• 마이크로전자및패키징학회지
• /
• 제9권2호
• /
• pp.39-43
• /
• 2002

48 $\mu$BGA 패키지에 Sn-37Pb 공정 솔더와 Sn-0.7Cu, Sn-3.5 Ag, Sn-2.0Ag-0.75Cu, Sn-2.0Ag-0.7Cu-3.0Bi 4종류의 무연 솔더를 적용하여, 미세 솔더 볼의 경도와 조성에 따른 솔더 접합부의 전단강도에 대해서 연구하였다. 실험 결과, 솔더 볼의 짖눌림은 Sn-2.0Ag-0.7Cu-3.0Bi에서 0.043mm로 큰 경도값을 얻었다. 또한 전단 강도 값은 무연 솔더가 Sn-37Pb 솔더보다 높았으며, Sn-2.0Ag-0.7Cu-3.0 Bi에서 최대 52% 높은 값을 나타내었다.

• 한국재료학회지
• /
• 제15권9호
• /
• pp.598-603
• /
• 2005

To develope new lead-free solders with the melting temperature close to that of Sn-37Pb$(183^{\circ}C)$, Sn-0.7Cu-5Pb-1Ga, Sn-0.7Cu-5Pb-1Ag, Sn-0.7Cu-5Pb-5Bi-1Ag, and Sn-0.7Cu-SBi-1Ag alloys were composed by adding low-netting elements such as Ga, Bi, Pb, and Ag to Sn-0.7Cu. Then the melting temperatures, microstructures, wettability, and adhesion properties of these alloys were evaluated. DSC analysis showed that the melting temperature of Sn-0.7Cu-SPb-1Ga was $211^{\circ}C$, and those of other alloys was in the range of $192\~200^{\circ}C$. Microstructures of these alloys after heat-treatment at $150^{\circ}C$ for 24 hrs were basically composed of coarsely- grown $\beta-Sn$ grains, and $Cu_6Sn_5$ and $Ag_3Sn$ intermetallic precipitates. Sn-0.7Cu-5Pb-1Ga and Sn-0.7Cu-5Pb-5Bi-1Ag showed excellent wettability, while Sn-0.7Cu-5Bi-1Ag and Sn-0.7Cu-5Pb-5Bi-1Ag revealed good adhesion strength with the Cu substrates. Among 4 alloys, Sn-0.7Cu-5Pb-5Bi-1Ag with the lowest melting temperature $(192^{\circ}C)$ and relatively excellent wettability and adhesion strength was suggested to be the best candidate solder to replace Sn-37Pb.

• 마이크로전자및패키징학회지
• /
• 제14권4호
• /
• pp.21-25
• /
• 2007

본 연구에서는 시차주사열량법, 젖음성 시험기, 비커스 경도계와 인장 시험기를 이용하여 Sn-0.7wt%Cu-Xwt%Re(X=$0.01{\sim}1.0$) 솔더의 특성에 관하여 평가하였다. 희토류 금속의 함량이 증가함에 따라 솔더의 용융 온도가 약간 상승하는 경향을 나타내었으나 $0.01{\sim}1.0%$의 희토류 금속이 첨가된 범위에서는 $233.9{\sim}234.7^{\circ}C$의 작은 용융 온도 범위를 갖는 것을 확인할 수 있었다. 솔더의 젖음성 시험 결과로부터 Sn-0.7Cu-0.1Re 솔더의 젖음성이 다른 솔더보다 우수한 것을 확인할 수 있었으며, Sn-0.7Cu-0.1Re 솔더의 젖음성이 Sn-0.7wt%Cu-0.01wt%P 솔더보다 우수한 것을 확인할 수 있었다. 또한 희토류 금속의 함량이 증가할수록 솔더의 경도와 인장 강도가 증가하는 경향을 확인할 수 있었다.

• 한국마이크로전자및패키징학회:학술대회논문집
• /
• 한국마이크로전자및패키징학회 2003년도 기술심포지움 논문집
• /
• pp.114-117
• /
• 2003

