• 한국진공학회지
• /
• 제1권1호
• /
• pp.162-167
• /
• 1992

반응성 RF 스파타 증착법으로 스테인레스 스틸 기판 위에 TiC 박막과 TiN 박막을 증착하였다. 스파타기체로 Ar를, 반응기체로 C2H2와 N2 기체를 사용하였다. 박막의 증착율 은 RF 출력증가에 따라 선형적으로 증가하였으며 스파타기체에 대한 반응 기체의 분압비 증가에 따라 급격하게 감소하였다. 박막의 성분은 TiC 박막의 경우 분압비 0.03에서, TiN 박막의 경우 분압비 0.05에서 stoichiometric한 성분이 된다. 이 TiC, TiN 박막의 morphology와 미세구조 및 계면을 AES, SEM 그리고 TEM으로 조사하였다. 또한 N+ 이온 을 주입하여 N+ 이온 주입효과와 열처리 효과도 조사하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 춘계학술대회 논문집 센서 박막재료 반도체재료 기술교육
• /
• pp.70-73
• /
• 2002

Thin films of vanadium oxide($VO_{x}$) have been deposited by r.f. magnetron sputtering from $V_{2}O_{5}$ target in gas mixture of argon and oxygen. The oxygen/(oxygen+argon) partial pressure ratio of 0% and 8% is adopted. Crystal structure, chemical composition, molecular structure and optical properties of films sputter-deposited under different oxygen gas pressures and in-situ annealed in vacuum at $400^{\circ}C$ for 1h and 4h are characterized through XRD. RBS, FTlR and optical absorption measurements. The films as-deposited are amorphous and those annealed for time longer than 4h are polycrystalline. $V_{2}O_{5}$ and lower oxides co-exist in sputter-deposited films and as the oxygen partial pressure is increased the films become more stoichiometric $V_{2}O_{5}$. When annealed at $400^{\circ}C$, the as-deposited films are reduced to a lower oxide. It is observed that the oxygen atoms located on the V-O plane of $V_{2}O_{5}$ layer participate more readily in the oxidation and reduction process. The optical transmission of the films annealed in vacuum decreases considerably than the as-deposited films and the optical absorption of all the films increases rapidly between 400 and 550nm.

• 한국재료학회지
• /
• 제23권6호
• /
• pp.304-308
• /
• 2013

The effect of a sputter deposition sequence of Cu, Zn, and Sn metal layers on the properties of $Cu_2ZnSnS_4$ (CZTS) was systematically studied for solar cell applications. The set of Cu/Sn/Zn/Cu multi metal films was deposited on a Mo/$SiO_2$/Si wafer using dc sputtering. CZTS films were prepared through a sulfurization process of the Cu/Sn/Zn/Cu metal layers at $500^{\circ}C$ in a $H_2S$ gas environment. $H_2S$ (0.1%) gas of 200 standard cubic centimeters per minute was supplied in the cold-wall sulfurization reactor. The metal film prepared by one-cycle deposition of Cu(360 nm)/Sn(400 nm)/Zn(400 nm)/Cu(440 nm) had a relatively rough surface due to a well-developed columnar structure growth. A dense and smooth metal surface was achieved for two- or three-cycle deposition of Cu/Sn/Zn/Cu, in which each metal layer thickness was decreased to 200 nm. Moreover, the three-cycle deposition sample showed the best CZTS kesterite structures after 5 hr sulfurization treatment. The two- and three-cycle Cu/Sn/Zn/Cu samples showed high-efficient photoluminescence (PL) spectra after a 3 hr sulfurization treatment, wheres the one-cycle sample yielded poor PL efficiency. The PL spectra of the three-cycle sample showed a broad peak in the range of 700-1000 nm, peaked at 870 nm (1.425 eV). This result is in good agreement with the reported bandgap energy of CZTS.

• 한국재료학회지
• /
• 제28권4호
• /
• pp.241-246
• /
• 2018

$TaN_x$ film is grown by plasma enhanced atomic layer deposition (PEALD) using t-butylimido tris(dimethylamido) tantalum as a metalorganic source with various reactive gas species, such as $N_2+H_2$ mixed gas, $NH_3$, and $H_2$. Although the pulse sequence and duration are the same, aspects of the film growth rate, microstructure, crystallinity, and electrical resistivity are quite different according to the reactive gas. Crystallized and relatively conductive film with a higher growth rate is acquired using $NH_3$ as a reactive gas while amorphous and resistive film with a lower growth rate is achieved using $N_2+H_2$ mixed gas. To examine the relationship between the chemical properties and resistivity of the film, X-ray photoelectron spectroscopy (XPS) is conducted on the ALD-grown $TaN_x$ film with $N_2+H_2$ mixed gas, $NH_3$, and $H_2$. For a comparison, reactive sputter-grown $TaN_x$ film with $N_2$ is also studied. The results reveal that ALD-grown $TaN_x$ films with $NH_3$ and $H_2$ include a metallic Ta-N bond, which results in the film's higher conductivity. Meanwhile, ALD-grown $TaN_x$ film with a $N_2+H_2$ mixed gas or sputtergrown $TaN_x$ film with $N_2$ gas mainly contains a semiconducting $Ta_3N_5$ bond. Such a different portion of Ta-N and $Ta_3N_5$ bond determins the resistivity of the film. Reaction mechanisms are considered by means of the chemistry of the Ta precursor and reactive gas species.

