정 없이 패터닝 가능성을 유 무를 판단하는 연구를 진행하였다. 기판은 Si wafer (100)를 사용하였으며 세척 후 표면에너지 증가를 위한 플라즈마 표면처리를 실시하였다. 분위기 가스는 Ar/$O_2$를 사용하였으며 입력전압 400 W에서 0, 5, 10, 15, 60초 동안 각각 실시하였다. ZnO nanorods의 seed layer를 도포하기 위하여 Zinc acetate dehydrate [Zn $(CH_3COO)_2{\cdot}2H_2O$, 0.03 M]를 ethanol 50 ml에 용해시킨 후 스핀코팅기를 이용하여 850 RPM, 15초로 5회 실시하였으며 $80^{\circ}C$에서 5분간 건조하였다. ZnO rods의 성장은 Zinc nitrate hexahydrate [$Zn(NO_3)_2{\cdot}6H_2O$, 0.025M], HMT [$C6H_{12}N_4$, 0.025M]를 deionized water 250 ml에 용해시켜 hotplate에 올리고 $300^{\circ}C$에서 녹인 후 $200^{\circ}C$에서 3시간 성장시켰다. ZnO nanorods의 성장 공정은(Fig. 1)과 같다. 먼저 플라즈마 처리한 시편의 표면에너지 측정을 위해 접촉각 측정 장치[KRUSS, DSA100]를 이용하였다. 그 결과 0, 5, 10, 15, 60 초로 플라즈마 표면 처리했던 시편이 각각 Fig. l, 2와 같이 $79^{\circ}$, $43^{\circ}$, $11^{\circ}$, $6^{\circ}$, $7.8^{\circ}$로 측정되었으며 이것을 각각 습식화학합성법으로 ZnO nanorods를 성장 시켰을 때 Fig. 3과 같이 밀도 차이를 확인할 수 있었다. 이러한 결과를 바탕으로 기판의 표면에너지를 제어하여 Fig. 4와 같이 나타나며 photolithography 공정없이 ZnO nanorods를 패터닝을 할 수 있었다. 본 연구에서는 플라즈마 표면 처리를 통하여 표면에너지의 변화를 제어함으로써 ZnO nanorods 성장의 밀도 차이를 나타냈었다. 이러한 저비용, 저온 공정으로 $O_2$, CO, $H_2$, $H_2O$와 같은 다양한 화학종에 반응하는 ZnO를 이용한 플렉시블 화학센서에 응용 및 사용될 수 있고, 플렉시블 디스플레이 및 3D 디스플레이 소자에 활용 가능하다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.110-110
• /
• 2016

금속재료 중 철강은 기계적 성질이 우수하고 대량생산에 의한 뛰어난 경제성을 가지기 때문에 다양한 산업 분야에서 널리 사용되고 있다. 그러나 스테인리스강 등과 같은 일부 특수한 용도의 강을 제외하고는 부식 환경에 취약하기 때문에 그 용도에 따라 표면처리를 함으로서 내식특성을 부여하고 있다. 일반적으로 이러한 철강재료에 대한 부식문제를 해결하기 위한 방법으로는 습식프로세스 중 아연(Zn)도금이 사용되는데, 아연은 그 자체가 보유하고 있는 차폐(barrier)효과는 물론 상대적으로 이온화 경향이 크기 때문에 철에 대하여 전자를 공급하는 희생양극적(Sacrificial anode)역할을 하여 철을 방식하는 원리를 가지고 있다. 하지만 최근에 이르러 기존의 도금 프로세스 처리된 제품의 사용 및 적용분야가 확대되고 가혹해 짐에 따라서 내식성 향상을 위한 새로운 재료 및 신기술 개발이 요구되고 있는 실정이다. 본 연구에서는 친환경 프로세스 방법인 PVD법 중 하나인 스퍼터링(Sputtering)을 이용하여 0.8mm 두께의 냉연강판 (cold rolled steel) 상에 Al에 대한 Mg 함량을 10~30wt.%로 하여 약 $5{\mu}m$ 두께의 막을 제작하였다. 이때 20wt.% 막의 경우 공정압력조건을 증가시켜 증착 막의 결정배향성을 변화시켰다. 뿐만 아니라 제작된 막들에 대해서 $400^{\circ}C$온도에서 10분간 열처리함으로서 코팅막의 성분변화에 따른 영향을 살펴보기 위해 시편을 추가 제작하였다. 이와 같이 제작된 막들에 대한 형성메커니즘과 내식성의 상관관계 해명을 위해 막의 조성분포, 표면 및 단면의 모폴로지 관찰 및 결정구조 등 재료특성분석과 더불어 염수분무(Salt spray test), 침지시험 그리고 양극분극 시험 등을 통해 내식성 평가를 진행하였다. 이상의 종합적인 결과를 살펴보면 제작된 Al-Mg 막은 마그네슘 함량비 및 열처리 조건에 따라 조성분포와 막의 모폴로지 및 결정배향성이 변화한다는 것을 알 수 있었는데, 마그네슘 함량이 증가하고 열처리한 막의 내식성이 가장 양호한 것으로 나타났다. 이것은 Al-Mg 성분이 표면을 중심으로 균일 분산-분포하며, Al에 대한 Mg의 고용으로 인해 안정적으로 형성된 부식생성물과 금속화합물의 단계적 반응 효과에 의해 차폐효과와 희생양극적 특성이 동시에 향상되었기 때문으로 생각된다. 한편 공정 압력을 증가시켜 형성한 막은 결정학적 구조에서 보다 높은 표면 에너지와 증가한 격자 정수에 의해 Mg이 부식환경에서 빠르게 반응하여 안정적 피막을 형성하기 때문에 내식성이 향상된 것으로 보여 진다. 이상의 연구를 통해서 고내식성을 Al-Mg막의 유효성 확인하였으며, 설계에 대한 기초적인 응용지침을 제시할 수 있을 것으로 사료된다.