본 연구에서는 계산을 통해 나온 Sn-Ag-Cu 삼원계 공정점(Sn-3.7Ag-0.9Cu)을 바탕으로 그 근처의 응고경로가 다른 6가지 조성(Sn-4.6Ag-0.4Cu, Sn-4.9Ag-1.0Cu, Sn-3.9Ag-1.3Cu, Sn-2.2Ag-1.2Cu, Sn-2Ag-0.7Cu, Sn-2.7Ag-0.3Cu)에 대한 솔더합금의 미세조직을 관찰하였다. 응고경로는 $L\;\rightarrow\;L+Primary\;\rightarrow\;L+Primary+Secondary\;\rightarrow\;Ternary\;Eutectic+Primary+Secondary$로 되며 6가지 경우를 예상할 수 있다 솔더합금의 미세조직은 느린 냉각으로 인하여 빠른 냉각, 보통 냉각에 비해 상대적으로 커다란 $\beta-Sn$ dendrite를 보였고 $Ag_3Sn,\;Cu_6Sn_5$과는 다르게 $\beta-Sn$는 약 $30^{\circ}C$의 과냉(DSC분석)이 존재하게 되어 Sn-4.6Ag-0.4Cu의 경우에는 $Ag_3Sn$상이, Sn-2.2Ag-1.2Cu의 경우에는 $Cu_6Sn_5$가 과대성장을 하였다. 솔더의 기계적 특성을 살펴보고자 Cu 기판위에서 각 조성의 솔더볼을 솔더링한 후 다양한 냉각 속도를 적용하여 reflow 솔더링을 하고 솔더/기판 접합에 대한 전단 강도 시험을 실시했다. 냉각 속도가 빠를수록 $\beta-Sn$의 dendrite가 미세해져서 높은 전단 강도를 보였고 6가지 조성의 솔더볼중 공정조직 분율이 낮은 Sn-2Ag-0.7Cu 조성의 경우에서 낮은 전단 강도가 나타났다.

• 마이크로전자및패키징학회지
• /
• 제7권3호
• /
• pp.55-61
• /
• 2000

직경 0.3 mm의 Sn-37Pb 및 Sn-3.5Ag-0.7Cu 솔더볼을 솔더링 온도와 기판의 이송속도 (conveyer speed)를 변화시켜 가며 리플로 솔더링 하였다. 리플로 솔더링 온도범위는 Sn-37Pb의 경우 220~$240^{\circ}C$, Sn-3.5Ag-0.7Cu의 경우는 230~ $260^{\circ}C$로 하였다. 실험결과, 전단강도 측면에서 최적 솔더링 조건을 Sn-37Pb의 경우 솔더링 온도 및 컨베이어 속도가 각각 $230^{\circ}C$, 0.7~0.8 m/min이고, Sn-3.5Ag-0.7Cu의 경우 각각 $250^{\circ}C$, 0.6 m/min으로 나타났다. 또한 최고 전단강도 값은 Sn-37Pb의 경우는 555 gf 이고 Sn-3.5Ag-0.7Cu의 경우는 617gf이다. 접합계면의 분석결과 Cu6Sn5층의 두께는 Sn-37Pb의 경우는 1.13~1.45 $\mu\textrm{m}$이고 Sn-3.5Ag-0.7Cu의 경우는 2.5~4.3 $\mu\textrm{m}$이다.

• Journal of Welding and Joining
• /
• 제20권6호
• /
• pp.59-59
• /
• 2002

Sn-Ag-Cu solder is known as most competitive in many kinds of Pb-free solders. In this study, effects of solderability with plated layers such as Cu, Cu/Sn, Cu/Ni and Cu/Ni/Au were investigated. Sn-3.5Ag-0.7Cu solder balls were reflowed in commercial reflow machine (peak temp. : 250℃ and conveyer speed : 0.6m/min). In wetting test, immersion speed was 5mm/sec., immersion time 5sec., immersion depth 4mm and temperature of solder bath was 250℃. Wettability of Sn-3.5Ag-0.7Cu on Cu, Cu/Sn (5㎛), Cu/Ni (5㎛), and Cu/Ni/Au (5㎛/500Å) layers was investigated. Cu/Ni/Au layer had the best wettability as zero cross time and equilibrium force, and the measured values were 0.93 sec and 7mN, respectively. Surface tension of Sn-3.5Ag-0.7Cu solder turmed out to be 0.52N/m. The thickness of IMC is reduced in the order of Cu, Cu/Sn, Cu/Mi and Cu/Ni/Au coated layer. Shear strength of Cu/Ni, Cu/Sn and Cu was around 560gf but Cu/Ni/Au was 370gf.