• The Korean Journal of Ceramics
• /
• 제4권1호
• /
• pp.9-14
• /
• 1998

Diamond-like carbon(DLC) films were deposited on buffer-layered ZnS substrates by radio frequency plasma enhanced chemical vapor deposition(RF-PECVD) method. Ge and GeC buffer layera were used between DLC and ZnS substrates to promote the adhesion of DLC on ZnS substrates. Ge buffer layers were sputter deposited by RF magnetron sputtering and $GeC^1$ buffer layers were deposited by same method except using acetylene reactive gas. The relatinship between film properties and deposition conditions was investigated using gas pressure, RF power and dc bias voltage as PECVD parameters. The hardness of DLC films were measured by micro Vickers hardness test and the adhesion of DLC films on buffer-layered ZnS substrates were studied by Sebastian V stud pull tester. The optical properties of DLC films on butter-layered ZnS substrates were characterized by ellipsometer and FTIR spectroscopy.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 추계학술대회 논문집 Vol.18
• /
• pp.124-125
• /
• 2005

ZnS:Mn thin films have attracted great interest as electroluminescence devices. In this study, inductively coupled BCl$_3$/Ar plasma was used to etch ZnS:Mn thin films. We obtained the maximum etch rate of ZnS:Mn thin films was 2209 ${\AA}$/min at a BCl$_3$(20%)/Ar(80%) gas mixing ratio, an RF power of 700 W, a DC bias voltage of-250 V, a total gas flow of 20 sccm, and a chamber pressure of 1 Pa. It was proposed that sputter etching is dominant etching mechanism while the contribution of chemical reaction is relatively low due to low volatility of etching products.

• 수산해양기술연구
• /
• 제29권4호
• /
• pp.272-278
• /
• 1993

The trimethylamine-sensing characteristics of ZnO based thin film semiconductors and the sensitivity enhancement by squttering conditions have been investigated to develop a new type sensor for detecting fish freshness. The sensor fabricated with a 300nm of ZnO thin film with 4 wt% Al sub(2) O sub(3) and 1 wt% TiO sub(2) exhibited the highest sensitivity of 155 at 30$0^{\circ}C$ of working temperature and to the 240 ppm TMA gas. Deposition of ZnO thin film using a RF magnetron sputter was carried out at a pressure of 10 super(-2) Torr in pure oxygen gas with an RF power of 100W. The sensor exhibited a large response to the actual gases produced by a mackerel at an early stage of decomposition.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 춘계학술대회 논문집
• /
• pp.578-581
• /
• 1999

The Co-Cr-Ta films are one of the most suitable candidates for perpendicular magnetic recording media. The facing targets sputtering(FTS) system has a advantage of preparing films over a wide range of working gas pressure on plasma-free substrates. In this study, we investigated the effect underlayers on the growths layers of Co-Cr-Ta recording layers. The Co-Cr-Ta/Ti(CoCr) double layers were deposited with sputter gas pressure$(P_N, 0.3-1mTorr)$ by using FTS apparatus at temperature of$40^{\circ}C~-300^{\circ}C$, respectively. Crystallographic and magnetic characteristics were evaluated by x-ray diffractometry(XRD) and vibrating sample magnetometer(VSM), respectively.

• Applied Science and Convergence Technology
• /
• 제23권2호
• /
• pp.90-96
• /
• 2014

Flexible $ZrO_2$ films as dielectric materials for high-energy-density capacitors were deposited on polyethylene terephthalate (PET) substrates by RF magnetron sputtering. The growth behavior, microstructure and electrical properties of the flexible $ZrO_2$ films were dependent on the sputtering pressure and gas ratio. Although $ZrO_2$ films were deposited at room temperature, all films showed a tetragonal crystalline structure regardless of the sputtering variables. The surface of the film became a surface with large white particles upon an increase in the $O_2/Ar$ gas ratio. The RMS roughness and crystallite size of the $ZrO_2$ films increased with an increase in the sputtering pressure. The electrical properties of the $ZrO_2$ films were affected by the microstructure and roughness. The $ZrO_2$ films exhibited a dielectric constant of 21~38 at 1 kHz and a leakage current density of $10^{-6}{\sim}10^{-5}A/cm^2$ at 300 kV/cm.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 춘계학술대회 논문집 센서 박막재료 반도체 세라믹
• /
• pp.131-135
• /
• 2003

Zinc Oxide(ZnO) thin films on Si (100) substrate were deposited by RF magnetron sputter with changing sputtering conditions such as argon/oxygen gas ratios, RF power, and substrate temperature, chamber pressure and target-substrate distance. To analyze a crystallographic properties of the films, $\theta/2\theta$ mode X-ray diffraction, SEM, and AFM analyses. C-axis preferred orientation, resistivity, and surface roughness highly depended on $Ar/O_2$ gas ratios. The resistivity of ZnO thin films rapidly increased with increasing oxygen ratio and the resistivity value of $9{\times}10^7{\Omega}cm$ was obtained at a working pressure of 10 mTorr with $Ar/O_2$=50/50. The surface roughness was also improved with increasing oxygen ratio and the ZnO films deposited with $Ar/O_2$=50/50 showed the excellent roughness value of $28.7{\AA}$.