• Korean Journal of Metals and Materials
• /
• v.50 no.6
• /
• pp.469-475
• /
• 2012

A high-energy mechanical milling (HEMM) process was introduced to improve sinter-ability, and rapid sintering of spark plasma sintering (SPS) under pressure was used to make ultra fine grain (UFG) of Ti-Nb-Mo-CPP composites, which have bio-attractive elements, for increasing mechanical properties. Ti-Nb-Mo-CPP composites were successfully fabricated by SPS at $1000^{\circ}C$ within 5 minutes under 70 MPa using HEMMed powders. The Vickers hardness of the composites increased with increased milling time and addition of CPP contents. Biocompatibility and corrosion resistance of the Ti-Nb-Mo alloys were improved by addition of CPP, and the Ti-35%Nb-10%Mo-10%CPP alloy had better biocompatibility and corrosion resistance than the Ti-6Al-4V ELI alloy.

• Journal of Ceramic Processing Research
• /
• v.19 no.5
• /
• pp.383-387
• /
• 2018

Highly transparent $Y_2O_3$ ceramics were produced using spark plasma sintering (SPS) at $1600^{\circ}C$ and 30 MPa for 5 min. When the SPS process was applied with various amounts of $La_2O_3$ as dopant. The specimen doped with 3 mol% $La_2O_3$ showed the highest density, and rapid particle growth and pore growth occurred, exhibiting that the relative density and average grain size are 99.2% and $17.2{\mu}m$, respectively. The specimen showed excellent transmittance of 79.44% in the visible light region (600 nm), resulting that $La_2O_3$ would be a useful dopant for improving the transmittance and mechanical properties of transparent $Y_2O_3$ ceramics produced with SPS.

• Journal of the Korean Ceramic Society
• /
• v.45 no.2
• /
• pp.94-98
• /
• 2008

Silicon nitride($Si_3N_4)$ is one of the most widely used structural ceramic materials. However silicon nitride is difficult to sinter because of its strong covalent bonding characteristics. In this study, $Si_3N_4$ ceramics were fabricated by spark plasma sintering process with $Y_2O_3$ and $Al_2O_3$ addition to improve the sinterability and the mechanical properties and their phase transformation behavior, microstructure and mechanical properties were evaluated. Fully densified $Si_3N_4$ ceramics could be obtained by spark plasma sintering process at a lower temperature than conventional sintering method. The formation of network microstructure was affected by the addition of $Al_2O_3$ because it could accelerate a to ${\alpha}$ to ${\beta}$ phase transformation of $Si_3N_4$. As a result, the mechanical properties depended on amounts of $Al_2O_3$ addition. The hardness value increased with increasing ${\alpha}$-phase fraction, but fracture toughness value increase with increasing ${\beta}$-phase fraction.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1205-1206
• /
• 2006

Dispersion-strengthened copper with $TiB_2$ was produced by ball-milling and spark plasma sintering (SPS).Ball-milling was performed at a rotation speed of 300rpm for 30 and 60min in Ar atmosphere by using a planetary ball mill (AGO-2). Spark-plasma sintering was carried out at $650^{\circ}C$ for 5min under vacuum after mechanical alloying. The hardness of the specimens sintered using powder ball milled for 60min at 300rpm increased from 16.0 to 61.8 HRB than that of specimen using powder mixed with a turbular mixer, while the electrical conductivity varied from 93.40% to 83.34%IACS. In the case of milled powder, hardness increased as milling time increased, while the electrical conductivity decreased. On the other hand, hardness decreased with increasing sintering temperature, but the electrical conductiviey increased slightly

• Journal of Powder Materials
• /
• v.13 no.5 s.58
• /
• pp.351-359
• /
• 2006

Ni based($Ni_{57}Zr_{20}Ti_{18}Si_2Sn_3$) bulk metallic glass(BMG) powders were produced by a gas atomization process, and ductile Cu powders were mixed using a spray drying process. The Ni-based amorphous powder and Cu mixed Ni composite powders were compacted by a spark plasma sintering (SPS) processes into cylindrical shape. The relative density varied with the used SPS mold materials such as graphite, hardened steel and WC-Co hard metal. The relative density increased from 87% to 98% when the sintering temperature increased up to $460^{\circ}C$ in the WC-Co hard metal mold.