• Journal of the Microelectronics and Packaging Society
• /
• v.14 no.1
• /
• pp.33-38
• /
• 2007

We studied a bonding at low temperature using polymer bump and Non-Conductive Adhesive (NCA), and studied the reliability of the polymer bump/Al pad joints. The polymer bumps were formed on oxidized Si substrates by photolithography process, and the thin film metals were formed on the polymer bumps using DC magnetron sputtering. The substrate used was AL metallized glass. The polymer bump and Al metallized glass substrates were joined together at $80^{\circ}C$ under various pressure. Two NCAs were applied during joining. Thermal cycling test ($0^{\circ}C-55^{\circ}C$, cycle/30 min) was carried out up to 2000 cycles to evaluate the reliability of the joints. The bondability was evaluated by measuring the contact resistance of the joints through the four point probe method, and the joints were observed by Scanning Electron Microscope (SEM). The contact resistance of the joints was $70-90m{\Omega}$ before the reliability test. The joints of the polymer bump/Al pad were damaged by NCA filler particles under pressure above 200 MPa. After reliability test, some joints were electrically failed since thinner metal layers deposited at the edge of bumps were disconnected.

• Journal of the Korean Magnetics Society
• /
• v.7 no.5
• /
• pp.243-248
• /
• 1997

The effect of $O_2$ partial pressure on microstructure and soft magnetic properties of as-deposited Fe-Hf-O thin film alloys, which are produced by rf magnetron sputtering method in $Ar+O_2$ mixed gas atmosphere, are investigated. Saturation magnetization ($4{\pi}M_s$) of Fe-Hf-O film were decreased with increasing $O_2$ partial pressure, the best soft magnetic properties exhibit at $O_2$ partial pressure of 10%. With further increase of $O_2$ partial pressure, soft magnetic properties decreased continuously. The $Fe_{82}Hf_{3.4}O_{14.6}$ film with $P_{O2}=10%$ exhibits good soft magnetic properties with $4{\pi}M_s=17.7kG$, $H_c=0.7Oe$ and ${\mu}_ {eff}$ (1~100 MHz)=2,500, respectively. The addition of O is effective in grain refinement. In case of $P_{O2}=15%$, it is observed that $Fe_3O_4$ compound is formed and high frequency soft magnetic properties are decrease. The electrical resistvity($\rho$) of Fe-Hf-O film is increased with increasing $O_2$ partial pressure. Electrical resistivity of $Fe_{82}Hf_{3.4}O_{14.6}$ film was 5 times higher than that of the film without oxygen. Thus, it is considered that the good magnetic properties of $Fe_{82}Hf_{3.4}O_{14.6}$ film results from decreasing the $\alpha$-Fe grain size by precipitates (Hf and O), high electrical resistivity.