• Journal of the Korean institute of surface engineering
• /
• v.35 no.1
• /
• pp.11-16
• /
• 2002

As environmental concerns increasing, the electronics industry is focusing more attention on lead free solder alternatives. In this research, we have researched wettability of intermediate solder of Sn3Ag9Bi5In, which include In and Bi and has similar melting temperature to Sn37Pb eutectic solder. We investigated the wetting property of Sn3Ag9Bi5In. To estimate wettability of Sn3Ag9Bi5In solder on various substrates, the wettability of Sn3Ag9Bi5In solder on high-pure Cu-coupon was measured. Cu-coupon that plated Sn, Ni and Au/Ni and Si-wafer adsorbed Ni/Cu under bump metallurgy on one side. As a result, the wetting property of Sn3Ag9Bi5In solder is a little better than that of Sn37Pb and Sn3.5Ag.

• Journal of Welding and Joining
• /
• v.16 no.3
• /
• pp.157-166
• /
• 1998

Recently as environmental pollution caused by Pb has posed a serious threat to the global environment, the trend to regulate the usage of Pb in electronic industry is one the rise. Currently, the solder alloy with high Pb content, Sn-37%Pb, is utilized in the electronic assembly therefore, the objective of this study is to develop an alternative solder alloy for the existing Sn-37%Pb solder alloy. First thing, this work choosed Sn-5%Pb-1.5%Ag, Sn-5%Pb-1.5%Ag-x%Bi(x=1~5%) for candidate solder alloys, and examined their properties such as melting range, wettability, microhardness, tensile property, oxidation behavior and microstructure. Wettability was on the same level of Sn-37%Pb. Dissolution of Pb ion in Sn-5%Pb solder was 0.46ppm. This solder alloy revealed cellular dendrite microstructure $\beta$-Sn matrix, Pb-rich phase, Ag/Sn, and Cu/Sn Intermetallic compounds. The range of solidification temperature was within 3$0^{\circ}C$. Also these alloy displayed higher tensile strength and lower elongation than Sn-37%Pb. The resistance of oxidation in Sn-5%Pb-1.5%Ag solder alloy was superior to that of Sn-37%Pb solder alloy. But that of Sn-5%Pb-1.5%Ag-5%Bi solder alloy was equal to that of Sn-37%Pb solder alloy.

• Journal of Welding and Joining
• /
• v.21 no.3
• /
• pp.92-98
• /
• 2003

This paper describes the numerical prediction of the thermal fatigue life of a $\mu$BGA(Micro Ball Grid Array) solder joint. Finite element analysis(FEA) was employed to simulate thermal cycling loading for solder joint reliability. Strain values, along with the result of mechanical fatigue tests for solder alloys were then used to predict the solder joint fatigue life using the Coffin-Manson equation. The results show that Sn-3.5mass%Ag solder had the longest thermal fatigue life in low cycle fatigue. Also a practical correlation for the prediction of the thermal fatigue life was suggested by using the dimensionless variable ${\gamma}$, which was possible to use several lead free solder alloys for prediction of thermal fatigue life. Furthermore, when the contact angle of the ball and chip has 50 degrees, solder joint has longest fatigue life.

• Journal of Welding and Joining
• /
• v.16 no.3
• /
• pp.148-156
• /
• 1998

The purpose of this study is to investigate the characteristics of Pb-Free Sn-2%Ag-Bi solder alloys. The solder alloys used in this study is Sn-2%Ag-(3,5,7,9%) Bi It is examined that their properties such as melting range, wettability, microstructure, microhardness, and tensile property. The addition of Bi(3,5,7,9%) lowered the melting point of the solder and the melting range was 196~203$^{\circ}C$. The wettability of the solder as equal to that of Sn-37% Pb solder. The morphology of structure did not change largely by addition of Bi. But the structure of cellular dendrite of linear type displayed. The tensile strength of the solder was superior to that of Sn-37%Pb solder. But the elongation was inferior to that of Sn-37%Pb solder. The hardness of Sn-2%Ag solder was tow times and that of Sn-2%Ag-Bi solder was three times of that in Sn-37%Pb solder. But the effect of increment of Bi content did not change largely.

• Journal of the Microelectronics and Packaging Society
• /
• v.10 no.4
• /
• pp.81-86
• /
• 2003

Electromigration of Sn-3.5Ag solder bump was investigated using flip chip specimens which consisted of upper Si chip and lower Si substrate. While the resistance of the flip chip sample did not almost change until the time right before the failure, the resistivity increased abruptly at the moment when complete failure of the solder joint occurred in the flip chip sample. At current densities of $3\times 10^4$∼$4\times 10^4$A/$\textrm{cm}^2$, the activation energy for electromigration of the Sn-3.5Ag solder bump was characterized as ∼0.7 eV. Failure of the Sn-3.5Ag solder bump occurred at the solder/UBM interface due to the formation and propagation of voids at cathode side of the solder bump.

• Korean Journal of Metals and Materials
• /
• v.47 no.12
• /
• pp.842-851
• /
• 2009

The long-term reliability of Sn-0.3wt%Ag-0.7wt%Cu solder joints was evaluated and compared with Sn-3.0wt%Ag-0.5wt%Cu under thermal shock conditions. Test vehicles were prepared to use Sn-0.3Ag-0.7Cu and Sn-3.0Ag-0.5Cu solder alloys. To compare the shear strength of the solder joints, 0603, 1005, 1608, 2012, 3216 and 4232 multi-layer ceramic chip capacitors were used. A reflow soldering process was utilized in the preparation of the test vehicles involving a FR-4 material-based printed circuit board (PCB). To compare the shear strength degradation following the thermal shock cycles, a thermal shock test was conducted up to 2,000 cycles at temperatures ranging from $-40^{\circ}C$ to $85^{\circ}C$, with a dwell time of 30 min at each temperature. The shear strength of the solder joints of the chip capacitors was measured at every 500 cycles in each case. The intermetallic compounds (IMCs) of the solder joint interfaces werealso analyzed by scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). The results showed that the reliability of Sn-0.3Ag-0.7Cu solder joints was very close to that of Sn-3.0Ag-0.5Cu. Consequently, it was confirmed that Sn-0.3Ag-0.7Cu solder alloy with a low silver content can be replaced with Sn-3.0Ag-0.5Cu.

