• Journal of the Korean Ceramic Society
• /
• v.34 no.1
• /
• pp.79-87
• /
• 1997

Anti-reflective and anti-static double layered films were prepared on the VDT panel by sol-gel spin-coating method. Their electrical, opticla, and mechanical properties were investigated. The outer SiO2 film with low re-fractive index was coated over the inner ATO(Antimony-doped Tin Oxide)-SiO2 film which was prepared by mixing ATO sol with SiO2 at molar ratio of 68:32 to satisfy the interference condition of double layers. The heat treatment was conducted at 45$0^{\circ}C$ for 30 min where residual organics were completely removed. The sheet resistance of ATO single layer showed the minimum value of 6$\times$107$\Omega$/$\square$ at 3 mol% addition of Sb and that of SiO2/ATO-SiO2 increased slightly with increasing SiO2 mol% up to 30 mol%, and then increased steeply to the value of 3$\times$108$\Omega$/$\square$ at 32 mol%. The reflectance of double layered films was about 0.64% at the wavelength of 550nm and the transmittance increased about 3.20%. The hardness of double layered films was almost the same as that of uncoated VDT panel, 471.4kg.f/mm2.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.296-296
• /
• 2007

Ferroelectric neodymium-substituted $Bi_4Ti_3O_{12}$(BTO) thin films have been successfully deposited on Pt/Ti/$SiO_2$/Si substrate by a sol-gel spin-coating process and the effect of crystallization temperature on their microstructure and ferroelectric properties were studied systematically. $Bi(TMHD)_3$, $Nd(TMHD)_3$, $Ti(O^iPr)_4$ were used as the precursors, which were dissolved in 2-methoxyethanol. The thin films were annealed at various temperatures from 600 to $720^{\circ}C$ in oxygen ambient for 1 hr, which was followed by post-annealed for 1 hr after depositing a Pt electrode to enhance the electrical properties. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to analyze the crystallinity and surface morphology of layered perovskite phase, respectively. The crystallinity of the BNT films was improved and the average grain size increased as the crystallization temperature increased from 600 to $720^{\circ}C$ at an interval of $40^{\circ}C$. The polarization values of the films were a monotonous function of the crystallization temperature. The remanent polarization value of the BNT thin films annealed at $720^{\circ}C$ was $24.82\;{\mu}C/cm^2$ at an applied voltage of 5 V.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.204.2-204.2
• /
• 2013

Wide band gap II-VI semiconductors have attracted the interest of many research groups during the past few years due to the possibility of their applications in light-emitting diodes and laser diodes. Among the II-VI semiconductors, ZnO is an important optoelectronic device material for use in the violet and blue regions because of its wide direct band gap (Eg ~3.37 eV) and large exciton binding energy (60 meV). F-doped ZnO (FZO) and undoped ZnO thin films were grown onto quartz substrate by the sol-gel spin-coating method. The doping level in the solution, designated by F/Zn atomic ratio of was varied from 0 to 5 in 1 steps. To investigate the effects of the structure and optical properties of FZO thin films were investigated using X-ray diffraction (XRD), UV-visible spectroscopy, and photoluminescence (PL). In the XRD, the residual stress, FWHM, bond length, and average grain size were changed with increasing the doping concentration. For the PL spectra, the high INBE/IDLE ratio of the FZO thin films doping concentration at 1 at.% than the other samples.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.39-42
• /
• 2000

The effect of excess Pb contents on the etching of PZT thin films and their electrical properties has been investigated. Ferroelectric PZT(53/47) thin films were prepared by the metal alkoxide-based Sol-Gel method, in which they were spin-coating on P7Ti/Si02/Si substrate using the PZT(53/47) stock solutions with various excess Pb contents. Etching of PZT film was performed using planar inductively coupled Ar/Cl$_2$/BCl$_3$ plasma. The etch rate of PZT film was 2450 $\AA$/min at Ar(20)/BCl$_3$(80) gas mixing ratio and substrate temperature of 8$0^{\circ}C$.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.137-137
• /
• 2003

Optical amplificator have been used to compensate the losses in the optical signal transmission and processing. Today, there has been increasing demand for the very low cost optical amplifier. Sol-gel offers considerable potential both low cost manufacture, and for great flexibility in materials composition and structure. In addition, the sol-gel process is a very attractive method for producing porous materials with controlled structure. In this work, we present the potoluminescence properties of Er doped A1$_2$O$_3$/SiO$_2$ films. Erbium doped alumina nano sol was prepared by Al(NO$_3$)$_3$.9$H_2O$ and Er(NO$_3$)$_3$.5$H_2O$ through hydrolysis and peptization, and then GPS (3-Glycidoxypropyltrimethoxysilane) was added into Er doped alumina nano sol for organic- inorganic hybridization. Er doped A1$_2$O$_3$/SiO$_2$ film was obtained by spin coating, dip coating and thermal treatment from 30$0^{\circ}C$~120$0^{\circ}C$, and there were crack-free after thermal treatment. The thickness of film was measured SEM, and the porosity of film was characterized by BET and TGA. The crystal phase of Er doped A1$_2$O$_3$/SiO$_2$ were determined by XRD. Finally, the photoluminescence properties of Er doped A1$_2$O$_3$/SiO$_2$ films will be discuss with the consideration of porosity and crystallity.

