• Journal of Hydrogen and New Energy
• /
• v.21 no.6
• /
• pp.500-506
• /
• 2010

The metal monolith catalyst coated with 15wt% Ni/$MgAl_2O_4$ is applied to the natural gas steam reforming for hydrogen production. To address the improvement of adherence between metal monolith and catalyst coating layer, the pre-calcination temperature as well as the coating conditions of $Al_2O_3$ sol are optimized. When the Fe-Cr alloy monolith is pre-calcined at $900^{\circ}C$ for 6 h, $Al_2O_3$ layer was formed uniformly on the entire surface of the metal substrate. It is seen that the formation of $Al_2O_3$ layer on the monolith surface is essential for the uniform coating of $Al_2O_3$ sol onto the monolith substrate. The monolith catalyst coated with 10wt% $Al_2O_3$ sol shows high $CH_4$ conversion and good thermal stability as compared with the monolith catalyst without $Al_2O_3$ sol coating under severe reaction conditions with high GHSV of 30,000 $h^{-1}$ at $700^{\circ}C$. In addition, the metal monolith catalyst shows higher catalytic activity and better thermal conductivity than 15wt% Ni/$MgAl_2O_4$ pellet catalyst.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.2
• /
• pp.307-314
• /
• 1998

PZT thin films were fabricated by the Sol-gel method. Starting materials used for the preparation of the stock solution were Pb-acetate trihydrate, Zr-normal propoxide and Ti-isopropoxide. 2-Methoxyethanol and iso-propanol were used for solution. For studying the diffusion of Pb ion into the substrates. We used bare Si substrate, $SiO_2/Si$ substrates which was produced by thermal oxidation and $TiO_2/SiO_2/Si$ which was mad by Sol-gel method. Densification and adhesion of thin films were observed by SEM. Phase formation of thin films and diffusion of Pb ion into the substrate were examined by XRD and ESCA, respectively. In the case of bare Si and $SiO_2/Si$ substrate, we obtained the perovskite phase at $700^{\circ}C$ and restricted a little the diffusion of Si ion into the film with $SiO_2$ buffer layer. In the case of $TiO_2/SiO_2/Si$, perovskite phase were obtained at $500^{\circ}C$ and the diffusion of Pb ion and Si ion were restriced.

• Journal of the Korean Ceramic Society
• /
• v.47 no.4
• /
• pp.343-352
• /
• 2010

A zirconia gel/polymer hybrid nanofiber was produced in a nonwoven fabric mode by electrospinning a sol derived from hydrolysis of zirconium butoxide with a polyvinyl butyral. Results indicated that the hydroxyl groups on the vinyl alcohol units in the backbone of the polymer were involved in the hydrolysis as well as grafting the hydrolyzed zirconium butoxide. In addition, use of acetic acid as a catalyst resulted in further hydrolysis and condensation in the sol, which led to the growth of -Zr-O-Zr- networks among the polymer chains. These networks gradually transformed into a crystalline zirconia structure upon heating. The as-spun fiber was smooth but partially wrinkled on the surface. The average fiber diameter was $690{\pm}110\;nm$. The fiber exhibited a strong but broad blue photoluminescence with its maximum intensity at a wavelength of ~410 nm at room temperature. When the fiber was heat-treated at $400^{\circ}C$, the fiber diameter shrunk to $250{\pm}60\;nm$. Nanocrystals which belonged to a tetragonal zirconia phase and were ~5 nm in size appeared. A strong white photoluminescence was observed in this fiber. This suggests that oxygen or carbon defects associated with the formation of the nanocrystals play a role in generating the photoluminescence. Further heating to $800^{\circ}C$ resulted in a monoclinic phase beginning to form In the heat-treated fibers, coloring occurred but varied depending on the heating temperature. Crystallization, coloring, and phase transition to the monoclinic structure influenced the photoluminescence. At $600^{\circ}C$, the fiber appeared to be fully crystallized to a tetragonal zirconia phase.