• Journal of Powder Materials
• /
• v.21 no.2
• /
• pp.97-101
• /
• 2014

The 304 stainless steel powders were prepared by high energy ball milling and subsequently sintered by spark plasma sintering, and the microstructural characteristics and micro-hardness were investigated. The initial size of the irregular shaped 304 stainless steel powders was approximately 42 ${\mu}m$. After high energy ball milling at 800 rpm for 5h, the powders became spherical with a size of approximately 2 ${\mu}m$, and without formation of reaction compounds. From TEM analysis, it was confirmed that the as-milled powders consisted of the aggregates of the nano-sized particles. As the sintering temperature increased from 1073K to 1573K, the relative density and micro-hardness of sintered sample increased. The sample sintered at 1573K showed the highest relative density of approximately 95% and a micro-hardness of 550 Hv.

• Journal of Powder Materials
• /
• v.22 no.3
• /
• pp.157-162
• /
• 2015

SKD11(ASTM D2) tool steel is a versatile high-carbon, high-chromium, air-hardening tool steel that is characterized by a relatively high attainable hardness and numerous, large, chromium rich alloy carbide in the microstructure. SKD11 tool steel provides an effective combination of wear resistance and toughness, tool performance, price, and a wide variety of product forms. Adding of CNTs increased the performance of mechanical properties more. 1, 3 vol.% CNTs was dispersed in SKD11 matrix by mechanical alloying. SKD11 carbon nanocomposite powder was sintered by spark plasma sintering process. FE-SEM, HR-TEM and Raman analysis were carried out SKD11 carbon nanocomposites.

• Korean Journal of Materials Research
• /
• v.17 no.6
• /
• pp.337-341
• /
• 2007

[ $Mg_{97}Zn_1Y_2$ ] alloy powders were prepared from gas atomization process, followed by consolidation using spark plasma sintering (SPS) process. The atomized $Mg_{97}Zn_1Y_2$ alloy particles were entirely spherical in shape and dendritic microstructure. The compacts sintered by SPS process had theoretical density more than 99%. The compressive yield strength was decreased as sintering temperature increased. It was found that the compressive strength showed the maximum value of 303MPa at the $Mg_{97}Y_2Zn_1$ specimen sintered under load of 255 MPa at $350^{\circ}C$.

• Journal of Powder Materials
• /
• v.10 no.3
• /
• pp.176-180
• /
• 2003

Pure WC powders which does not include a binder phase were consolidated by spark plasma sintering (SPS) process at 1600~185$0^{\circ}C$ for 0~30 min under 50 MPa. Microstructure alid mechanical properties of binderless WC prepared by SPS were investigated. With increasing sintering temperature, sintered density and Vickers hardness of binderless WC increased. The fracture toughness of binderless WC was 7~15 MPa $m^{1/2}$ depending on the sintered density and decreased with increasing the Vickers hardness. It is found that the binderless WC prepared by SPS at 175$0^{\circ}C$ for 10 min under 50 MPa showed nearly full densification with fine-grained structure and revealed excellent mechanical properties of high hardness (~HV 2400) and considerably high fracture toughness (~7 MPa $m^{1/2}$).

• Journal of the Korean Ceramic Society
• /
• v.46 no.5
• /
• pp.467-471
• /
• 2009

Effects of boron and carbon on the densification and thermal decomposition of an AlN-SiC-$TiB_2$ system were investigated. $SiO_2$ was mostly removed by the addition of carbon, while $Al_2O_3$ formed $Al_4O_4C$ and promoted the densification of the systems above $1850^{\circ}C$. Rather porous specimens were obtained without the additives after hot pressing at $2100^{\circ}C$, while densification was mostly completed at $2000^{\circ}C$ by using the additives. The sintering temperature decreased further to $1950^{\circ}C$ by applying spark plasma sintering. The additives promoted the shrinkage of AlN by forming a liquid phase which was originated from the carbo- and boro-thermal reduction of $Al_2O_3$ and AlN.