• Journal of Welding and Joining
• /
• 제20권6호
• /
• pp.783-788
• /
• 2002

Sn-Ag-Cu solder is known as most competitive in many kinds of Pb-free solders. In this study, effects of solderability with plated layers such as Cu, Cu/Sn, Cu/Ni and Cu/Ni/Au were investigated. Sn-3.5Ag-0.7Cu solder balls were reflowed in commercial reflow machine (peak temp.:$250^{\circ}C$and conveyer speed:0.6m/min). In wetting test, immersion speed was 5mm/sec., immersion time 5sec., immersion depth 4mm and temperature of solder bath was $250^{\circ}C$. Wettability of Sn-3.5Ag-0.7Cu on Cu, Cu/Sn ($5\mu\textrm{m}$), Cu/Ni ($5\mu\textrm{m}$), and Cu/Ni/Au ($5\mu\textrm{m}/500{\AA}$) layers was investigated. Cu/Ni/Au layer had the best wettability as zero cross time and equilibrium force, and the measured values were 0.93 sec and 7mN, respectively. Surface tension of Sn-3.5Ag-0.7Cu solder turmed out to be 0.52N/m. The thickness of IMC is reduced in the order of Cu, Cu/Sn, Cu/Mi and Cu/Ni/Au coated layer. Shear strength of Cu/Ni, Cu/Sn and Cu was around 560gf but Cu/Ni/Au was 370gf.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2007년 추계학술발표대회 개요집
• /
• pp.211-214
• /
• 2007

Sn-0.3Ag-0.7Cu 조성의 젖음 특성과 반응 특성을 Sn-1.0Ag-0.5Cu 및 Sn-3.0Ag-0.5Cu 합금의 결과와 비교, 분석하였다. 또한 Sn-0.3Ag-0.7Cu 조성의 용융 및 응고 특성을 DSC로 측정하고, 인장시험을 통한 stress-strain curve를 관찰하였다. 아울러 할로겐 함유량이 많은 플럭스를 사용하여 Sn-0.3Ag-0.7Cu 조성의 젖음 특성을 향상 시킬 수 있는지를 조사하였으며, Sn-0.3Ag-0.7Cu 조성에 미량의 In을 첨가하여 젖음 특성의 개선 정도를 분석하였다. 그 결과 할로겐 함유량이 높은 플럭스를 사용한 경우보다 미량의 In을 첨가한 경우에서 wettability의 향상을 보다 효과적으로 유도할 수 있음을 관찰할 수 있었다.

• 대한금속재료학회지
• /
• 제47권12호
• /
• pp.842-851
• /
• 2009

The long-term reliability of Sn-0.3wt%Ag-0.7wt%Cu solder joints was evaluated and compared with Sn-3.0wt%Ag-0.5wt%Cu under thermal shock conditions. Test vehicles were prepared to use Sn-0.3Ag-0.7Cu and Sn-3.0Ag-0.5Cu solder alloys. To compare the shear strength of the solder joints, 0603, 1005, 1608, 2012, 3216 and 4232 multi-layer ceramic chip capacitors were used. A reflow soldering process was utilized in the preparation of the test vehicles involving a FR-4 material-based printed circuit board (PCB). To compare the shear strength degradation following the thermal shock cycles, a thermal shock test was conducted up to 2,000 cycles at temperatures ranging from $-40^{\circ}C$ to $85^{\circ}C$, with a dwell time of 30 min at each temperature. The shear strength of the solder joints of the chip capacitors was measured at every 500 cycles in each case. The intermetallic compounds (IMCs) of the solder joint interfaces werealso analyzed by scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). The results showed that the reliability of Sn-0.3Ag-0.7Cu solder joints was very close to that of Sn-3.0Ag-0.5Cu. Consequently, it was confirmed that Sn-0.3Ag-0.7Cu solder alloy with a low silver content can be replaced with Sn-3.0Ag-0.5Cu.

• 마이크로전자및패키징학회지
• /
• 제19권2호
• /
• pp.35-39
• /
• 2012

플립칩 접합시 발생하는 계면반응 거동과 접합특성을 계면에 생성되는 금속간화합물의 관점에서 접근하였다. 이를 위하여 Al/Cu와 Al/Ni의 under bump metallization(UBM) 층과 Sn-Cu계 솔더(Sn-3Cu, Sn-0.7Cu)와의 반응에 의한 금속간화합물의 형성거동 및 계면접합성을 분석하였다. Al/Cu UBM 상에서 Sn-0.7Cu 솔더를 리플로우한 경우에는 솔더/UBM 계면에서 금속간화합물이 형성되지 않았으며, Sn-3Cu를 리플로우한 경우에는 계면에서 생성된 $Cu_6Sn_5$ 금속간화합물이 spalling 되어 접합면이 분리되었다. 반면에 Al/Ni UBM 상에서 Sn-Cu계 솔더를 리플로우한 경우에는 0.7 wt% 및 3 wt%의 Cu 함량에 관계없이 $(Cu,Ni)_6Sn_5$ 금속간화합물이 계면에 형성되어 있었으며, 계면접합이 안정적으로 유지되었다.