• 한국전기전자재료학회논문지
• /
• 제34권5호
• /
• pp.321-326
• /
• 2021

We fabricated BiAlO thin film by a solution process with a brush coating to be used as liquid crystal (LC) alignment layer. Solution-processed BiAlO was coated on the glass substrate by brush process. Prepared thin films were annealed at different temperatures of 80℃, 180℃, and 280℃. To verify whether the BiAlO film was formed properly, X-ray photoelectron spectroscopy analysis was performed on Bi and Al. Using a crystal rotation method by polarized optical microscopy, LC alignment state was evaluated. At the annealing temperature of 280℃, the uniform homogenous LC alignment was achieved. To reveal the mechanism of LC alignment by brush coating, field emission scanning electron microscope was used. Through this analysis, spin-coated and brush coated film surface were compared. It was revealed that physical anisotropy was induced by brush coating at a high annealing temperature. Particles were aligned in one direction along which brush coating was made, resulting in a physical anisotropy that affects a uniform LC alignment. Therefore, it was confirmed that brush coating combined with BiAlO thin film annealed at high temperature has a significant potential for LC alignment.

• 반도체디스플레이기술학회지
• /
• 제14권1호
• /
• pp.61-65
• /
• 2015

We have fabricated poly(3,4-ethylenedioxythiophene) : poly(4-styrenesulfonate) (PEDOT : PSS) thin films using a slotdie coater for the applications of OLED lightings. It is demonstrated that the properties of slot-die coated PEDOT : PSS films are comparable with those of spin-coated ones. Namely, the average and peak-to-peak roughness of the slot-die coated 50-nm-thick PEDOT : PSS film are measured to be as low as 0.247 nm and 1.3 nm, respectively. Moreover, we have obtained excellent thickness uniformity (~1.91%). With the slot-die coated PEDOT : PSS films, we have fabricated green phosphorescent OLED devices. For comparison, we have also fabricated OLED devices with spin-coated PEDOT : PSS films. Both show almost no discrepancy in device performance. The power efficiency (25.4 lm/W) and emission uniformity (77%) of OLEDs with slot-die coated PEDOT : PSS films are shown to be slightly lower than those (27.3 lm/W, 80%) of OLEDs with spin-coated PEDOT : PSS films at the luminance of 1,000nit, increasing the feasibility of using a slot-die coating process for the fabrication of large-area OLED lighting sources at a competitive price.

• 한국전기전자재료학회논문지
• /
• 제25권4호
• /
• pp.290-293
• /
• 2012

This article introduces the characterization of spin coated ZnO transparent conducting oxide on the flexible substrates. As a II-IV compound semiconductor, ZnO has a wide band gap of 3.37 eV with transparent properties. Due to this transparent properties, ZnO materials can be also employed as the transparent conducting electrode materials. Therefore, strong demands have been required for the transparent electrodes with low temperature processing and cheap cost. So, We will investigate the electrical property and optical transmittance of ZnO transparent conducting oxide through the 4-point probe resistivity meter, and ultraviolet-vis spectrometer Lamda 35, respectively.

• 한국전기전자재료학회논문지
• /
• 제11권2호
• /
• pp.128-132
• /
• 1998

2/65/35 PLZT stock solution prepared by Sol-Gel processing was spin-coated on ITO coated glass and annealed by RTA(Rapid Thermal Annealing). The crystal structure of films was reported based on the observation of crystallization process and microstructure of the film fabricated at different fabrication condition. Films were crystallized into rhombohedral structure by annealing at $750^{\circ}C$ for 5 min. As the annealing temperature increased, the size of rosette structure of the films was grown up from $2.4{\mu}m$ to $15{\mu}m$, dielectric constant was increased, coercive field was decreased 33.82 kV/cm, remnant polarization was increased to 39.84 ${\mu}C/cm^2$ and Optical transmittance was decreased.

• 한국재료학회지
• /
• 제33권11호
• /
• pp.475-481
• /
• 2023

Recently, the electron transport layer (ETL) has become one of the key components for high-performance perovskite solar cell (PSC). This study is motivated by the nonreproducible performance of ETL made of spin coated SnO₂ applied to a PSC. We made a comparative study between tin oxide deposited by atomic layer deposition (ALD) or spin coating to be used as an ETL in N-I-P PSC. 15 nm-thick Tin oxide thin films were deposited by ALD using tetrakisdimethylanmiotin (TDMASn) and using reactant ozone at 120 ℃. PSC using ALD SnO₂ as ETL showed a maximum efficiency of 18.97 %, and PSC using spin coated SnO₂ showed a maximum efficiency of 18.46 %. This is because the short circuit current (Jsc) of PSC using the ALD SnO₂ layer was 0.75 mA/cm² higher than that of the spin coated SnO₂. This result can be attributed to the fact that the electron transfer distance from the perovskite is constant due to the thickness uniformity of ALD SnO₂. Therefore ALD SnO₂ is a candidate as a ETL for use in PSC vacuum deposition.