• Bulletin of the Korean Chemical Society
• /
• v.28 no.11
• /
• pp.1951-1957
• /
• 2007

A new synthetic strategy based on the acid-base catalyzed sol-gel method was developed for the preparation of a series of mesoporous TiO2 nanoparticles. A key feature of the method involves a gradual change in pH (0.8- 9) during the sol-gel transition, which guarantees easy introduction of mesoporosity without relying on the well-established sonochemical or template approach. In addition, this method leads to the exclusive formation of the anatase phase stable enough to the calcination temperature up to 600 oC. The physicochemical properties of the particles in the series were characterized by various spectroscopic and analytical techniques such as wide-angle XRD, SAXRD, BET surface area, FE-SEM, TEM, FT-IR, TGA, and XPS. The photocatalytic efficiency of these materials was investigated for the oxidation of toluene under UV-irradiation. All but T-ad in the series exhibited high photocatalytic activity pushing the reaction into completion within 3 h. The reaction followed the first order kinetics, and the rate reaches as high as 3.9 × 10?2/min which exceeds the one with the commercially available Degussa P-25 by a factor of 3.2. When comparison is made among the catalysts, the reactivity increases with increase in the calcination temperature which in turn increases the crystallinity of the anatase phase, thus revealing the following rate orders: T-3 < T-4 < T-5 < T-6.

• Current Photovoltaic Research
• /
• v.3 no.1
• /
• pp.5-9
• /
• 2015

Absorption and luminescence characteristics of disperse red-19 (DR-19) and $TiO_2$ composite have been investigated with various poling electric field strengths. Two step synthetic processes were employed to employ the DR-19 to the $TiO_2$ sol-gel. Firstly, urethane bond formation between DR-19 (-OH) and 3-isocyanatopropyl triethoxysilane (ICPTES, -N=C=O) performed (ICPDR) prior incorporation to the $TiO_2$ sol-gel. Secondary, the hydrolysis of the ethoxy group from the ICPTES and condensation reaction between silanol groups from ICPTES and $TiO_2$ sol-gel were performed. The ICPDR and $TiO_2$ sol-gel ($DRTiO_2$) were mixed and stirred for several days. The composite was coated to the ITO coated glass substrate. Corona poling were performed before drying the composite with various electric field strengths. The absorption intensity decreased with the increase of the poling field strength, which resulted in the increase of poling efficiency. The photoluminescence also decreased as the poling field strength increased. There is long luminescence tail for the poled $DRTiO_2$ film compared with unpoled $DRTiO_2$ film. The luminescence long tail indicates that the self-trapped excitons and polarons were generated when the $DRTiO_2$ film was poled with electric field.

• Korean Journal of Ophthalmology
• /
• v.32 no.6
• /
• pp.433-437
• /
• 2018

Purpose: Various absorbable anti-adhesion agents have been used to prevent postoperative synechia formation after endonasal surgery. The purpose of this study was to evaluate the anti-adhesion effects of HyFence and Mediclore after endonasal dacryocystorhinostomy (DCR) compared to a mixed solution of hyaluronic acid and sodium carboxymethylcellulose (Guardix-Sol). Methods: In this retrospective study, endonasal DCR and silicone tube intubation were performed on 198 eyes of 151 patients. Three different anti-adhesion adjuvants were applied to the osteotomy site in the nasal cavity after standard endonasal DCR procedures. The subjects were classified into three respective groups: group A (71 eyes, Guardix-Sol 1.5 g), group B (89 eyes, HyFence 1.5 mL), and group C (38 eyes, Mediclore 1 cc). The three groups were evaluated by asking patients about subjective symptoms and by performing lacrimal irrigation tests and endoscopic examinations. Results: There were no statistically significant differences in age, sex, timing of tube removal, or follow-up period among the three groups. There were no statistically significant differences in success rates among the three groups (p = 0.990, 91.5% [65 / 71], 92.1% [82 / 89], and 92.1% [35 / 38], respectively). Conclusions: HyFence and Mediclore are safe and effective adjunctive modalities following endonasal DCR compared to Guardix-Sol. Therefore, these agents can be considered good alternatives to Guardix-Sol to increase the success rate of endonasal DCR in treating patients with poor prognosis.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.2
• /
• pp.70-74
• /
• 2009

Effect of the processing variables on the formation of $Pb(Sc_{1/2}Nb_{1/2})O_3$(hereafter PSN) thin layers prepared on Pt(111)/Ti/$SiO_2$/Si substrates using the sol-gel and the spin coating method has been studied. After each deposition, the coated films were heated at $370^{\circ}C$ for 5 min. Then they were finally sintered at temperature range of $600{\sim}700^{\circ}C$ by RTA(rapid thermal annealing). The final multilayered films showed a (111) preferred orientation. On a while, the layer-by-layer crystallization of multilayered amorphous thin films without the intermediate heating exhibited a (100) preferred orientation. In case of heat treatment in the tube furnace with the heating rate of $4^{\circ}C/min$, (100) and (111) oriented thin layers were formed simultaneously. The microstructure of the deposited films were dense and crack-free with thickness of 300nm, irrespective of the processing variables.

