• Korean Chemical Engineering Research
• /
• v.56 no.3
• /
• pp.327-334
• /
• 2018

Water-repellent coating solutions were prepared by sol-gel method using tetraethoxysilane (TEOS) and methyltrimethoxysilane (MTMS) as precursors. The solutions were spin-coated on a cold-rolled steel sheet and thermally cured to prepare a non-fluorine water-repellent coating films. The effects of molar ratios of MTMS/TEOS, water concentration and ammonia concentration on the hydrophobic properties of the coating films were studied. The contact angle of water on coating films prepared by varying the molar ratio of MTMS/TEOS to 1~20 showed a maximum value of $108^{\circ}$ when the MTMS/TEOS molar ratio was 10. With increasing water content, the coating films showed the larger contact angles and the better the water repellency. As the amount of ammonia added was increased, the contact angles of coating films were increased, showing the better the water repellency. It is considered that the larger the amount of ammonia added, the larger the size of the silica particles generated, which increases the surface roughness of the silica particles, thereby increasing the water repellency.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.11a
• /
• pp.175-179
• /
• 1996

Ferroelectric SrBi$_2$Ta$_2$$O_{9}$ thin films were fabricated by tole Sol-Gel method using a spin-on coating with MOD(Metal Organic Dccomposition) solution on Pt/Ti/SiO$_2$/Si(100) substratcs. The films were anncalcd at 80$0^{\circ}C$ for one hour in oxygen atmosphere. The effects of Bi/Ti mole ratios on crystalline orientations, surface morphologies, and subface composition SBT thin films with a Bi/Ta mole ratios from 1.1 to 1.3 were investigated using X-ray Diffractometry (XRD). Atomic Force (AFM), X-Ray Photoelectron Spectroscopy(XPS). Ferroelectric properties of these films were also measured.d.

• Journal of the Korean institute of surface engineering
• /
• v.32 no.3
• /
• pp.456-460
• /
• 1999

Transparent conducting tin (IV) oxide thin films have been studies and developed for the electrode materials of solar cell substrate. Fabrication of tin oxide thin films by sol-gel method is process development of lower cost photovoltaic solar cell system. The research is focused on the establishment of process condition and development of precursor. The precursor solution was made of tin isopropoxide dissolved in isopropyl alcohol. The hydrolysis rate was controlled by addition of triethanolamine. Dip and spin coating technique were applied to coat tin oxide on borosilicate glass. The resistivity of the thin film was lower than 0.1Ω-cm and the transmittance is higher than 90% in a visible range.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1995.05a
• /
• pp.14-16
• /
• 1995

Pb($Zr_{0.52}Ti_{0.48}$)$O_3$ ceramic thin films were fabricated from an alkoxide-based solution by Sol-Gel method. Pb($Zr_{0.52}Ti_{0.48}$)$O_3$ co-ramic thin films were formed by spin coating method on Pt/$SiO_2$/Si substrate at 4000[rpm] for 30 [sec]. Coated specimens were dried on the hot-plate at 400[$^{\circ}C$] for 10[min]. The coating process was repeated 6 times and then sintered at temperature between 500 ~ 800[$^{\circ}C$] for 1 hour. The ferroelectric perovskite phases precipitated under the sintering of 700[$^{\circ}C$] for 1 hour. Pb($Zr_{0.52}Ti_{0.48}$)$O_3$ thin film sintered at 700[$^{\circ}C$] for 1hour showed good dielectric constant (2133) and dielectric loss (2.2[%]) Properties. The switching voltage, switching time and leakage currents density were 3.0[V], 1.7[${\mu}$sec] , 160[pA/$\textrm{cm}^2$] repectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1994.11a
• /
• pp.168-170
• /
• 1994

Pb($Zr_{0.52}$$Ti_{0.48}$)$O_3$ ceramic thin films were fabricated from an alkoxide-based solution by Sol-Gel method. Pb($Zr_{0.52}$$Ti_{0.48}$)$O_3$ ceramic thin films were formed by spin coating method on Pt/$SiO_2$Si substrate at 4000ppm for 30 seconds. The coating process was repeated 6 times and then heat-treated at temperature between 500∼800[$^{\circ}C$] for 1 hour. The final thickness of the thin films were about 4800[A]. The ferroelectric perovskite phases precipitated under the heat-treated at 700[$^{\circ}C$] for 1 hour. Pb($Zr_{0.52}$$Ti_{0.48}$)$O_3$ thin films heat-treated at 700[$^{\circ}C$] for 1 hour showed good dielectric and ferroclectric properties.

• Proceedings of the KIEE Conference
• /
• 1994.07b
• /
• pp.1454-1456
• /
• 1994

$Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramic thin films were fabricated from an alkoxide-based solution by Sol-Gel method. $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramic thin films were formed by spin coating method on $Pt/SiO_2/Si$ substrate at 3000rpm for 30 seconds. The coating process was repeated 6 times and then heat-treated at temperature between 500 - $800[^{\circ}C]$ for 1 hour. The final thickness of the thin films were about 4800[A]. The 100% ferroelectric perovskite phases precipitated under the heat treated at $700[^{\circ}C]$ for 1 hour. $Pb(Zr_{0.52}Ti_{0.48})O_3$ thin films heat-treated at $700[^{\circ}C]$ for 1 hour showed good dielectric constant (812) property.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.11a
• /
• pp.247-250
• /
• 1998

Ferroelectric PZT(10/90)PZT(90/10) heterolayered thin films were fabricated by spin-coating method on the Pt/Ti/SiO$^2$/Si substrate alternately using PZT(10/90) and PZT(90/10) metal alkoxide solutions. The coating and heating procedure was repeated six times to form PZT heterolayered films. The surface, cross-sectional microstructures and thickness of the films were observed using scanning electron microscope(SEM). The relative dielectric constant and dielectric loss of the 5-coated PZT heterolayered films were 1331 and 4.8% respectively.

• Proceedings of the KIEE Conference
• /
• 2009.07a
• /
• pp.1342_1342
• /
• 2009

Zinc tin oxide (ZTO) based thin-film transistors (TFTs) were fabricated on glass substrate by using sol-gel method. The fabricated ZTO TFT had bottom gate and top contact structure with ZTO layer formed by spin coating from ZTO solution. The fabricated TFT showed field-effect mobility of about 2 - $4\;cm^2/V{\cdot}s$ with on/off current ratios >$10^7$, and threshold voltage of 2 V.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.305-306
• /
• 2006

Ga-doped and Al-doped ZnO thin films were fabricated via a sol-gel technique and electrical and optical properties of the films were investigated. Film deposition was performed by spin coating at 4000 rpm for 30 s on $SiO_2$ glass substrate FE-SEM was used to obtain the surface morphology images and the film thickness Four-point probe and UV-VIS spectrophotometer were used to measure the sheet resistance and the optical transparency, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.1
• /
• pp.57-61
• /
• 1998

In this study, PLZT stock solutions were prepared by Sol-Gel processing after the compositions were selected in the memory region of PLZT bulk phase diagram. PLZT solutions were deposited on the ITO glass substrate by spin-coating method. The thin films were annealed by rapid thermal processing. The electric characteristics, hysteresis loop, C-V characteristics of thin films in the memory region were measured in order to investigate the electrical characteristics of PLZT thin films. In selected compositions the decrease in Zr/Ti ratio led to an increase in dielectric constant and the decrease in remanent polarization and coercieve field which brought about slim hysteresis loop.