• Journal of the Korean Ceramic Society
• /
• v.41 no.2
• /
• pp.136-142
• /
• 2004

A homogeneous and stable ZnO sol was prepared by dissolving the zinc acetate dihydrate(Zn(CH$_3$COO)$_2$$.$2H$_2$O) in solution of isopropanol((CH$_3$)$_2$$.$CHOH) and monoethanolamine(MEA:H$_2$NCH$_2$CH$_2$OH). ZnO thin films were prepared by sol-gel spin-coating method and investigated for c-axis preferred orientation and physical properties with preheating temperature. The c-axis growth had a difference as increaing preheating temperature. ZnO thin film preheated at 275$^{\circ}C$ and post-heated at 650$^{\circ}C$ was highly oriented along the (002) plane. After preheating at 200∼300$^{\circ}C$ and post-heating at 650$^{\circ}C$, the transmittance of ZnO thin films by UV-vis. measurement was over 85% in visible range and exhibited absorption edges at about 370 nm. The optical band gap energy was obtained about 3.22 eV, The photoluminescence emission characteristics of ZnO thin film preheated at 275$^{\circ}C$ and post-heated at 650$^{\circ}C$ was found to orange emission(620 nm, 2.0 eV) by PL measurement, which revealed the possibility for application of inorganic photoluminescence device.

• Korean Journal of Materials Research
• /
• v.25 no.4
• /
• pp.171-176
• /
• 2015

We present the detection characteristics of nitrogen monoxide(NO) gas using p-type copper oxide(CuO) thin film gas sensors. The CuO thin films were fabricated on glass substrates by a sol-gel spin coating method using copper acetate hydrate and diethanolamine as precursors. Structural characterizations revealed that we prepared the pure CuO thin films having a monoclinic crystalline structure without any obvious formation of secondary phase. It was found from the NO gas sensing measurements that the p-type CuO thin film gas sensors exhibited a maximum sensitivity to NO gas in dry air at an operating temperature as low as $100^{\circ}C$. Additionally, these CuO thin film gas sensors were found to show reversible and reliable electrical response to NO gas in a range of operating temperatures from $60^{\circ}C$ to $200^{\circ}C$. It is supposed from these results that the p-type oxide semiconductor CuO thin film could have significant potential for use in future gas sensors and other oxide electronics applications using oxide p-n heterojunction structures.

• Korean Chemical Engineering Research
• /
• v.53 no.6
• /
• pp.762-769
• /
• 2015

The titania ($TiO_2$) nanoparticles with a diameter 2?3 nm were synthesized by controlling hydrolysis of titanium tetraisopropoxide (TTIP) in acid solution. Organic-inorganic hybrid coating solutions were prepared by reacting the titania nanoparticles with 3-glycidoxypropyl trimethoxysilane (GPTMS) by the sol-gel method. The hard coating films with high refractive index were obtained by curing thermally at $120^{\circ}C$ after spin-coating the coating solutions on the polycarbonate (PC) sheets. The coating films showed high optical transparency of 90% in the visible range and exhibited a pencil hardness of 2H. Also, the refractive index at 633 nm wavelength of coating films enhanced from 1.502 to 1.584 as the weight content of titania nanoparticles in the coating solutions increased from 4% to 25%.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.11
• /
• pp.1014-1019
• /
• 2006

The influence of the number of solution coatings on the densification of the PZT thick films was studied. PZT powder and PZT precursor solution was prepared by a sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The powder and solution of composition were (A) PZT(80/20)/PZT(20/80), (B) PZT(70/30)/PZT(30/70) and (C) PZT(60/40)/PZT(40/60), (D) PZT(52/48)/PT. The coating and drying procedure was repeated 4 times. And then the PZT precursor solution was spin-coated on the PZT thick films. A concentration of a coating solution was 0.5 moth and the number of coating was repeated from 0 to 6. The porosity of the thick films was decreased with increasing the number of coatings and the PZT thick films with 6-times coated showed the dense microstructure and thickness of about $60{\mu}m$. A grain size was increased with increasing the coating number. All PZT thick films showed the typical XRD patterns of a typical perovskite polycrystalline structure. The relative dielectric constant of PZT thick films was improved 30-100% as the number of coatings.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.369-369
• /
• 2007

ZnO film has been investigated during several decades because it has excellent optical property like a transmittance among the range of visible light for using transparent conducting oxide (TCO) films. But ZnO film has not enough conductivity for applying to TCO devices. Therefore we synthesized platinum nanoparticles and they incorporated into ZnO due to improve the electrical property of ZnO film by sol-gel synthesis method. Also, we fabricated photosensitive ZnO thin film containing Pt nanoparticles by sol-gel process and spin-coating for using photochemical solution deposition. Photosensitive ZnO film could carry out the direct-pattern which allow the etching process to be convenient. The optical and electrical properties of ZnO film with or without various atomic percent of Pt nanoparticles annealed at various temperatures were investigated by using UV-Vis spectroscopy and 4-point probe method, respectively. We characterized the ZnO thin film containing Pt nanoparticles using X-ray diffraction, scanning electron microscopy, and X-ray photoelectron spectroscopy.