• Korean Journal of Materials Research
• /
• v.8 no.11
• /
• pp.1011-1019
• /
• 1998

This work designed Sn-5%Pb-1.5%Ag-x%In solder alloy to develop the solder alloy with low Pb content. This solder alloy doesn't cause environmental pollution. and this study reviewed the probability of replacement of Sn-37%Pb solder as evaluation of melting range, wettability. microstructure, microhardne'ss, tensile strength, drossability of this new solder alloys. The level of international regulation in dissolution amount of Pb ion was 3ppm. But dissolution amount of Pb ion in Sn-5%Pb solder alloy confirmed not to threat the global environmental is 0.46ppm. The melting range of this solder alloy was $183-192^{\circ}C$. Also the range of solidification was very narrow within $5^{\circ}C$. The wettability was similar to Sn-37%Pb solder, and the effect of amount of In addition of wettability couldn't be founded. The probability of replacement in the melting range and wettability is very high. And microhardness of this solder alloy was 1.5 times of conventional type solder. Tensile strength of new solder alloys was a little high than that of conventional type solder. With increasing amount of In% addition, tensile strength was increased, but elongation was decreased. The solder alloy of l%In addition revealed AgSn and Pb on dendrite microstructure boundary, and $Ag_3Sn$, $Ag_3In$ and Pb were revealed on it at the solder alloy of 3% In addition. The drossability was superior to Sn-37%Pb solder alloy and the solder alloys of 2% In addition was not generated for 3hrs.

• Journal of the Microelectronics and Packaging Society
• /
• v.9 no.2
• /
• pp.39-43
• /
• 2002

The eutectic solder Sn-37Pb and the lead free solder alloys with the compositions of Sn-0.7Cu, Sn-3.5Ag, Sn-3.5Ag-0.75Cu, Sn-2.0Ag-0.7Cu-3.0Bi were applied to the 48 BGA packages, and then it was discussed for the shear strength at the solder joints as the hardness and the composition of the small solder ball. As a result of experiments, the high degree of hardness with the displacement of 0.043 mm was obtained in Sn-2.0Ag-0.7Cu-3.0Bi. The shear strength of the lead free solder was higher than that of Sn-37Pb solder, and it can be obtained the maximum value of about 52% in Sn-2.0Ag-0.7Cu-3.0Bi.

• Journal of Welding and Joining
• /
• v.20 no.2
• /
• pp.77-81
• /
• 2002

Many kinds of Pb-free solder have been investigated because of the environmental concerns. Sn-Ag-Cu system is well blown as most competitive Pb-free solder. However, since Sn-Ag-Cu system has relatively high melting point compared to Sn-Pb eutectic, it may a limitation, the some application. In this study, Bi and In contained solder of $Sn_3Ag_8Bi_5In$ which has relatively lower melting point, $188~204^{\circ}C$, was investigated. $Sn_3Ag_8Bi_5In$ solder ball of $500\mu\textrm{m}$ diameter was set on the Ni/Cu/Cr-UBM and reflow soldered in the range of $220~240^{\circ}C$ for 5~15s. The maximum shear strength of the solder ball was around 170mN by reflowing at $240^{\circ}C$ for 10s. Intermetallic compound formed on the UBM of Si-wafer was analysed by SEM(scanning electron microscope) and XRD(X-ray diffractometer).

• Journal of Welding and Joining
• /
• v.23 no.3
• /
• pp.61-67
• /
• 2005

Since lead (Pb)-free solders for electronics have higher melting points than that of eutectic Sn-Pb solder, they need higher soldering temperatures. In order to decrease the soldering temperature we tried to coat Sn-Bi layer on $Sn-3.5\%Ag$ solder by electroplating, which applies the mechanism of transient liquid phase bonding to soldering. During heating Bi will diffuse into the $Sn-3.5\%Ag$ solder and this results in decreasing soldering temperature. As bonding samples, the 1608 capacitor electroplated with Sn, and PCB, its surface was finished with electroless-plated Ni/Au, were selected. The $Sn-95.7\%Bi$ coated Sn-3.5Ag was supplied as a solder between the capacitor and PCB land. The samples were reflowed at $220^{\circ}C$, which was lower than that of normal reflow temperature, $240\~250^{\circ}C$, for the Pb-free. As experimental result, the joint of $Sn-95.7\%Bi$ coated Sn-3.5Ag showed high shear strength. In the as-reflowed state, the shear strength of the coated solder showed 58.8N, whereas those of commercial ones were 37.2N (Sn-37Pb), 31.4N (Sn-3Ag-0.5Cu), and 40.2N (Sn-8Zn-3Bi). After thermal shock of 1000 cycles between $-40^{\circ}C$ and $+125^{\circ}C$, shear strength of the coated solder showed 56.8N, whereas the previous commercial solders were in the range of 32.3N and 45.1N. As the microstructures, in the solder $Ag_3Sn$ intermetallic compound (IMC), and along the bonded interface $Ni_3Sn_4$ IMC were observed.