• Journal of the Korean Chemical Society
• /
• v.61 no.1
• /
• pp.29-33
• /
• 2017

Formation of Au particles in nonstoichiometric $Cu_{2-x}{^I}Cu{_2}^{II}O_{3-{\delta}}$ ($x{\approx}0.20$; ${\delta}{\approx}0.10$) oxide from aniline + hydrochloric acid mixtures and chloroauric acid in the ratios 30 : 1; 60 : 1; 90 : 1 (S1-S3) by volume and 0.01 mol of copper acetate, $Cu(OCOCH_3)_2.H_2O$, in each case is performed by sol-gel growth. Powder x-ray diffraction (XRD) results show Au particles are dispersed in tetragonal nonstoichiometric dicopper (I) dicopper (II) oxides, $Cu_{2-x}{^I}Cu{_2}^{II}O_{3-{\delta}}$ ($x{\approx}0.20$; ${\delta}{\approx}0.10$). Average crystallite sizes of Au particles determined using Scherrer equation are found to be in the approximate ranges ${\sim}85-140{\AA}$, ${\sim}85-150{\AA}$ and ${\sim}80-150{\AA}$ in S1-S3, respectively which indicate the formation of Au nano-micro size particles in $Cu_{2-x}{^I}Cu{_2}^{II}O_{3-{\delta}}$ ($x{\approx}0.20$; ${\delta}{\approx}0.10$) oxides. Hysteresis behaviour at 300 K having low loop areas and magnetic susceptibility values ${\sim}5.835{\times}10^{-6}-9.889{\times}10^{-6}emu/gG$ in S1-S3 show weakly ferromagnetic nature of the samples. Broad and isotropic electron paramagnetic resonance (EPR) lineshapes of S1-S4 at 300, 77 and 8 K having $g_{iso}$-values ${\sim}2.053{\pm}0.008-2.304{\pm}0.008$ show rapid spin-lattice relaxation process in magnetic $Cu^{2+}$ ($3d^9$) sites as well as delocalized electrons in Au ($6s^1$) nano-micro size particles in the $Cu_{2-x}{^I}Cu{_2}^{II}O_{3-{\delta}}$ ($x{\approx}0.20$; ${\delta}{\approx}0.10$) oxides. Broad and weak UV-Vis diffuse reflectance optical absorption band ~725 nm is assigned to $^2B_{1g}{\rightarrow}^2A_{1g}$ transitions, and the weak band ~470 nm is due to $^2B_{1g}{\rightarrow}^2E_g$ transitions from the ground state $^2B_{1g}$(${\mid}d_{x^2-y^2}$>) of $Cu^{2+}$ ($3d^9$) ions in octahedral coordination having tetragonal distortion.

• Bulletin of the Korean Chemical Society
• /
• v.16 no.12
• /
• pp.1148-1152
• /
• 1995

Oxidative dimerization of methane to C2-hydrocarbons was performed over lead aluminate spinel catalysts. These spinel catalysts were prepared by co-precipitation, aerogel, and sol-gel methods. The active phase of lead aluminate oxides was found to be PbAl2O4 spinel. The activities of the catalysts were strongly dependent on the preparation method as well as the composition of PbAl2O4 phase. The proper oxygen mobility of PbAl2O4 spinel oxides appeared to be important to get high catalytic activity and selectivity for C2-hydrocarbon formation.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 2000.06a
• /
• pp.143-150
• /
• 2000

Wet-chemical process using ammonia to precipitate aluminum ion dissolved in a zirconia sol solution is examined. Formation of crystalline bayerite is unfavorable for fine dispersion of zirconia nanoparticles in alumina matrix after heat treatment. To avoid the bayerite formation, it was preferred to make a precipitation with a diluted ammonia or with an ammonia gas flow at high temperature. By optimizing the precipitation process and the calcination temperature, we successfully prepared the uniform microstructure in which tetragonal zirconia particles of ∼30nm is finely dispersed within the alumina grains.