• 한국세라믹학회지
• /
• 제34권3호
• /
• pp.314-322
• /
• 1997

극저 유전특성을 갖는 SiO2 에어로겔의 박막화의 층간 절연막으로써의 응용성이 연구되었다. 점도가 10~14cP인 SiO2 폴리머 졸을 이소프로판을 분위기 하에서 1000~7000m으로 p-Si(111) 웨이퍼 상에 스핀코팅한 습윤겔 박막을 25$0^{\circ}C$와 1160 psing 조건에서 초임계건조하여 0.5 g/㎤ 정도의 밀도(78% 기공율) 와 4000~21000$\AA$ 범위의 두께를 갖는 SiO2 에어로겔 박막을 제조하였다. 박막의 두께와 미세구조를 제어할 수 있는 주요 인자는 졸의 농도, 회전속도 및 습윤겔 숙성시간임을 알 수 있었다. SiO2 에어로겔 박막의 유전상수 값은 giga급 이상의 차세대 반도체 소자에 충분히 응용될 수 있을 정도로 낮은 2.0 정도이었다.

• 한국진공학회지
• /
• 제9권1호
• /
• pp.69-75
• /
• 2000

We have investigated the feasibility of spin on glass (SOG) film from polysilazane-type resin as a premetal dielectric (PMD) layer of the next-generation ultra-large scale integrated (ULSI) devices. A commercial polysilazane resin and a polysilazane-type resin with oxidizing agent were spin-coated and cured to form SOG films. In order to study the effect of oxidizing agent and annealing, the SOG films were characterized as cured and after annealing at $400^{\circ}C$ to $900^{\circ}C$. the density and the resistance against wet chemical of the SOG films were improved by the addition of oxidizing agent, because oxidizing agent enhanced the conversion from polysilazane polymer to $SiO_2$. The hole profile issue associated with insufficient curing of polysilazane in narrow gaps was also resolved by oxidizing agent, while the gapfill capability of SOG was not deteriorated by oxidizing agent.

• 한국세라믹학회지
• /
• 제30권9호
• /
• pp.695-700
• /
• 1993

In this study, we prepared Pb-Ti stock solution by sol-gel processing and deposited PbTiO3 thin film on a Pt coated SiO2/Si wafer by spin coating using the stock solution. We used lead acetate trihydrate and titanium isopropoxide. The stock solution was partially hydrolized and finally a 0.25M coating solution was prepared. We achieved spin coating at 4000rpm for 30 seconds and heated the thin film at 375$^{\circ}C$ for 5 minutes and at $600^{\circ}C$ for 5 minutes successively, first and second heating state. And the thin film was finally sintered at 90$0^{\circ}C$ for 1 hour in the air. The upper electrode of the thin film was made by gold sputtering and was cricle shape with radius 0.4mm. Measured dielectric constant, dissipation factor and phase transition temperature(Cuire Temp.) were about 275, 0.02 and 521$^{\circ}C$ respectively. To observe ferroelectric characteristics we calculated Pr(remnant polarization) and Ec(coercive field) byhysteresis curve. Ec was 72kV/cm and Pr was 11.46$\mu$C/$\textrm{cm}^2$.

• 한국진공학회지
• /
• 제13권3호
• /
• pp.99-102
• /
• 2004

유기 절연층을 사용한 유기 박막 트랜지스터의 특성 향상을 위해 절연층 표면에 Ar플라즈마 처리를 하였다. 플라즈마 처리는 절연체 표면의 화학적, 물리적 특성 변화를 통해 그 후에 이어지는 활성층 성막시 분자들의 결정성을 향상시키기 위한 방법이다. 활성층으로 사용된 물질은 pentacene이며, 절연층으로 사용된 물질은 PVP(poly-vinyl-phenol)이다. Pentacene는 약 $10^{-6}$ Torr에서 0.5 $\AA$/sec의 속도로, PVP는 spin coating법에 의해 각각 성막되었다. 형성된 절연층을 일정 시간동안 H플라즈마 처리 한 후 각 소자의 전기적 특성을 측정하여 표면처리에 의한 특성 변화를 살펴보았다.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2009년도 제40회 하계학술대회
• /
• pp.1240_1241
• /
• 2009

In this paper, sol-gel-spin coated $Pb(ZrTi)O_3$ thin film with $ZrO_2$ buffer-layer and $PbTiO_3$ seed-layer was investigated for vibration MEMS energy harvester to scavenge power from ambient vibration via d33 piezoelectric mode. Piezoelectric thin film deposition techniques on insulating layer is the important key for $d_{33}$ mode of piezoelectric vibration energy harvester. $ZrO_2$ buff-layer was utilized as an insulating layer. $PbTIO_3$ seed-layer was applied as an inter-layer between PZT and $ZrO_2$ layer to improve the crystalline of PZT thin film. The fabricated PZT thin film had a remanent polarization of 5.3uC/$cm^2$ and the coercive field of 60kV/cm. The fabricated energy harvester using PZT thin film with PTO seed-layer generated 1.1uW of electrical power to $2.2M{\Omega}$ of load with $4.4V_{pvp}$ from vibration of 0.39g at 528Hz.